TECHNICAL FIELD

This invention relates to a dispersant composition, more specifically, relates to a dispersant composition for cement, mortar or concrete.

BACKGROUND ART

Superplasticizers, also known as water reducers, are used as dispersants to avoid particle segregation and to improve the flow characteristics of suspensions such as in concrete applications. Superplasticizers are added to concrete or mortar to reduce the water to cement ratio with no affecting the workability of the mixture. The strength of concrete increases when the water to cement ratio decrease. One important class of superplasticizers is polycarboxylate ether-based superplasticizers (PCEs) which enables good particle dispersion due to their chemical structures i.e. methacrylic acid copolymers as the main chains and methoxy-polyethylene glycol copolymer as the side chains. A low dosage of PCEs leads to a dramatic water reduction. Another important class of superplasticizers are naphthalene sulfonate formaldehyde condensate (BNS) of which the main varieties are beta-naphthalene sulfonate formaldehyde condensate. BNS shows stable performance in various suspensions and working temperatures of enabling a good flowability of the suspensions. Moreover, BNS holds obvious advantages when applied in clay-bearing aggregates. It seems promising to combine PCEs and BNS to reach both advantages of them, however, the mixture of PCEs and BNS leads to a severe thickening of the mixture and the dispersant composition rapidly loose the function of dispersion. Therefore, the most common practice is to store PCEs and BNS separately and use them in different steps.

WO2016158921A1 disclosed a dispersant composition for a hydraulic composition comprising (A) a high-molecular compound having monomer units including a naphthalene ring; (B) a polymer having a weight-average molecular weight of 1,000 to 1,000,000 and having monomer units having an alkyleneoxy group and monomer units having a group selected from a carboxylic acid group, a phosphoric acid group, a group which changes to a carboxylic acid group by hydrolysis, and a group which changes to a phosphoric acid group by hydrolysis; and (C) a specific compound represented by general formulas (C1) through (C4).

[Image Omitted]

R¹¹is a hydrocarbon group that R¹¹—H has an HLB of 5.10 or less; R²¹is a hydrocarbon group that R²¹—H has an HLB of 5.10 or less; R³¹is a hydrocarbon group that R³¹. H has an HLB of 5.10 or less; R⁴¹is a hydrocarbon group that R⁴¹—H has an HLB of 5.10 or less; R²², R³², R³³are independent with each other selected from hydrogen or hydrocarbon group having C1 to C3; Y¹and Y²are independently with each other selected from hydrogen group or —SO₃M and at least one of Y¹and Y²is —SO₃M; M is a counter ion; AO is alkyleneoxy group having C2 to C4; X is —O— or —C(O)O—; n1 is an integer number from 0 to 300; n2 is an integer number from 1 to 300; n3 and n4 are integer number no less than 0 and the sum of n3 and n4 is from 1 to 300; n5 and n6 are integer number no less than 0 and the sum of n3 and n4 is from 1 to 300; Y¹is a hydrogen group when n5 is 0; Y²is a hydrogen group when n6 is 0.

WO2016158921A1 provides a possible solution to the problem that PCEs and BNS are not able to be used simultaneously as superplasticizers, however, in WO2016158921A1 the huge number of the possible Components (C) leads to a latent problem i.e. the dramatic fluctuation in flowability of mortar and in its examples such fluctuation is verified. Moreover, for most examples, only the performance of flowability is tested but the performance compressive strength is not, which leave a potential problem that those Components (C) that improve the flowability of mortar might have negative influence on the compressive strength of mortar. Therefore, it is still not so clear for the skilled persons in the art what types of Components (C) enable to bring good effects to mortar or concrete in all required aspects including flowability and compressive strength.

SUMMARY OF INVENTION

One object of this invention is to provide a dispersant composition comprising: a). at least one polymer constituted of monomers having naphthalene ring and/or melamine; b). at least one polymer having carboxylic acid and/or phosphoric acid group and/or any group that is hydrolyzed into carboxylic or phosphoric; and c). at least one polymer having a structure of Formula I:

[Image Omitted]

R¹is hydrogen or alkyl group having carbon number not less than 1, cycloalkyl or cycloalkenyl group having carbon number not less than 3, alkenyl group having carbon number not less than 2, aryl group having carbon number not less than 6; R²is hydrogen or alkyl group having carbon number from 1 to 3; A is alkylene group having carbon number from 3 or 4; m and n are interger numbers wherein m is more than n and the sum of m and n is more than 9 and less than 12.

Another object of this invention is to provide a use of the dispersant composition in a mortar or concrete, and the weight percentage of the dispersant composition is from 0.01% to 2.5% based on the weight of cement in mortar.

Another object of this invention is to provide an aqueous composition comprising the dispersant composition.

DETAILED DESCRIPTION OF INVENTION
Technical Problem

Different surfactants are added to solve the problem that the dispersant admixtures of Polycarboxylate ether-based superplasticizers (PCEs) and naphthalene sulfonate formaldehyde condensate (BNS) get thickening and finally loose dispersibility in the cement, mortar or concrete. However, many surfactants tend to obviously decrease the compressive strength of the obtained concrete. Since compressive strength is one of the critical mechanical properties of concrete, it is significant to find surfactants that improve the compatibility of PCEs and BNS and increase the compressive strength of the concrete simultaneously.

Technical Solution

To solve the technical problem, it is provided a dispersant composition comprising

a) at least one polymer constituted of monomers having naphthalene ring and/or melamine;

b). at least one polymer having carboxylic acid and/or phosphoric acid group and/or any group that is hydrolyzed into carboxylic or phosphoric; and

c). at least one polymer having a structure of Formula I:

[Image Omitted]

R¹is hydrogen or alkyl group having carbon number not less than 1, cycloalkyl or cycloalkenyl group having carbon number not less than 3, alkenyl group having carbon number not less than 2, aryl group having carbon number not less than 6; R²is hydrogen or alkyl group having carbon number from 1 to 3; A is alkylene group having carbon number from 3 or 4; m and n are interger numbers wherein m is more than n and the sum of m and n is more than 9 and less than 12.

Component a) is naphthalene-based and/or melamine-based dispersant and Component b) is polycarboxylic ether-based and/or phosphoric acid-contained dispersant. When a naphthalene and/or melamine type dispersant and a polycarboxylic and/or phosphoric type dispersant are mixed, the viscosity of the mixture increases quickly and the dispersion performance turns to worse. The reason behind is the naphthalene ring of naphthalene-based dispersant and/or the melamine ring of melamine-based dispersant interacts with the polyalkyleneoxy group of polycarboxylic ether-based dispersant to form the coagulations that have an apparent high molecular weight. Such coagulations decrease the contact surface of dispersant with cement and therefore the dispersion performance gets worse. Component c) is prone to interact with the naphthalene ring of naphthalene-based dispersant and/or melamine ring of melamine-based dispersant and therefore eliminate the interaction of Component a) and Component b). The unentangled Component a) and Component b) absorbs to the surface of cement particles in different forms and therefore the synergistic effects of Component a) and Component b) are fulfilled in the concrete.

Preferably, Component a) is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and/or Formula II-(b):

[Image Omitted]

- R³, R⁴are independently from each other selected from hydrogen, methyl, ethyl, propyl, butyl and hydroxyl group; R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group.
- More preferably, Component a) is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

- R³, R⁴are independently from each other selected from hydrogen, methyl, ethyl, propyl, butyl, hydroxyl group.
- Even more preferably, Component a) is a condensate polymer obtained from the condensation of formaldehyde and one or more selected from naphthalene, methylnaphthalene, ethylnaphthalene, butylnaphthalene, hydroxynaphthalene.
- To reach a good fluidity in the concrete, the weight-average molecular weight of Component a) is from 1,000 to 100,000 and preferably from 2,000 to 50,000 and even more preferably from 5,000 to 30,000.
- Preferably, Component b) is a copolymer of the structure of Formula III and one or more selected from the structure of Formula IV-(a) and Formula IV-(b), and/or a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

- R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶, R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group; R⁹, R¹⁹are independently from each other selected from hydrogen and alkyl group having carbon number from 1 to 30; R¹³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine; R²⁰and R²¹, are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4; A is alkylene group having carbon number from 2 to 18; x is an integer number from 0 to 2; y is an integer number from 0 to 1; h is selected from an integer number from 1 to 3; z and j are independently from each other selected from an integer number from 1 to 500.
- More preferably, Component b) is a copolymer of the structure of Formula III and one or more selected from the structure of Formula IV-(a) and Formula IV-(b), and/or a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

- R⁷, R⁸, R¹⁰, R¹¹, R¹², R⁵, R¹⁶, R¹⁸, R²²are independently from each other selected from hydrogen and methyl group; R⁹, R¹⁹are independently from each other selected from hydrogen and alkyl group having carbon number from 1 to 30; R¹³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine; R²⁰and R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4; A is alkylene group having carbon number from 2 to 4; x is an integer number from 0 to 2; y is an integer number from 0 to 1; h is selected from an integer number from 1 to 3; z and j are independently from each other selected from an integer number from 1 to 250.
- To reach a good fluidity in the concrete, the weight-average molecular weight of Component b) is from 1,000 to 500,000 and preferably from 5,000 to 200,000 and even more preferably from 10,000 to 100,000.
- The ratio by weight of said Component a) to Component b) is preferably from 1: 10 to 10:1 and more preferably from 1:3 to 3:1 and most preferably from 1:2 to 2:1.
- Component c) is added into the mixture of Component a) and Component b) to stabilize the mixture and avoid thickening of the dispersant. Preferably, Component c) is the structure of Formula I:

[Image Omitted]

- R¹is hydrogen or alky group having carbon number not less than 1 and no more than 34, cycloalkyl or cycloalkenyl group having carbon number not less than 3 and no more than 8, alkenyl group having carbon number not less than 2 and no more than 18, aryl group having carbon number not less than 6; R²is hydrogen or alky group having carbon number from 1 to 3; A is alkylene group having carbon number from 3 or 4; m is an integer number selected from 5 to 11 and n is an integer number selected from 1 to 7, wherein m is more than n and the sum of m and n is more than 9 and less than 12.

More preferably, Component c) is a mixture of at least one selected from Group I consist of polyoxyalkylene [polyoxyethylene(5) polyoxybuthylene(4)] nonyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(3)] nonyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(2)] nonyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(1)] nonyl ether, polyoxyalkylene [polyoxyethylene(5) polyoxybuthylene(4)] decyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(3)] decyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(2)] decyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(1)] decyl ether, polyoxyalkylene [polyoxyethylene(5) polyoxybuthylene(4)] undecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(3)] undecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(2)] undecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(1)] undecyl ether, polyoxyalkylene [polyoxyethylene(5) polyoxybuthylene(4)] tridecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(3)] tridecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(2)] tridecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(1)] tridecyl ether, polyoxyalkylene [polyoxyethylene(5) polyoxybuthylene(4)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(3)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(2)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(1)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(5)polyoxypropylene(4)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(6)polyoxypropylene(3)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(7)polyoxypropylene(2)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(8)polyoxypropylene(1)] 2-propylheptanol ether; and at least one selected from Group II consist of polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] nonyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] nonyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] nonyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] nonyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] nonyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] nonyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] nonyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] nonyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] nonyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] decyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] decyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] decyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] decyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] decyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] decyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] decyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] decyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] decyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] undecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] undecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] undecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] undecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] undecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] undecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] undecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] undecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] undecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] tridecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] tridecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] tridecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] tridecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] tridecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] tridecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] tridecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] tridecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] tridecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] pentadecyl ether, polyoxyakylene [polyoxyethylene(9) polyoxybuthylene(1)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(6)polyoxypropylene(4)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(7)polyoxypropylene(3)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(8)polyoxypropylene(2)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(9)polyoxypropylene(1)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(6)polyoxypropylene(5)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(7)polyoxypropylene(4)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(8)polyoxypropylene(3)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(9)polyoxypropylene(2)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(10)polyoxypropylene(1)] 2-propylheptanol ether and Group III consist of polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(5)] nonyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(4)] nonyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(3)] nonyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(2)] nonyl ether, polyoxyalkylene [polyoxyethylene(11) polyoxybuthylene(1)] nonyl ether, polyoxyalkylene [polyoxyethylene(7) poyoxybuthylene(5)] decyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(4)] decyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(3)] decyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(2)] decyl ether, polyoxyalkylene [polyoxyethylene(11) polyoxybuthylene(1)] decyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(5)] undecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(4)] undecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(3)] undecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(2)] undecyl ether, polyoxyalkylene [polyoxyethylene(11) polyoxybuthylene(1)] undecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(5)] tridecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(4)] tridecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(3)] tridecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(2)] tridecyl ether, polyoxyalkylene [polyoxyethylene(11) polyoxybuthylene(1)] tridecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(5)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(4)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(3)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(2)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(11) polyoxybuthylene(1)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(7)polyoxypropylene(5)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(8)polyoxypropylene(4)] 2-propylheptanol jhk'ether polyoxyalkylene [polyoxyethylene(9)polyoxypropylene(3)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(10)polyoxypropylene(2)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(11)polyoxypropylene(1)] 2-propylheptanol ether.

More preferably, Component c) is a mixture of at least one selected from Group III consist of polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(5)] nonyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(4)] nonyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(3)] nonyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(2)] nonyl ether, polyoxyalkylene [polyoxyethylene(11) polyoxybuthylene(1)] nonyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(5)] decyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(4)] decyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(3)] decyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(2)] decyl ether, polyoxyalkylene [polyoxyethylene(11) polyoxybuthylene(1)] decyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(5)] undecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(4)] undecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(3)] undecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(2)] undecyl ether, polyoxyalkylene [polyoxyethylene(11) polyoxybuthylene(1)] undecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(5)] tridecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(4)] tridecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(3)] tridecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(2)] tridecyl ether, polyoxyalkylene [polyoxyethylene(11) polyoxybuthylene(1)] tridecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(5)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(4)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(3)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(2)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(11) polyoxybuthylene(1)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(7)polyoxypropylene(5)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(8)polyoxypropylene(4)] 2-propylheptanol jhk'ether polyoxyalkylene [polyoxyethylene(9)polyoxypropylene(3)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(10)polyoxypropylene(2)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(11)polyoxypropylene(1)] 2-propylheptanol ether; and at least one selected from Group I consist of polyoxyalkylene [polyoxyethylene(5) polyoxybuthylene(4)] nonyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(3)] nonyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(2)] nonyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(1)] nonyl ether, polyoxyalkylene [polyoxyethylene(5) polyoxybuthylene(4)] decyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(3)] decyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(2)] decyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(1)] decyl ether, polyoxyalkylene [polyoxyethylene(5) polyoxybuthylene(4)]undecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(3)] undecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(2)] undecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(1)] undecyl ether, polyoxyalkylene [polyoxyethylene(5) polyoxybuthylene(4)] tridecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(3)] tridecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(2)] tridecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(1)] tridecyl ether, polyoxyalkylene [polyoxyethylene(5) polyoxybuthylene(4)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(3)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(2)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(1)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(5)polyoxypropylene(4)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(6)polyoxypropylene(3)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(7)polyoxypropylene(2)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(8)polyoxypropylene(1)] 2-propylheptanol ether and Group II consist of polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] nonyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] nonyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] nonyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] nonyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] nonyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] nonyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] nonyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] nonyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] nonyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] decyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] decyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] decyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] decyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] decyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] decyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] decyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] decyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] decyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] undecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] undecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] undecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] undecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] undecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] undecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] undecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] undecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] undecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] tridecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] tridecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] tridecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] tridecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] tridecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] tridecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] tridecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] tridecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] tridecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(6)polyoxypropylene(4)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(7)polyoxypropylene(3)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(8)polyoxypropylene(2)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(9)polyoxypropylene(1)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(6)polyoxypropylene(5)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(7)polyoxypropylene(4)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(8)polyoxypropylene(3)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(9)polyoxypropylene(2)] 2-propylheptanol ether, polyoxyalkylene (polyoxyethylene(10)polyoxypropylene(1)] 2-propylheptanol ether.

More preferably, Component c) is at least one selected from Group II consist of polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] nonyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] nonyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] nonyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] nonyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] nonyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] nonyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] nonyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] nonyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] nonyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] decyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] decyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] decyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] decyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] decyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] decyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] decyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] decyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] decyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] undecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] undecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] undecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] undecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] undecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] undecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] undecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] undecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] undecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] tridecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] tridecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] tridecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] tridecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] tridecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] tridecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] tridecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] tridecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] tridecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(4)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(3)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(2)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(1)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(6) polyoxybuthylene(5)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(7) polyoxybuthylene(4)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(8) polyoxybuthylene(3)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(9) polyoxybuthylene(2)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(10) polyoxybuthylene(1)] pentadecyl ether, polyoxyalkylene [polyoxyethylene(6)polyoxypropylene(4)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(7)polyoxypropylene(3)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(8)polyoxypropylene(2)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(9)polyoxypropylene(1)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(6)polyoxypropylene(5)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(7)polyoxypropylene(4)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(8)polyoxypropylene(3)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(9)polyoxypropylene(2)] 2-propylheptanol ether, polyoxyalkylene [polyoxyethylene(10)polyoxypropylene(1)] 2-propylheptanol ether.

The ratio by weight of said Component c) to the sum of Component a) and b) is preferably from 1:100 to 1:5 and preferably from 1:50 to 1:6.

The dispersant composition comprising Component a), b) and c) is preferably used in the mortar or concrete as the superplasticizer. When it is used, the weight percentage of said composition is preferably from 0.01% to 2.5% based on the weight of cement in mortar. The dispersant composition is preferably dissolved in water to get an aqueous composition that is added into the mortar or concrete with the ratio by weight of the composition and water from 1:10 to 1:1 and preferably from 1:6 to 1:1.5.

High air content in the mortar leads to a good flowability but tends to decrease the compressive strength of the cured concrete. The Component c) of this invention solved this problem and the concrete added with the dispersant composition shows excellent flowability, workability as well as high compressive strength. The outstanding compressive strength is correlated with the low air content in the concrete.

Embodiment

The 1^stembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³, R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹²are independently from each other selected from hydrogen, methyl and ethyl group, R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2, y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 2^ndembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³, R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹²are independently from each other selected from hydrogen, methyl and ethyl group, R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2, y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 3^rdembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³, R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹²are independently from each other selected from hydrogen, methyl and ethyl group, R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2, y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 4^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³, R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group, R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2, y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 5^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³, R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group, R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2, y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 6^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³, R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group, R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2, y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 7^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³, R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula II and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³, R¹and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an Integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 8^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³, R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 9^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³, R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³, R⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 10^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³, R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 11^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³, R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 12^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³, R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 13^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹²are independently from each other selected from hydrogen, methyl and ethyl group, R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2, y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 14^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹²are independently from each other selected from hydrogen, methyl and ethyl group, R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2, y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group II and at least one selected from Group I and Group II.

The 15^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹²are independently from each other selected from hydrogen, methyl and ethyl group, R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2, y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 16^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 17^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group II and at least one selected from Group I and Group II.

The 18^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 19^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹²are independently from each other selected from hydrogen, methyl and ethyl group, R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2, y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 20^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹²are independently from each other selected from hydrogen, methyl and ethyl group, R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2, y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 21^stembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹²are independently from each other selected from hydrogen, methyl and ethyl group, R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2, y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 22^ndembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group I and Group III.

The 23^rdembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 24^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 25^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 26^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 27^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; Component b) that is a copolymer of the structure of Formula II and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 28^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 29^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 30^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 31^stembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁵are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 32^ndembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 33^rdembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 34^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁸are independently from each other selected from hydrogen, methyl an ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 35^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 36^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 37^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³and R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a mixture of a copolymer of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 38^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³and R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a mixture of a copolymer of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 39^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³and R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a mixture of a copolymer of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 40^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³and R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a mixture of a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 41^stembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³and R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 42^ndembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³and R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) is at least one selected from Group II.

The 43^rdembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³and R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 44^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³and R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 4^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a):

[Image Omitted]

R³and R⁴are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) is at least one selected from Group II.

The 46^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a mixture of a copolymer of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 47^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a mixture of a copolymer of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 48^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a mixture of a copolymer of Formula II and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl an ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 49^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 50^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methy and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 51^stembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 52^ndembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 53^rdembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 54^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(b):

[Image Omitted]

R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 55^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁵are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a mixture of a copolymer of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 56^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a mixture of a copolymer of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 57^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a mixture of a copolymer of Formula III and Formula IV-(a):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R³is selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) that is at least one selected from Group II.

The 58^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 59th embodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) is a mixture that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 60^thembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) is at least one selected from Group II.

The 61^stembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) is a mixture that is a mixture of at least one selected from Group I and at least one selected from Group II and Group III.

The 62^ndembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁵are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁸, R¹⁰, R¹¹, R¹², R⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R³, R¹³and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) is a mixture that is a mixture of at least one selected from Group III and at least one selected from Group I and Group II.

The 63^rdembodiment is the dispersant composition comprising Component a) that is a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula II-(a) and Formula II-(b):

[Image Omitted]

R³, R⁴, R⁵, R⁶are independently from each other selected from hydrogen, methyl and ethyl group; and Component b) that is a copolymer of the structure of Formula III and Formula IV-(a) and IV-(b):

[Image Omitted]

R⁷, R⁶, R¹⁰, R¹¹, R¹², R¹⁵, R¹⁶are independently from each other selected from hydrogen, methyl and ethyl group; R⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R¹³, R¹⁴and R¹⁷are independently from each other selected from hydrogen, methyl, ethyl, hydroxy propyl, alkaline metal, alkaline earth metal, ammonium and amine, A is alkylene group having carbon number from 2 to 18, x is an integer number from 0 to 2; y is an integer number from 0 to 1, z is selected from an integer number from 1 to 500 and a condensate polymer obtained from the condensation of formaldehyde with the structure of Formula V and Formula VI:

[Image Omitted]

R¹⁸, R²²are independently from each other selected from hydrogen, methyl and ethyl group, R¹⁹is selected from hydrogen and alkyl group having carbon number from 1 to 30, R²⁰, R²¹are independently from each other selected from hydrogen, alkyl group having carbon number from 1 to 4, A is alkylene group having carbon number from 2 to 18, h is selected from an integer number from 1 to 3, j is selected from an integer number from 1 to 500; and Component c) is at least one selected from Group II.

Example

Below examples are used to further illustrate the invention without limitation on the claimed protective scope.

The dispersant composition comprising Component a), b) and c) is mixed with water and the resultant mixture is added into concrete to test its performances of initial slump, flowability and compressive strength.

As an example, the samples of the dispersant aqueous solution are prepared as follows: 500 g of the aqueous solution of Component a) with the solid content of 40% by weight, 200 g of the aqueous solution of Component b) with the solid content of 50% by weight and 10 g of Component c) are mixed and further add water to obtain a mixture of 1000 g in total.

As an example, 400 g of cement, 813 g of sand, 961 g of stone and 180 g of water are mixed to obtain 1 m³of concrete.

The mixture of water and the dispersant composition is added into the concrete by stirring and the resultant concrete is ready for initial slump and flowability test according to EN 12350-2 and air content test according to EN 12350-7. Specimens of the resultant concrete are cured according to EN 12390-2 and the resultant cured speciments are ready for compressive strength test according to EN 12390-3.

Table 1 list samples and comparative samples of preparing the mixture of water of the dispersant composition.

Table 2 list the test results of concrete flowability, concrete initial slump, air content of concrete as well as the compressive strength of the cured concrete with addition of samples list in Table 1. Examples 0, 1, 2, C1, C2 correspond to performance tests of mortar and concrete with addition of Samples 0, 1, 2 and comparative samples 1 and 2.

TABLE 1

Sample of Dispersant

Composition
Component a)
Component b)
Component c)
Water

Sample 0
100 g
50 g
/
350 g

Sodium salt of
Polycarboxylate

beta-naphthalene
Ether

sulfonic acid

formaldehyde

condensate

Sample 1
100 g Sodium salt of beta-naphthalene sulfonic acid formaldehyde condensate
50 g Polycarboxylate Ether

[Image Omitted]

350 g

Comparative Sample 1
100 g Sodium salt of beta-naphthalene sulfonic acid formaldehyde condensate
50 g Polycarboxylate Ether

[Image Omitted]

350 g

Sample 2
100 g Sodium salt of beta-naphthalene sulfonic acid formaldehyde condensate
50 g Polycarboxylate Ether

[Image Omitted]

350 g

Comparative Sample 2
100 g Sodium salt of beta-naphthalene sulfonic acid formaldehyde condensate
50 g Polycarboxylate Ether

[Image Omitted]

350 g

TABLE 2

Intitial
Air
Compressive Strength

Flowability
Slump
content
(MPa)

Example
(cm)
(cm)
(%)
3 days
7 days
28 days

0
41
20.0
2.7
36.9
43.3
47.6

1
46
22.0
2.1
39.6
45.2
53.5

C1
47
22.5
4.5
27.8
34.4
37.1

2
47
23
2.1
39.1
44.1
53.3

C2
57
24.5
4.5
32.5
36.7
40.7