RELATED APPLICATIONS

Reference is made to the following related applications:

Copending and commonly assigned U.S. Ser. No. 14/______ filed on even date herewith by Wexler, Bennett, and Lindner and entitled â€œCrosslinkable Reactive Polymersâ€ (Attorney Docket K001382/MT).

Copending and commonly assigned U.S. Ser. No. 14/______ filed on even date herewith by Wexler, Bennett, and Lindner, and entitled â€œForming Patterns Using Crosslinkable Reactive Polymersâ€ (Attorney Docket K001384/MT).

Copending and commonly assigned U.S. Ser. No. 14/______ filed on even date herewith by Irving and entitled â€œElectroless Plating Methodâ€ (Attorney Docket K001626/MT).

Copending and commonly assigned U.S. Ser. No. 14/______ filed on even date herewith by Irving and entitled â€œElectroless Plating Method Using Bleachingâ€ (Attorney Docket K001627/MT).

Copending and commonly assigned U.S. Serial No. 14/filed on even date herewith by Irving and entitled â€œElectroless Plating Method Using Halideâ€ (Attorney Docket K001628/JLT).

Copending and commonly assigned U.S. Ser. No. 14/______ filed on even date herewith by Irving and entitled â€œElectroless Plating Method Using Non-Reducing Agentâ€ (Attorney Docket K001629/JLT).

FIELD OF THE INVENTION

This invention relates to methods for forming metallic patterns, for example using electroless plating, using reactive polymers that can be crosslinked upon suitable irradiation.

BACKGROUND OF THE INVENTION

In recent decades accompanying rapid advances in information-oriented society, there have also been rapid technological advances to provide devices and systems for gathering and communicating information. Of these, display devices have been designed for television screens, commercial signage, personal and laptop computers, personal display devices, and phones of all types, to name the most common information sharing devices.

As the increase in the use of such devices has exploded in frequency and necessity by displacing older technologies, there has been a concern that electromagnetic radiation emission from such devices may cause harm to the human body or neighboring devices or instruments over time. To diminish the potential effects from the electromagnetic radiation emission, display devices are designed with various transparent conductive materials that can be used as electromagnetic wave shielding materials.

In display devices where a continuous conductive film is not practical for providing this protection from electromagnetic radiation emission, it has been found that conductive mesh or patterns can be used for this electromagnetic wave shielding purpose for example as described in U.S. Pat. No. 7,934,966 (Sasaki et al.).

Other technologies have been developed to provide new microfabrication methods to provide metallic, two-dimensional, and three-dimensional structures with conductive metals. Patterns have been provided for these purposes using photolithography and imaging through mask materials as described for example in U.S. Pat. No. 7,399,579 (Deng et al.).

Improvements have been proposed for providing conductive patterns using photosensitive silver salt compositions such as silver halide emulsions as described for example in U.S. Pat. No. 8,012,676 (Yoshiki et al.). Such techniques have a number of disadvantages that are described in this patent and the efforts continue to make additional improvements.

In addition, as the noted display devices have developed in recent years, their attraction has increased greatly with the use of touch screen technology whereby a light touch on the screen surface with a finger or stylus can create signals to cause changes in screen views or cause the reception or sending of information, telecommunications, interaction with the internet, and many other features that are being developed at an ever-increasing pace of innovation. The touch screen technology has been made possible largely by the use of transparent conductive grids on the primary display so that the location of the noted touch on the screen surface can be detected by appropriate electrical circuitry and software.

For a number of years, touch screen displays have been prepared using indium tin oxide (ITO) coatings to create arrays of capacitive patterns or areas used to distinguish multiple point contacts. ITO can be readily patterned using known semiconductor fabrication methods including photolithography and high vacuum processing. However, the use of ITO coatings has a number of disadvantages. Indium is an expensive rare earth metal and is available in limited supply. Moreover, ITO is a ceramic material and is not easily bent or flexed and such coatings require expensive vacuum deposition methods and equipment. In addition, ITO conductivity is relatively low, requiring short line lengths to achieve desired response rates (upon touch). Touch screens used in large displays are broken up into smaller segments in order to reduce the conductive line length to an acceptable electrical resistance. These smaller segments require additional driving and sensing electronics, further adding to the cost of the devices.

Silver is an ideal conductor having conductivity that is 50 to 100 times greater than that of ITO. Unlike most metal oxides, silver oxide is still reasonably conductive and its use reduces the problem of making reliable electrical connections. Moreover, silver is used in many commercial applications and is available from numerous commercial sources.

In other technologies, transparent polymeric films have been treated with conductive metals such as silver, copper, nickel, and indium by such methods as sputtering, ion plating, ion beam assist, wet coating, as well as the vacuum deposition. However, all of these technologies are expensive, tedious, or extremely complicated so that the relevant industries are spending considerable resources to design improved means for forming conductive patterns for various devices especially touch screen displays.

A similar level of transparency and conductivity for patterns can be achieved by producing very fine lines of about 5-6 Î¼m in width of highly conductive material such as copper or silver metal or conductive polymers. There is a need for a way to make these thin conductive lines with less expensive materials and plating techniques in order to achieve a substantial improvement in cost, reliability, and availability of conductive patterns for various devices. The present invention addresses this need as described in considerable detail below.

SUMMARY OF THE INVENTION

The present invention provides a method for using the reactive polymers described herein to address some of the noted problems.

A method for providing a pattern in a polymeric layer, the method comprising:

providing a polymeric layer comprising a reactive composition that comprises reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer,

patternwise exposing the polymeric layer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, to provide a polymeric layer comprising non-exposed regions and exposed regions comprising a polymer comprising sulfonic acid groups,

contacting the exposed regions of the polymeric layer with electroless seed metal ions to form a pattern of electroless seed metal ions in the exposed regions of the polymeric layer,

reducing the pattern of electroless seed metal ions to provide a pattern of corresponding electroless seed metal nuclei in the exposed regions of the polymeric layer, and

electrolessly plating the corresponding electroless seed metal nuclei in the exposed regions of the polymeric layer with a metal that is the same as or different from the corresponding electroless seed metal nuclei.

The invention also provides a precursor article useful in the practice of this invention, which precursor article comprises a substrate and having disposed thereon a polymeric layer comprising a reactive composition that comprises a reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer.

Moreover, the present invention can provide an intermediate article comprising a substrate and having disposed thereon a polymeric layer comprising exposed regions and non-exposed regions,

the exposed regions comprising a pattern of electroless seed metal ions in a de-blocked and crosslinked polymer derived from a reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer, and

the non-exposed regions comprising a reactive composition that comprises the reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer.

In addition, another intermediate article provided by the present invention comprises a substrate and having disposed thereon a polymeric layer comprising exposed regions and non-exposed regions,

the exposed regions comprising a pattern of corresponding electroless seed metal nuclei in a de-blocked and crosslinked polymer derived from a reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer, and

the non-exposed regions comprising a reactive composition that comprises the reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer.

The result of the method of the present invention is a product article comprising a substrate and having disposed thereon a polymeric layer comprising exposed regions and non-exposed regions,

the exposed regions comprising corresponding electroless seed metal nuclei that have been electrolessly plated with the same or different metal in a de-blocked and crosslinked polymer derived from a reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer, and

the non-exposed regions comprising a reactive composition that comprises the reactive polymer that comprises: (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer.

Another product article of this invention comprises a substrate and having disposed thereon a polymeric layer comprising exposed regions and non-exposed regions,

the exposed regions comprising corresponding electroless seed metal nuclei that have been electrolessly plated with the same or different metal in a de-blocked and crosslinked polymer derived from a reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer, and

the non-exposed regions comprising no reactive composition (in other words, the reactive composition has been removed) that comprises the reactive polymer that comprises: (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer.

The present invention provides an efficient method for forming conductive metal patterns using a specifically designed reactive polymer that can be de-blocked and crosslinked for use in pattern formation. The reactive polymer can undergo one or more chemical reactions upon irradiation to provide pendant sulfonic acid groups and to provide sites that promote polymer crosslinking in the reactive composition as well as reactive sites that will complex with catalytic metal ions such as silver ions or palladium ions. The chemical reactions also increase the hydrophilicity of exposed regions to allow diffusion of hydrophilic compounds such as aqueous metal ions, dyes, non-reducing reagents, and reducing agents and to promote strong adhesion of the polymeric layer to a substrate using crosslinking to minimize dissolution in various aqueous-based baths, solutions, or dispersions used in electroless plating methods.

The necessary pendant sulfonic acid groups are generated in the reactive polymer during exposure for example to ultraviolet light. The resulting pendant sulfonic acid groups increase the hydrophilicity of the polymer and are available to complex or react with metal ions or other charged molecules.

The present invention avoids the use of known expensive high vacuum processes necessary for making conductive patterns using indium tin oxide (ITO) coatings and is more readily carried out using high-speed roll-to-roll machines to provide higher manufacturing efficiencies.

DETAILED DESCRIPTION OF THE INVENTIONDefinitions

As used herein to define various ethylenically unsaturated polymerizable monomer components (or recurring units) of the reactive polymers, solutions, reactive compositions, aqueous-based solutions, and polymeric layers, unless otherwise indicated, the singular forms â€œaâ€ , â€œanâ€ , and â€œtheâ€ are intended to include one or more of the components (that is, including plurality referents).

Each term that is not explicitly defined in the present application is to be understood to have a meaning that is commonly accepted by those skilled in the art. If the construction of a term would render it meaningless or essentially meaningless in its context, the term definition should be taken from a standard dictionary.

The use of numerical values in the various ranges specified herein, unless otherwise expressly indicated otherwise, are considered to be approximations as though the minimum and maximum values within the stated ranges were both preceded by the word â€œaboutâ€ . In this manner, slight variations above and below the stated ranges can be used to achieve substantially the same results as the values within the ranges. In addition, the disclosure of these ranges is intended as a continuous range including every value between the minimum and maximum values.

Unless otherwise indicated, the term â€œweight %â€ refers to the amount of a component or material based on the total solids of a composition, formulation, or layer. Unless otherwise indicated, the percentages can be the same for either a dry layer or pattern, or for the total solids of the formulation or composition.

The term â€œhomopolymerâ€ is meant to refer to polymeric materials that have the same repeating or recurring unit along a reactive polymer backbone. The term â€œcopolymerâ€ refers to polymeric materials composed of two or more different repeating or recurring units that are arranged randomly along the reactive polymer backbone.

For reactive polymers used in the present invention, the term â€œarranged randomlyâ€ means that blocks of recurring units are not intentionally incorporated into the reactive polymers, but that recurring units are incorporated into the backbone in a random fashion using known polymerization procedures that do not encourage the formation of block copolymers.

Recurring units in reactive polymers described herein are generally derived from the corresponding ethylenically unsaturated polymerizable monomers used in a polymerization process, which ethylenically unsaturated polymerizable monomers have the desired pendant groups. Alternatively, pendant groups can be modified within recurring units after polymerization of ethylenically unsaturated polymerizable monomers having requisite precursor pending groups.

The term â€œreactive polymerâ€ is used herein to refer to the polymers described below that comprise at least one pendant labile group that can be changed, such as de-blocked (or unblocked), during appropriate irradiation to provide pendant sulfonic acid groups, and further comprise groups that can provide crosslinking in the presence of the pendant sulfonic acid groups.

The term â€œaqueous-basedâ€ refers to solutions, baths, or dispersions in which the predominant solvent, or at least 50 weight % of the solvents, is water.

Unless otherwise indicated, the term â€œmol %â€ when used in reference to recurring units in reactive polymers, refers to either the nominal (theoretical) amount of a recurring unit based on the amount of ethylenically unsaturated polymerizable monomer used in the polymerization process, or to the actual amount of recurring unit in the resulting reactive polymer.

Uses

The methods of this invention can be used to provide conductive metal patterns that can be incorporated into various devices including but not limited to touch screen or other display devices that are being used in numerous industrial and commercial products.

Reactive Polymers for Pattern Formation

In general, the reactive polymers useful in the practice of this invention two essential features: (1) they have labile groups that upon exposure to suitable radiation are de-blocked and provide pendant sulfonic acid groups, and (2) upon such irradiation, they are capable of being crosslinked only in exposed regions. While the reactive polymers can be supplied in reactive compositions as solutions in appropriate solvents, they are best used when applied to a substrate that can be a large or small surface, including the outer surfaces of inorganic or organic particles and then dried.

The reactive polymers can be either condensation or vinyl polymers as long as the requisite labile pendant groups are connected to the polymer backbone. In most embodiments, the useful reactive polymers are vinyl polymers derived from one or more ethylenically unsaturated polymerizable monomers using solution or emulsion polymerization techniques and conditions, initiators, surfactants, catalysts, and solvents, all of which would be readily apparent to one skilled in the art from the teaching provided herein.

The useful reactive polymers generally comprise at least some recurring units that comprise pendant groups attached to the polymer backbone, which pendant groups comprise a labile sulfonic acid. The term â€œlabileâ€ means that the labile sulfonic acid groups can provide pendant sulfonic acid groups (such as aromatic sulfonic acid groups) upon de-blocking when the reactive polymer is exposed to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, or more likely exposed to radiation having a Î»_maxof at least 150 nm and up to and including 330 nm (sometimes known as â€œshort UVâ€ ). Prior to the noted irradiation, the labile sulfonic acid groups are considered â€œblockedâ€ and are not available for reaction or causing reaction.

The reactive polymers become de-blocked and crosslinked during the noted irradiation and generation of the pendant sulfonic acid groups. In many embodiments, such crosslinking can be provided with distinct pendant acid-crosslinkable groups that are incorporated randomly along the reactive polymer backbone. Crosslinking further can be provided using distinct compounds that are dispersed as crosslinking agents within the polymeric layer (described below) comprising one or more reactive polymers.

Once suitable pendant sulfonic acid groups are generated upon irradiation, the resulting polymer can be either water-soluble or water-insoluble in irradiated or exposed regions of the polymeric layer, depending upon the extent of crosslinking in the resulting polymeric layer.

Particularly useful reactive polymers used in the present invention can be represented by the following -A-, -B-, and optional -C- recurring units in random order along the polymer backbone.

In particular, the -A- recurring units are derived from any ethylenically unsaturated polymerizable monomer having appropriate pendant aromatic groups that are capable of providing pendant aromatic sulfonic acid groups from aromatic sulfonic acid oxime ester groups having a cleavable â€”S(â• O)₂â€”Oâ€”Nâ• C<moiety (for example a â€œblocking groupsâ€ ). The sulfur atom of this moiety is typically connected to a carbocyclic aromatic group that is in turn attached to the polymer backbone, and the nitrogen atom of the moiety can have linear or branch substituents.

The -B- recurring units can be derived from any ethylenically unsaturated polymerizable monomer that has pendant groups that can provide sulfonic acid-catalyzed crosslinking in the irradiated polymer. Such pendant groups are well known in the art and some useful examples are described below.

More particularly, the -A-, -B-, and -C- recurring units can be represented as follows:

[Image Omitted]

In these formulae, the -A- recurring units comprise blocked (labile) pendant aromatic sulfonic acid oxime ester groups that are capable of providing pendant aromatic sulfonic acid groups upon irradiation from exposing radiation having a Î»_max(maximum wavelength) of at least 150 nm and up to and including 450 nm (or a Î»_maxof at least 150 nm and up to and including 250 nm).

Within the -A- recurring units, the moiety identified as Aâ€² can represent a single bond (wherein â€œiâ€ is 0) but Aâ€² is most likely a divalent linking group (wherein â€œiâ€ is 1) such as a substituted or unsubstituted arylene group including but not limited to a substituted or unsubstituted phenylene or naphthalene group. Possible substituents on the arylene group include but are not limited to alkyl groups having 1 to 3 carbon atoms and any other group that would be readily apparent to a skilled worker in the art to not interfere with removal of the L blocking group and such groups can be in any suitable position on the arylene ring. Particularly useful Aâ€² groups are substituted or unsubstituted phenylene, and unsubstituted phenylene is most useful.

Moreover, â€œLâ€ is a blocking group that is readily removed during irradiation of the polymer as noted above such as an oxime ester group containing a â€”S(â• O)â€”Oâ€”Nâ• C<oxime ester moiety. This moiety is readily cleaved at the 0-N bond as this bond is relatively weak in the range of 40 to 60 kcal of energy to provide pendant aromatic sulfonic acid groups in the resulting reacted and crosslinked polymer. The carbon atom in the noted oxime ester moiety can be attached to the same or different substituted or unsubstituted hydrocarbon group including but not limited to, substituted or unsubstituted alkyl (linear, branched, or cyclic) and substituted or unsubstituted aryl groups, or the carbon atom can be part of a saturated or unsaturated carbocyclic ring (including fused ring systems).

Once the blocking group has been removed from the -A- recurring units during irradiation, the -A- recurring units become â€œreacted -A- recurring unitsâ€ .

In some embodiments, the reactive polymers comprise greater than 50 mol % -A- recurring units derived from one or more ethylenically unsaturated polymerizable monomers, which recurring units can be represented by the following Structure Dâ€²:

[Image Omitted]

wherein R₁represents hydrogen or an alkyl group having 1 to 3 carbon atoms, and R₂and R₃can be the same or different and represent hydrogen, a substituted or unsubstituted alkyl group (branched or linear and including cycloalkyl groups) having 1 to 10 carbon atoms, a substituted or unsubstituted aryl group having 6 or 10 carbon atoms in the aromatic ring, or a substituted or unsubstituted alkenyl group (branched or linear, and including cycloalkenyl groups) having 2 to 10 carbon atoms.

Alternatively, R₂and R₃together with the carbon atom to which they are attached can form a substituted or unsubstituted non-aromatic carbocyclic ring 5 to 14 carbon atoms in the cyclic ring (including fused rings), which cyclic ring can also have some carbon-carbon unsaturation but not to the extent to give the cyclic ring aromaticity. Such cyclic rings can be substituted, where valences allow, with one or more oxo (â• O) groups, or with alkyl groups having 1 to 3 carbon atoms.

Particularly useful -A- recurring units comprise a cyclic oxime ester group and can be derived for example, from 1,2,3,4-tetrahydro-1,-naphthylideneamino-p-styrenesulfonate (sometimes known in the art as â€œTOSSâ€ ethylenically unsaturated polymerizable monomer).

Representative useful -A- recurring units for reactive polymers are shown as follows (the first structure showing recurring units derived from TOSS), which -A- recurring units can be derived from the corresponding ethylenically unsaturated polymerizable monomers:

[Image Omitted]

The -B- recurring units can be derived from any suitable ethylenically unsaturated polymerizable monomer, or group of monomers, having the same or different Bâ€² group that is capable of providing acid-catalyzed crosslinking when the pendant aromatic sulfonic acid groups are generated in the -A- recurring units during irradiation. For example, the -B- recurring units can comprise pendant Bâ€² groups that comprise an epoxy (such as a glycidyl group) or epithiopropyl group. Particularly useful -B- recurring units comprise pendant crosslinkable epoxy groups such as glycidyl groups and can be derived from glycidyl methacrylate or glycidyl acrylate. Other useful ethylenically unsaturated polymerizable monomers that have sulfonic acid-catalyzed crosslinking groups would be readily apparent to one skilled in the art.

Upon irradiation, the -B- recurring units can provide the crosslinking as described above, and are then considered to be â€œreacted -B-recurring unitsâ€ .

In addition to the -A- and -B- recurring units described above that are essential in the reactive polymers of this invention, the reactive polymers can further comprise one or more additional recurring units that are different from all -A- and -B- recurring units, and herein identified as -C- recurring units. A skilled polymer chemist would understand how to choose such additional recurring units, and for example, they can be derived from one or more ethylenically unsaturated polymerizable monomers selected from the group consisting of alkyl acrylates, alkyl methacrylates, (meth)acrylamides, styrene and styrene derivatives, vinyl ethers, vinyl imides, and other materials that a skilled worker in the art would understand could provide desirable properties to the reactive polymer. Thus, the D groups in the C recurring units can be for example, substituted or unsubstituted alkyl groups, substituted or unsubstituted aryl groups (such as substituted or unsubstituted phenyl groups), alkyl ester groups, aryl ester groups, or ether groups. In many useful C recurring units, the D groups are alkyl carboxyl ester groups wherein the alkyl moiety has 1 to 6 carbon atoms and is linear, branched, or cyclic in form.

In all of the -A-, -B-, and -C- recurring units, R and Râ€² can be the same or different hydrogen, methyl, ethyl, or chloro groups and each type of recurring unit can have the same or different R and Râ€² groups along the polymer backbone. In most embodiments, R and Râ€² are hydrogen or methyl, and R and Râ€² can be the same or different for the various -A-, -B-, and -C- recurring units in a given reactive polymer.

In the -A-B-, and -C- recurring unit formulae shown above, â€œmâ€ , â€œnâ€ , and â€œpâ€ are used to represent the respective molar amounts of recurring units, based on total recurring units, in a given reactive polymer, so that the sum of m, n, and p equal 100 mol % in a given reactive polymer.

In general, m is greater than 50 mol %, or even at least 60 mol % and up to and including 98 mol %, or at least 60 mol % and up to and including 95 mol %, based on the total recurring units in the reactive polymer. In addition, n generally represents at least 2 mol % and less than 50 mol %, or more typically at least 5 mol % and up to and including 40 mol %, or even at least 5 mol % and up to and including 25 mol %, based on the total recurring units in the reactive polymer. Moreover, while p can be 0 mol %, it can be up to and including 25 mol %, or typically at least 3 mol % and up to and including 20 mol %, or at least 5 mol % and up to and including 12 mol %, based on the total recurring units in the reactive polymer.

The mol % amounts of the various recurring units defined herein for the reactive polymers of this invention are meant to refer to the actual molar amounts present in the reactive polymers. It is understood by one skilled in the art that the actual mol % values may differ from those theoretically possible from the amount of ethylenically unsaturated polymerizable monomers that are used in the polymerization procedure. However, under most polymerization conditions that allow high polymer yield and optimal reaction of all monomers, the actual mol % of each monomer is generally within +15 mol % of the theoretical amounts.

Some representative reactive polymer embodiments include but are not limited to, the following copolymers and terpolymers (TOSS is identified above) wherein the molar ratios are theoretical (nominal) amounts based on the actual molar ratio of ethylenically unsaturated polymerizable monomers used in the polymerization process. The actual molar amounts of recurring units can differ from the theoretical (nominal) amounts of monomers if the polymerization reactions are not carried out to completion.

poly(TOSS-co-glycidyl methacrylate) (60:40);

poly(TOSS-co-glycidyl methacrylate) (80:20);

poly(TOSS-co-glycidyl methacrylate-co-n-butyl acrylate) (80:10:10);

poly(TOSS-co-glycidyl methacrylate-co-n-butyl methacrylate) (80:10:10);

poly(TOSS-co-2-phenoxyethyl acrylate) (80:20);

poly(TOSS-co-n-butyl acrylate) (80:20);

poly(TOSS-co-glycidyl methacrylate-co-n-butyl acrylate) (70:20:10); and

poly(TOSS-co-glycidyl methacrylate-co-2-phenoxyethyl acrylate) (70:20:10).

The reactive polymers generally have a molecular weight (M_w) of at least 30,000 and up to and including 300,000 as measured by gel permeation chromatography (GPC) or by size exclusion chromatography (SEC).

Examples of reactive polymers can be prepared using known free radical solution polymerization techniques using known starting materials, free radical initiators, and reaction conditions in suitable organic solvents such as tetrahydrofuran that can be adapted from known polymer chemistry. Where starting materials (such as ethylenically unsaturated polymerizable monomers) are not available commercially, such starting materials can be synthesized using known chemical starting materials and procedures.

Representative preparations of particularly useful reactive polymers are provided below for the Invention Examples.

In general, the reactive polymers can be stored in solution in suitable solvents. Depending upon the sensitivity of the reactive polymer to light (such as room light), during and after preparation, the reactive polymers can be kept in the dark or away from light exposure until they are formulated into reactive compositions and used for various purposes. To enhance storage stability, one or more acid scavengers, such as hindered amines, can be added to the reactive polymer solution during or after polymerization. A skilled polymer chemist would know what compounds would be suitable as acid scavengers and how much to use with a particular reactive polymer and desired storage stability.

Reactive Compositions:

The reactive polymers described herein can be used in reactive compositions in polymeric layers in various methods for forming conductive patterns for example using electroless plating.

Each reactive composition has only one essential component: one or more reactive polymers as described above, each of which provides pendant sulfonic acid groups upon exposure to radiation having Î»_maxof at least 150 nm and up to and including 450 nm, as described below, and which reactive polymer can also comprise pendant acid-crosslinkable groups so that a separate crosslinking agent or crosslinking precursor, while optional, is not necessary. While various other optional components can be included as described below, only the reactive polymer is essential for providing the desired pattern in the reactive composition forming the polymeric layer.

One or more reactive polymers as described above are generally present in the reactive composition (and in the resulting dry polymeric layer) in an amount of at least 50 weight % and up to and including 100 weight %, or typically at least 80 weight % and up to and including 95 weight %, based on the total solids in the reactive composition (or dry polymeric layer weight).

Individual compounds that provide an acid having a pKa of less than 2 (as measured in water) during the noted exposure to radiation are not necessary in most embodiments of the present invention and can be excluded from the reactive composition. However, in some embodiments, additional imaging sensitivity can be provided by incorporating onium salts that decompose upon irradiation. An onium salt (also known as an onium compound) is a compound that is formed by the attachment of a proton to a mononuclear parent hydride of a Group 15 element (for example nitrogen and phosphorus), a chalcogen of Group 16 (for example sulfur and selenium), or a halogen (such as fluorine, chlorine, and iodine). Particularly useful onium salts include but not limited to, sulfonium salts, phosphonium salts, iodonium salts, and aryldiazonium salts. In such embodiments, the sulfonium salts, phosphonium salts, and iodonium salts are particularly useful, including but not limited to the arylsulfonium salts and aryliodonium salts that can provide an acid having a pKa less than 2, or even less than 0, as measured in water.

In addition, the reactive compositions generally do not include separate crosslinking agents or crosslinking agent precursors because the reactive polymer itself includes sufficient pendant acid-crosslinkable groups. However, if desired for enhanced crosslinking, the reactive composition can include crosslinking agents that will react with pendant sulfonic acid groups or other moieties in the irradiated reactive polymer.

For example, some optional crosslinking agents include but are not limited to, melamine formaldehyde resins, glycoluril formaldehyde resins, polycarboxylic acids and anhydrides, polyamines, epihalohydrins, diepoxides, dialdehydes, diols, carboxylic acid halides, ketenes, aziridines, carbodiimides, isocyanates, and mixtures thereof. Such crosslinking agents can be present in the reactive composition in an amount of at least 1 weight % and up to and including 30 weight %, based on the total solids in the reactive composition.

While not essential, it is sometimes desirable to enhance the sensitivity of some reactive polymers to longer wavelengths (for example, greater than 300 nm) by including one or more photosensitizers in the reactive composition used in this invention. A variety of photosensitizers are known in the art such as aromatic tertiary amines, aromatic tertiary diamines and certain aromatic polycyclic compounds such as substituted or unsubstituted anthracene compounds, as described for example in U.S. Pat. No. 4,069,054 (Smith) and 7,537,452 (Dede et al.). Particularly useful photosensitizers include unsubstituted anthracene and substituted anthracenes such as 9,10-diethoxyanthracene and 2-t-butyl-9,10-diethoxyanthracene.

One or more photosensitizers can be optionally present in the reactive composition (and dry polymeric layer) in an amount of at least 1 weight % and up to and including 30 weight %, or more likely at least 5 weight % and up to and including 15 weight %, based on the total solids in the reactive composition (or dry polymeric layer weight).

The reactive compositions can optionally include one or more addenda such as film-forming compounds, surfactants, plasticizers, filter dyes, viscosity modifiers, high boiling solvents that are compatible with the reactive polymers (such as phthalated esters including dibutyl phthalate and dioctyl phthalate), and any other optional components that would be readily apparent to one skilled in the art, and such addenda can be present in amounts that would also be readily apparent to one skilled in the art.

The essential reactive polymer and any optional compounds described above are generally dissolved in a suitable organic solvent (or mixture of organic solvents) to form a reactive composition that can be applied to a suitable substrate (described below). Useful organic solvents include but are not limited to, cyclic ketones such as 2-butanone, cyclopentanone and cyclohexanone, substituted benzenes such as chlorobenzene and anisole, ethyl lactate, propylene glycol methyl ether acetate, or Î³-butyrolactone. Various mixtures of these organic solvents can be used if desired especially to dilute more toxic organic solvents with less toxic organic solvents such as blends of cyclopentanone with any of ethyl lactate, propylene glycol methyl ether acetate, or Î³-butyrolactone.

Articles

The reactive composition described above can be applied to a suitable substrate using any suitable method including but not limited to, spin coating, bead coating, blade coating, curtain coating, or spray coating, from a suitable reservoir to form a polymeric layer. Useful substrates can be chosen for particular use or method as long as the substrate material will not be degraded by the reactive composition or any treatments to which the resulting precursor articles are subjected during the methods of this invention. The reactive composition can be applied multiple times if desired to obtain a thicker coating (reactive layer) of the reactive composition, and dried between each coating or dried only after the last application. Solvent can be removed from the reactive composition using any suitable drying technique.

In general the final dry coating of reactive composition can have an average dry thickness of at least 10 nm and up to and including 10 mm, with a dry thickness of at least 0.1 Î¼m and up to and including 100 Î¼m being more useful. The average dry thickness can be determined by measuring the dry layer thickness in at least 10 different places within a 10 cm by 10 cm square of the dry reactive layer using an electron microscope or other suitable diagnostic device.

Thus, useful substrates can be composed of glass, quartz, and ceramics as well as a wide variety of flexible materials such as cellulosic papers and polyesters including poly(ethylene terephthalate) and poly(ethylene naphthalate), polycarbonates, polyamides, poly(meth)acrylates, and polyolefins. Useful polymeric substrates can be formed by casting or extrusion methods. Laminates of various substrate materials can also be put together to form a composite substrate. Any of the substrates can be treated to improve adhesion using for example corona discharge, oxygen plasma, ozone or chemical treatments using silane compounds such as aminopropyltriethoxysilane. The substrates can be of any suitable dry thickness including but not limited to at least 10 Î¼m and up to and including 10 mm, depending upon the intended use of the resulting articles.

Particularly useful substrates are composed of poly(ethylene terephthalate) such as biaxially oriented poly(ethylene terephthalate) (PET) films that have broad uses in the electronics market. These PET films, ranging in dry thickness of at least 50 Î¼m and up to and including 200 Î¼m, can also comprise, on at least one side, a polymeric primer layer (also known as a subbing layer, adhesive layer, or binder layer) that can be added prior to or after film stretching. Such polymeric primer layers can comprise poly(acrylonitrile-co-vinylidene chloride-co-acrylic acid), poly(methyl acrylate-co-vinylidene chloride-co-itaconic acid), poly(glycidyl methacrylate-co-butyl acrylate), or various water-dispersible polyesters, water-dispersible polyurethanes, or water-dispersible polyacrylics, as well as sub-micrometer silica particles. The dry thickness of the primer layer can be at least 0.1 Î¼m and up to and including 1 Î¼m.

Thus, with the application of the described reactive composition to a suitable substrate, with or without appropriate drying, the present invention provides a precursor article comprising a substrate and having disposed thereon a polymeric layer comprising a reactive composition that comprises a reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer.

Uses of Reactive Compositions

The reactive compositions described herein can be used to form surface patterns for various purposes as described above. The following discussion provides some details about representative electroless plating methods in which the reactive compositions can be used.

In these electroless plating methods, each aqueous-based â€œprocessingâ€ solution, dispersion, or bath (for example, solutions containing electroless seed metal ions, reducing agent solutions, and solutions for electroless plating, as well as rinsing solutions) used at various points can be specifically designed with essential components as well as optional addenda that would be readily apparent to one skilled in the art. For example, one or more of those aqueous-based processing solutions can include such addenda as surfactants, anti-coagulants, anti-corrosion agents, anti-foamants, buffers, pH modifiers, biocides, fungicides, and preservatives. The aqueous-based reducing solutions can also include suitable antioxidants.

The method of this invention for forming a pattern in a polymeric layer, comprises:

providing a polymeric layer (as in forming the described precursor article), the polymeric layer comprising the reactive composition described above, comprising a reactive polymer as described above. This polymeric layer can be formed on a suitable substrate, if desired, as described above by suitable application of the reactive composition, after which the reactive composition is typically dried before the resulting article is used in the method of this invention.

This polymeric layer in the precursor article, usually in dry form, can be then patternwise exposed to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm or to radiation having a Î»_maxof at least 150 nm and up to and including 330 nm, to provide a polymeric layer comprising non-exposed regions and exposed regions comprising a polymer comprising pendant aromatic sulfonic acid groups. This exposure can be provided with any suitable exposing source or device that provides the desired radiation including but not limited to, various arc lamps and LED sources. The particular exposing source can be chosen depending upon the absorption characteristics of the reactive composition used. The exposing radiation can be projected through lenses or a lens or mask element that can be in physical contact or in proximity with the outer surface of the polymeric layer. Exposure time can range from a fraction (0.1) of a second and up to and including 10 minutes depending upon the intensity of the radiation source and the reactive composition. Suitable masks can be obtained by known methods including but not limited to photolithographic methods, flexographic methods, or vacuum deposition of a chrome mask onto a suitable substrate such as quartz or high quality optical glass followed by photolithographic patterning.

It is not necessary to heat or bake the polymeric layer in the reactive composition in the precursor article simultaneously with or after the patternwise exposure and generally before contacting the exposed polymeric layer with electroless seed metal ions (described below). Thus, such a heating or baking step or procedure that is used in other methods can be omitted in the present invention.

The polymeric layer is generally hydrophilic in the exposed regions while still being hydrophobic in the non-exposed regions such that immersion in aqueous-based solutions (described below) will allow the aqueous molecules, ions, or reagent molecules to rapidly diffuse into the exposed regions.

At any time after the patternwise exposing procedure, the reactive composition remaining in the non-exposed regions of the polymeric layer can be removed using an organic solvent in which the polymeric layer comprising the reactive composition is soluble or dispersible. In such procedures at least 50 weight % and typically at least 80 weight % or even at least 90 weight % of the reactive composition in the polymeric layer is removed in the non-exposed regions, based on the total amount of reactive composition originally present in those non-exposed regions. Upon this removal of reactive composition from the non-exposed regions of the polymeric layer, the various articles described herein will contain de-blocked and crosslinked polymer in the exposed regions of the polymeric layer, along with reducing agent molecules, electroless seed metal ions, electroless seed metal nuclei, or electroless plated metal, depending upon the stage at which the non-exposed reactive composition has been removed.

The removal procedure can be carried out in any suitable manner, including immersion of the intermediate article into a suitable organic solvent or mixture of organic solvents or by spraying the organic solvent or mixture of organic solvents onto the intermediate article surface. Contact with the organic solvent (or mixture thereof) can be carried out for a suitable time and temperature so that reactive composition is desirably removed in the non-exposed regions but little removal (less than 10 weight % of the total material) occurs in the exposed regions containing the de-blocked and crosslinked polymer. For example, the contact time can be at least 10 seconds and up to and including 10 minutes, and the contact temperature can be at room temperature (about 20Â° C.) and up to and including 50Â° C.

Organic solvents that can used for this purpose include but are not limited to, ketones such as 2-butanone, cyclopentanone and cyclohexanone, substituted benzenes such as chlorobenzene and anisole, ethyl lactate, propylene glycol methyl ether acetate, or Î³-butyrolactone. Various mixtures of these organic solvents can be used if desired especially to dilute more toxic organic solvents with less toxic organic solvents such as blends of cyclopentanone with any of ethyl lactate, propylene glycol methyl ether acetate, or Î³-butyrolactone.

In many embodiments, removing the reactive composition in the non-exposed regions of the polymeric layer is carried out immediately after the patternwise exposure.

At this point, an intermediate article has been created in which the exposed regions of the polymeric layer on the substrate comprise de-blocked and crosslinked polymer derived from the reactive polymer in the reactive composition described herein, and the non-exposed regions of the polymeric layer comprise little or no reactive composition.

Once patternwise exposure has been carried out, the exposed regions of the polymeric layer are contacted with an aqueous-based solution or dispersion of electroless seed metal ions to form a pattern of electroless seed metal ions in the exposed regions of the polymeric layer. There are various ways that this contacting can be carried out. Typically, the entire intermediate article is immersed within a dilute aqueous-based solution, bath, or dispersion of the electroless seed metal ions for a sufficient time to coordinate the optimum number of electroless seed metal ions within the de-blocked and crosslinked polymer. For example, this contact with the electroless seed metal ions can be carried out for at least 1 second and up to and including 30 minutes, at room temperature (about 20Â° C.) or at a higher temperature of up to and including 95Â° C. The time and temperature for this contact can be optimized for a given reactive composition and electroless seed metal ions that are to be used.

Representative electroless seed metal ions that can be used in these procedures are selected from the group consisting of silver ions, platinum ions, palladium ions, gold ions, tin ions, rhodium ions, iridium ions, nickel ions, and copper ions. Most noble metal ions can serve as electroless seed metal ions in the present invention. These electroless seed metal ions can be provided in the form of a suitable metal salt or metal-ligand complex (that can have an overall positive, negative, or neutral charge). Useful materials of this type include but are not limited to, metal salts and metal-ligand complexes of nitrates, halides, acetates, cyanides, thiocyanates, amines, nitriles, and sulfates. Thus, the electroless seed metal ions can be provided from simple salts or in the form of metal-ligand complexes. The amount of metal salts or metal-ligand complexes present in the aqueous-based solution would be readily apparent to one skilled in the art and can be optimized for a particular reactive composition and exposure procedure. For example, the metal salts or metal-ligand complexes can be present in the aqueous-based solution in an amount sufficient to provide at least 0.00001 molar and up to and including 2 molar of the desired electroless metal ions. In one embodiment, a 0.4 molar silver nitrate solution can be used at room temperature to provide electroless seed silver ions.

The contact with the electroless seed metal ions produces an intermediate article comprising a substrate and having disposed thereon a polymeric layer comprising exposed regions and non-exposed regions,

the exposed regions comprising a pattern of electroless seed metal ions within the de-blocked and crosslinked polymer derived from a reactive polymer in a reactive composition described above, and

the non-exposed regions comprising the reactive composition described herein comprising a reactive polymer as described above.

After the requisite time to react the electroless seed metal ions within with the de-blocked and crosslinked polymer in the exposed regions, the polymeric layer can be rinsed with distilled or deionized water or another aqueous-based solution for a suitable time and at a suitable temperature, for example usually room temperature or slightly higher.

Optionally at this point, the reactive composition can be removed in the non-exposed regions as described above, leaving the pattern of electroless seed metal ions with de-blocked and crosslinked polymer in the exposed regions of the polymeric layer.

If this removal procedure is carried out, an intermediate article is created, which intermediate article comprises a substrate and having disposed thereon exposed regions of the polymeric layer containing de-blocked and crosslinked polymer derived from a reactive polymer in a reactive composition as described above, and non-exposed regions of the polymeric layer comprising little or no reactive composition, wherein the exposed regions further comprise a pattern of electroless seed metal ions coordinated within the de-blocked and crosslinked polymer.

After forming the pattern of electroless seed metal ions, the electroless seed metal ions can be reduced to provide the corresponding electroless seed metal nuclei in a pattern in the exposed regions of the polymeric layer. This can be done by contacting the polymeric layer (or at least the exposed regions) with a suitable reducing agent for the electroless seed metal ions. For example, the intermediate article comprising the polymeric layer can be immersed within an aqueous-based reducing solution containing one or more reducing agents for a suitable time to cause sufficient metal ion reduction. Alternatively, an aqueous-based reducing solution comprising the reducing agent can be sprayed or rolled uniformly onto the polymeric layer.

Useful reducing agents include but are not limited to, an organic borane, an aldehyde such as formaldehyde, aldehyde sugar, hydroquinone, or sugar (or polysaccharide) such as ascorbic acid, and metal ions such as tin(II). These reducing agents can be used individually or in combination, and the total amount in the aqueous-based reducing solution used for the reducing procedure can be at least 0.01 weight % and up to and including 20 weight % based on the total reducing solution weight. The amount of reducing agent to be used will depend upon the particular electroless seed metal ions and reducing agent to be used, and this can be readily optimized using routine experimentation. The time and temperature for the reduction can also be readily optimized in the same manner. Generally, the reducing temperature is at least room temperature (about 20Â° C.) and up to and including 99Â° C. and the reducing time can be for at least 1 second and up to and including 30 minutes.

For example, some embodiments of the present invention can be carried out using an immersion bath comprising 1 reducing solution weight % of an organic borane such as dimethylamine borane (DMAB) at room temperature for up to 3 minutes. Longer or shorter times at higher temperatures are possible if needed.

After this reducing procedure, the polymeric layer, especially the exposed regions, can be again washed using distilled water or deionized water or another aqueous-based solution at a suitable temperature for a suitable time.

At this point, the method of this invention has provided yet another intermediate article, comprising a substrate and having disposed thereon a polymeric layer comprising exposed regions and non-exposed regions,

the exposed regions comprising a pattern of corresponding electroless seed metal nuclei within the de-blocked and crosslinked polymer resulting from the irradiation of the reactive polymer in the reactive composition described above, and

the non-exposed regions comprising the reactive composition described herein comprising a reactive polymer as described above.

Optionally at this point, the reactive composition in the non-exposed regions of the polymeric layer can be removed (as described above) after this reducing procedure. This would produce yet another intermediate article that would comprise exposed regions in the polymeric layer comprising a pattern of corresponding electroless seed metal nuclei within the de-blocked and crosslinked polymer resulting from irradiation of the reactive polymer in a reactive composition described herein, but comprise little or no reactive composition in the non-exposed regions of the polymeric layer.

This intermediate article can be immediately immersed in an aqueous-based electroless metal plating bath or solution, or the intermediate article can be stored with just the catalytic pattern comprising corresponding electroless seed metal nuclei for use at a later time.

The intermediate article can be contacted with an electroless plating metal that is the same as or different from the corresponding electroless seed metal nuclei. In most embodiments, the electroless plating metal is a different metal from the corresponding electroless seed metal nuclei.

Any metal that will likely electrolessly â€œplateâ€ on the corresponding electroless seed metal nuclei can be used at this point, but in most embodiments, the electroless plating metal can be for example copper(II), silver(I), gold(IV), palladium(II), platinum(II), nickel(II), chromium(ID, and combinations thereof. Copper(II), silver(I), and nickel(II) are particularly useful electroless plating metals.

The one or more electroless plating metals can be present in the aqueous-based electroless plating bath or solution in an amount of at least 0.01 weight % and up to and including 20 weight % based on total solution weight.

Electroless plating can be carried out using known temperature and time conditions, as such conditions are well known in various textbooks and scientific literature. It is also known to include various additives such as metal complexing agents or stabilizing agents in the aqueous-based electroless plating solutions. Variations in time and temperature can be used to change the metal electroless plating thickness or the metal electroless plating deposition rate.

A useful aqueous-based electroless plating solution or bath is an electroless copper(II) plating bath that contains formaldehyde as a reducing agent. Ethylenediaminetetraacetic acid (EDTA) or salts thereof can be present as a copper complexing agent. For example, copper electroless plating can be carried out at room temperature for several seconds and up to several hours depending upon the desired deposition rate and plating rate and plating metal thickness.

Other useful aqueous-based electroless plating solutions or baths comprise silver(I) with EDTA and sodium tartrate, silver(I) with ammonia and glucose, copper(II) with EDTA and dimethylamineborane, copper(II) with citrate and hypophosphite, nickel(II) with lactic acid, acetic acid, and a hypophosphite, and other industry standard aqueous-based electroless baths or solutions such as those described by Mallory et al. in Electroless Plating: Fundamentals and Applications 1990.

After the electroless plating procedure, the product article is removed from the aqueous-based electroless plating bath or solution and can again be washed using distilled water or deionized water or another aqueous-based solution to remove any residual electroless plating chemistry. At this point, the polymeric layer and electrolessly plated metal are generally stable and can be used for their intended purpose.

Thus, this method provides a product article comprising a substrate and having disposed thereon a polymeric layer comprising exposed regions and non-exposed regions,

the exposed regions comprising a pattern of corresponding electroless seed metal nuclei (for example, in a pattern) that have been electrolessly plated with the same or different metal in the de-blocked and crosslinked polymer derived from the reactive polymer described above, and

the non-exposed regions comprising a reactive composition as described herein comprising a reactive polymer as described above.

Optionally at this point, the reactive composition can be removed from the non-exposed regions of the polymeric layer after electrolessly plating the corresponding electroless seed metal nuclei so that the resulting product article comprises a pattern of electrolessly plated metal in the exposed regions of the polymeric layer, but it comprises little or no reactive composition in the non-exposed regions of the polymeric layer.

To change the surface of the electroless plated metal for visual or durability reasons, it is possible that a variety of post-treatments can be employed including surface plating of still at least another (third or more) metal such as nickel or silver on the electrolessly plated metal (this procedure is sometimes known as â€œcappingâ€ ), or the creation of a metal oxide, metal sulfide, or a metal selenide layer that is adequate to change the surface color and scattering properties without reducing the conductivity of the electrolessly plated (second) metal. Depending upon the metals used in the various capping procedures of the method, it may be desirable to treat the electrolessly plated metal with a metal catalyst to facilitate deposition of additional metals. Depending upon the metals used in the various capping procedures of the method, it may be desirable to treat the electrolessly plated metal with a seed metal catalyst in an aqueous-based seed metal catalyst solution to facilitate deposition of additional metals.

As one skilled in the art should appreciate, the individual treatments or steps described above for this method can be carried out two or more times before proceeding to the next procedure or step. For example, the treatment with the aqueous-based solution containing electroless seed metal ions can be carried out two or more times in sequence, for example, with a rinsing step between sequential treatments. The electroless seed metal ions can be the same or different for the sequential treatments and the treatment conditions can be the same or different.

In addition, multiple treatments with an aqueous-based reducing solution or aqueous-based seed metal catalyst solution can be carried out in sequence, using the same or different conditions. Sequential washing or rinsing steps can also be carried out where appropriate.

Further, the electroless plating procedures can be carried out multiple times, in sequence, using the same or different electroless plating metal and the same or different electroless plating conditions and times.

It is also possible to use the product article provided by this method that comprises the noted pattern of an electrolessly plated metal, to incorporate a second or more patterns in the non-exposed regions. This can be accomplished by subjecting this product article to the same sequence of procedures or steps using the same or different reagents and aqueous-based solutions to provide at least a second pattern in what would be considered second exposed regions since the electrolessly plated metal would be in what is considered the first exposed regions. The second exposed regions can comprise all of the original non-exposed regions, or they can comprise only some of the non-exposed regions. For example, to create a second pattern in the article having the electrolessly plated metal, the product article can be treated or processed as follows, using conditions and aqueous-based solutions similar to or the same as those described above:

a) patternwise exposing the previously non-exposed regions to form second exposed regions in the polymeric layer,

b) optionally heating the polymeric layer,

c) contacting at least the second exposed regions with an aqueous-based solution containing electroless seed metal ions, and optionally rinsing,

d) reducing the coordinated electroless seed metal ions with an aqueous-based reducing solution, and optionally rinsing, and

e) electrolessly plating the same or different metal in the second exposed regions.

The present invention provides at least the following embodiments and combinations thereof, but other combinations of features are considered to be within the present invention as a skilled artisan would appreciate from the teaching of this disclosure:

1. A method for providing a pattern in a polymeric layer, the method comprising:

providing a polymeric layer comprising a reactive composition that comprises a reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer,

patternwise exposing the polymeric layer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, to provide a polymeric layer comprising non-exposed regions and exposed regions comprising a polymer comprising pendant sulfonic acid groups,

contacting the exposed regions of the polymeric layer with electroless seed metal ions to form a pattern of electroless seed metal ions in the exposed regions of the polymeric layer,

reducing the pattern of electroless seed metal ions to provide a pattern of corresponding electroless seed metal nuclei in the exposed regions of the polymeric layer, and

electrolessly plating the corresponding electroless seed metal nuclei in the exposed regions of the polymeric layer with a metal that is the same as or different from the corresponding electroless seed metal nuclei.

2. The method of embodiment 1, comprising contacting the exposed regions of the polymeric layer with electroless seed metal ions selected from the group consisting of silver ions, platinum ions, palladium ions, gold ions, rhodium ions, iridium ions, nickel ions, tin ions, and copper ions.

3. The method of embodiment 1 or 2, wherein the electroless seed metal ions are provided as a metal salt or metal-ligand complex.

4. The method of any of embodiments 1 to 3, comprising electrolessly plating with a metal that is selected from the group consisting of copper(II), silver(I), gold(IV), palladium(II), platinum(II), nickel(II), chromium(II), and combinations thereof.

5. The method of any of embodiments 1 to 4, comprising providing the polymeric layer on a substrate.

6. The method of any of embodiments 1 to 5, comprising patternwise exposing the polymeric layer to radiation having a Î»_maxof at least 150 nm and up to and including 330 nm.

7. The method of any of embodiments 1 to 6, comprising reducing the pattern of electroless seed metal ions in the exposed regions of the polymeric layer with a borane, aldehyde, hydroquinone, or sugar reducing agent.

8. A precursor article comprising a substrate and having disposed thereon a polymeric layer comprising a reactive composition that comprises a reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer.

9. An intermediate article comprising a substrate and having disposed thereon a polymeric layer comprising exposed regions and non-exposed regions,

the exposed regions comprising a pattern of corresponding electroless seed metal ions in a de-blocked and crosslinked polymer derived from a reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer, and

the non-exposed regions comprising a reactive composition that comprises the reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer.

10. An intermediate article comprising a substrate and having disposed thereon a polymeric layer comprising exposed regions and non-exposed regions,

the exposed regions comprising a pattern of corresponding electroless seed metal nuclei in a de-blocked and crosslinked polymer derived from a reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer, and

the non-exposed regions comprising a reactive composition that comprises the reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer.

11. A product article comprising a substrate and having disposed thereon a polymeric layer comprising exposed regions and non-exposed regions,

the exposed regions comprising a pattern of corresponding electroless seed metal ions that have been electrolessly plated with the same or different metal in a de-blocked and crosslinked polymer derived from a reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer, and

the non-exposed regions comprising a reactive composition that comprises the reactive polymer that comprises: (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer.

12. A product article comprising a substrate and having disposed thereon a polymeric layer comprising exposed regions and non-exposed regions,

the exposed regions comprising a pattern of corresponding electroless seed metal ions that have been electrolessly plated with the same or different metal in a de-blocked and crosslinked polymer derived from a reactive polymer that comprises (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer, and

the non-exposed regions comprising no reactive composition that comprises the reactive polymer that comprises: (1) pendant groups that are capable of providing pendant sulfonic acid groups upon exposure of the reactive polymer to radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, and (2) pendant groups that are capable of reacting in the presence of the sulfonic acid groups to provide crosslinking in the reactive polymer.

13. Any of embodiments 1 to 12, wherein the reactive polymer comprises a backbone and at least -A- and -B- recurring units, arranged randomly along the backbone, wherein:

the -A- recurring units comprise pendant aromatic sulfonic acid oxime ester groups, which recurring units are capable of providing pendant aromatic sulfonic acid groups upon irradiation with radiation having a Î»_maxof at least 150 nm and up to and including 450 nm, the -A- recurring units being present in the reactive polymer in an amount of at least 25 mol % and up to and including 98 mol % based on total reactive polymer recurring units, and the -B- recurring units comprise pendant groups that can provide crosslinking upon generation of the pendant aromatic sulfonic acid groups in the -A- recurring units, the -B- recurring units being present in an amount of at least 2 mol % and up to and including 75 mol % based on total reactive polymer recurring units.

14. Embodiment 13, wherein the -A- recurring units are present in the reactive polymer in an amount of at least 40 mol % and up to and including 95 mol % based on total reactive polymer recurring units, and the -B- recurring units are present in the reactive polymer in an amount of at least 5 mol % and up to and including 60 mol % based on total reactive polymer recurring units.

15. Embodiment 13 or 14, wherein the -A- recurring units are present in the reactive polymer in an amount of at least 60 mol % and up to and including 95 mol % based on total reactive polymer recurring units, and the -B-recurring units are present in the reactive polymer in an amount of at least 5 mal % and up to and including 40 mol % based on total reactive polymer recurring units.

16. Any of embodiments 13 to 15, wherein the -B- recurring units comprise pendant crosslinking epoxy groups.

17. Any of embodiments 13 to 16, wherein the reactive polymer further comprises one or more additional recurring units that are different from all -A- and -B- recurring units.

18. Embodiment 17, wherein the reactive polymer further comprises one or more additional recurring units that are derived from one or more ethylenically unsaturated polymerizable monomers selected from the group consisting of alkyl acrylates, alkyl methacrylates, (meth)acrylamides, vinyl esters, (meth)acrylonitrile, maleic anhydrides, maleic imides, and styrene and styrene derivatives.

19. Embodiment 17 or 18, wherein the one or more additional recurring units are present in an amount of at least 1 mol % and up to and including 25 mol % based on the total reactive polymer recurring units.

20. Any of embodiments 1 to 19, wherein the reactive polymer comprises at least 50 weight % and up to and including 100 weight % of the total dry weight of the polymeric layer.

The following Examples are provided to illustrate the practice of this invention and are not meant to be limiting in any manner.

The â€œTOSSâ€ monomer was prepared using the following synthetic preparation:

I-1 Inventive Reactive Polymer and C-1 comparative polymer were prepared using the following general synthetic scheme showing a copolymer 4 derived from the TOSS monomer and glycidyl methacrylate (Gm) which general synthetic reaction scheme is not to be considered limiting for the present invention. The reactants 1 and 2 and TOSS monomer 3 were prepared as described below.

[Image Omitted]

p-Styrenesulfonyl chloride 1 was prepared from sodium p-styrenesulfonate and thionyl chloride according to the method reported by Kamogawa et al. [Bull. Chem. Soc. Jpn., 56, 762-765 (1983)].

Î±-Tetralone oxime 2 was prepared from a-tetralone according to the method reported by Zhao et al. [Organic Lett., 10, 505-507 (2008)] with the following modifications:

A single neck 1 liter round bottom flask with magnetic stirring was charged with Î±-tetralone oxime (33.00 g, 0.226 mol), hydroxylamine hydrochloride (24.0 g, 0.345 mol), sodium acetate (31.67 g, 0.386 mol), 200 ml of water, and 200 ml of methanol and heated under nitrogen at reflux temperature for 4 hours. The mixture was allowed to cool and then placed in a freezer overnight to crystallize the reaction product. The resulting white crystals were collected, rinsed with methanol, and dried to yield 28.54 g (78%) of the desired oxime 2.

1,2,3,4-Tetrahydro-1,-naphthylideneamino p-styrenesulfonate 3 was prepared according to the method reported by M. Shirai et al. [Macromoledules, 25, 195-200 (1992)] with the following modifications (the prepared reaction solution and resulting TOSS monomer 3 were protected from room light as much as possible during the reaction and workup):

A single neck 250 ml amber round bottom flask with magnetic stirring was charged with a-tetralone oxime (7.95 g, 0.049 mol), pyridine (15.0 g, 0.380 mol) and cooled in an ice bath to 0Â° C. p-Styrenesulfonyl chloride (10.0 g, 0.049 mol) was added dropwise while keeping the reaction solution temperature below 5Â° C. The reaction solution was allowed to warm to room temperature and the reaction was monitored by thin layer chromatography (TLC, silica gel with 100% methylene chloride eluting solvent). When the desired reaction was complete (about 4 hours), methylene chloride (100 ml) and a 10% hydrochloric acid solution (100 ml) were added and the desired product was extracted twice using 100 ml of methylene chloride. The extracts were combined and washed with water (twice with 100 ml), dried over magnesium sulfate, and evaporated to dryness. The residue was purified by TLC (silica gel with 100% methylene chloride eluting solvent) to yield 11.66 g (72%) of a white solid TOSS monomer 3. Due to the instability of the TOSS monomer as a solid, it was stored as a solution in tetrahydrofuran (THF, 25% solids) in the refrigerator for up to 3 days before it was used to prepare reactive polymers as described below.

The â€œFLOSSâ€ monomer having the following recurring units structure was prepared similarly to the TOSS monomer using the synthesis described by Shirai et al. Reactive & Functional Polymers, 37 (1998), pp. 147-154:

[Image Omitted]

Preparation of I-1 Inventive Reactive Polymer:

During preparation and use, all of the reactive polymers were protected from room light as much as possible. For I-1 inventive reactive polymer, having a composition of 80:20 nominal mol ratio of TOSS monomer (â€œ-A-â€ recurring units) 3 1,2,3,4-tetrahydro-1,-naphthylideneamino p-styrenesulfonate (3.00 g, 0.0092 mol) and glycidyl methacrylate (Gm, 0.33 g, 0.0023 mol), the two ethylenically unsaturated polymerizable monomers were dissolved in THF (10.0 g, 25% solids) in a 100 ml amber round bottom and purged with nitrogen for about 30 minutes. A polymerization initiator, 2,2â€²-azobisisobutyronitrile, was added (0.06 g, 0.0003 mol, 3 mol % of combined monomers) and the flask was sealed with a secured septum and set in a preheated oil bath at 65Â° C. for 10 hours (polymerizations were run between 5 and 10 hours with 8 hours being the optimum time). The reaction solution was cooled and precipitated into ethyl acetate (300 ml) and the resulting solid reactive polymer was collected by filtration and dried. The solid reactive polymer was redissolved in THF at 25% solids and precipitated into methanol (300 ml). The solid reactive polymer was collected by filtration and dried to yield 2.46 g (74%) that were dissolved in THF at 15% solids and 1,2,2,6,6-pentamethylpiperidine (12.3 Î¼l, 1 mol % based on the -A- recurring units in the reactive polymer) was added to provide storage stability. The resulting solution was stored in the refrigerator for up to 4 months before use. The resulting I-1 inventive reactive polymer was characterized as follows to determine that the desired reactive polymer was obtained.

Characterization Data by NMR:

Approximately 150 mg of I-1 inventive reactive polymer was dissolved in 3 ml of CD₂Cl₂. TMS was added as a chemical shift reference and Cr(acac)₃was added as a relaxation agent. A ¹³C NMR spectrum was obtained at 125 MHz under quantitative conditions. The actual mol % of each type of recurring unit in the desired reactive polymer was determined from integral averages from several resonances of each recurring unit.

Characterization Data by SEC:

The sample of I-1 inventive reactive polymer was examined using size-exclusion chromatography (SEC) at 35.0Â° C. in N,N-dimethylformamide (DMF) containing 0.01 molar lithium nitrate. The column set consisted of three 8 mmÃ—300 mm GRAM Linear M columns from Polymer Standards Services, calibrated with narrow-molecular-weight distribution poly(methyl methacrylate) (PMMA) standards. This system has multiple detectors that measure differential refractive index, UV-Visible absorption, and viscosity of the eluent. The results were plotted as the normalized differential logarithmic molecular weight distribution where the ordinate â€œW_n(log M)â€ is the weight fraction of polymer per log M increment. The number-average (M_n), weight-average (M_w), z-average (M_z) molecular weights and intrinsic viscosity in units of dl/g in DMF at 35.0Â° C. (if applicable) are determined. The long-term 3Ïƒ coefficient of variation for M_wof a broad PMMA standard was Â±5%. Only M_wvalues are shown below in TABLE I.

I-2 through I-11 inventive reactive polymers and C-1 through C-5 comparative polymers (outside the invention) were prepared in the same manner with varying nominal molar ratios of the ethylenically unsaturated polymerizable monomers as shown below in TABLE I. These polymers were also characterized for actual recurring unit mol % and molecular weight in the same manner. The -C- Monomer and -C- Recurring Units refer to specific additional ethylenically unsaturated polymerizable monomer used to prepare inventive reactive polymers and comparative polymers as identified in TABLE I. The TOSS and FLOSS recurring units are representative examples of the -A- recurring units and Gm is a representative example of the -B- recurring units in the definition of the inventive reactive polymers.

TABLE 1TOSSMonomerTOSS recurringGm MonomerGm Recurringâ€”Câ€” Monomerâ€”Câ€” Recurringnominal molUnit (actual mol(nominal molUnit^b(actual(nominal molUnit (actual molPolymer%)%)^a%)mol %)^a%)%)^aPolymer M_wI-1808620140039,900I-2606940310047,300I-3808520150096,300C-11001000000108,000I-48084201600126,000I-5808320170082,900C-2202480760045,600I-6505550450049,700I-78087109.410n-butyl-acrylate292,0003.5I-88083107.710n-butyl277,000methacrylate8.8C-3808900202-phenoxyethyl64,700acrylate11C-48090.80020n-butyl acrylate73,4009.2I-98085101110n-butyl acrylate223,0003.8I-107077101910n-butyl acrylate109,0004I-1170792016102-phenoxyethyl101,000acrylate4.5^amol % determined by NMR^bDerived from glycidyl methacrylate

Additional inventive reactive polymers and comparative polymers were prepared as described above for I-1 inventive reactive polymer and TABLE II below provides a summary of these additional polymers and the nominal mol % of the recurring units derived from the noted ethylenically unsaturated polymerizable monomers. Polymers A, C, D, E, F, I, and K were inventive reactive polymers useful in the practice of the present invention and Polymers B, G, H, and J were comparative polymers outside the present invention.

TABLE IIGlycidyln-Butyl2-TOSSmethacrylateacrylatePhenoxyethylFLOSSPolymerMonomer(Gm)(B)acrylate (Pg)MonomerA8020000B1000000C6040000D9010000E80101000F70201000G8002000H8000200I0200080J2080000K5050000

Preparation of the Electroless Silver Plating Bath S1:

The following components were dissolved in a glass container that was cleaned with concentrated nitric acid followed by a thorough rinse with distilled water to eliminate any trace of metal on the glass: 11.3 g of silver nitrate, 67.5 g of tetrasodium EDTA (ethylenediaminetetraacetic acid, tetrahydrate), 14 g of a 0.01 molar 3,5 diiodotyrosine solution, 76.6 g of a 0.4 molar sodium tartrate solution, 831 g of distilled water, and several drops of a 45 weight % sodium hydroxide solution to adjust the pH to 11.3.

Preparation of the Electroless Copper Plating Bath C1:

The following components were dissolved in a glass container that was cleaned with concentrated nitric acid followed by a thorough rinse with distilled water to eliminate any trace of metal on the glass: 1.8 g of copper(II) sulfate pentahydrate, 6.25 g of tetrasodium EDTA (ethylenediaminetetraacetic acid, tetrahydrate), 0.005 g of potassium ferrocyanide trihydrate, 2.25 g of 37 weight % formaldehyde solution, 80 g of distilled water, and about 2 to 3 g of a 45 weight % sodium hydroxide solution to adjust the pH to 12.8.

Preparation of the Electroless Copper Plating Bath C2:

The following components were dissolved in a glass container that was cleaned with concentrated nitric acid followed by a thorough rinse with distilled water to eliminate any trace of metal on the glass (all chemical components were commercially available from RBP Chemical Technology Incorporated: 8 g of Circutek EC-1050A, 8 g of Circutek EC-1050B, 4 g Circutek EC-1050M, and 60 g of distilled water to yield a final pH of 12.8.

Preparation of Precursor Articles and Patternwise Exposure:

Reactive composition formulations were prepared using the dry isolated powder of Inventive reactive polymers and Comparative polymers by dissolving each of them in an organic solvent to yield a concentration of 15% solids. An amount (0.15% solids) of 1,2,2,6,6-pentamethyl piperidine was added to each solution to act as a storage stabilizer. A polymeric layer of each reactive formulation was prepared by either extrusion coating or spin coating each formulation at 1200 RPM onto a poly(ethylene terephthalate) film (PET) having thereon a crosslinked adhesion layer comprising a copolymer derived from n-butyl acrylate and glycidyl methacrylate, to form precursor articles.

Each resulting precursor article having the polymeric layer was pattemwise exposed to broadband ultraviolet light through a chrome-on-quartz contact mask. Each patternwise exposed precursor article was then immersed in a series of processing baths as described below in the following Examples.

Invention Example 1

Polymer A was dissolved in dichloromethane solvent to 15% solids as per the above method and 2.28 g of this Polymer A solution was added to 0.3 g of cyclopentanone and the resulting reactive composition was spin coated onto the PET substrate to form a precursor article. After being dried, the resulting polymeric layer was exposed through a mask using a handheld 254 nm lamp for 20 minutes. The exposed polymeric layer was then contacted at room temperature with a 0.4 molar silver nitrate solution for 5 minutes, followed by a 20 second distilled water rinse, and contact with a 1 weight % solution of dimethylamine borane (DMAB) for 2 minutes. The polymeric layer was then rinsed with distilled water for 2 minutes and then immersed in electroless silver plating bath S1 at 20Â° C. for 4 minutes. The silver plated pattern was then washed in distilled water for 4 minutes and dried under compressed nitrogen. A brilliant continuous silver film was formed in all exposed regions of the polymeric layer in the resulting product article. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and the silver pattern exhibited high electrical conductivity.

Invention Example 2

Polymer A was dissolved in dichloromethane solvent to 15% solids as described above and 2.28 g of this Polymer A solution was added to 0.3 g of cyclopentanone and the resulting reactive composition was spin coated onto the PET substrate to form a precursor article. After being dried, the resulting polymeric layer was exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. The exposed polymer layer was then contacted at room temperature with a 0.4 molar silver nitrate solution for 5 minutes, followed by a 5 second distilled water rinse, and contact with a 1 weight % solution of dimethylamine borane (DMAB) for 2 minutes. The polymeric layer was rinsed with distilled water for 2 minutes and then immersed in electroless copper plating bath C1 at 20Â° C. for 3 minutes. The copper plated pattern was then washed in distilled water for 4 minutes and dried under compressed nitrogen. A brilliant continuous copper film was formed in all exposed regions of the polymeric layer in the resulting product article. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and the copper pattern exhibited high electrical conductivity.

Invention Example 3

Polymer A was dissolved in dichloromethane solvent to 15% solids as described above and 2.28 g of this Polymer A solution was added to 0.3 g of cyclopentanone and the resulting reactive composition was spin coated onto the PET substrate to form a precursor article. After being dried, the resulting polymeric layer was exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. The exposed polymeric layer was then contacted at room temperature with a 0.4 molar silver nitrate solution for 5 minutes, followed by a 5 second distilled water rinse, followed by contact with a 1 weight % solution of dimethylamine borane (DMAB) for 2 minutes. The polymeric layer was rinsed with distilled water for 2 minutes and then immersed to electroless copper plating bath C2 at 20Â° C. for 3 minutes. The copper plated pattern was then washed in distilled water for 4 minutes and dried under compressed nitrogen. A brilliant continuous copper film was formed in all exposed regions of the polymeric layer of the resulting product article. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and the copper pattern exhibited high electrical conductivity.

Invention Example 4

Polymer A was dissolved in dichloromethane solvent to 15% solids as described above and 2.28 g of this Polymer A solution was added to 0.3 g of cyclopentanone and the resulting reactive composition was spin coated onto the PET substrate to form a precursor article. After being dried, the resulting polymeric layer was exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. The exposed polymeric layer was then contacted at room temperature with a 0.4 molar silver nitrate solution for 5 minutes, followed by a 5 second distilled water rinse, followed by contact with a 1 weight % solution of dimethylamine borane (DMAB) for 2 minutes. The polymeric layer was rinsed with distilled water for 2 minutes and then immersed into electroless copper plating bath C2 at 60Â° C. for 3 minutes. The copper plated pattern was then washed in distilled water for 4 minutes and dried under compressed nitrogen. A brilliant continuous copper film was formed in all exposed regions of the polymeric layer of the resulting product article. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and exhibited electrical conductivity higher than the product article provided in Inventive Example 3 due to a thicker copper layer plated at a higher temperature.

Invention Examples 5-17

Polymer A was dissolved in dichloromethane solvent to 15% solids as described above and 1.7 g of this Polymer A solution was added to 1.8 g of dichloromethane and 0.5 g of cyclopentanone and the resulting reactive composition extrusion coated onto PET substrates using a 2 mil (0.005 cm) gap to form precursor articles. After being dried, each resulting polymeric layer was exposed through a mask to an Oriel high intensity IJV lamp for 200 seconds.

The polymeric layers in the exposed articles were then contacted at room temperature with a silver nitrate solution for a variable time, followed by a 5 second distilled water rinse, followed by contact with a solution of dimethylamine borane (DMAB) for various times. The silver nitrate concentrations, silver nitrate bath times, DMAB concentrations, and DMAB bath times were varied as summarized below in TABLE III. Each polymeric layer was rinsed with distilled water for 2 minutes and then immersed in electroless copper plating bath C2 at 20Â° C. for 1 minute. The copper plated patterns were then washed in distilled water for 4 minutes and dried under compressed nitrogen. Brilliant continuous copper was formed in all regions of each polymeric layer in each product article. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and exhibited electrical conductivity. This set of Invention Examples shows the effective nature of the processing steps to form nuclei suitable for electroless plating amplification.

TABLE IIIMolAg Seed IonWeight %DMABExampleAg/literTimeDMABTimeInvention 50.15 minutes1.02 minutesInvention 60.45 minutes1.02 minutesInvention 71.25 minutes1.02 minutesInvention 82.45 minutes1.02 minutesInvention 90.41 minutes1.02 minutesInvention 100.45 minutes0.12 minutesInvention 110.45 minutes0.52 minutesInvention 120.45 minutes2.02 minutesInvention 130.45 minutes1.01 minutesInvention 140.45 minutes1.05 minutesInvention 150.15 minutes0.15 minutesInvention 162.45 minutes2.05 minutesInvention 170.15 minutes1.02 minutes

Invention Examples 18-20

Polymer A was dissolved in dichloromethane solvent to 15% solids as described above and 1.7 g of this Polymer A solution was added to 1.8 g of chloromethane and 0.5 g of cyclopentanone and the resulting reactive composition was extrusion coated onto a PET substrate using a 2 mil (0.005 cm) gap to form precursor articles. After being dried, each of the resulting polymeric layers was exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. The exposed polymeric layers were then contacted at room temperature with a silver solution for 5 minutes, followed by a 5 second distilled water rinse, followed by contact with a 1 weight % solution of dimethylamine borane (DMAB) for 5 minutes.

In Invention Example 18, a 0.4 molar silver nitrate solution was used. In Invention Example 19, a 0.4 molar silver nitrate solution to which had been added an 18 molar concentrated ammonia solution was used. Invention

Example 20 was prepared by adding 12.4 g of a 5.7 molar silver nitrate solution to 44 g of distilled water and 44 g of acetonitrile. The exposed and treated polymeric layers were treated using the silver ion solutions described below in TABLE IV. Each polymeric layer was rinsed with distilled water for 2 minutes and then immersed in electroless copper plating bath C1 at 20Â° C. for 2.5 minutes. The resulting copper patterns were then washed in distilled water for 4 minutes and dried under compressed nitrogen. Brilliant continuous copper was formed in all exposed regions of the polymeric layers of the resulting product articles. Line widths of 5 to 6 average diameter were faithfully reproduced and exhibited electrical conductivity.

This set of Invention Examples shows the effective nature of the source of silver complex to form nuclei suitable for electroless plating amplification.

TABLE IVExampleSilver complex ionInvention 18Ag⁺Invention 19Ag(NH₃)₂⁺Invention 20Ag(CH₃CN)₂⁺

Invention Examples 21-24

Polymer A was dissolved in dichloromethane solvent to 15% solids as described above and 1.7 g of this Polymer A solution was added to 1.8 g of dichloromethane and 0.5 g of cyclopentanone, and the resulting reactive composition was extrusion coated onto a PET substrate using a 2 mil (0.005 cm) gap to form precursor articles. After being dried, each of the resulting polymeric layers was exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. Each of the exposed polymeric layers was then contacted at room temperature with a 0.4 molar silver nitrate solution for 5 minutes, followed by distilled water rinse (for various times), and by contact with a 1 weight % solution of dimethylamine borane (DMAB) for 2 minutes.

The variable rinse times after contact with the silver nitrate solution are summarized below in TABLE V. Each polymeric layer was rinsed with distilled water for 5 minutes and then immersed in electroless copper plating bath C1 at 20Â° C. for 2.5 minutes. The resulting copper patterns were then washed in distilled water for 4 minutes and dried under compressed nitrogen. Brilliant continuous copper was formed in all exposed regions of the polymeric layer of each product article. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and exhibited electrical conductivity.

This set of Invention Examples shows that various wash times can be used to form nuclei suitable for electroless plating amplification.

TABLE VRinse Time after SilverExampleSeed Ion ContactInvention 211secondInvention 225secondsInvention 2315secondsInvention 2430seconds

Invention Examples 25-28

Polymer C was dissolved in dichloromethane solvent to 15% solids as described above, and 1.7 g of this Polymer C solution was added to 1.8 g of dichloromethane and 0.5 g of cyclopentanone, and the resulting reactive compositions were extrusion coated on PET substrates using a 2 mil (0.005 cm) gap to form precursor articles. After being dried, each resulting polymeric layer was exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. Each exposed polymeric layer was then contacted at room temperature with a 0.4 molar silver nitrate solution for 5 minutes, followed by a distilled water rinse (for various times), followed by contact with a 1 weight % solution of dimethylamine borane (DMAB) for 2 minutes. The various wash times after contact with the silver nitrate solution are summarized below in TABLE VI.

Each exposed and treated polymeric layer was rinsed with distilled water for 5 minutes and then immersed in electroless copper plating bath C1 at 20Â° C. for 1 minute. Each resulting copper pattern was then washed in distilled water for 4 minutes and dried under compressed nitrogen. Brilliant continuous copper was formed in all exposed regions of the polymeric layer in each article on the resulting product article. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and exhibited electrical conductivity.

This set of Invention Examples shows the effective nature of the polymer monomer (recurring unit) mol ratio in Polymer C and the wash time to form nuclei suitable for electroless plating amplification.

TABLE VIRinse Time After SilverExampleSeed Ion ContactInvention 251secondInvention 265secondsInvention 2715secondsInvention 28120seconds

Invention Examples 29-33

Polymer A was dissolved in dichloromethane solvent to 15% solids as described above, and 1.7 g of this Polymer A solution was added to 1.8 g of dichloromethane and 0.5 g of cyclopentanone, and the resulting reactive compositions were extrusion coated on PET substrates using a 2 mil (0.005 cm) gap to form precursor articles. After being dried, each resulting polymeric layer was exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. Each exposed polymeric layer was then contacted at room temperature with a 0.4 molar silver nitrate solution for 5 minutes, followed by a distilled water rinse (for various times), followed by contact with a 1 weight % solution of various reducing agents for 5 minutes.

The reducing agents used in these experiments were dimethylamine borane, D-glucose, ascorbic acid, 4-(hydroxymethyl)-4-methyl-1-phenyl-3-pyrazolidinone (MOP), and sodium tartrate. All of the reducing baths were adjusted to a common pH of 10.0 before use by adding concentrated potassium hydroxide. The various reducing agents are identified below in TABLE VII.

Each polymeric layer was rinsed after contact with the reducing agent using distilled water for 5 minutes and then immersed into electroless copper plating bath C1 at 20Â° C. for 1 minute. Each resulting copper pattern was then washed in distilled water for 4 minutes and dried under compressed nitrogen. Brilliant continuous copper was formed in all exposed regions of the polymeric layers in the articles in the resulting product articles. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and exhibited electrical conductivity.

This set of Invention Examples shows the desirable use of various reducing agents to form nuclei suitable for electroless plating amplification.

TABLE VIIExampleReducing AgentInvention 29dimethylamine boraneInvention 30D-glucoseInvention 31ascorbic acidInvention 32MOPInvention 33sodium tartrate

Invention Examples 34-42

Polymer A was dissolved in dichloromethane solvent to 15% solids as described above and 1.0 g of this Polymer A solution was added to 2.4 g of dichloromethane and 1.6 g of cyclopentanone. Variable amounts (weight % shown in TABLE VIII below) of the additives 1,2,2,6,6 pentamethyl piperidine (PMP) and dibutyl phthalate (DBP) were added to the reactive compositions, compensating for the amounts with slightly lower solvent additions. Each of the resulting reactive compositions was spin coated at 1500 rpm on a PET substrate to form a precursor article. After being dried, each resulting polymeric layer was exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. Each exposed polymeric layer was then contacted at room temperature with a 0.4 molar silver nitrate solution for 3 minutes, followed by a 60 second distilled water rinse, followed by contact with a 1 weight % solution of dimethylamine borane (DMAB) for 3 minutes. Each polymeric layer was rinsed with distilled water for 4 minutes and then immersed into electroless copper plating bath C1 at 20 C for 3 minutes. The resulting copper patterns were then washed in distilled water for 4 minutes and dried under compressed nitrogen. Brilliant continuous copper was formed in all exposed regions of the polymeric layers in the resulting product articles. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and exhibited high electrical conductivity.

The results showed that each reactive composition was effective with the addition of a base (PMP) and a plasticizer (DBP).

TABLE VIIIExampleAdditiveAdditive AmountInvention 34Noneâ€”Invention 35PMP0.1%Invention 36PMP0.4%Invention 37PMP1.2%Invention 38PMP3.0%Invention 39DBP0.1%Invention 40DBP0.4%Invention 41DBP1.2%Invention 42DBP3.0%

Invention Examples 43-45 and Comparison Example 1

Each of Polymers A, B, C, and D was separately dissolved in dichloromethane solvent to 15% solids as described above and 1.1 g of each Polymer solution was added to 1.7 g of dichloromethane and 1.3 g of cyclopentanone. Each resulting reactive composition was spin coated at 1500 rpm onto a PET substrate to form a precursor article. After being dried, each resulting polymeric layer was exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. Each exposed polymeric layer was then contacted at room temperature with a 0.4 molar silver nitrate solution for 3 minutes, followed by a 60 second distilled water rinse, followed by contact with a 1 weight % solution of dimethylamine borane (DMAB) for 3 minutes. The polymeric layers were rinsed with distilled water for 4 minutes and then immersed into electroless copper plating bath C1 at 20Â° C. for 3 minutes. Each resulting copper pattern was then washed in distilled water for 4 minutes and dried under compressed nitrogen. Brilliant continuous copper was formed in all exposed regions of the polymeric layer in the product articles.

The Comparative product article did not exhibit the formation of a brilliant copper pattern since the exposed regions of the polymeric layer dissolved in the processing baths. However, line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and high electrical conductivity was exhibited by the copper patterns formed in the Invention Examples. The results are summarized below in TABLE IX and show that the de-blocked and crosslinked polymers described herein according to the present invention, that is derived at least in part from the Gm monomer are more likely to survive the aqueous-based processing baths.

TABLE IXReactiveNominalExposedExamplePolymerMonomer RatioRegionsInvention 43A80:20ConductiveComparison 1B100:0â€ƒNon-conductiveInvention 44C60:40ConductiveInvention 45D90:10Conductive

Invention Example 46 and Comparison Example 2

Polymers B and C were separately dissolved in dichloromethane solvent to 15% solids as described above and 1.1 g of each polymer solution was added to 1.7 g of dichloromethane and 1.3 g of cyclopentanone. Each resulting reactive composition was spin coated onto a PET substrate at 1500 rpm as shown below in TABLE X to form a precursor article. After being dried, the polymeric layers were exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. Each exposed polymeric film was then contacted at room temperature with a 0.001 molar palladium chloride solution in a 50:50 mixture of water and acetonitrile solution for 3 minutes, followed by a 60 second distilled water rinse, and contact with a 0.11 weight % solution of dimethylamine borane (DMAB) for 3 minutes. Each polymeric layer was rinsed with distilled water for 4 minutes and then immersed in electroless copper plating bath C1 at 20Â° C. for 3 minutes. Each resulting copper pattern was then washed in distilled water for 4 minutes and dried under compressed nitrogen. Brilliant continuous copper was formed in all areas of the exposed regions of the resulting product article for Invention Example 47 that was prepared using Polymer C. However, a brilliant continuous copper pattern was not formed in the product article of Comparison Example 2 that was prepared using Polymer B since the exposed regions dissolved in the processing baths. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and showed high electrical conductivity in the resulting product article of Invention Example 47. These results show that it is desirable to incorporate the crosslinking groups from the Gm monomer into the reactive polymer for the exposed regions to best survive the processing baths. The Invention Example also shows that palladium metal nuclei can catalyze the plating of copper.

TABLE XNominalMonomer RatioPatternedExamplePolymer(TOSS to Gm)RegionsComparison 2B100:0Non-conductiveInventive 46Câ€ƒ60:40Conductive

Invention Example 47 and Comparison Examples 3-5

Polymers A and B were separately dissolved in dichloromethane solvent to yield 15% solids as described above and 1.6 g of each polymer solution was added to 4.4 g of mixed solvents that were by weight 60% toluene, 20% methanol, and 20% cyclopentanone. Polymers G and H were separately dissolved in mixed solvents that were by weight 60% toluene, 20% methanol, and 20% cyclopentanone to yield 10% solids, and 2.4 g of each polymer solution was added to 3.6 g of mixed solvents that were by weight 60% toluene, 20% methanol, and 20% cyclopentanone. Each of the resulting reactive compositions was uniformly spin coated onto a PET substrate at 1500 rpm to form a precursor article. After being dried, the resulting polymeric layer was exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. The exposed polymeric layers were then contacted at room temperature with a 0.4 molar silver nitrate solution for 3 minutes, followed by a 60 second distilled water rinse, followed by contact with a 1 weight % solution of dimethylamine borane (DMAB) for 3 minutes. Each exposed and treated polymeric layer was rinsed with distilled water for 4 minutes and then immersed in electroless copper plating bath C1 at 20Â° C. for 3 minutes. The resulting copper patterns were then washed in distilled water for 4 minutes and dried under compressed nitrogen. Brilliant continuous copper was formed in all exposed regions of the polymeric layer of the product article of Invention Example 47. The copper did not form brilliant continuous copper pattern in the product articles formed in Comparison Examples 3-5 since the exposed regions of the polymeric layer dissolved in the processing baths. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and showed high electrical conductivity in Inventive Example 47. These results show (TABLE XI) that it is desirable to have crosslinking groups in the reactive polymer used to form the polymeric layer for the exposed regions to survive the processing baths.

TABLE XINon-TOSSPatternedExamplePolymerMonomerRegionsInvention 47AGmConductiveComparison 3BNoneNon-conductiveComparison 4GBNon-conductiveComparison 5HPgNon-conductive

Invention Examples 48-51

Polymers A and D were separately dissolved in dichloromethane solvent to yield 15% solids as described above. Polymers E and F were separately dissolved in mixed solvents that were by weight 60% toluene, 20% methanol, and 20% cyclopentanone, and 2.0 g of each polymer solution was added to 4.0 g of mixed solvents that were by weight 60% toluene, 20% methanol, and 20% cyclopentanone. Each reactive composition was uniformly spin coated onto a PET substrate at 1500 rpm to form a precursor article. After being dried, the resulting polymeric layer was exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. Each polymeric layer was then contacted at room temperature with a 0.4 molar silver nitrate solution for 3 minutes, followed by a 60 second distilled water rinse, and contact with a 1 weight % solution of dimethylamine borane (DMAB) for 3 minutes. Each exposed and treated polymeric layer was were rinsed with distilled water for 3 minutes and then immersed in electroless copper plating bath C1 at 20Â° C. for 3 minutes. The resulting copper patterns were then washed in distilled water for 4 minutes and dried under compressed nitrogen. Brilliant continuous copper was formed in all exposed regions of the polymeric layer in the resulting product articles. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and exhibited high electrical conductivity. The results shown in TABLE XII below show that different ethylenically unsaturated polymerizable monomers can be used to make useful reactive polymers for the present invention.

TABLE XIINominalMonomer RatioPatternedExamplePolymerTOSS:Gm:BRegionsInvention 48A80:20:0â€‚ConductiveInvention 49D90:10:0â€‚ConductiveInvention 50E80:10:10ConductiveInvention 51F70:20:10Conductive

Invention Examples 52-53 and Comparison Example 6

Polymers A, J, and K were separately dissolved in dichloromethane solvent to yield 15% solids as described above and 3.3 g of each polymer solution was added to 1.7 g of cyclopentanone. Each of the resulting reactive compositions was uniformly spin coated onto a PET substrate at 1500 rpm to form a precursor article. Each polymeric layer was exposed through a mask to an Oriel high intensity UV lamp for 200 seconds. After being dried, each exposed polymeric layer was then contacted at room temperature with a 0.4 molar silver nitrate solution for 3 minutes, followed by a 120 seconds distilled water rinse, and contact with a 1 weight % solution of dimethylamine borane (DMAB) for 5 minutes. The resulting copper patterns were rinsed with distilled water for 2 minutes and then immersed in electroless copper plating bath C1 at 20Â° C. for 3 minutes in the resulting product articles. The polymeric layers were then washed in distilled water for 4 minutes and dried under compressed nitrogen. The results are shown below in TABLE XIII.

The product articles for Inventive Examples 52-53 demonstrated a thick copper coating that had low resistance while the product article prepared in Comparison Example 6 demonstrated a thin copper coating of higher resistance (less conductivity). Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced in all product articles. The results show that the recurring units derived from the photosensitive monomer (TOSS) should be greater than 20 mol % of all polymer recurring units to enable best ion exchange of metal ion during electroless plating.

TABLE XIIINominalMonomer RatioVisualResistanceExamplePolymerTOSS:Gmdensity(ohms)Invention 52A80:205.32.1Comparison 6J20:800.911.8Invention 53K50:502.71.0

Invention Examples 54-55

Polymer I was dissolved in cyclopentanone solvent to 10% solids as described above and 2.5 g of this Polymer I solution was added to 2.5 g of a solvent mixture that was 50% cyclopentanone and 50% tetrahydrofuran. A resulting reactive composition was spin coated onto a PET substrate at 1500 rpm to form a precursor article. A second reactive composition coating was made using the 10% polymer solution in an undiluted state. After being dried, each polymeric layer was exposed through a mask an Oriel high intensity UV lamp for 300 seconds. The exposed polymeric layer was then contacted at room temperature with a 0.4 molar silver nitrate solution for 3 minutes, followed by a 60 second distilled water rinse, and then with a 1 weight % solution of dimethylamine borane (DMAB) for 3 minutes. Each polymeric layer was rinsed with distilled water for 3 minutes and then immersed in electroless silver plating bath S1 at 20Â° C. for 2 minutes. The resulting silver pattern was then washed in distilled water for 4 minutes and dried under compressed nitrogen. A brilliant continuous silver pattern was formed in exposed regions of the polymeric layer in the product article. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and exhibited high electrical conductivity.

TABLE XIVExamplePolymerVisual densityResistance (ohms)Invention 54I2.11.9Invention 55I2.41.7

Invention Examples 56-60

Polymer A was dissolved in dichloromethane solvent to 15% solids as described above and 2.1 g of this Polymer A solution was added to 3.3 g of dichloromethane and 2.6 g of cyclopentanone. The resulting reactive composition was spin coated on a PET substrate at 1500 rpm to form a precursor article. After being dried, each resulting precursor article with the polymeric layer was exposed through a mask to an Oriel high intensity UV lamp for 300 seconds. Each exposed polymeric layer was then contacted at room temperature with a 0.4 molar silver nitrate solution for 3 minutes, followed by a 60 second distilled water rinse, and followed by contact with a 1 weight % solution of a reducing agent for 5 minutes. The reducing agents used for this procedure were dimethylamine borane (DMAB), D-glucose, ascorbic acid, sodium tartrate, and formaldehyde. Each reducing bath was adjusted to a common pH of 10.0 before use by adding concentrated potassium hydroxide. The various tested reducing agents are shown below in TABLE XV. Each treated polymeric layer was rinsed with distilled water for 4 minutes and then immersed into electroless copper plating bath C1 at 20Â° C. for 4 minutes. The resulting copper patterns were then washed in distilled water for 4 minutes and dried under compressed nitrogen. Brilliant continuous copper was formed in all exposed regions of the polymeric layers in the product articles. Line widths of 5 to 6 Î¼m average diameter were faithfully reproduced and showed electrical conductivity. This set of Invention Examples shows the effective nature of various reducing agents to form nuclei suitable for electroless plating amplification.

TABLE XVExampleReducing AgentInvention 56dimethylamine boraneInvention 57D-glucoseInvention 58ascorbic acidInvention 59sodium tartrateInvention 60formaldehyde

The invention has been described in detail with particular reference to certain preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention.