This application is a continuation application claiming priority under 35 U.S.C. Â§120 to co-pending U.S. patent application Ser. No. 13/681,445, filed Nov. 20, 2012, which in turn is a continuation application claiming priority under 35 U.S.C. Â§120 to U.S. patent application Ser. No. 12/610,577, issued as U.S. Pat. No. 8,337,749, which in turn claims priority under 35 U.S.C. Â§120 as a continuation-in-part of U.S. patent application Ser. No. 12/034,183, issued as U.S. Pat. No. 8,337,748, and which in turn claims priority to U.S. Provisional Patent Application Ser. No. 61/015,264, filed Dec. 20, 2007.

BACKGROUND

1. Field of Technology

The present disclosure relates to an austenitic stainless steel. In particular, the present disclosure relates to a cost-effective stabilized austenitic stainless steel composition including, inter alia, a low Ni level, no more than an incidental level of Mo, high yield strength, and at least comparable corrosion resistance and high temperature properties relative to certain higher Ni austenitic alloys such as, for example, T-321 alloy (UNS S32100).

2. Description of the Background of the Technology

Austenitic stainless steels exhibit a combination of highly desirable properties that make them useful for a wide variety of industrial applications. These steels possess a base composition of Fe that is balanced by the addition of austenite-promoting and stabilizing elements, such as Ni, Mn, and N, to allow additions of ferrite-promoting elements, such as Cr and Mo, which enhance corrosion resistance, to be made while maintaining an austenitic structure at room temperature. The austenitic structure provides the steel with highly desirable mechanical properties, particularly toughness, ductility, and formability.

A specific example of an austenitic stainless steel is AISI Type 316 stainless steel (UNS S31600), which is a 16-18% Cr, 10-14% Ni, and 2-3% Mo-containing alloy. The ranges of alloying ingredients in this alloy are maintained within the ranges specified in order to maintain a stable austenitic structure. As is understood by one skilled in the art, Ni, Mn, Cu, and N contents, for example, contribute to the stability of the austenitic structure. However, the rising costs of Ni and Mo have created the need for cost-effective alternatives to S31600 which still exhibit high corrosion resistance and good formability.

Another alloy alternative is Grade 216 (UNS S21600), which is described in U.S. Pat. No. 3,171,738. S21600 contains 17.5-22% Cr, 5-7% Ni, 7.5-9% Mn, and 2-3% Mo. Although S21600 is a lower Ni, higher Mn variant of S31600, the strength and corrosion resistance properties of S21600 are much higher than those of S31600. However, as with the duplex alloys, the formability of S21600 is not as good as that of S31600. Also, because S21600 contains the same amount of Mo as does S31600, there is no cost savings for Mo.

A variant of S31600 also exists which is primarily intended for use at high temperatures. This alloy is designated as Type 316Ti (UNS S31635). The significant difference between S31600 and S31635 is the presence of a small addition of titanium balanced to the amount of C and N present in the steel. The resulting steel, S31635, is less prone to the deleterious formation of Cr carbides at elevated temperatures and during welding, a phenomenon known as sensitization. Such additions can also enhance elevated temperature properties due to the strengthening effects of primary and secondary carbide formation. The specified range for titanium in S31635 is given by the following equation:

[5Ã—(% C+% N)]â‰¦Tiâ‰¦0.70%.

However, S31635 uses costly raw material.

Another example of an austenitic stainless steel is Type 321 stainless steel (UNS S32100), which includes, in weight percentages, 17.00-19.00% Cr, 9.00-12.00% Ni, up to 2.00% Mn, up to 0.08% C, up to 0.75% Si, [5Ã—(% C+% N)]â‰¦Tâ‰¦0.70%, up to 0.045% P, up to 0.030% S, up to 0.10% N, and balance Fe. Type 321 alloy is stabilized against Cr carbide formation by the addition of titanium balanced to the amount of C and N present in the steel. Although Type 321 alloy does not include an intentional addition of Mo, it does include a significant level of costly alloying elements.

Other examples of alloys include numerous stainless steels in which Ni is replaced with Mn to maintain an austenitic structure, such as is practiced with Type 201 steel (UNS S20100) and similar grades. However, a need remains for a corrosion resistant, lower cost alternative to relatively highly alloyed austenitic stainless steels such as Type 321 alloy and that provides at least comparable strength and hardness properties to Type 321 alloy.

SUMMARY

Accordingly, the alloy according to the present disclosure provides a solution that is not currently available in the marketplace, which is a stabilized austenitic stainless steel alloy composition exhibiting at least comparable corrosion resistance, strength, and hardness properties relative to Type 321 austenitic stainless steel, while providing a significant raw material cost savings relative to Type 321 alloy. Accordingly, the present alloy is a stabilized austenitic stainless steel that includes controlled levels of carbide-forming elements to improve corrosion resistance and elevated temperature properties. The present alloy also includes combined levels of Mn, Cu, and N sufficient to provide an alloy exhibiting certain properties at least similar to those of higher Ni alloys, but at a significantly lower raw material cost.

The alloy according to the present disclosure is an austenitic stainless steel that uses a combination of Mn, Cu, and N as substitutes for the more costly element Ni. The result is an alloy having lower cost and at least comparable formability, corrosion resistance, and elevated temperature strength properties relative to, for example, Type 321. Embodiments of the alloy according to the present disclosure may be fabricated to light gauge, and include a clean microstructure with relatively fine grains to enhance formability.

An embodiment of the alloy according to the present disclosure is directed to an austenitic stainless steel including, in weight percentages, up to 0.20 carbon (C), 2.0 to 9.0 manganese (Mn), up to 2.0 silicon (Si), 15.0 to 23.0 chromium (Cr), 1.0 to 9.5 nickel (Ni), up to 3.0 molybdenum (Mo), up to 3.0 copper (Cu), 0.05 to 0.35 nitrogen (N), (7.5(% C))â‰¦(% niobium+% titanium+% vanadium+% tantalum+% zirconium)â‰¦1.5, iron (Fe), and incidental impurities. Certain embodiments of the austenitic stainless steel may include up to 0.01% boron (B). Certain embodiments may include at least 0.1% niobium, or may include niobium in a concentration of at least (7.5(% C)).

Another embodiment according to the present disclosure is directed to an austenitic stainless steel, comprising, in weight percentages, up to 0.10 C, 2.0 to 8.0 Mn, up to 1.00 Si, 16.0 to 22.0 Cr, 1.0 to 7.0 Ni, 0.10 to 2.0 Mo, up to 1.00 Cu, 0.08 to 0.30 N, (7.5(% C))â‰¦(% niobium+% titanium+% vanadium+% tantalum+% zirconium)â‰¦1.5, up to 0.040 phosphorus (P), up to 0.030 sulfur (S), Fe, and incidental impurities. Certain embodiments of the austenitic stainless steel may include up to 0.01% B. Certain embodiments may include at least 0.1% niobium, or may include niobium in a concentration of at least (7.5(% C)).

An alternative embodiment according to the present disclosure is directed to an austenitic stainless steel comprising, in weight percentages, up to 0.08 C, 3.5 to 6.5 Mn, up to 1.00 Si, 17.0 to 21.0 Cr, 3.0 to 6.0 Ni, 0.1 to 1.0 Mo, up to 1.0 Cu, 0.08 to 0.30 N, (7.5(% C))â‰¦(% niobium+% titanium+% vanadium+% tantalum+% zirconium)â‰¦1.0, up to 0.035 P, up to 0.005 S, Fe, and incidental impurities. Certain embodiments of the austenitic stainless steel may include up to 0.01% B. Certain embodiments may include at least 0.1% niobium, or may include niobium in a concentration of at least (7.5(% C)).

In certain embodiments, the austenitic stainless steel according to the present disclosure has one or more of a PRE_Nvalue greater than 18, a ferrite number less than 12, and an MD₃₀value of less than 34Â° C.

One method of producing an austenitic stainless steel according to the present disclosure is by melting a charge in an electric arc furnace, refining in an AOD, casting into ingots or continuously cast slabs, reheating the ingots or slabs and hot rolling them to produce plates or coils, cold rolling coils to a specified thickness, and annealing and pickling the material. Other methods of producing the invented material may also be used, including melting and/or re-melting in a vacuum or under a special atmosphere, casting into shapes, or the production of a powder that is consolidated into slabs or shapes.

An austenitic stainless steel according to the present disclosure may be used in numerous applications. According to one example, alloys of the present disclosure may be included in articles of manufacture adapted for use in low temperature or cryogenic environments. Additional non-limiting examples of articles of manufacture that may be fabricated from or include the present alloy are flexible connectors for automotive and other applications, bellows, flexible pipe, chimney liners, and flue liners.

DETAILED DESCRIPTION

In the present description, other than in the operating examples or where otherwise indicated, all numbers expressing quantities or characteristics of ingredients and products, processing conditions, and the like are to be understood as being modified in all instances by the term â€œaboutâ€ . Accordingly, unless indicated to the contrary, any numerical parameters set forth in the following description are approximations that may vary depending upon the desired properties one seeks to obtain in the product and methods according to the present disclosure. At the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques. All numerical ranges stated herein include all sub-ranges subsumed therein. For example, a range of â€œ1 to 10â€ is intended to include all sub-ranges between and including the recited minimum value of 1 and the recited maximum value of 10.

Embodiments of the austenitic stainless steel according to the present disclosure will now be described in detail. In the following description, â€œ%â€ or â€œpercentâ€ refer to weight percentages, unless otherwise specified. The present disclosure is directed to an austenitic stainless steel exhibiting at least comparable corrosion resistance, elevated temperature strength properties, and formability relative to Type 321 alloy, and at lower overall cost of raw materials. The austenitic stainless steel composition may include, in weight percentages, up to 0.20 C, 2.0 to 9.0 Mn, up to 2.0 Si, 15.0 to 23.0 Cr, 1.0 to 9.5 Ni, up to 3.0 Mo, up to 3.0 Cu, 0.05 to 0.35 N, (7.5(% C))â‰¦(% niobium+% titanium+% vanadium+% tantalum+% zirconium)â‰¦1.5, Fe, and incidental impurities. Certain embodiments of the austenitic stainless steel may include up to 0.01 B. Certain embodiments of the austenitic stainless steel may include at least 0.1% niobium, or may include niobium in a concentration of at least (7.5(% C)).

Another embodiment of the invention is an austenitic stainless steel, including, in weight %, up to 0.10 C, 2.0 to 8.0 Mn, up to 1.00 Si, 16.0 to 22.0 Cr, 1.0 to 7.0 Ni, 0.10 to 2.0 Mo, up to 1.00 Cu, 0.08 to 0.30 N, (7.5(% C))â‰¦(% niobium+% titanium+% vanadium+% tantalum+% zirconium)â‰¦1.5, up to 0.040 P, up to 0.030 Si, Fe, and incidental impurities. Certain embodiments of the austenitic stainless steel may include up to 0.01 B. Certain embodiments of the austenitic stainless steel may include at least 0.1% niobium, or may include niobium in a concentration of at least (7.5(% C)).

According to an alternative embodiment, the present disclosure is directed to an austenitic stainless steel including, in weight percentages, up to 0.08 C, 3.5 to 6.5 Mn, up to 1.00 Si, 17.0 to 21.0 Cr, 3.0 to 6.0 Ni, 0.5 to 1.0 Mo, up to 1.0 Cu, 0.08 to 0.30 N, (7.5(% C))â‰¦(% niobium+% titanium+% vanadium+% tantalum+% zirconium)â‰¦1.0, up to 0.035 P, up to 0.005 S, Fe, and incidental impurities. Certain embodiments of the austenitic stainless steel may include up to 0.01 B. Certain embodiments of the austenitic stainless steel may include at least 0.1% niobium, or may include niobium in a concentration of at least (7.5(% C)).

C: Up to 0.20%

C acts to stabilize the austenite phase and inhibits the deformation-induced martensitic transformation. However, C also increases the probability of forming Cr carbides, especially during welding, which reduces corrosion resistance and toughness. Accordingly, the austenitic stainless steel of the present invention has up to 0.20% C. In an embodiment of the invention, the content of C may be 0.10% or less. Alternatively, the content of C may be 0.08% or less, 0.03% or less, or 0.02% or less.

Si: Up to 2.0%

Having greater than 2% Si promotes the formation of embrittling phases, such as sigma, and reduces the solubility of N in the alloy. Si also stabilizes the ferritic phase, and greater than 2% Si requires additional austenite stabilizers to maintain the austenitic phase. Accordingly, in certain embodiments the austenitic stainless steel of the present invention has up to 2.0% Si. In an embodiment of the invention, the Si content may be 1.0% or less. Si helps to minimize the reactivity of certain alloying elements with niobium and assists with phase balance in the alloy. In certain embodiments according to the present disclosure, the effects of Si addition are balanced by adjusting the Si content to 0.5-1.0%. In other embodiments, the effects of Si addition are balanced by adjusting the Si content to 0.1-0.4%. Alternatively, in certain embodiments according to the present disclosure the Si content may be 0.5% or less, 0.4% or less, or 0.3% or less.

Mn: 2.0-9.0%

Mn stabilizes the austenitic phase and generally increases the solubility of N, a beneficial alloying element. To sufficiently produce these effects, a Mn content of not less than 2.0% is required. Both Mn and N are effective substitutes for the more expensive element, Ni. However, having greater than 9.0% Mn degrades the material's workability and its corrosion resistance in certain environments. Also, because of the difficulty in decarburizing stainless steels with high levels of Mn, such as greater than 9.0%, high Mn levels significantly increase the processing costs of manufacturing the material. Accordingly, in order to properly balance the corrosion resistance, phase balance, ductility and other mechanical properties in the austenitic stainless steel of the present invention, the Mn level is set at 2.0-9.0%. In certain embodiments according to the present disclosure, the Mn content may be 2.0-8.0%, 3.5-7.0%, or 7%.

Ni: 1.0-9.5%

The present inventors sought to limit the Ni content of the alloy while maintaining acceptable properties. At least 1% Ni is required to stabilize the austenitic phase with respect to both ferrite and martensite formation. Ni also acts to enhance toughness and formability. However, due to the relatively high cost of Ni, it is desirable to keep the Ni content as low as possible. Although Mn and N may be partial substitutes for Ni, high levels of Mn and N will result in unacceptable levels of work hardening, reducing formability. Therefore, the alloy must include a minimum concentration of Ni to provide for acceptable formability. The inventors have found that 1.0-9.5% range of Ni can be used in addition to the other defined ranges of elements to achieve an alloy having corrosion resistance and formability as good as or better than those of higher Ni alloys. Accordingly, the austenitic stainless steel of the present invention has 1.0-9.5% nickel. In an embodiment, the Ni content may be 2.0-6.5%, or may be 3.0-6.0%.

Cr: 15.0-23.0%

Cr is added to impart corrosion resistance to stainless steels by forming a passive film on the alloy surface. Cr also acts to stabilize the austenitic phase with respect to martensitic transformation. At least 15% Cr is required to provide adequate corrosion resistance. On the other hand, because Cr is a powerful ferrite stabilizer, a Cr content exceeding 23% requires the addition of more costly alloying elements, such as Ni or cobalt, to keep the ferrite content acceptably low. Having more than 23% Cr also makes the formation of undesirable phases, such as sigma, more likely. Accordingly, the austenitic stainless steel of the present invention has 15.0-23.0% Cr. In an embodiment, the Cr content may be 16.0-22.0%, or alternatively may be 17.0-21.0%.

N: 0.05-0.35%

N is included in the present alloy as a partial replacement for the austenite stabilizing element Ni and the corrosion resistance enhancing element Mo. N also improves alloy strength. At least 0.05% N is necessary for strength and corrosion resistance and to stabilize the austenitic phase. The addition of more than 0.35% N may exceed the solubility of N during melting and welding, which results in porosity due to N gas bubbles. Even if the solubility limit is not exceeded, a N content of greater than 0.35% increases the propensity for the precipitation of nitride particles, which degrades corrosion resistance and toughness. The present inventors have determined that a N content up to 0.35% is compatible with the possible Nb levels in the alloy, without the formation of a problematic level of niobium carbonitride precipitates. Accordingly, the austenitic stainless steel of the present invention has 0.05-0.35% N. In an embodiment, the N content may be 0.08-0.30%, or alternatively may be 0.05-0.2%.

Mo: Up to 3.0%

The present inventors sought to limit the Mo content of the alloy while maintaining acceptable properties. Mo is effective in stabilizing the passive oxide film that forms on the surface of stainless steels and protects against pitting corrosion by the action of chlorides. In certain embodiments, the Mo content may be 0.1-3.0%, which is adequate to provide the required corrosion resistance in combination with the proper amounts of Cr and N. A Mo content exceeding 3.0% causes deterioration of hot workability by increasing the fraction of ferrite to potentially detrimental levels. High Mo content also increases the likelihood of forming deleterious intermetallic phases, such as sigma phase. In addition, Mo is an expensive alloying element. Accordingly, the austenitic stainless steel composition of the present invention has up to 3.0% Mo. In certain embodiments according to the present disclosure, the alloy includes no intentional addition of Mo. In other embodiments, the Mo content may be 0.1-1.0%, or may be 0.5-1.0%.

B: Up to 0.01%

Additions as low as 0.0005% B optionally may be added to the alloy of the present disclosure to improve the hot workability and surface quality of stainless steels. However, additions of more than 0.01% B degrade the corrosion resistance and workability of the alloy. Accordingly, certain embodiments of an austenitic stainless steel composition according to the present disclosure may include up to 0.01% B. In an embodiment, the B content may be up to 0.008%, or may be up to 0.005%. In another embodiment, the B content may be 0.001-0.003%

Cu: Up to 3.0%

Cu is an austenite stabilizer and may be used to replace a portion of the Ni in this alloy. It also improves corrosion resistance in reducing environments and improves formability by reducing the stacking fault energy. However, additions of more than 3% Cu have been shown to reduce the hot workability of austenitic stainless steels. Accordingly, the austenitic stainless steel composition of the present invention has up to 3.0% Cu. In an embodiment, Cu content may be up to 1.0%. In another embodiment, Cu content may be 0.4-0.8%.

W: Up to 4.0%

W provides a similar effect to that of molybdenum in improving resistance to chloride pitting and crevice corrosion. W may also reduce tendency for sigma phase formation when substituted for molybdenum. However, additions of more than 4% may reduce the hot workability of the alloy. Accordingly, the austenitic stainless steel composition of the present invention has up to 4.0% W. In an embodiment, W content may be 0.05-0.60%.

1.05â‰¦(Ni+Co)â‰¦9.5

Nickel and cobalt both act to stabilize the austenitic phase with respect to ferrite formation. At least 1% (Ni+Co) is required to stabilize the austenitic phase in the presence of ferrite stabilizing elements such as Cr and Mo, which must be added to ensure proper corrosion resistance. However, both Ni and Co are costly elements, so it is desirable to keep the (Ni+Co) content less than 9.5%. In an embodiment, the (Ni+Co) content may be greater than 4.0% but less than 7.5%.

(7.5(% C))â‰¦(% Nb+% Ti+% V+% Ta+% Zr)â‰¦1.5

Niobium (Nb) reacts with C, and to a lesser extent N, to form carbides and carbonitrides in the form of small particles. These particles effectively prevent the formation of deleterious chromium carbides during elevated temperature service and during welding, which improves corrosion resistance. These particles, when produced using an effective heat treatment, can also improve elevated temperature strength and creep resistance. A minimum addition of (7.5Ã—% C) provides for one atom of Nb for every one atom of C present dissolved in the metal. Higher levels of Nb will consume beneficial N, so it is desirable to keep the Nb content less than 1.5%. Other elements which form stable carbides, including but not limited to titanium (Ti), vanadium (V), tantalum (Ta), and zirconium (Zr) may be added in substitution for niobium. However, such substitutes react more strongly with N than Nb and therefore are controlled to provide a beneficial effect, such as improved weldabilty. The inventors have determined that the sum of the weight percentages of Nb, Ti, V, Ta, and Zr should be maintained in the range of (7.5(% C)) up to 1.5%. Stated differently, (7.5(% C))â‰¦(% Nb+% Ti+% V+% Ta+% Zr)â‰¦1.5%. In certain embodiments, (7.5(% C))â‰¦(% Nb+% Ti+% V+% Ta+% Zr)â‰¦1.0%. In certain preferred embodiments, the alloy includes at least 0.1% Nb, and the sum of the weight percentages of Nb, Ti, V, Ta, and Zr is in the range of (7.5(% C)) up to 1.5% or 1.0%. In certain embodiments, Ti, V, Ta, and Zr are present only as incidental impurities or are maintained at levels as low as practical. In certain embodiments, in order to optimize corrosion resistance, elevated temperature strength, creep resistance, and weldabilty properties of the alloy, certain embodiments of the alloy include a Nb content of at least (7.5(% C)), and Ti, V, Ta, and Zr are present only as incidental impurities. In certain embodiments, the Ti content may be less than 0.01%. Also, in certain embodiments, the Ti content may be 0.001-0.005%. The present inventors have determined that a Nb content up to 1.5% is compatible with the alloy's N content of 0.05-0.35% in that the combination does not result in a level of niobium carbonitride precipitates that unacceptably degrades creep resistance.

In certain embodiments according to the present disclosure, the balance of the stabilized austenitic stainless steel of the present invention includes Fe and unavoidable impurities, such as P and S. The unavoidable impurities are preferably kept to the lowest practical and economically justifiable level, as understood by one skilled in the art.

Elements that form very stable nitrides, such as Al, should be kept to low levels.

The stabilized austenitic stainless steel of the present invention can also be defined by equations that quantify the properties they exhibit, including, for example, pitting resistance equivalence number, ferrite number, and MD₃₀temperature.

The pitting resistance equivalence number (PRE_N) provides a relative ranking of an alloy's expected resistance to pitting corrosion in a chloride-containing environment. The higher the PRE_N, the better the expected corrosion resistance of the alloy. The PRE_Ncan be calculated by the following formula:

PRE_N=% Cr+3.3(% Mo)+16(% N)

Alternatively, a factor of 1.65(% W) can be added to the above formula to take into account the presence of tungsten in an alloy. Tungsten improves the pitting resistance of stainless steels and is about half as effective as molybdenum by weight. When tungsten is included in the calculation, the pitting resistance equivalence number is designated as PRE_W, which is calculated by the following formula:

PRE_W=% Cr+3.3(% Mo)+1.65(% W)+16(% N)

The alloy of the present invention has a PRE_Nvalue of greater than 18. In certain embodiments, the PRE_Nvalue may be 18-24. In certain embodiments, the PRE_Nvalue may be 18-22. In certain embodiments, the PRE_Nvalue may be 20-22.

The alloy of the invention also may be defined by its ferrite number. A positive ferrite number generally correlates to the presence of ferrite, which improves an alloy's solidification properties and helps to inhibit hot cracking of the alloy during hot working and welding operations. A small amount of ferrite is thus desired in the initial solidified microstructure for good castability and for prevention of hot-cracking during welding. On the other hand, too much ferrite can result in problems during service, including but not limited to, microstructural instability, limited ductility, and impaired high temperature mechanical properties. The ferrite number can be calculated using the following equation:

FN=3.34(Cr+1.5Si+Mo+2Ti+0.5Cb)âˆ’2.46(Ni+30N+30C+0.5Mn+0.5Cu)âˆ’28.6

The alloy of the present invention has a ferrite number of up to 12, and preferably is a positive number. In certain embodiments according to the present disclosure, the ferrite number may be greater than 0 to 10, or may be 1 to 4.

The MD₃₀temperature of an alloy is defined as the temperature at which cold deformation of 30% will result in a transformation of 50% of the austenite to martensite. The lower the MD₃₀temperature is, the more resistant a material is to martensite formation. Resistance to martensite formation results in a lower work hardening rate, which results in good formability, especially in drawing applications. MD₃₀is calculated according to the following equation:

MD₃₀(Â° C.)=413âˆ’462(C+N)âˆ’9.2Siâˆ’8.1Mnâˆ’13.7Crâˆ’9.5Niâˆ’17.1Cuâˆ’18.5Mo

The alloy of the present invention has an MD₃₀temperature of less than 34Â° C., preferably less than 10Â° C. In certain embodiments, the MD₃₀temperature may be less than âˆ’10Â° C. In certain embodiments, the MD₃₀temperature may be less than âˆ’20Â° C.

EXAMPLESExample 1

Table 1 includes the compositions and calculated parameter values for Experimental Alloys 1-5 and Comparative Alloys S31600, S31635, S21600, and S20100.

Experimental Alloys 1-5 were melted in a laboratory-size vacuum furnace and poured into 50-lb ingots. These ingots were re-heated and hot rolled to produce material about 0.250â€³ thick. This material was annealed, blasted, and pickled. Some of that material was cold rolled to 0.100â€³-thick, and the remainder was cold rolled to 0.050 or 0.040â€³-thick. The cold rolled material was annealed and pickled. Comparative Alloys S31600, S31635, S21600, and S20100 were commercially available when the testing was performed and the data shown for these alloys were taken from published literature or measured from testing of material produced for commercial sale.

The calculated PRE_Wvalues for each alloy are shown in Table 1. Using the equation discussed herein above, the alloys having a PRE_Wgreater than 24.0 would be expected to have better resistance to chloride pitting than Comparative Alloy S31635 material, while those having a lower PRE_Wwould pit more easily.

The ferrite number for each alloy in Table 1 has also been calculated. The ferrite number for each of Experimental Alloys 1-5 is in the range of less than 10.

The MD₃₀values were also calculated for the alloys in Table 1. According to the calculations, Experimental Alloys 1-5, particularly Experimental Alloys 4 and 5, exhibit similar resistance to martensite formation to Comparative Alloys S31600 and S31635.

TABLE 1Experimental AlloysComparative Alloys12345S31600S31635S21600S20100C0.0170.0150.0140.0140.0160.0170.0160.0180.02Mn4.74.84.75.14.91.241.818.36.7Si0.260.270.280.290.30.450.500.400.40Cr16.616.616.618.118.216.316.819.716.4Ni5.25.25.25.55.510.110.76.04.1Mo1.471.471.471.001.12.12.112.50.26Cu0.400.400.390.400.50.380.360.400.43N0.0750.1040.0810.1290.1700.040.0130.370.15P0.0110.0120.0120.0140.0140.030.0310.030.03S0.00100.00120.00120.00160.00160.00100.00040.00100.0010W0.100.100.090.040.090.110.100.100.1B0.00190.00180.00160.00220.00220.00250.00250.00250.0005FeBalBalBalBalBal.Bal.Bal.Bal.Bal.Nb0.7100.4980.2880.5000.260.350.020.100.10Co0.220.190.150.190.15â€”â€”â€”â€”Tiâ€”â€”â€”â€”â€”â€”0.22â€”â€”FN8.35.87.56.63.74.16.7âˆ’6.2âˆ’2.3PRE_W22.923.423.123.624.724.024.033.919.7MD₃₀19.36.617.2âˆ’22.2âˆ’46.2âˆ’63âˆ’72.4âˆ’217.40.7RMCI0.630.630.620.590.600.961.000.800.41Yield47.047.046.148.453.743.541.55543Tensile102.0105.5104.5105.9106.490.692.0100100% E434948414956674556OCH0.420.390.400.410.430.45â€”â€”â€”

Table 1 also shows a raw material cost index (RMCI), which compares the material costs for each alloy to that of Comparative Alloy S31635. The RMCI was calculated by multiplying the average October 2007 cost for the raw materials Fe, Cr, Mn, Ni, Mo, W, and Co by the percent of each element contained in the alloy and dividing by the cost of the raw materials in Comparative Alloy S31635. As the calculated values show, each of Experimental Alloys 1-5 has an RMCI of less than 0.65, which means the cost of the raw materials contained therein are less than 65% of those in Comparative Alloy S31635 based on the October 2007 cost values. That a material could be made that has similar properties to Comparative Alloy S31635 at a significantly lower raw material cost is surprising and was not anticipated from the prior art.

The mechanical properties of Experimental Alloys 1-5 have been measured and compared to those of Comparative Alloys S31600, S31635, S21600, and S20100. The measured yield strength, tensile strength, percent elongation over a 2-inch gage length, and Olsen cup height are shown in Table 1. The tensile tests were conducted on 0.100â€³ gage material, the Charpy tests were conducted on 0.197â€³ thick samples, and the Olsen cup tests were run on material between 0.040- and 0.050-inch thick. All tests were performed at room temperature. Units for the data in Table 1 are as follows: yield strength and tensile strength, ksi; elongation, percent; Olsen cup height, inches. As can be seen from the data, the Experimental Alloys 1-5, and in particular Experimental Alloys 4 and 5, exhibited comparable properties to those of the S31635 material. Experimental Alloys 1-5, however, included less than half the concentration of nickel and also significantly less molybdenum than in Comparative Alloy S31635. The significantly lower concentration of the costly alloying elements nickel and molybdenum is such that the RMCI of Comparative Alloys 4 and 5 is at least 40% less than for Comparative Alloy S31635. Despite their substantially reduced levels of nickel and molybdenum, however, Experimental Alloys 4 and 5 had an austenitic microstructure and exhibited yield and tensile strength significantly better than for Comparative Alloy S31635.

Example 2

Table 2 includes the compositions and calculated parameter values for Experimental Alloys 6-10 and Comparative Alloys S32100 and Type 216Cb. As shown in Table 2, Experimental Alloys 6-10 generally include increased levels of Mn, N, and Nb and reduced levels of Ni compared to Comparative Alloy S32100. Experimental Alloys 6-10 also include decreased levels of Mo compared to Comparative Alloy T216Cb and Experimental alloys 1-5.

Experimental Alloys 6-10 were melted in a laboratory-size vacuum furnace and poured into 50-lb ingots. These ingots were re-heated and hot rolled to produce material about 0.250â€³ thick. This material was annealed, blasted, and pickled. Some of that material was cold rolled to 0.100â€³ thick, and the remainder was cold rolled to 0.050â€³ or 0.040â€³ thick. The cold rolled material was annealed and pickled. Comparative Alloy S32100 is commercially available, and the data shown for this alloy was taken from published literature or measured from testing of material recently produced for commercial sale. Comparative Alloy T216Cb is described in U.S. Patent Publication No. 2009-0162237 A1 (U.S. patent application Ser. No. 12/034,183), and the data shown for this alloy was measured from testing of material produced according to the description therein or taken from published literature.

The calculated PRE_Nvalues for each alloy are shown in Table 2. Using the equation discussed herein above, the alloys having a PRE_Ngreater than 18 would be expected to have better resistance to chloride pitting than Comparative Alloy S32100 material, while those having a PRE_Nlower than 24 would be expected to pit more readily than the material of Comparative Alloy T216Cb. The PRE_Nvalues for each of Experimental Alloys 6-10 is in a preferred range of 18-24.

The ferrite number for each alloy in Table 2 has also been calculated. The ferrite number for each of Experimental Alloys 6-10 is in the preferred range of less than 12. According to the calculations, Experimental Alloys 8-10 would exhibit improved formability compared to Comparative Alloy S32100.

The MD₃₀values were also calculated for the alloys in Table 2. According to the calculations, Experimental Alloys 6-10, and particularly Experimental Alloys 3 and 5, would exhibit improved resistance to martensite formation compared to Comparative Alloy S32100.

TABLE 2Experimental AlloysComparative Alloys678910S32100S32100T216CbT216CbC0.0170.0170.0170.0190.0170.0170.0170.0160.02Mn6.96.96.96.84.41.81.94.94.86Si0.340.350.340.330.160.550.520.30.36Cr18.318.218.216.718.217.318.218.218.02Ni5.04.03.53.04.59.39.45.55.54Mo0.300.300.300.300.290.350.251.10.92Cu0.520.520.520.520.620.320.23â€”â€”N0.0510.0940.1710.1490.1830.0110.0110.170.17P0.0200.0200.0200.0210.0200.0280.0270.0140.024S0.00190.00180.00000.00000.00130.00010.00080.00160.0005B0.00260.00180.00250.00240.0024â€”0.0030â€”â€”FeBalBalBalBalBal.Bal.Bal.Bal.Bal.Nb0.260.260.260.260.260.030.000.260.23Ti0.0040.0040.0040.0040.0040.1870.047â€”â€”FN9.18.13.81.52.36.68.24.53.2PRE_N20.120.721.920.122.118.719.224.623.8MD₃₀10.30.9âˆ’30.25.4âˆ’25.1âˆ’6.131.9âˆ’37.3âˆ’34.0RMCI0.730.650.610.560.681.000.990.860.83Yield43.446.650.148.349.933.525.653.565.6Tensile90.293.0102.7118.2104.981.578.9106.0115.6% E484748485258.5604752

Table 2 also shows a raw material cost index (RMCI), which compares the material costs for each alloy to that of Comparative Alloy S32100. The RMCI was calculated by multiplying the average October 2009 cost for the raw materials Fe, Cr, Mn, Ni, Mo, Cu, Nb, and Ti by the percent of each element contained in the alloy and dividing by the cost of the raw materials in Comparative Alloy S32100. As the calculated values show, Experimental Alloys 6-10 have an RMCI of less than or equal to 0.73, which means the cost of the raw materials contained therein are less than or equal to 73% of those in Comparative Alloy S32100. That a material that is a suitable alternative to Comparative Alloy S32100 could be made at a significantly lower raw material cost is surprising and unexpected.

The mechanical properties of Experimental Alloys 6-10 have been measured and compared to Comparative Alloys S32100 and T216Cb. The measured yield strength, tensile strength, and percent elongation over a 2-inch gage length are shown in Table 2. The tensile tests were conducted on 0.100â€³ gage material. All tests were performed at room temperature. Units for the data in Table 2 are as follows: yield strength and tensile strength, ksi; elongation, percent. As can be seen from the data, the Experimental Alloys 6-10 exhibited yield strength and tensile strength significantly better than for Comparative Alloy S32100 despite their substantially reduced levels of Ni. The amount of increase in yield strength compared to Comparative Alloy S32100 is surprising and was not anticipated from the prior art. The Experimental Alloys also included significantly less Mo than in Comparative Alloy T216Cb. The significantly lower concentration of the costly alloying elements Ni and Mo is such that the RMCI of Experimental Alloys 9 and 10 are at least 32% less than the RMCI for Comparative Alloy S32100.

The potential uses of these new alloys are numerous. As described and evidenced above, the austenitic stainless steel compositions described herein are capable of replacing S32100 in many applications. Additionally, due to the high cost of Ni, a significant cost savings will be recognized by switching from S32100 to the inventive alloy composition. Another benefit is that because these alloys are fully austenitic, they will not be susceptible to either a sharp ductile-to-brittle transition (DBT) at sub-zero temperature or 885Â° F. embrittlement at elevated temperatures. Therefore, unlike duplex alloys, they can be used at temperatures above 650Â° F. and are prime candidate materials for low temperature and cryogenic applications. Specific articles of manufacture for which the alloys according to the present disclosure would be particularly advantageous include, for example, flexible connectors for automotive exhaust and other applications, bellows, flexible pipe, and chimney/flue liners. Those having ordinary skill may readily manufacture these and other articles of manufacture from the alloys according to the present disclosure using conventional manufacturing techniques.

Although the foregoing description has necessarily presented only a limited number of embodiments, those of ordinary skill in the relevant art will appreciate that various changes in the apparatus and methods and other details of the examples that have been described and illustrated herein may be made by those skilled in the art, and all such modifications will remain within the principle and scope of the present disclosure as expressed herein and in the appended claims. It is understood, therefore, that the present invention is not limited to the particular embodiments disclosed or incorporated herein, but is intended to cover modifications that are within the principle and scope of the invention, as defined by the claims. It will also be appreciated by those skilled in the art that changes could be made to the embodiments above without departing from the broad inventive concept thereof.