TECHNICAL FIELD

The present invention relates to a polycarbonate resin composition having excellent weatherability, hue, transparency, heat resistance, thermal stability, moldability, and mechanical strength and to a molded article obtained therefrom.

BACKGROUND ART

Polycarbonate resins are generally produced using bisphenols as a monomer ingredient, and are being extensively utilized as so-called engineering plastics in the fields of electrical/electronic parts, automotive parts, medical parts, building materials, films, sheets, bottles, optical recording media, lenses, etc. so as to take advantage of the superiority thereof such as transparency, heat resistance, and mechanical strength.

However, the conventional polycarbonate resins deteriorate in hue, transparency, and mechanical strength when used over a long period in places where the resins are exposed to ultraviolet rays or visible light. There hence have been limitations on outdoor use thereof and on use thereof in the vicinity of illuminators. Furthermore, use of the conventional polycarbonate resins as various molded articles has encountered a problem that the polycarbonate resins show poor mold release characteristics during melt molding and it is difficult to use the resins as transparent materials, optical materials, or the like.

Techniques in which a benzophenone-based ultraviolet absorber, benzotriazole-based ultraviolet absorber, or benzoxazine-based ultraviolet absorber is added to a polycarbonate resin in order to overcome such problems are widely known (for example, non-patent document 1).

It is also widely known that addition of a hindered amine-based (HALS) light stabilizer to a polycarbonate resin is impracticable because polycarbonate resins are unstable to basic ingredients, e.g., alkalis, even at ordinary temperature and are hydrolyzed by HALSs.

The bisphenol compounds for use in producing conventional polycarbonate resins have a benzene ring structure and hence show high absorption of ultraviolet rays. This leads to a deterioration in the light resistance of the polycarbonate resins. Consequently, use of monomer units derived from an aliphatic dihydroxy compound or alicyclic dihydroxy compound which has no benzene ring structure in the molecular framework or from a cyclic dihydroxy compound having an ether bond in the molecule, such as isosorbide, is expected to theoretically improve light resistance. In particular, polycarbonate resins produced using, as a monomer, isosorbide obtained from biomass resources have excellent heat resistance and mechanical strength, and many investigations thereon hence have come to be made in recent years (for example, patent documents 1 to 7).

It is also widely known that a benzotriazole, benzophenone, or cyanoacrylate compound is added as an ultraviolet absorber to a polycarbonate resin composition obtained using a monomer having an ether bond in the molecule, such as isosorbide, isomannide, or isoidide, which has no benzene ring structure in the molecular framework (patent document 8).

PRIOR-ART DOCUMENTSPatent Documents

Patent Document 1: International Publication No. 2004/111106
Patent Document 2: JP-A-2006-232897
Patent Document 3: JP-A-2006-28441
Patent Document 4: JP-A-2008-24919
Patent Document 5: JP-A-2009-91404
Patent Document 6: JP-A-2009-91417
Patent Document 7: JP-A-2008-274007
Patent Document 8: JP-A-2007-70391

Non-Patent Document

Non-Patent Document 1: HONMA Seiichi, ed., PorikÄ bonÄ“to Jushi Handobukku, published by The Nikkan Kogyo Shinbun, Ltd., Aug. 28, 1992.

SUMMARY OF THE INVENTIONProblems that the Invention is to Solve

However, addition of ultraviolet absorbers such as those described in non-patent document 1 poses the following problems although the addition brings about improvements in hue retention through ultraviolet irradiation, etc. Namely, there have been problems, for example, that the addition of the ultraviolet absorbers deteriorates the hue, heat resistance, and transparency which are inherent in the resin and that the ultraviolet absorbers volatilize during molding to foul the mold.

Furthermore, since aliphatic dihydroxy compounds, alicyclic dihydroxy compounds, and cyclic dihydroxy compounds having an ether bond in the molecule, such as isosorbide, have no phenolic hydroxyl group, it is difficult to polymerize these compounds by the interfacial process which is widely known as a process for polycarbonate resin production using bisphenol A as a starting material. Usually, polycarbonate resins are produced from those compounds by the process which is called a transesterification process or a melt process, as described in patent documents 1 to 7. In this process, any of those dihydroxy compounds and a carbonic diester, e.g., diphenyl carbonate, are subjected to transesterification at a high temperature of 200Â° C. or above in the presence of a basic catalyst, and the by-product, e.g., phenol, is removed from the system to allow the polymerization to proceed, thereby obtaining a polycarbonate resin. However, the polycarbonate resins obtained using monomers having no phenolic hydroxyl group, such as those shown above, have poor thermal stability as compared with polycarbonate resins obtained using monomers having phenolic hydroxyl groups, e.g., bisphenol A, and hence have had the following problem. The polycarbonate resins take a color during the polymerization or molding in which the resins are exposed to high temperatures and, as a result, the polycarbonate resins come to absorb ultraviolet rays and visible light and hence have impaired light resistance. Especially when a monomer having an ether bond in the molecule, such as isosorbide, was used, the polycarbonate resin considerably deteriorates in hue. A significant improvement has been desired. Furthermore, when such polycarbonate resins are to be used as various molded articles, the resins are melt-molded at high temperatures. For this application also, there has been a desire for a material having satisfactory thermal stability and excellent moldability and mold release characteristics.

Moreover, addition of an ultraviolet absorber in the manner described in patent document 8 has encountered a problem that the addition of the ultraviolet absorber deteriorates the hue, heat resistance, and transparency in a weatherability test which are inherent in the resin.

An object of the invention is to eliminate the problems of prior-art techniques described above and to provide a polycarbonate resin composition having excellent weatherability, hue, transparency, heat resistance, thermal stability, moldability, and mechanical strength and a molded article formed therefrom.

Means for Solving the Problems

The present inventors diligently made investigations in order to overcome those problems. As a result, the inventors have found that a polycarbonate resin composition which includes a polycarbonate resin (A) containing constituent units derived from a dihydroxy compound (a) having the portion represented by the following general formula (1) as part of the structure thereof and constituent units derived from a dihydroxy compound (b) of an alicyclic hydrocarbon having up to 11 carbon atoms and an aromatic polycarbonate resin (B) represented by the following general formula (2) not only has excellent light resistance but also has excellent hue, transparency, heat resistance, thermal stability, moldability, and mechanical strength. The invention has been thus achieved.

[Chem. 1]

î¢ CH₂â€”Oî¢ â€ƒâ€ƒ(1)

(The case where the portion represented by the general formula (1) is part of â€”CH₂â€”Oâ€”H is excluded.)

[Chem. 2]

[Image Omitted]

(R¹to R⁸in the general formula (2) each independently represent a hydrogen atom or a substituent. Y represents a single bond or a divalent group.)

Essential points of the invention reside in the following [1] to [8].

[1] A polycarbonate resin composition which comprises a polycarbonate resin (A) containing constituent units derived from a dihydroxy compound (a) having the portion represented by the following general formula (1) as part of the structure thereof and constituent units derived from a dihydroxy compound (b) of an alicyclic hydrocarbon having up to 11 carbon atoms and an aromatic polycarbonate resin (B) represented by the following general formula (2).

[Chem. 3]

î¢ CH₂â€”Oî¢ â€ƒâ€ƒ(1)

(The case where the portion represented by the general formula (1) is part of â€”CH₂â€”Oâ€”H is excluded.)

[Image Omitted]

(R¹to R⁸in the general formula (2) each independently represent a hydrogen atom or a substituent. Y represents a single bond or a divalent group.)

[2] The polycarbonate resin composition according to [1] wherein the difference between the initial yellowness index (YI) value of a molded object having a thickness of 3 mm formed from the polycarbonate resin composition and the yellowness index (YI) value thereof measured after the molded object has undergone a 500-hour irradiation treatment with a sunshine carbon arc lamp at a discharge voltage of 50 V and a discharge current of 60 A at a black panel temperature of 63Â° C. in an environment having a relative humidity of 50% and a rainfall spray period per hour of 12 minutes is 10 or less.
[3] The polycarbonate resin composition according to [1] or [2] wherein the dihydroxy compound (a) is a dihydroxy compound represented by the following general formula (3).

[Image Omitted]

[4] The polycarbonate resin composition according to any one of [1] to [3] which further contains an ultraviolet absorber in an amount of 0.0001-1 part by weight per 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B).
[5] The polycarbonate resin composition according to any one of [1] to [4] which further contains a hindered amine-based light stabilizer in an amount of 0.001-1 part by weight per 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B).
[6] The polycarbonate resin composition according to any one of [1] to [5] which further contains an antioxidant in an amount of 0.0001-1 part by weight per 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B).
[7] The polycarbonate resin composition according to any one of [1] to [6] which further contains a release agent in an amount of 0.0001-2 parts by weight per 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B).
[8] A polycarbonate resin molded article obtained by molding the polycarbonate resin composition according to any one of [1] to [7].

Effects of the Invention

According to the invention, a polycarbonate resin composition which has excellent weatherability, hue, transparency, heat resistance, thermal stability, moldability, and mechanical strength and a molded article formed therefrom can be provided.

MODES FOR CARRYING OUT THE INVENTION

Modes for carrying out the invention will be explained below in detail. The following explanations on constituent elements are for embodiments (representative embodiments) of the invention, and the invention should not be construed as being limited to the embodiments unless the invention departs from the spirit thereof.

The polycarbonate resin (A) to be used in the invention is obtained using dihydroxy compounds including both a dihydroxy compound (a) having the portion represented by the following general formula (1) as part of the structure thereof and a dihydroxy compound (b) of an alicyclic hydrocarbon having up to 11 carbon atoms (hereinafter, those dihydroxy compounds are often referred to simply as â€œdihydroxy compoundsâ€ ) and a carbonic diester as starting materials, by condensation-polymerizing the starting materials by means of a transesterification reaction. Namely, the polycarbonate resin (A) to be used in the invention contains constituent units derived from a dihydroxy compound (a) having the portion represented by the following general formula (1) as part of the structure thereof and constituent units derived from a dihydroxy compound (b) of an alicyclic hydrocarbon having up to 11 carbon atoms.

[Chem. 6]

î¢ CH₂â€”Oî¢ â€ƒâ€ƒ(1)

(The case where the portion represented by the general formula (1) is part of â€”CH₂â€”Oâ€”H is excluded.)

The dihydroxy compounds to be used in the invention are not particularly limited so long as the compounds include a dihydroxy compound (a) having the portion represented by the general formula (1) as part of the structure thereof and a dihydroxy compound (b) of an alicyclic hydrocarbon having up to 11 carbon atoms. Examples of the dihydroxy compound (a) having the portion represented by the general formula (1) as part of the structure thereof include oxyalkylene glycols such as diethylene glycol, triethylene glycol, and tetraethylene glycol, compounds which have an aromatic group as a side chain and have, in the main chain, ether groups each bonded to an aromatic group, such as 9,9-bis(4-(2-hydroxyethoxy)phenyl)fluorene, 9,9-bis(4-(2-hydroxyethoxy)-3-methylphenyl)fluorene, 9,9-bis(4-(2-hydroxyethoxy)-3-isopropylphenyl)fluorene, 9,9-bis(4-(2-hydroxyethoxy)-3-isobutylphenyl)fluorene, 9,9-bis(4-(2-hydroxyethoxy)-3-tert-butylphenyl)fluorene, 9,9-bis(4-(2-hydroxyethoxy)-3-cyclohexylphenyl)fluorene, 9,9-bis(4-(2-hydroxyethoxy)-3-phenylphenyl)fluorene, 9,9-bis(4-(2-hydroxyethoxy)-3,5-dimethylphenyl)fluorene, 9,9-bis(4-(2-hydroxyethoxy)-3-tert-butyl-6-methylphenyl)fluorene and 9,9-bis(4-(3-hydroxy-2,2-dimethylpropoxy)phenyl)fluorene, anhydrous sugar alcohols represented by dihydroxy compounds represented by the following general formula (3), and compounds having a cyclic ether structure, such as the Spiro glycol, represented by the following formula (4) and formula (5). Of these, oxyalkylene glycols such as diethylene glycol and triethylene glycol and compounds having a cyclic ether structure are preferred from the standpoints of availability, handling, reactivity during polymerization, and the hue of the polycarbonate resin (A) to be obtained. Preferred of the compounds having a cyclic ether structure are compounds having a plurality of cyclic structures. Preferred from the standpoint of heat resistance are anhydrous sugar alcohols represented by dihydroxy compounds represented by the following formula (3) and the compound having a cyclic ether structure which is represented by the following formula (4). Especially preferred are anhydrous sugar alcohols represented by dihydroxy compounds represented by the following formula (3).

These compounds may be used alone or may be used in combination of two or more thereof, according to the performances required of the polycarbonate resin (A) to be obtained.

[Image Omitted]

Examples of the dihydroxy compounds represented by the general formula (3) include isosorbide, isomannide, and isoidide, which are stereoisomers. These compounds may be used alone or in combination of two or more thereof.

From the standpoint of the light resistance of the polycarbonate resin (A), it is preferred to use dihydroxy compounds having no aromatic ring structure among those dihydroxy compounds. Most preferred of these dihydroxy compounds is isosorbide from the standpoints of availability, ease of production, light resistance, optical properties, moldability, heat resistance, and carbon neutrality. Isosorbide is obtained by the dehydrating condensation of sorbitol, which is produced from various starches that are plant-derived abundant resources and are easily available.

The dihydroxy compound (b) of an alicyclic hydrocarbon having up to 11 carbon atoms is a compound which has a hydrocarbon framework of a cyclic structure and two hydroxy groups. The hydroxy groups each may have been directly bonded to the cyclic structure or may have been bonded to the cyclic structure through a substituent. The cyclic structure may be monocyclic or polycyclic. Examples of the dihydroxy compound (b) include hexanediols such as 1,2-cyclohexanediol, 1,3-cyclohexanediol, 1,4-cyclohexanediol, and 2-methyl-1,4-cyclohexanediol, cyclohexenediols such as 4-cyclohexene-1,2-diol, cyclohexanedimethanols such as 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, and 1,4-cyclohexanedimethanol, cyclohexenedimethanols such as 4-cyclohexene-1,2-dimethanol, norbornanedimethanols such as 2,3-norbornanedimethanol and 2,5-norbornanedimethanol, tricyclodecanedimethanol, pentacyclopentadecanedimethanol, 1,3-adamantanediol, and 2,2-adamantanediol. Preferred of these are 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, and 1,4-cyclohexanedimethanol.

Use of dihydroxy compounds including both a dihydroxy compound (a) having the portion represented by the general formula (1) as part of the structure thereof and a dihydroxy compound (b) of an alicyclic hydrocarbon having up to 11 carbon atoms makes it possible to obtain the effects of improving the flexibility of the polycarbonate resin (A), improving the heat resistance thereof, improving the moldability thereof, etc. Furthermore, use of the alicyclic-hydrocarbon dihydroxy compound (b) in which the number of carbon atoms is not larger than the given value makes it possible to obtain a polycarbonate resin composition having excellent weatherability and an excellent hue. The number of carbon atoms in the alicyclic-hydrocarbon dihydroxy compound (b) is generally 11 or less, preferably 10 or less, more preferably 8 or less.

The dihydroxy compounds to be used for the invention may contain stabilizers such as a reducing agent, antioxidant, free-oxygen scavenger, light stabilizer, antacid, pH stabilizer, and heat stabilizer. Since the dihydroxy compounds to be used for the invention are apt to alter especially under acidic conditions, it is preferred that the dihydroxy compounds should contain a basic stabilizer. Examples of the basic stabilizer include the hydroxides, carbonates, phosphates, phosphites, hypophosphites, borates, and fatty acid salts of Group-1 or Group-2 metals of the long-form periodic table (Nomenclature of Inorganic Chemistry IUPAC Recommendations 2005). Examples thereof further include basic ammonium compounds such as tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, trimethylethylammonium hydroxide, trimethylbenzylammonium hydroxide, trimethylphenylammonium hydroxide, triethylmethylammonium hydroxide, triethylbenzylammonium hydroxide, triethylphenylammonium hydroxide, tributylbenzylammonium hydroxide, tributylphenylammonium hydroxide, tetraphenylammonium hydroxide, benzyltriphenylammonium hydroxide, methyltriphenylammonium hydroxide, and butyltriphenylammonium hydroxide and amine compounds such as 4-aminopyridine, 2-aminopyridine, N,N-dimethyl-4-aminopyridine, 4-diethylaminopyridine, 2-hydroxypyridine, 2-methoxypyridine, 4-methoxypyridine, 2-dimethylaminoimidazole, 2-methoxyimidazole, imidazole, 2-mercaptoimidazole, 2-methylimidazole, and aminoquinoline. Of these, the phosphates and phosphites of sodium or potassium are preferred from the standpoints of the effect thereof and the ease of removal thereof by distillation which will be described later. Especially preferred are disodium hydrogen phosphate and disodium hydrogen phosphite.

There are no particular limitations on the content of those basic stabilizers in the dihydroxy compounds to be used for the invention. In the case where the content thereof is too low, there is a possibility that the effect of preventing the alteration of the dihydroxy compounds to be used for the invention might not be obtained. When the content thereof is too high, there are the cases where the dihydroxy compounds to be used for the invention are altered. Consequently, the content of those basic stabilizers is generally 0.0001-1% by weight, preferably 0.001-0.1% by weight, based on each dihydroxy compound to be used for the invention.

When the dihydroxy compounds to be used for the invention which contain those basic stabilizers are used as a starting material for producing a polycarbonate resin, not only the basic stabilizers themselves serve as a polymerization catalyst to make it difficult to control polymerization rate and quality, but also the presence of the basic stabilizers leads to a deterioration in initial hue, resulting in molded articles having impaired light resistance. It is therefore preferred that the basic stabilizers should be removed with an ion-exchange resin or by distillation or the like before the dihydroxy compounds are used as a starting material for producing a polycarbonate resin.

In the case where a dihydroxy compound to be used for the invention is a compound having a cyclic ether structure, e.g., isosorbide, this dihydroxy compound is apt to be gradually oxidized by oxygen. It is therefore important to prevent water inclusion during storage or production in order to prevent decomposition caused by oxygen. It is also important to use a free-oxygen scavenger or the like or to handle the dihydroxy compound in a nitrogen atmosphere. There are the cases where isosorbide, upon oxidation, generates decomposition products including formic acid. For example, in the case where isosorbide containing those decomposition products is used as a starting material for producing a polycarbonate resin, there is the possibility of resulting in a colored polycarbonate resin. There also is a possibility that the decomposition products considerably deteriorate the properties of the resin. In addition, there are the cases where the decomposition products affect the polymerization reaction to make it impossible to obtain a polymer having a high molecular weight. Use of such isosorbide hence is undesirable.

It is preferred to conduct purification by distillation in order to obtain a dihydroxy compound to be used for the invention which does not contain the oxidative-decomposition products and to remove the basic stabilizers described above. The distillation in this case may be simple distillation or continuous distillation, and is not particularly limited. With respect to distillation conditions, it is preferred to conduct distillation at a reduced pressure in an inert gas atmosphere such as argon or nitrogen. From the standpoint of inhibiting thermal alteration, it is preferred to conduct the distillation under the conditions of 250Â° C. or lower, preferably 200Â° C. or lower, especially 180Â° C. or lower.

Through such purification by distillation, the content of formic acid in the dihydroxy compound to be used for the invention is reduced to 20 weight ppm or less, preferably 10 weight ppm or less, especially preferably 5 weight ppm or less. As a result, when dihydroxy compounds including this dihydroxy compound to be used for the invention are used as a starting material for producing a polycarbonate resin, polymerizability is not impaired and a polycarbonate resin (A) having an excellent hue and excellent thermal stability can be produced. The content of formic acid is determined by ion chromatography.

The polycarbonate resin (A) to be used in the invention can be obtained using dihydroxy compounds including the dihydroxy compounds to be used for the invention described above and a carbonic diester as starting materials, by condensation-polymerizing the starting materials by means of a transesterification reaction.

Examples of the carbonic diester to be used usually include compounds represented by the following general formula (6). One of these carbonic diesters may be used alone, or a mixture of two or more thereof may be used.

[Image Omitted]

(In the general formula (6), A¹and A²each independently are a substituted or unsubstituted aliphatic group having 1-18 carbon atoms or a substituted or unsubstituted aromatic group.)

Examples of the carbonic diesters represented by the general formula (6) include diphenyl carbonate, substituted diphenyl carbonates, e.g., ditolyl carbonate, dimethyl carbonate, diethyl carbonate, and di-t-butyl carbonate. Preferred are diphenyl carbonate and substituted diphenyl carbonates. Especially preferred is diphenyl carbonate. Incidentally, there are the cases where carbonic diesters contain impurities such as chloride ions and where the impurities inhibit the polymerization reaction and impair the hue of the polycarbonate resin to be obtained. It is therefore preferred that a carbonic diester which has been purified by, for example, distillation should be used according to need.

The polycarbonate resin (A) to be used in the invention may be produced by subjecting dihydroxy compounds including the dihydroxy compounds to be used for the invention as described above and a carbonic diester represented by the general formula (6) to a transesterification reaction. More specifically, the polycarbonate resin is obtained by subjecting the starting materials to transesterification and removing the by-product monohydroxy compound, etc. from the system. In this case, polycondensation is usually conducted by means of a transesterification reaction in the presence of a transesterification reaction catalyst.

The transesterification reaction catalyst (hereinafter often referred to simply as â€œcatalystâ€ or â€œpolymerization catalystâ€ ) which can be used for producing the polycarbonate resin (A) to be used in the invention can affect light transmittance as measured especially at a wavelength of 350 nm and yellowness index value.

The catalyst to be used is not limited so long as the catalyst enables the polycarbonate resin (A) produced therewith to satisfy, in particular, light resistance among light resistance, transparency, hue, heat resistance, thermal stability, and mechanical strength. Examples thereof include compounds of metals belonging to the Group 1 or Group 2 of the long-form periodic table (hereinafter referred to simply as â€œGroup 1â€ or â€œGroup 2â€ ) and basic compounds such as basic boron compounds, basic phosphorus compounds, basic ammonium compounds, and amine compounds. It is preferred to use a Group-1 metal compound and/or a Group-2 metal compound.

It is possible to use a basic compound such as a basic boron compound, basic phosphorus compound, basic ammonium compound, or amine compound as an auxiliary together with a Group-1 metal compound and/or a Group-2 metal compound. It is, however, especially preferred to use a Group-1 metal compound and/or a Group-2 metal compound only.

With respect to the form of the Group-1 metal compound and/or Group-2 metal compound, the compound is used usually in the form of a hydroxide or a salt such as carbonate, carboxylate, or phenolate. However, hydroxides, carbonates, and acetates are preferred from the standpoints of availability and handleability, and acetates are preferred from the standpoints of hue and activity in polymerization.

Examples of the Group-1 metal compound include sodium hydroxide, potassium hydroxide, lithium hydroxide, cesium hydroxide, sodium hydrogen carbonate, potassium hydrogen carbonate, lithium hydrogen carbonate, cesium hydrogen carbonate, sodium carbonate, potassium carbonate, lithium carbonate, cesium carbonate, sodium acetate, potassium acetate, lithium acetate, cesium acetate, sodium stearate, potassium stearate, lithium stearate, cesium stearate, sodium boron hydride, potassium boron hydride, lithium boron hydride, cesium boron hydride, phenylated boron-sodium compounds, phenylated boron-potassium compounds, phenylated boron-lithium compounds, phenylated boron-cesium compounds, sodium benzoate, potassium benzoate, lithium benzoate, cesium benzoate, disodium hydrogen phosphate, dipotassium hydrogen phosphate, dilithium hydrogen phosphate, dicesium hydrogen phosphate, disodium phenyl phosphate, dipotassium phenyl phosphate, dilithium phenyl phosphate, dicesium phenyl phosphate, alcoholates or phenolates of sodium, potassium, lithium, and cesium, and the disodium salt, dipotassium salt, dilithium salt, and dicesium salt of bisphenol A. Preferred of these are the lithium compounds.

Examples of the Group-2 metal compound include calcium hydroxide, barium hydroxide, magnesium hydroxide, strontium hydroxide, calcium hydrogen carbonate, barium hydrogen carbonate, magnesium hydrogen carbonate, strontium hydrogen carbonate, calcium carbonate, barium carbonate, magnesium carbonate, strontium carbonate, calcium acetate, barium acetate, magnesium acetate, strontium acetate, calcium stearate, barium stearate, magnesium stearate, and strontium stearate. Preferred of these are the magnesium compounds, the calcium compounds, and the barium compounds. From the standpoints of activity in polymerization and the hue of the polycarbonate resin to be obtained, the magnesium compounds and/or the calcium compounds are more preferred, and the calcium compounds are most preferred.

Examples of the basic boron compounds include the sodium salts, potassium salts, lithium salts, calcium salts, barium salts, magnesium salts, or strontium salts of tetramethylboron, tetraethylboron, tetrapropylboron, tetrabutylboron, trimethylethylboron, trimethylbenzylboron, trimethylphenylboron, triethylmethylboron, triethylbenzylboron, triethylphenylboron, tributylbenzylboron, tributylphenylboron, tetraphenylboron, benzyltriphenylboron, methyltriphenylboron, and butyltriphenylboron.

Examples of the basic phosphorus compounds include triethylphosphine, tri-n-propylphosphine, triisopropylphosphine, tri-n-butylphosphine, triphenylphosphine, tributylphosphine, and quaternary phosphonium salts.

Examples of the basic ammonium compounds include tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, trimethylethylammonium hydroxide, trimethylbenzylammonium hydroxide, trimethylphenylammonium hydroxide, triethylmethylammonium hydroxide, triethylbenzylammonium hydroxide, triethylphenylammonium hydroxide, tributylbenzylammonium hydroxide, tributylphenylammonium hydroxide, tetraphenylammonium hydroxide, benzyltriphenylammonium hydroxide, methyltriphenylammonium hydroxide, and butyltriphenylammonium hydroxide.

Examples of the amine compounds include 4-aminopyridine, 2-aminopyridine, N,N-dimethyl-4-aminopyridine, 4-diethylaminopyridine, 2-hydroxypyridine, 2-methoxypyridine, 4-methoxypyridine, 2-dimethylaminoimidazole, 2-methoxyimidazole, imidazole, 2-mercaptoimidazole, 2-methylimidazole, and aminoquinoline.

The amount of the polymerization catalyst to be used is preferably 0.1-300 Î¼mol, more preferably 0.5-100 Î¼mol, per mole of all dihydroxy compounds subjected to the polymerization. Especially in the case where use is made of one or more compounds containing at least one metal selected from the group consisting of lithium and the Group-2 metals of the long-form periodic table, in particular, in the case where a magnesium compound and/or a calcium compound is used, the amount of this catalyst is preferably 0.1 Î¼mol or more, more preferably 0.5 Î¼mol or more, especially preferably 0.7 Î¼mol or more, in terms of metal amount per mole of all dihydroxy compounds. The suitable upper limit thereof is preferably 20 Î¼mol, more preferably 10 Î¼mol, especially preferably 3 Î¼mol, most preferably 1.5 Î¼mol, in particular 1.0 Î¼mol.

In the case where the amount of the catalyst is too small, the rate of polymerization is too low. As a result, a higher polymerization temperature must be used in order to obtain a polycarbonate resin (A) having a desired molecular weight, and the polycarbonate resin (A) thus obtained has an impaired hue and impaired light resistance. In addition, there is a possibility that an unreacted starting material might volatilize during the polymerization to change the molar proportions of the dihydroxy compounds including the dihydroxy compounds to be used for the invention and of the carbonic diester represented by the general formula (6) and a desired molecular weight might not be reached. On the other hand, in the case where the polymerization catalyst is used in too large an amount, there is a possibility that the resultant polycarbonate resin (A) might have an impaired hue and impaired light resistance.

In the case where diphenyl carbonate or a substituted diphenyl carbonate, e.g., ditolyl carbonate, is used as a carbonic diester represented by the general formula (6) to produce a polycarbonate resin (A) to be used in the invention, phenol or a substituted phenol generates as a by-product and unavoidably remains in the polycarbonate resin (A). However, since phenol and the substituted phenol also have an aromatic ring, there are the cases where not only these compounds absorb ultraviolet rays to serve as a factor contributing to a deterioration in light resistance but also the compounds are causative of an odor during molding. After an ordinary batch reaction, the polycarbonate resin (A) contains an aromatic monohydroxy compound having an aromatic ring, e.g., by-product phenol, in an amount of 1,000 weight ppm or more. From the standpoints of light resistance and odor diminution, it is preferred to reduce the content of the aromatic monohydroxy compound to preferably 700 weight ppm or less, more preferably 500 weight ppm or less, especially 300 weight ppm or less, using a horizontal reactor having excellent volatilizing performance or using an extruder having a vacuum vent. It is, however, noted that it is difficult to industrially completely remove the aromatic monohydroxy compound, and the lower limit of the content thereof is generally 1 weight ppm or higher.

Those aromatic monohydroxy compounds may, of course, have substituents, depending on the starting materials used. For example, the compounds may have an alkyl group having up to 5 carbon atoms or the like.

There is a possibility that when Group-1 metals, especially sodium, potassium, and cesium, in particular, lithium, sodium, potassium, and cesium, are contained in the polycarbonate resin (A) in a large amount, these metals might adversely affect the hue. These metals do not come only from the catalyst used but may come from starting materials and the reactor. Consequently, the total amount of compounds of those metals in the polycarbonate resin (A) is generally 1 weight ppm or less, preferably 0.8 weight ppm or less, more preferably 0.7 weight ppm or less, in terms of metal amount.

The content of metals in the polycarbonate resin (A) can be determined by recovering the metals contained in the polycarbonate resin by a technique such as wet ashing and then determining the amount of the metals using a technique such as atomic emission, atomic absorption, or inductively coupled plasma (ICP) spectroscopy.

Although the polycarbonate resin (A) to be used in the invention is obtained by condensation-polymerizing dihydroxy compounds including the dihydroxy compounds to be used for the invention with a carbonic diester represented by the general formula (6) by means of a transesterification reaction, it is preferred to evenly mix the starting materials, i.e., the dihydroxy compounds and the carbonic diester, prior to the transesterification reaction.

The temperature at which the starting materials are mixed together is generally 80Â° C. or higher, preferably 90Â° C. or higher, and the upper limit thereof is generally 250Â° C. or lower, preferably 200Â° C. or lower, more preferably 150Â° C. or lower. Especially suitable is a temperature of 100-120Â° C. So long as the lower limit of the mixing temperature is within that range, the starting materials show a satisfactory dissolution rate and satisfactory solubility, and troubles such as solidification are less apt to arise. So long as the upper limit of the mixing temperature is within that range, the dihydroxy compounds are less apt to deteriorate thermally and, as a result, the polycarbonate resin obtained has a satisfactory hue, which does not adversely affect light resistance.

It is preferred from the standpoint of preventing hue deterioration that an operation for mixing the dihydroxy compounds including the dihydroxy compounds to be used for the invention and the carbonic diester represented by the general formula (6), which are starting materials for the polycarbonate resin (A) to be used in the invention, should be conducted in an atmosphere having an oxygen concentration of 10 vol % or less, preferably 0.0001-10 vol %, especially 0.0001-5 vol %, in particular 0.0001-1 vol %.

It is preferred that for obtaining the polycarbonate resin (A) to be used in the invention, the carbonic diester represented by the general formula (6) should be used in such an amount that the molar proportion thereof to the dihydroxy compounds to be subjected to the reaction, which include the dihydroxy compounds to be used for the invention, is 0.90-1.20. The molar proportion thereof is more preferably 0.95-1.10.

So long as the molar proportion thereof is not less than the lower limit, the polycarbonate resin produced is prevented from having an increased amount of terminal hydroxyl groups. This polymer hence has thermal stability and does not take a color upon molding. Furthermore, this transesterification reaction is less apt to encounter troubles that the rate of the reaction decreases and that a desired high-molecular polymer is not obtained.

So long as the molar proportion thereof is not higher than the upper limit, there is no possibility that the rate of transesterification reaction might decrease or that it might be difficult to produce a polycarbonate resin (A) having a desired molecular weight. The decrease in the rate of transesterification reaction enhances heat history during the polymerization reaction, resulting in a possibility that the enhanced heat history might impair the hue and light resistance of the polycarbonate resin obtained.

Furthermore, when the molar proportion of the carbonic diester represented by the general formula (6) to the dihydroxy compounds including the dihydroxy compounds to be used for the invention is too high, there are the cases where the polycarbonate resin (A) obtained has an increased content of the residual carbonic diester and the residual carbonic diester absorbs ultraviolet rays to impair the light resistance of the polycarbonate resin. Such too high proportions of the carbonic diester are hence undesirable. The concentration of the carbonic diester remaining in the polycarbonate resin (A) to be used in the invention is preferably 200 weight ppm or less, more preferably 100 weight ppm or less, even more preferably 60 weight ppm or less, especially preferably 30 weight ppm or less. Actually, the polycarbonate resin (A) may contain unreacted carbonic diesters. A lower limit of the concentration thereof is generally 1 weight ppm or higher.

In the invention, a process in which the dihydroxy compounds are condensation-polymerized with the carbonic diester is conducted in the presence of the catalyst described above usually in multiple stages using a plurality of reactors. The mode of reaction operation may be any of the batch type, the continuous type, and a combination of the batch type and the continuous type.

It is preferred that in the initial stage of the polymerization, the polymerization should be conducted at a relatively low temperature and under relatively low vacuum to obtain a prepolymer, and that in the late stage of the polymerization, the polymerization should be conducted at a relatively high temperature under relatively high vacuum to heighten the molecular weight to a given value. It is, however, important from the standpoints of hue and light resistance that a jacket temperature, an internal temperature, and an internal pressure of the system should be suitably selected for each molecular-weight stage. For example, in the case where either temperature or pressure is changed too speedily before the polymerization reaction reaches a given value, an unreacted monomer is distilled off to change the molar ratio of the dihydroxy compounds to the carbonic diester. This may result in a decrease in polymerization rate or make it impossible to obtain a polymer having a given molecular weight or having given end groups. There hence is a possibility that the objects of the invention cannot finally be accomplished.

To provide a polymerizer with a reflux condenser is effective for inhibiting the monomers from being distilled off. This effect is high especially in the reactor for the initial stage of polymerization, in which the amount of unreacted monomer ingredients is large. The temperature of the coolant which is being introduced into the reflux condenser can be suitably selected according to the monomers used. However, the temperature of the coolant being introduced into the reflux condenser, as measured at the inlet of the reflux condenser, is generally 45-180Â° C., preferably 80-150Â° C., especially preferably 100-130Â° C. In the case where the temperature of the coolant being introduced into the reflux condenser is too high, the amount of the monomers being refluxed decreases, resulting in a decrease in the effect of the refluxing. In the case where the temperature thereof is too low, the efficiency of the removal by distillation of the monohydroxy compound to be removed by distillation tends to decrease. As the coolant, use may be made of hot water, steam, a heat-medium oil, or the like. Preferred is steam or a heat-medium oil.

The selection of the kind and amount of a catalyst described above is important for maintaining a suitable polymerization rate and inhibiting the monomers from being distilled off and for simultaneously enabling the finally obtained polycarbonate resin to have intact properties such as hue, thermal stability, and light resistance.

It is preferred that the polycarbonate resin (A) to be used in the invention should be produced by polymerizing the starting materials in multiple stages using a catalyst and a plurality of reactors. The reasons why the polymerization is conducted in a plurality of reactors are that in the initial stage of the polymerization reaction, since the monomers are contained in a large amount in the liquid reaction mixture, it is important that the monomers should be inhibited from volatilizing off while maintaining a necessary polymerization rate, and that in the late stage of the polymerization reaction, it is important to sufficiently remove by distillation the by-product monohydroxy compound in order to shift the equilibrium to the polymerization side. For thus setting different sets of polymerization reaction conditions, it is preferred to use a plurality of polymerizers arranged serially, from the standpoint of production efficiency.

The number of reactors to be used in the process of the invention is not limited so long as the number thereof is at least 2 as described above. From the standpoints of production efficiency, etc., the number thereof is 3 or more, preferably 3-5, especially preferably 4.

In the invention, the process may be conducted in various manners so long as two or more reactors are used. For example, a plurality of reaction stages differing in conditions are formed in any of the reactors, or the temperature and the pressure may be continuously changed in any of the reactors.

In the invention, the polymerization catalyst can be introduced into a starting-material preparation tank or a starting-material storage tank, or can be introduced directly into a polymerization vessel. However, from the standpoints of stability of feeding and polymerization control, a catalyst supply line is disposed somewhere in a starting-material line before a polymerization vessel, and the catalyst is supplied preferably in the form of an aqueous solution. With respect to polymerization reaction temperature, too low temperatures result in a decrease in productivity and cause the product to undergo an enhanced heat history. Too high temperatures not only result in monomer volatilization but also result in the possibility of enhancing degradation and coloring of the polycarbonate resin.

Specifically, the reaction in the first stage may be conducted at a temperature of 140-270Â° C., preferably 180-240Â° C., more preferably 200-230Â° C., in terms of the maximum internal temperature of the polymerizer, and a pressure of 110-1 kPa, preferably 70-5 kPa, more preferably 30-10 kPa (absolute pressure) for 0.1-10 hours, preferably 0.5-3 hours, while the monohydroxy compound which generates is being removed from the reaction system by distillation.

In the second and any succeeding stages, the pressure of the reaction system is gradually lowered from the pressure used in the first stage, and the polymerization is conducted while the monohydroxy compound which generates is being continuously removed from the reaction system. Finally, the pressure (absolute pressure) of the reaction system is lowered to 200 Pa or below. The second and any succeeding stages are thus conducted at a maximum internal temperature of 210-270Â° C., preferably 220-250Â° C., for a period of generally 0.1-10 hours, preferably 1-6 hours, especially preferably 0.5-3 hours.

Especially from the standpoints of inhibiting the polycarbonate resin (A) from taking a color or deteriorating thermally and of thereby obtaining the polycarbonate resin (A) having a satisfactory hue and satisfactory light resistance, it is preferred that the maximum internal temperature in all reaction stages should be lower than 250Â° C., in particular 225-245Â° C. From the standpoints of inhibiting the rate of polymerization from decreasing in the latter half of the polymerization reaction and of thereby minimizing the deterioration caused by heat history, it is preferred to use, in the final stage of the polymerization, a horizontal reactor having excellent plug flow characteristics and interface renewal characteristics.

In the case where the polymerization is conducted at too high a temperature or for too long a period in order to obtain a polycarbonate resin (A) having a given molecular weight, there is a tendency that the resultant polycarbonate resin has a reduced ultraviolet transmittance and an increased YI value.

From the standpoint of effective utilization of resources, it is preferred that the monohydroxy compound which generated as a by-product should be reused as a starting material for diphenyl carbonate, bisphenol A, or the like after purified according to need.

The polycarbonate resin (A) to be used in the invention, after having been obtained through polycondensation as described above, is usually solidified by cooling and pelletized with a rotary cutter or the like.

Methods for the pelletization are not limited. Examples thereof include: a method in which the polycarbonate resin is discharged in a molten state from the final polymerizer, cooled and solidified in a strand form, and pelletized; a method in which the resin is fed in a molten state from the final polymerizer to a single- or twin-screw extruder, melt-extruded, subsequently cooled and solidified, and pelletized; and a method which includes discharging the resin in a molten state from the final polymerizer, cooling and solidifying the resin in a strand form, temporarily pelletizing the resin, thereafter feeding the resin to a single- or twin-screw extruder again, melt-extruding the resin, and then cooling, solidifying, and pelletizing the resin.

During such operations, residual monomers can be removed by volatilization under vacuum within the extruder. It is also possible to add generally known additives such as a heat stabilizer, neutralizing agent, ultraviolet absorber, release agent, colorant, antistatic agent, slip agent, lubricant, plasticizer, compatibilizing agent, and flame retardant and knead the mixture within the extruder.

The temperature to be used for melt kneading in the extruder depends on the glass transition temperature and molecular weight of the polycarbonate resin (A). However, the melt kneading temperature is generally 150-300Â° C., preferably 200-270Â° C., more preferably 230-260Â° C. In the case where the melt kneading temperature is lower than 150Â° C., the polycarbonate resin (A) has a high melt viscosity and imposes an increased load on the extruder, resulting in a decrease in productivity. In the case where the melt kneading temperature is higher than 300Â° C., the polycarbonate thermally deteriorates considerably, resulting in a decrease in mechanical strength due to the decrease in molecular weight and further resulting in coloring and gas evolution.

When the polycarbonate resin (A) to be used in the invention is produced, it is desirable to dispose a filter in order to prevent inclusion of foreign matter. The position where a filter is disposed preferably is on the downstream side of the extruder. The rejection size (opening size) of the filter is preferably 100 Î¼m or smaller in terms of 99% removal filtration accuracy. Especially when the resin is for use in film applications or the like for which inclusion of minute foreign particles should be avoided, the opening size of the filter is preferably 40 Î¼m or smaller, more preferably 10 Î¼m or smaller.

From the standpoint of preventing inclusion of foreign matter from occurring after extrusion, it is desirable that the polycarbonate resin (A) to be used in the invention should be extruded in a clean room having a cleanliness preferably higher than class 7 defined in JIS B 9920 (2002), more preferably higher than class 6.

Furthermore, for cooling and pelletizing the extruded polycarbonate resin, it is preferred to use a cooling method such as air cooling or water cooling. It is desirable that air from which airborne foreign matter has been removed beforehand with a high-efficiency particulate air filter or the like should be used for the air cooling to prevent airborne foreign matter from adhering again. In the case of conducting water cooling, it is desirable to use water from which metallic substances have been removed with an ion-exchange resin or the like and from which foreign matter has been removed with a filter. It is preferred that the filter to be used should have an opening size of 10-0.45 Î¼m in terms of 99% removal filtration accuracy.

The molecular weight of the thus-obtained polycarbonate resin (A) to be used in the invention can be expressed in terms of reduced viscosity. The reduced viscosity thereof is generally 0.30 dL/g or higher, preferably 0.35 dL/g or higher. The upper limit of the reduced viscosity thereof may be 1.20 dL/g or less and is more preferably 1.00 dL/g or less, even more preferably 0.80 dL/g or less.

So long as the reduced viscosity of the polycarbonate resin (A) is not less than the lower limit, the polycarbonate resin (A) gives molded articles having sufficient mechanical strength. Such reduced viscosities hence are preferred. So long as the reduced viscosity thereof is not higher than the upper limit, this polycarbonate resin (A) is prevented from showing poor flowability during molding, resulting in improvements in productivity and moldability.

Incidentally, the reduced viscosity of a polycarbonate is determined by preparing a solution thereof having a polycarbonate concentration precisely adjusted to 0.6 g/dL using methylene chloride as a solvent and measuring the viscosity of the solution with an Ubbelohde viscometer at a temperature of 20.0Â±0.1Â° C.

In the polycarbonate resin (A) to be used in the invention, the lower limit of the concentration of the end group represented by the following general formula (7) is generally 20 Î¼eq/g or higher, preferably 40 Î¼eq/g or higher, especially preferably 50 Î¼eq/g or higher. The upper limit thereof is generally 160 Î¼eq/g or less, preferably 140 Î¼eq/g or less, especially preferably 100 Î¼eq/g or less.

In the case where the concentration of the end group represented by the following general formula (7) is too high, there is a possibility that even when the polycarbonate resin has a satisfactory hue immediately after polymerization or during molding, the high end group concentration might result in a hue deterioration through exposure to ultraviolet rays. Conversely, in the case where the concentration thereof is too low, there is a possibility that this polycarbonate resin might have reduced thermal stability.

Examples of methods for regulating the concentration of the end group represented by the following general formula (7) include: to regulate the molar proportions of the starting materials, i.e., dihydroxy compounds including the dihydroxy compounds to be used for the invention and a carbonic diester represented by the general formula (6); and to control factors during the transesterification reaction, such as the kind and amount of a catalyst, polymerization pressure, and polymerization temperature.

[Image Omitted]

When the number of moles of the H bonded to the aromatic rings of the polycarbonate resin (A) to be used in the invention is expressed by C and the number of moles of the H bonded to the part other than the aromatic rings is expressed by D, then the proportion of the number of moles of the H bonded to the aromatic rings to the number of moles of all H is expressed by C/(C+D). Since there is a possibility that the aromatic rings, which have ultraviolet-absorbing ability, might affect light resistance as stated above, it is preferred that C/(C+D) should be 0.1 or less, more preferably 0.05 or less, even more preferably 0.02 or less, especially preferably 0.01 or less. The value of C/(C+D) can be determined by ¹H NMR spectroscopy.

The polycarbonate resin to be used in the invention can be formed into molded objects by generally known techniques such as injection molding, extrusion molding, and compression molding.

Before the polycarbonate resin (A) to be used in the invention is molded by various molding techniques, additives such as a heat stabilizer, neutralizing agent, ultraviolet absorber, release agent, colorant, antistatic agent, slip agent, lubricant, plasticizer, compatibilizing agent, and flame retardant can be incorporated into the polycarbonate resin (A) according to need by means of a tumbling mixer, supermixer, floating mixer, twin-cylinder mixer, Nauta mixer, Banbury mixer, extruder, or the like.

The polycarbonate resin (A) has a glass transition temperature of preferably 75-105Â° C., more preferably 80-105Â° C., even more preferably 85-105Â° C. By using the polycarbonate resin (A) having a glass transition temperature within that range, molded articles having excellent heat resistance can be provided.

The aromatic polycarbonate resin (B) to be used in the invention can be a polycarbonate resin which is made up of constituent units derived from one or more dihydroxy compounds and linked to each other through a carbonate bond, and which has constituent units represented by the following general formula (2) as constituent units derived from a dihydroxy compound.

[Image Omitted]

(R¹to R⁸in the general formula (2) each independently represent a hydrogen atom or a substituent. Y represents a single bond or a divalent group.)

Examples of the substituents represented by R¹to R⁸in the general formula (2) include alkyl groups which have 1-10 carbon atoms and may have one or more substituents, alkoxy groups which have 1-10 carbon atoms and may have one or more substituents, halogen radicals, halogenated alkyl groups having 1-10 carbon atoms, or aromatic groups which have 6-20 carbon atoms and may have one or more substituents. Preferred of these are alkyl groups which have 1-10 carbon atoms and may have one or more substituents or aromatic groups which have 6-20 carbon atoms and may have one or more substituents. Examples of the divalent group Y in the general formula (2) include chain-structure alkylene groups which have 1-6 carbon atoms and may have one or more substituents, chain-structure alkylidene groups which have 1-6 carbon atoms and may have one or more substituents, cyclic-structure alkylene groups which have 3-6 carbon atoms and may have one or more substituents, and cyclic-structure alkylidene groups which have 3-6 carbon atoms and may have one or more substituents, and further include â€”Oâ€”, â€”Sâ€”, â€”COâ€”, or â€”SO₂â€”. The substituents are not particularly limited unless the effects of the invention are lessened thereby. However, the substituents usually have a molecular weight of 200 or less. The substituents possessed by the chain-structure alkylene groups having 1-6 carbon atoms preferably are aryl groups, and phenyl is especially preferred.

The aromatic polycarbonate resin (B) to be used in the invention may be a homopolymer or a copolymer. When the resin (B) is a copolymer, this copolymer preferably is a polycarbonate resin in which constituent units derived from a dihydroxy compound represented by the general formula (1) are contained in a largest proportion among all constituent units each derived from a dihydroxy compound. It is more preferred to use a polycarbonate resin in which the proportion of the structures derived from a dihydroxy compound represented by the general formula (1) to all constituent units each derived from a dihydroxy compound is 50% by mole or higher, even more preferably 70% by mole or higher, especially preferably 90% by mole or higher.

The aromatic polycarbonate resin (B) may have a branched structure or a linear structure, or may be a mixture of a branched structure and a linear structure. Furthermore, the aromatic polycarbonate resin (B) to be used in the invention may be a resin which contains constituent units derived from a dihydroxy compound having the portion represented by the general formula (1). It is, however, noted that when the aromatic polycarbonate resin (B) to be used is a polycarbonate resin which contains constituent units derived from a dihydroxy compound having the portion represented by the general formula (1), then this polycarbonate resin differs in structure from the polycarbonate resin (A).

The constituent units which are derived from one or more dihydroxy compounds and which constitute the aromatic polycarbonate resin (B) to be used in the invention each is a unit formed by removing the hydrogen atoms from the hydroxyl groups of a dihydroxy compound. Examples of the corresponding dihydroxy compounds include the following.

Biphenyl compounds such as 4,4â€²-biphenol, 2,4â€²-biphenol, 3,3â€²-dimethyl-4,4â€²-dihydroxy-1,1â€²-biphenyl, 3,3â€²-dimethyl-2,4â€²-dihydroxy-1,1â€²-biphenyl, 3,3â€²-di(t-butyl)-4,4â€²-dihydroxy-1,1â€²-biphenyl, 3,3â€²,5,5â€²-tetramethyl-4,4â€²-dihydroxy-1,1â€²-biphenyl, 3,3â€²,5,5â€²-tetra(t-butyl)-4,4â€²-dihydroxy-1,1â€²-biphenyl, and 2,2â€²,3,3â€²,5,5â€²-hexamethyl-4,4â€²-dihydroxy-1,1â€²-biphenyl.

Bisphenol compounds such as bis(4-hydroxy-3,5-dimethylphenyl)methane, bis(4-hydroxyphenyl)methane, bis(4-hydroxy-3-methylphenyl)methane, 1,1-bis(4-hydroxyphenyl)ethane, 1,1-bis(4-hydroxyphenyl)propane, 2,2-bis(4-hydroxyphenyl)propane, 2,2-bis(4-hydroxy-3-methylphenyl)propane, 2,2-bis(4-hydroxyphenyl)butane, 2,2-bis(4-hydroxyphenyl)pentane, 2,2-bis(4-hydroxyphenyl)-3-methylbutane, 2,2-bis(4-hydroxyphenyl)hexane, 2,2-bis(4-hydroxyphenyl)-4-methylpentane, 1,1-bis(4-hydroxyphenyl)cyclopentane, 1,1-bis(4-hydroxyphenyl)cyclohexane, bis(3-phenyl-4-hydroxyphenyl)methane, 1,1-bis(3-phenyl-4-hydroxyphenyl)ethane, 1,1-bis(3-phenyl-4-hydroxyphenyl)propane, 2,2-bis(3-phenyl-4-hydroxyphenyl)propane, 1,1-bis(4-hydroxy-3-methylphenyl)ethane, 2,2-bis(4-hydroxy-3-ethylphenyl)propane, 2,2-bis(4-hydroxy-3-isopropylphenyl)propane, 2,2-bis(4-hydroxy-3-sec-butylphenyl)propane, 1,1-bis(4-hydroxy-3,5-dimethylphenyl)ethane, 2,2-bis(4-hydroxy-3,5-dimethylphenyl)propane, 1,1-bis(4-hydroxy-3,6-dimethylphenyl)ethane, bis(4-hydroxy-2,3,5-trimethylphenyl)methane, 1,1-bis(4-hydroxy-2,3,5-trimethylphenyl)ethane, 2,2-bis(4-hydroxy-2,3,5-trimethylphenyl)propane, bis(4-hydroxy-2,3,5-trimethylphenyl)phenylmethane, 1,1-bis(4-hydroxy-2,3,5-trimethylphenyl)phenylethane, 1,1-bis(4-hydroxy-2,3,5-trimethylphenyl)cyclohexane, bis(4-hydroxyphenyl)phenylmethane, 1,1-bis(4-hydroxyphenyl)-1-phenylethane, 1,1-bis(4-hydroxyphenyl)-1-phenylpropane, bis(4-hydroxyphenyl)diphenylmethane, bis(4-hydroxyphenyl)dibenzylmethane, 4,4â€²-[1,4-phenylenebis(1-methylethylidene)]bis[phenol], 4,4â€²-[1,4-phenylenebismethylene]bis[phenol], 4,4â€²-[1,4-phenylenebis(1-methylethylidene)]bis[2,6-dimethylphenol], 4,4â€²-[1,4-phenylenebismethylene]bis[2,6-dimethylphenol], 4,4â€²-[1,4-phenylenebismethylene]bis[2,3,6-trimethylphenol], 4,4â€²-[1,4-phenylenebis(1-methylethylidene)]bis[2,3,6-trimethylphenol], 4,4â€²-[1,3-phenylenebis(1-methylethylidene)]bis[2,3,6-trimethylphenol], 4,4â€²-dihydroxydiphenyl ether, 4,4â€²-dihydroxydiphenyl sulfone, 4,4â€²-dihydroxydiphenyl sulfide, 3,3â€²,5,5â€²-tetramethyl-4,4â€²-dihydroxydiphenyl ether, 3,3â€²,5,5â€²-tetramethyl-4,4â€²-dihydroxydiphenyl sulfone, 3,3â€²,5,5â€²-tetramethyl-4,4â€²-dihydroxydiphenyl sulfide, phenolphthalein, 4,4â€²-[1,4-phenylenebis(1-methylvinylidene)]bisphenol, 4,4â€²-[1,4-phenylenebis(1-methylvinylidene)]bis[2-methylphenol], (2-hydroxyphenyl)(4-hydroxyphenyl)methane, (2-hydroxy-5-methylphenyl)(4-hydroxy-3-methylphenyl)methane, 1,1-(2-hydroxyphenyl)(4-hydroxyphenyl)ethane, 2,2-(2-hydroxyphenyl)(4-hydroxyphenyl)propane, and 1,1-(2-hydroxyphenyl)(4-hydroxyphenyl)propane.

Halogenated bisphenol compounds such as 2,2-bis(3,5-dibromo-4-hydroxyphenyl)propane and 2,2-bis(3,5-dichloro-4-hydroxyphenyl)propane.

Preferred of these dihydroxy compounds are bis(4-hydroxy-3,5-dimethylphenyl)methane, bis(4-hydroxyphenyl)methane, bis(4-hydroxy-3-methylphenyl)methane, 1,1-bis(4-hydroxyphenyl)ethane, 2,2-bis(4-hydroxyphenyl)propane, 2,2-bis(4-hydroxy-3-methylphenyl)propane, 2,2-bis(4-hydroxy-3,5-dimethylphenyl)propane, 1,1-bis(4-hydroxyphenyl)cyclohexane, bis(4-hydroxyphenyl)phenylmethane, 1,1-bis(4-hydroxyphenyl)-1-phenylethane, 1,1-bis(4-hydroxyphenyl)-1-phenylpropane, bis(4-hydroxyphenyl)diphenylmethane, 2-hydroxyphenyl(4-hydroxyphenyl)methane, and 2,2-(2-hydroxyphenyl)(4-hydroxyphenyl)propane.

Especially preferred of these are bis(4-hydroxyphenyl)methane, bis(4-hydroxy-3-methylphenyl)methane, bis(4-hydroxy-3,5-dimethylphenyl)methane, 2,2-bis(4-hydroxyphenyl)propane, 2,2-bis(4-hydroxy-3-methylphenyl)propane, 2,2-bis(4-hydroxy-3,5-dimethylphenyl)propane, and 1,1-bis(4-hydroxyphenyl)cyclohexane.

For producing the aromatic polycarbonate resin (B) to be used in the invention, any conventionally known process, such as a phosgene method, transesterification method, or pyridine method, may be used. A process for producing the aromatic polycarbonate resin (B) by a transesterification method is explained below as an example. The transesterification method is a production method in which a dihydroxy compound and a carbonic diester are subjected to melt transesterification polycondensation in the presence of a basic catalyst and an acidic substance for neutralizing the basic catalyst. Examples of the dihydroxy compound include the biphenyl compounds and bisphenol compounds shown above as examples.

Representative examples of the carbonic diester include diphenyl carbonate, ditolyl carbonate, bis(chlorophenyl) carbonate, di-m-cresyl carbonate, dinaphthyl carbonate, bis(biphenyl) carbonate, diethyl carbonate, dimethyl carbonate, dibutyl carbonate, and dicyclohexyl carbonate. It is especially preferred to use diphenyl carbonate among these.

From the standpoint of a balance between dynamic properties and moldability, the viscosity-average molecular weight of the aromatic polycarbonate resin (B) to be used in the invention is in the range of generally from 8,000 to 30,000, preferably from 10,000 to 25,000.

The reduced viscosity of the aromatic polycarbonate resin (B) is determined by preparing a solution thereof having a polycarbonate concentration precisely adjusted to 0.60 g/dL using methylene chloride as a solvent and measuring the viscosity of the solution at a temperature of 20.0Â±0.1Â° C. The reduced viscosity thereof is in the range of generally from 0.23 dL/g to 0.72 dL/g, preferably from 0.27 dL/g to 0.61 dL/g.

In the invention, one aromatic polycarbonate resin (B) may be used alone or a mixture of two or more aromatic polycarbonate resins (B) may be used.

It is preferred that the polycarbonate resin composition according to the invention should have a single glass transition temperature from the standpoint of enabling the polycarbonate resin composition and molded articles of the polycarbonate resin to retain transparency.

The polycarbonate resin (A) and aromatic polycarbonate resin (B) in the polycarbonate resin composition may be any polycarbonate resins of different kinds. It is preferred that the polycarbonate resin (A) should have a cyclic structure. In particular, it is especially preferred that the polycarbonate resin (A) should contain isosorbide as a dihydroxy compound having the portion represented by the general formula (1) as part of the structure thereof.

The polycarbonate resin composition according to the invention is a polycarbonate resin composition which includes a polycarbonate resin (A) containing constituent units derived from a dihydroxy compound (a) having the portion represented by the following general formula (1) as part of the structure thereof and constituent units derived from a dihydroxy compound (b) of an alicyclic hydrocarbon and an aromatic polycarbonate resin (B).

[Chem. 11]

î¢ CH₂â€”Oî¢ â€ƒâ€ƒ(1)

(The case where the portion represented by the general formula (1) is part of â€”CH₂â€”Oâ€”H is excluded.)

[Image Omitted]

(R¹to R⁸in the general formula (2) each independently represent a hydrogen atom or a substituent. Y represents a single bond or a divalent group.)

In the polycarbonate resin composition, the proportion of constituent units derived from the dihydroxy compound (b) of an alicyclic hydrocarbon in the polycarbonate resin (A) is generally 35 mol % or higher, preferably 40 mol % or higher, more preferably 50 mol % or higher, especially preferably 55 mol % or higher. On the other hand, the proportion thereof is preferably 90 mol % or less, more preferably 80 mol % or less, especially preferably 70 mol % or less.

In the case where the proportion of constituent units derived from the dihydroxy compound (b) of an alicyclic hydrocarbon in the polycarbonate resin (A) is too low, the composition tends to have an increased value of yellowness index (YI) after the sunshine weatherometer irradiation test which will be described later.

The proportion of the aromatic polycarbonate resin (B) in the polycarbonate resin composition constituted of the polycarbonate resin (A) and the aromatic polycarbonate resin (B) is preferably 20% by weight or higher, preferably 30% by weight or higher, more preferably 50% by weight or higher, especially preferably 55% by weight or higher. On the other hand, the proportion thereof is preferably 90% by weight or less, more preferably 80% by weigh or less, especially preferably 70% by weight or less.

The polycarbonate resin composition and polycarbonate resin molded article of the invention can contain not only resins other than polycarbonate resins but also additives which are not resins.

Examples of resins which are not polycarbonate resins and can be incorporated for the purpose of further improving or regulating moldability or other properties include resins such as polyester resins, polyethers, polyamides, polyolefins, and poly(methyl methacrylate) and rubbery modifiers such as core-shell type, graft type, or linear random and block copolymers. With respect to the amount of such resins to be incorporated other than polycarbonate resins, it is preferred to incorporate such other resins in an amount of 1-30 parts by weight per 100 parts by weight of the mixture of the polycarbonate resin (A) to be used in the invention and the aromatic polycarbonate resin (B). The amount of such other resins to be incorporated is more preferably 3-20 parts by weight, even more preferably 5-10 parts by weight.

A heat stabilizer can be incorporated into the polycarbonate resin composition and polycarbonate resin molded article of the invention in order to prevent the composition from decreasing in molecular weight and deteriorating in hue during molding. Examples of the heat stabilizer include phosphorous acid, phosphoric acid, phosphonous acid, phosphonic acid, and esters thereof. Specific examples thereof include triphenyl phosphite, tris(nonylphenyl) phosphite, tris(2,4-di-tert-butylphenyl) phosphite, tridecyl phosphite, trioctyl phosphite, trioctadecyl phosphite, didecyl monophenyl phosphite, dioctyl monophenyl phosphite, diisopropyl monophenyl phosphite, monobutyl diphenyl phosphite, monodecyl diphenyl phosphite, monooctyl diphenyl phosphite, bis(2,6-di-tert-butyl-4-methylphenyl) pentaerythritol diphosphite, 2,2-methylenebis(4,6-di-tert-butylphenyl) octyl phosphite, bis(nonylphenyl) pentaerythritol diphosphite, bis(2,4-di-tert-butylphenyl) pentaerythritol diphosphite, distearyl pentaerythritol diphosphite, tributyl phosphate, triethyl phosphate, trimethyl phosphate, triphenyl phosphate, diphenyl mono-o-xenyl phosphate, dibutyl phosphate, dioctyl phosphate, diisopropyl phosphate, tetrakis(2,4-di-tert-butylphenyl) 4,4â€²-biphenylenediphosphinate, dimethyl benzenephosphonate, diethyl benzenephosphonate, and dipropyl benzenephosphonate. Preferred of these are trisnonylphenyl phosphite, trimethyl phosphate, tris(2,4-di-tert-butylphenyl) phosphite, bis(2,4-di-tert-butylphenyl) pentaerythritol diphosphite, bis(2,6-di-tert-butyl-4-methylphenyl) pentaerythritol diphosphite, and dimethyl benzenephosphonate.

One of these heat stabilizers may be used alone, or two or more thereof may be used in combination. With respect to the amount of the heat stabilizer to be incorporated, it is preferred to incorporate the heat stabilizer in an amount of 0.0001-1 part by weight per 100 parts by weight of the mixture of the polycarbonate resin (A) to be used in the invention and the aromatic polycarbonate resin (B). The amount of the heat stabilizer to be incorporated is more preferably 0.0005-0.5 parts by weight, even more preferably 0.001-0.2 parts by weight. By incorporating a heat stabilizer in an amount within that range, the resins can be prevented from decreasing in molecular weight or discoloring, while preventing the additive from bleeding or arousing other troubles.

A generally known antioxidant can be incorporated into the polycarbonate resin composition and polycarbonate resin molded article of the invention for the purpose of preventing oxidation. Examples of the antioxidant include one or more of pentaerythritol tetrakis(3-mercaptopropionate), pentaerythritol tetrakis(3-laurylthiopropionate), glycerol 3-stearylthiopropionate, triethylene glycol bis[3-(3-tert-butyl-5-methyl-4-hydroxyphenyl)propionate], 1,6-hexanediol bis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate], pentaerythritol tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate], octadecyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, 1,3,5-trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxyphenyl)benzene, N,N-hexamethylenebis(3,5-di-tert-butyl-4-hydroxyhydrocinnamamide), diethyl 3,5-di-tert-butyl-4-hydroxybenzylphosphonate, tris(3,5-di-tert-butyl-4-hydroxybenzyl) isocyanurate, tetrakis(2,4-di-tert-butylphenyl) 4,4â€²-biphenylenediphosphinate, 3,9-bis{1,1-dimethyl-2-[Î²-(3-tert-butyl-4-hydroxy-5-methylphenyl)propionyloxy]ethyl}-2,4,8,10-tetraoxaspiro(5,5)undecane, and the like. With respect to the amount of the antioxidant to be incorporated, it is preferred to incorporate the antioxidant in an amount of 0.0001-1 part by weight per 100 parts by weight of the mixture of the polycarbonate resin (A) to be used in the invention and the aromatic polycarbonate resin (B). The amount of the antioxidant to be incorporated is more preferably 0.0005-0.5 parts by weight, even more preferably 0.001-0.2 parts by weight. By incorporating an antioxidant in an amount within that range, the resins can be prevented from oxidatively deteriorating, while preventing the antioxidant from bleeding to the surfaces of the molded articles and from reducing the mechanical properties of various molded articles.

An ultraviolet absorber can be incorporated for the purpose of further improving the weatherability of the polycarbonate resin composition and polycarbonate resin molded article of the invention. Examples of the ultraviolet absorber include 2-(2â€²-hydroxy-5â€²-tert-octylphenyl)benzotriazole, 2-(3-tert-butyl-5-methyl-2-hydroxyphenyl)-5-chlorobenzotriazole, 2-(5-methyl-2-hydroxyphenyl)benzotriazole, 2-[2-hydroxy-3,5-bis(Î±,Î±-dimethylbenzyl)phenyl]-2H-benzotriazole, 2,2â€²-methylenebis(4-cumyl-6-benzotriazolephenyl), and 2,2â€²-p-phenylenebis(1,3-benzoxazin-4-one). Ultraviolet absorbers having a melting point in the range of, in particular, 120-250Â° C. are preferred. When an ultraviolet absorber having a melting point of 120Â° C. or higher is used, the surface dulling of molded articles which is caused by a gas is mitigated. Specifically, use is made of a benzotriazole-based ultraviolet absorber such as 2-(2â€²-hydroxy-5â€²-methylphenyl)benzotriazole, 2-(2â€²-hydroxy-3â€²-tert-butyl-5â€²-methylphenyl)-5-chlorobenzotriazole, 2-[2â€²-hydroxy-3â€²-(3â€³,4â€³,5â€³,6â€³-tetrahydrophthalimidomethyl)-5â€²-methylphenyl]benzotriazole, 2,2-methylenebis[4-(1,1,3,3-tetramethylbutyl)-6-(2H-benzotriazol-2-yl)phenol, or 2-(2-hydroxy-3,5-dicumylphenyl)benzotriazole. Especially preferred of these are 2-(2-hydroxy-3,5-dicumylphenyl)benzotriazole and 2,2-methylenebis[4-(1,1,3,3-tetramethylbutyl)-6-(2H-benzotriazol-2-yl)phenol. One of these ultraviolet absorbers may be used alone, or two or more thereof may be used in combination. With respect to the amount of the ultraviolet absorber to be incorporated, it is preferred to incorporate the ultraviolet absorber in an amount of 0.0001-1 part by weight per 100 parts by weight of the mixture of the polycarbonate resin (A) to be used in the invention and the aromatic polycarbonate resin (B). The amount of the ultraviolet absorber to be incorporated is more preferably 0.0005-0.5 parts by weight, even more preferably 0.001-0.2 parts by weight. By incorporating an ultraviolet absorber in an amount within that range, the weatherability of the resin composition and various molded articles can be improved while preventing the ultraviolet absorber from bleeding to the surfaces of the molded articles and from reducing the mechanical properties of the molded articles.

<Hindered-Amine Light Stabilizer>

A hindered-amine light stabilizer can be incorporated for the purpose of further improving the weatherability of the polycarbonate resin composition and polycarbonate resin molded article of the invention. Examples of the hindered-amine light stabilizer include bis(2,2,6,6-tetramethyl-4-piperidyl) sebacate, bis(1,2,2,6,6-pentamethyl-4-piperidyl) sebacate, poly[[6-(1,1,3,3-tetramethylbutyl)amino-1,3,5-triazine-2,4-diyl][(2,2,6,6-tetramethyl-4-piperidyl)imino]hexamethylene[(2,2,6,6-tetramethyl-4-piperidyl)imino]], N,Nâ€²-bis(3-aminopropyl)ethylenediamine/2,4-bis[N-butyl-N-(1,2,2,6,6-pentamethyl-4-piperidylamino)-6-chloro-1,3,5-triazine condensates, and polycondensates of dibutylamine, 1,3,5-triazine, or N,Nâ€²-bis(2,2,6,6)-tetramethyl-4-piperidyl-1,6-hexamethylenediamine with N-(2,2,6,6-tetramethyl-4-piperidyl)butylamine. Preferred of these are bis(2,2,6,6-tetramethyl-4-piperidyl) sebacate and bis(1,2,2,6,6-pentamethyl-4-piperidyl) sebacate.

With respect to the amount of the hindered-amine light stabilizer to be incorporated, it is preferred to incorporate the hindered-amine light stabilizer in an amount of 0.001-1 part by weight per 100 parts by weight of the mixture of the polycarbonate resin (A) to be used in the invention and the aromatic polycarbonate resin (B). The amount of the hindered-amine light stabilizer to be incorporated is more preferably 0.005-0.5 parts by weight, especially preferably 0.01-0.2 parts by weight. By incorporating a hindered-amine light stabilizer in an amount within that range, the weatherability of various molded articles obtained by molding the polycarbonate resin composition of the invention can be improved while preventing the hindered-amine light stabilizer from bleeding to the surface of the polycarbonate resin composition and from reducing the mechanical properties of the molded articles.

It is preferred that the polycarbonate resin composition of the invention should further contain a release agent from the standpoint that the composition shows further improved releasability from the mold during melt molding. Examples of the release agent include higher fatty acids, higher fatty acid esters of mono- or polyhydric alcohols, natural animal waxes such as bees wax, natural vegetable waxes such as carnauba wax, natural petroleum waxes such as paraffin wax, natural coal waxes such as montan wax, olefin waxes, silicone oils, and organopolysiloxanes. Especially preferred are higher fatty acids and higher fatty acid esters of mono- or polyhydric alcohols.

The higher fatty acid esters preferably are partial or complete esters of substituted or unsubstituted, mono- or polyhydric alcohols having 1-20 carbon atoms with substituted or unsubstituted, saturated fatty acids having 10-30 carbon atoms. Examples of the partial or complete esters of mono- or polyhydric alcohols with saturated fatty acids include stearic monoglyceride, stearic diglyceride, stearic triglyceride, stearic acid monosorbitate, stearyl stearate, behenic monoglyceride, behenyl behenate, pentaerythritol monostearate, pentaerythritol tetrastearate, pentaerythritol tetrapelargonate, propylene glycol monostearate, stearyl stearate, palmityl palmitate, butyl stearate, methyl laurate, isopropyl palmitate, biphenyl biphenate, sorbitan monostearate, and 2-ethylhexyl stearate. Preferred of these are stearic monoglyceride, stearic triglyceride, pentaerythritol tetrastearate, and behenyl behenate.

The higher fatty acids preferably are substituted or unsubstituted, saturated fatty acids having 10-30 carbon atoms. Examples of such saturated fatty acids include myristic acid, lauric acid, palmitic acid, stearic acid, and behenic acid. One of these release agents may be used alone, or a mixture of two or more thereof may be used. The content of the release agent, per 100 parts by weight of the mixture of the polycarbonate resin (A) to be used in the invention and the aromatic polycarbonate resin (B), is preferably 0.0001 part by weight or more, more preferably 0.01 part by weight or more, especially preferably 0.1 part by weight or more, and is preferably 2 parts by weight or less, more preferably 1 part by weight or less, especially preferably 0.5 parts by weight or less.

The time at which the release agent is to be incorporated into the polycarbonate resin composition in this embodiment and methods for the addition are not particularly limited. Examples of the time of addition include the time when polymerization reaction is completed, in the case where a polycarbonate resin was produced by a transesterification method. Examples thereof further include, regardless of polymerization method: the time when a polycarbonate resin is in a molten state, for example, during kneading of the polycarbonate resin and other ingredients; and the time when a solid-state polycarbonate resin in the form of pellets, powder, or the like is blended with other ingredients and kneaded by means of an extruder or the like. Examples of addition methods include: a method in which the release agent is directly added, through mixing or kneading, to a polycarbonate resin; and a method in which the release agent is added in the form of a high-concentration master batch produced using a small amount of a polycarbonate resin, another resin, etc. and the release agent.

In this embodiment, the polycarbonate resin composition described above is molded to obtain a polycarbonate resin molded article. Methods of molding for obtaining the polycarbonate resin molded article are not particularly limited. Examples thereof include: a method in which raw materials including the polycarbonate resin (A) and the aromatic polycarbonate resin (B) and optionally further including other resins, additives, etc. are directly mixed together and the mixture is introduced into an extruder or an injection molding machine and molded; and a method in which the raw materials are melt-mixed by means of a twin-screw extruder and extruded into strands to produce pellets and the pellets are introduced into an extruder or an injection molding machine and molded. Since the polycarbonate resin molded article of the invention has excellent light resistance and transparency, the resin molded article can be used in applications such as noise insulation walls for roads, arcade ceiling sheets, arcade ceiling plates, roofing materials for facilities, and wall materials for facilities.

The irradiation treatment with a sunshine carbon arc lamp in the invention is a treatment in which using a specific apparatus, specific filter, etc. and using a sunshine carbon arc lamp at a discharge voltage of 50 V and a discharge current of 60 A, a sample is irradiated for 500 hours with light mainly having wavelengths of 300-1,100 nm at a black panel temperature of 63Â° C. in an environment having a relative humidity of 50% and a rainfall spray period per hour of 12 minutes, as will be described later.

The difference between the initial yellowness index (YI) value of a molded object (thickness, 3 mm) formed from the polycarbonate resin composition of the invention and the yellowness index (YI) value thereof measured after the molded object has undergone the 500-hour irradiation treatment with the sunshine carbon arc lamp is preferably 10 or less, more preferably 8 or less, especially preferably 6 or less.

EXAMPLES

The invention will be explained below in more detail by reference to Examples. However, the invention should not be construed as being limited by the following Examples unless the invention departs from the spirit thereof.

In the following, properties of polycarbonate resins, polycarbonate resin compositions, molded articles, etc. were evaluated by the following methods.

(1) Measurement of Reduced Viscosity

A sample of a polycarbonate resin was dissolved using methylene chloride as a solvent to prepare a polycarbonate solution having a concentration of 0.6 g/dL. Using an Ubbelohde viscometer manufactured by Moritomo Rika Kogyo, a measurement was made at a temperature of 20.0Â±0.1Â° C. The relative viscosity Î·rel was determined from the flow-down time of the solvent t₀and the flow-down time of the solution t using the following equation.

Î·rel=t/t₀

The specific viscosity lisp was determined from the relative viscosity using the following equation.

Î·sp=(Î·âˆ’Î·₀)/Î·₀=Î·relâˆ’1

The specific viscosity was divided by the concentration c (g/dL) to determine the reduced viscosity Î·sp/c. The larger the value thereof, the higher the molecular weight.

(2) Hue Measurement

In accordance with JIS K7105 (1981), an injection-molded piece (60 mm (width)Ã—60 mm (length)Ã—3 mm (thickness)) was examined for yellowness index (YI) value by the illuminant-C transmission method using a spectroscopic color-difference meter (SE2000, manufactured by Nippon Denshoku Kogyo K.K.). The smaller the YI value, the less the yellowness and the better the quality.

(3) Measurement of Total Light Transmittance

In accordance with JIS K7105 (1981), an injection-molded piece was examined for total light transmittance using a hazeometer (NDH2000, manufactured by Nippon Denshoku Kogyo K.K.) and illuminant D65.

(4) Sunshine Weatherometer Irradiation Test

In accordance with JIS B7753 (2007), sunshine weatherometer S80, manufactured by Suga Test Instruments Co., Ltd., which employed a sunshine carbon arc illuminator (four pairs of ultralong-life carbon arc lamps) was used to irradiate a square surface of an injection-molded flat plate (60 mm (width)Ã—60 mm (length)Ã—3 mm (thickness)) with light for 500 hours at a discharge voltage of 50 V and a discharge current of 60 A in the irradiation and surface spraying (rainfall) mode under the conditions of a black panel temperature of 63Â° C. and a relative humidity of 50%. The period of surface spraying (rainfall) was set at 12 minutes per hour. The glass filter used was of the type A. The YI and total light transmittance of the flat plate which had undergone the irradiation treatment were measured, and the difference between the YI measured after the 500-hour treatment and the YI measured before the treatment was determined.

[Aliphatic Polycarbonate Resin (A)]PC1:

(Constituent units derived from isosorbide)/(constituent units derived from 1,4-cyclohexanedimethanol)=40/60 mol %; reduced viscosity, 0.63 dL/g

PC2:

(Constituent units derived from isosorbide)/(constituent units derived from 9,9-[4-(2-hydroxyethoxy)phenyl]fluorene)=70/30 mol %; reduced viscosity, 0.57 dL/g

[Aromatic Polycarbonate Resin (B)]PC3:

Novarex 7022J (aromatic polycarbonate resin having, as the only units, structures derived from 2,2-bis(4-hydroxyphenyl)propane; viscosity-average molecular weight, 22,000), manufactured by Mitsubishi Engineering-Plastics Corp.

EXAMPLE 1

PC1 was dry-blended with PC3 in a weight ratio of 80:20, and the mixture was extruded at a resin temperature of 250Â° C. using a twin-screw extruder (TEX30HSS-32) manufactured by The Japan Steel Works, Ltd. The extrudate was solidified by cooling with water and then pelletized with a rotary cutter. The pellets were dried at 80Â° C. for 10 hours in a nitrogen atmosphere and subsequently fed to an injection molding machine (Type J75EII, manufactured by The Japan Steel Works, Ltd.) to mold injection-molded plates (60 mm (width)Ã—60 mm (length)Ã—3 mm (thickness)) under the conditions of a resin temperature of 250Â° C., a mold temperature of 60Â° C., and a molding cycle of 40 seconds. The samples obtained were subjected to the measurements of total light transmittance and YI. The results thereof are shown in Table 1.

EXAMPLE 2

Sample production and evaluation were conduced in the same manners as in Example 1, except that PC1 and PC3 were mixed in a weight ratio of 60:40. The results obtained are shown in Table 1.

EXAMPLE 3

Sample production and evaluation were conduced in the same manners as in Example 1, except that PC1 and PC3 were mixed in a weight ratio of 40:60. The results obtained are shown in Table 1.

Comparative Example 1

Sample production and evaluation were conduced in the same manners as in Example 1, except that PC2 and PC3 were mixed in a weight ratio of 80:20. The results obtained are shown in Table 1.

TABLE 1Component proportions by weight and propertiesof polycarbonate resin compositionsCompara-Exam-Exam-Exam-tiveple 1ple 2ple 3Example 1AliphaticPC1806040â€”PC2â€”â€”â€”80AromaticPC320406020Initial YI value6.25.03.67.0YI value after 500-hour11.69.49.535.0treatment with sunshineweatherometerDifference in YI value5.44.45.928.0between before and after500-hour treatment withsunshine weatherometerIn Table 1, â€œâ€”â€ indicates that the material was not used.

While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof This application is based on a Japanese patent application filed on Dec. 10, 2009 (Application No. 2009-280865), a Japanese patent application filed on Dec. 18, 2009 (Application No. 2009-288107), and a Japanese patent application filed on Aug. 20, 2010 (Application No. 2010-185054), the contents thereof being incorporated herein by reference.