CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority under 35 U.S.C. Â§119 from U.S. Provisional Application Ser. Nos. 61/222713 and 61/222720, both filed on Jul. 2, 2009.

FIELD OF THE INVENTION

The invention relates to the field of medical adhesives. More specifically, the invention relates to a hydrogel tissue adhesive formed by reacting an aldehyde-functionalized polysaccharide containing pendant aldehyde groups with a water-dispersible, multi-arm amine.

BACKGROUND OF THE INVENTION

Tissue adhesives have many potential medical applications, including wound closure, supplementing or replacing sutures or staples in internal surgical procedures, preventing leakage of fluids such as blood, bile, gastrointestinal fluid and cerebrospinal fluid, adhesion of synthetic onlays or inlays to the cornea, drug delivery devices, and as anti-adhesion barriers to prevent post-surgical adhesions. Conventional tissue adhesives are generally not suitable for a wide range of adhesive applications. For example, cyanoacrylate-based adhesives have been used for topical wound closure, but the release of toxic degradation products limits their use for internal applications. Fibrin-based adhesives are slow curing, have poor mechanical strength, and pose a risk of viral infection. Additionally, fibrin-based adhesives do not bond covalently to the underlying tissue.

Several types of hydrogel tissue adhesives have been developed, which have improved adhesive and cohesive properties and are nontoxic (see for example Sehl et al., U.S. Patent Application Publication No. 2003/0119985, and Goldmann, U.S. Patent Application Publication No. 2005/0002893). These hydrogels are generally formed by reacting a component having nucleophilic groups with a component having electrophilic groups, which are capable of reacting with the nucleophilic groups of the first component, to form a crosslinked network via covalent bonding. However, these hydrogels typically swell, dissolve away too quickly, or lack sufficient adhesion or mechanical strength, thereby decreasing their effectiveness as surgical adhesives. Kodokian et al. (copending and commonly owned U.S. Patent Application Publication No. 2006/0078536) describe a polysaccharide-based hydrogel tissue adhesives formed by reacting an oxidized polysaccharide with a water-dispersible, multi-arm polyether amine. These adhesives provide improved adhesion and cohesion properties, crosslink readily at body temperature, maintain dimensional stability initially, do not degrade rapidly, and are nontoxic to cells and non-inflammatory to tissue. However, for certain applications, such as the prevention of undesired tissue-to tissue-adhesions resulting from trauma or surgery, a more rapidly degrading hydrogel tissue adhesive is needed. For example, an adhesion prevention composition should not persist at the site once the healing process has begun, typically not longer than 1 to 3 weeks.

Therefore, the need exists for a hydrogel tissue adhesive that has the desirable properties of the oxidized polysaccharide-based tissue adhesives described by Kodokian et al., supra, but has a shorter degradation time.

SUMMARY OF THE INVENTION

The present invention addresses the above need by providing a hydrogel tissue adhesive that has good adhesion and cohesion properties, crosslinks readily at body temperature, maintains dimensional stability initially, is nontoxic to cells and non-inflammatory to tissue, and degrades more rapidly than the oxidized polysaccharide-based hydrogel tissue adhesives.

Accordingly, in one embodiment the invention provides a kit comprising:

- a) at least one aldehyde-functionalized polysaccharide containing pendant aldehyde groups, said aldehyde-functionalized polysaccharide having a weight-average molecular weight of about 1,000 to about 1,000,000 Daltons and a degree of aldehyde substitution of about 10% to about 200%; and
- b) at least one water-dispersible, multi-arm amine wherein at least three of the arms are terminated by at least one primary amine group, said multi-arm amine having a number-average molecular weight of about 450 to about 200,000 Daltons.

In another embodiment, the invention provides a dried hydrogel formed by a process comprising the steps of:

- a) combining in a solvent (i) at least one aldehyde-functionalized polysaccharide containing pendant aldehyde groups, said aldehyde-functionalized polysaccharide having a weight-average molecular weight of about 1,000 to about 1,000,000 Daltons and a degree of aldehyde substitution of about 10% to about 200% with (ii) at least one water-dispersible, multi-arm amine, wherein at least three of the arms are terminated by at least one primary amine group, said multi-arm amine having a number-average molecular weight of about 450 to about 200,000 Daltons, to form a hydrogel; and
- b) treating said hydrogel to remove at least a portion of said solvent to form the dried hydrogel.

In another embodiment, the invention provides a composition comprising the reaction product of:

- a) at least one aldehyde-functionalized polysaccharide containing pendant aldehyde groups, said aldehyde-functionalized polysaccharide having a weight-average molecular weight of about 1,000 to about 1,000,000 Daltons and a degree of aldehyde substitution of about 10% to about 200%, and
- b) at least one water-dispersible, multi-arm amine wherein at least three of the arms are terminated by at least one primary amine group, said multi-arm amine having a number-average molecular weight of about 450 to about 200,000 Daltons.

In another embodiment, the invention provides a crosslinked hydrogel composition comprising:

- a) at least one aldehyde-functionalized polysaccharide containing pendant aldehyde groups, said aldehyde-functionalized polysaccharide having a weight-average molecular weight of about 1,000 to about 1,000,000 Daltons and having a degree of aldehyde substitution of about 10% to about 200%; and
- b) at least one water-dispersible, multi-arm amine wherein at least three of the arms are terminated by at least one primary amine group, said multi-arm amine having a number-average molecular weight of about 450 to about 200,000 Daltons;
  wherein said at least one aldehyde-functionalized polysaccharide and said at least one water-dispersible, multi-arm amine are crosslinked through covalent bonds formed between the pendant aldehyde groups of the polysaccharide and the primary amine groups of the water-dispersible, multi-arm amine.

DETAILED DESCRIPTION

As used above and throughout the description of the invention, the following terms, unless otherwise indicated, shall be defined as follows:

The term â€œaldehyde-functionalized polysaccharideâ€ as used herein, refers to a polysaccharide that has been chemically modified to introduce pendant aldehyde groups into the molecule. The pendant aldehyde groups may be single aldehyde groups or dialdehydes. As defined herein, aldehyde-functionalized polysaccharides do not include polysaccharides that are oxidized by cleavage of the polysaccharide rings to introduce aldehyde groups. Oxidation of the polysaccharide rings results in dialdehydes formed by opening the rings of the polysaccharide.

The term â€œpendant aldehyde groupâ€ refers to an aldehyde group that is attached to the carbohydrate of the polysaccharide via one of the ring hydroxyl groups.

The term â€œdegree of aldehyde substitutionâ€ refers to the mole percent of pendant aldehyde groups per mole of carbohydrate repeat units, i.e., (moles of pendant aldehyde groups/moles of carbohydrate repeat units)Ã—100.

The term â€œwater-dispersible, multi-arm amineâ€ refers to a polymer having three or more polymer chains (â€œarmsâ€ ), which may be linear or branched, emanating from a central structure, which may be a single atom, a core molecule, or a polymer backbone, wherein at least three of the branches (â€œarmsâ€ ) are terminated by at least one primary amine group. The water-dispersible, multi-arm amine is water soluble or is able to be dispersed in water to form a colloidal suspension capable of reacting with a second reactant in aqueous solution or dispersion.

The term â€œdispersionâ€ as used herein, refers to a colloidal suspension capable of reacting with a second reactant in an aqueous medium.

The term â€œwater-dispersible, multi-arm polyether amineâ€ refers to a water-dispersible, multi-arm amine wherein the polymer is a polyether.

The term â€œpolyetherâ€ refers to a polymer having the repeat unit [-O-R]-, wherein R is a hydrocarbylene group having 2 to 5 carbon atoms. The polyether may also be a random or block copolymer comprising different repeat units which contain different R groups.

The term â€œhydrocarbylene groupâ€ refers to a divalent group formed by removing two hydrogen atoms, one from each of two different carbon atoms, from a hydrocarbon.

The term â€œbranched polyetherâ€ refers to a polyether having one or more branch points (â€œarmsâ€ ), including star, dendritic, comb, highly branched, and hyperbranched polyethers. Branches radiate from one or more trifunctional or higher functional branch points.

The term â€œdendritic polyetherâ€ refers to a highly branched polyether having a branching structure that repeats regularly with each successive generation of monomer radiating from a core molecule.

The term â€œcomb polyetherâ€ refers to a branched polyether in which linear side-chains emanate from trifunctional branch points on a linear polymer backbone.

The term â€œstar polyetherâ€ refers to a branched polyether in which linear side-chains emanate from a single atom or a core molecule having a point of symmetry.

The term â€œhyperbranched polyetherâ€ refers to a highly branched polyether which is more branched than â€œhighly branched,â€ with order approaching that of an imperfect dendrimer.

The term â€œhighly branched polyetherâ€ refers to a branched polyether having many branch points, such that the distance between branch points is small relative to the total length of arms.

The term â€œprimary amineâ€ refers to a neutral amino group having two free hydrogens. The amino group may be bound to a primary, secondary or tertiary carbon.

The term â€œmulti-functional amineâ€ refers to a chemical compound comprising at least two functional groups, at least one of which is a primary amine group.

The term â€œcrosslinkâ€ refers to a bond or chain of atoms attached between and linking two different polymer chains.

The term â€œcrosslink densityâ€ is herein defined as the reciprocal of the average number of chain atoms between crosslink connection sites.

The term â€œ% by weightâ€ , also referred to herein as â€œwt %â€ refers to the weight percent relative to the total weight of the solution or dispersion, unless otherwise specified.

The term â€œanatomical siteâ€ refers to any external or internal part of the body of humans or animals.

The term â€œtissueâ€ refers to any biological tissue, both living and dead, in humans or animals.

The term â€œhydrogelâ€ refers to a water-swellable polymeric matrix, consisting of a three-dimensional network of macromolecules held together by covalent crosslinks that can absorb a substantial amount of water to form an elastic gel.

The term â€œdried hydrogelâ€ refers to a hydrogel that has been treated to remove at least a portion of the solvent contained therein. Preferably, substantially all of the solvent is removed from the hydrogel.

The term â€œPEGâ€ as used herein refers to poly(ethylene glycol).

The term â€œM_wâ€ as used herein refers to the weight-average molecular weight.

The term â€œM_nâ€ as used herein refers to the number-average molecular weight.

The term â€œM_zâ€ as used herein refers to the z-average molecular weight.

The term â€œmedical applicationâ€ refers to medical applications as related to humans and animals.

The meaning of abbreviations used is as follows: â€œminâ€ means minute(s), â€œhâ€ means hour(s), â€œsecâ€ means second(s), â€œdâ€ means day(s), â€œmLâ€ means milliliter(s), â€œLâ€ means liter(s), â€œÎ¼Lâ€ means microliter(s), â€œcmâ€ means centimeter(s), â€œmmâ€ means millimeter(s), â€œÎ¼mâ€ means micrometer(s), â€œmolâ€ means mole(s), â€œmmolâ€ means millimole(s), â€œgâ€ means gram(s), â€œmgâ€ means milligram(s), â€œmol %â€ means mole percent, â€œVolâ€ means volume, â€œw/wâ€ means weight per weight, â€œDaâ€ means Daltons, â€œkDaâ€ means kiloDaltons, the designation â€œ10Kâ€ means that a polymer molecule possesses a number-average molecular weight of 10 kiloDaltons, â€œMâ€ means molarity, â€œkPaâ€ means kilopascals, â€œpsiâ€ means pounds per square inch, â€œrpmâ€ means revolutions per minuteâ€ , â€œ¹H NMRâ€ means proton nuclear magnetic resonance spectroscopy, â€œ13-C NMRâ€ means carbon 13 nuclear magnetic resonance spectroscopy, â€œppmâ€ means parts per million, â€œcPâ€ means centipoise, PBSâ€³ means phosphate-buffered saline, â€œMWCOâ€ means molecular weight cut off.

A reference to â€œAldrichâ€ or a reference to â€œSigmaâ€ means the said chemical or ingredient was obtained from Sigma-Aldrich, St. Louis, Mo.

Disclosed herein is a hydrogel tissue adhesive formed by reacting an aldehyde-functionalized polysaccharide containing pendant aldehyde groups with a water-dispersible, multi-arm amine. The hydrogel may be useful as a tissue adhesive or sealant for medical applications that require more rapid degradation, including but not limited to, prevention of undesired tissue-to tissue adhesions resulting from trauma or surgery.

Aldehyde-Functionalized Polysaccharides

Aldehyde-functionalized polysaccharides suitable for use herein are polysaccharides that have been chemically modified to introduce pendant aldehyde groups into the molecule. The pendant aldehyde groups may be single aldehyde groups or dialdehydes. The pendant aldehyde groups of the aldehyde-functionalized polysaccharides disclosed herein are attached to the polysaccharide through linking groups. In one embodiment, the linking groups comprise carbon, hydrogen, and oxygen atoms, but do not contain a nitrogen atom, and are attached to the polysaccharide by ether linkages. As demonstrated in the Examples herein below, aldehyde-functionalized polysaccharides having these types of linking groups are more stable in aqueous solution that oxidized polysaccharides or aldehyde-functionalized polysaccharides having other types of linking groups, such as those that contain a nitrogen atom or are linked to the polysaccharide by other chemical linkages (e.g., amide or urethane). In one embodiment, the linking group contains an alkoxy group alpha to the pendant aldehyde group (i.e., on an adjacent carbon atom). In another embodiment, the linking group does not contain an alkoxy group beta to the pendant aldehyde group (i.e., on the second carbon atom from the aldehyde group).

As used herein, aldehyde-functionalized polysaccharides do not include polysaccharides that are oxidized by cleavage of the polysaccharide rings to introduce aldehyde groups. Oxidation of the polysaccharide rings results in dialdehydes formed by opening the rings of the polysaccharide. Therefore, the dialdehyde groups formed by oxidation of polysaccharide rings are not pendant aldehyde groups as defined herein.

Aldehyde-functionalized polysaccharides may be prepared by chemically modifying a polysaccharide to introduce pendant aldehyde groups. Useful aldehyde-functionalized polysaccharides include, but are not limited to, aldehyde-functionalized derivatives of: dextran, carboxymethyldextran, starch, agar, cellulose, hydroxyethylcellulose, carboxymethylcellulose, pullulan, inulin, levan, and hyaluronic acid. The starting polysaccharides are available commercially from sources such as Sigma Chemical Co. (St. Louis, Mo.). Typically, polysaccharides are a heterogeneous mixture having a distribution of different molecular weights, and are characterized by an average molecular weight, for example, the weight-average molecular weight (M_w), or the number average molecular weight (M_n), as is known in the art. Therefore, the aldehyde-functionalized polysaccharides prepared from these polysaccharides are also a heterogeneous mixture having a distribution of different molecular weights. Suitable aldehyde-functionalized polysaccharides have a weight-average molecular weight of about 1,000 to about 1,000,000 Daltons, more particularly about 3,000 to about 250,000 Daltons, more particularly about 5,000 to about 60,000 Daltons, and more particularly about 7,000 to about 20,000 Daltons. In one embodiment, the aldehyde-functionalized polysaccharide is aldehyde-functionalized dextran. In another embodiment, the aldehyde-functionalized polysaccharide is aldehyde-functionalized inulin.

Aldehyde-functionalized polysaccharides may be prepared using methods known in the art. Aldehyde-functionalized polysaccharides may be prepared using any of the methods described by Mehta et al. (WO 99/07744). For example, dextran may be reacted with allyl glycidyl ether in an acid aqueous medium to form allyloxy dextran which is then oxidized by ozonolysis to cleave the double bond and introduce a terminal aldehyde group, as described in detail in the Examples herein below. Additionally, glycidol may be reacted with a polysaccharide, such as dextran, in a basic aqueous medium to give an alkylated polysaccharide, as described by Chen (Biotechnology Techniques 3:131-134, 1989). Periodate oxidation of the alkylated polysaccharide yields an aldehyde-functionalized polysaccharide having pendant aldehyde groups. The aldehyde-functionalized polysaccharides may also be prepared by the method described by Solarek et al. (U.S. Pat. No. 4,703,116) wherein a polysaccharide is reacted with a derivatizing acetal reagent in the presence of base and then the acetal is hydrolyzed by adjusting the pH to less than 7.0.

Aldehyde-functionalized polysaccharides having dialdehyde functional groups can be prepared by first attaching a pendant group containing either a terminal diene or by attaching a cyclic, disubstituted olefin to the polysaccharide ring. Attachment of the pendant groups can be accomplished using a variety of methods, including reaction of the polysaccharide with glycidyl ethers containing cyclic olefins or terminal dienes, or reaction with carboxylic acids or derivatives thereof which also contain cyclic olefins or terminal dienes. Oxidation of the polysaccharides derivatized with cyclic olefins or terminal dienes using methods known in the art, such as ozonolysis, yield polysaccharides derivatized with pendant dialdehydes.

The degree of aldehyde substitution may be determined using methods known in the art. For example, the degree of aldehyde substitution may be determined by titrating the aldehyde-functionalized polysaccharide with hydroxyl amine hydrochloride according to the method of Zhao and Heindel (Pharmaceutical Research 8:400, 1991). Suitable aldehyde-functionalized polysaccharides have a degree of aldehyde substitution of about 10% to about 200%, more particularly about 30% to about 200%, more particularly about 35% to about 120%, and more particularly about 40% to about 120%.

Water-Dispersible, Multi-Arm Amines:

Suitable water-dispersible, multi-arm amines include, but are not limited to, water-dispersible multi-arm polyether amines, amino-terminated dendritic polyamidoamines, and multi-arm branched end amines. Typically, multi-arm amines suitable for use herein have a number-average molecular weight of about 450 to about 200,000 Daltons, more particularly from about 2,000 to about 40,000 Daltons.

In one embodiment, the water-dispersible, multi-arm amine is a multi-arm polyether amine, which is a water-dispersible polyether having the repeat unit [-O-R]-, wherein R is a hydrocarbylene group having 2 to 5 carbon atoms. Suitable multi-arm polyether amines include, but are not limited to, amino-terminated star polyethylene oxides, amino-terminated dendritic polyethylene oxides, amino-terminated comb polyethylene oxides, amino-terminated star polypropylene oxides, amino-terminated dendritic polypropylene oxides, amino-terminated comb polypropylene oxides, amino-terminated star polyethylene oxide-polypropylene oxide copolymers, amino-terminated dendritic polyethylene oxide-polypropylene oxide copolymers, amino-terminated comb polyethylene oxide-polypropylene oxide copolymers, and polyoxyalkylene triamines, sold under the trade name JeffamineÂ® triamines, by Huntsman LLC. (Houston, Tex.). Examples of star polyethylene oxide amines, include, but are not limited to, various multi-arm polyethylene glycol amines, and star polyethylene glycols having 3, 4, 6, or 8 arms terminated with primary amines (referred to herein as 3, 4, 6, or 8-arm star PEG amines, respectively). Examples of suitable JeffamineÂ® triamines include, but are not limited to, JeffamineÂ® T-403 (CAS No. 39423-51-3), JeffamineÂ® T-3000 (CAS No. 64852-22-8), and JeffamineÂ® T-5000 (CAS No. 64852-22-8). In one embodiment, the water-dispersible multi-arm polyether amine is an eight-arm polyethylene glycol having eight arms terminated by a primary amine group and having a number-average molecular weight of about 10,000 Daltons.

The multi-arm polyether amines are either available commercially, as noted above, or may be prepared using methods known in the art. For example, multi-arm polyethylene glycols, wherein at least three of the arms are terminated by a primary amine group, may be prepared by putting amine ends on multi-arm polyethylene glycols (e.g., 3, 4, 6, and 8-arm star polyethylene glycols, available from companies such as Nektar Transforming Therapeutics; SunBio, Inc., Anyang City, South Korea; NOF Corp., Tokyo, Japan; or JenKem Technology USA, Allen, Tex.) using the method described by Buckmann et al. (Makromol. Chem. 182:1379-1384, 1981). In that method, the multi-arm polyethylene glycol is reacted with thionyl bromide to convert the hydroxyl groups to bromines, which are then converted to amines by reaction with ammonia at 100Â° C. The method is broadly applicable to the preparation of other multi-arm polyether amines. Additionally, multi-arm polyether amines may be prepared from multi-arm polyols using the method described by Chenault (copending and commonly owned U.S. Patent Application Publication No.2007/0249870). In that method, the multi-arm polyether is reacted with thionyl chloride to convert the hydroxyl groups to chlorine groups, which are then converted to amines by reaction with aqueous or anhydrous ammonia. Other methods that may be used for preparing multi-arm polyether amines are described by Merrill et al. in U.S. Pat. No. 5,830,986, and by Chang et al. in WO 97/30103.

Water-dispersible, multi-arm amines suitable for use herein may also be amino-terminated dendritic polyamidoamines, sold under the trade name StarburstÂ® Dendrimers (available from Sigma-Aldrich, St Louis, Mo.).

In one embodiment, the water-dispersible, multi-arm amine is a multi-arm branched end amine, as described by Arthur (copending and commonly owned International Patent Application Publication No. WO 2008/066787). The multi-arm branched end amines are branched polymers having two or three primary amine groups at the end of each of the polymer arms. The multiplicity of functional groups increases the statistical probability of reaction at a given chain end and allows more efficient incorporation of the branched molecules into a polymer network. The starting materials used to prepare the branched end amines may be branched polymers such as multi-arm polyether polyols including, but not limited to, comb and star polyether polyols. The branched end amines can be prepared by attaching multiple amine groups to the ends of the polymer by reaction with the hydroxyl groups using methods well known in the art. For example, a branched end amine having two amine functional groups on each end of the polymer arms can be prepared by reacting the starting material, as listed above, with thionyl chloride in a suitable solvent such as toluene to give the chloride derivative, which is subsequently reacted with tris(2-aminoethyl)amine to give the branched end reactant having two primary amine groups at the end of the polymer arms.

In one embodiment, the water-dispersible, multi-arm amine is an eight-arm branched end polyethylene glycol amine having two primary amine groups at the end of the polymer arms and having a number-average molecular weight of about 10,000 Daltons.

In another embodiment, the water-dispersible, multi-arm amine is a mixture of an eight-arm branched end polyethylene glycol amine having two primary amine groups at the end of the polymer arms and having a number-average molecular weight of about 10,000 Daltons, and an eight-arm polyethylene glycol amine having eight arms terminated by a primary amine group and having a number-average molecular weight of about 10,000 Daltons.

It should be recognized that the water-dispersible, multi-arm amines are generally a somewhat heterogeneous mixture having a distribution of arm lengths and in some cases, a distribution of species with different numbers of arms. When a multi-arm amine has a distribution of species having different numbers of arms, it can be referred to based on the average number of arms in the distribution. For example, in one embodiment the multi-arm amine is an 8-arm star PEG amine, which comprises a mixture of multi-arm star PEG amines, some having less than and some having more than 8 arms; however, the multi-arm star PEG amines in the mixture have an average of 8 arms. Therefore, the terms â€œ8-armâ€ , â€œ6-armâ€ , â€œ4-armâ€ and â€œ3-armâ€ as used herein to refer to multi-arm amines, should be construed as referring to a heterogeneous mixture having a distribution of arm lengths and in some cases, a distribution of species with different numbers of arms, in which case the number of arms recited refers to the average number of arms in the mixture.

Methods of Using the Hydrogel Tissue Adhesive

The hydrogel tissue adhesive disclosed herein may be used in various forms. In one embodiment, the aldehyde-functionalized polysaccharide containing pendant aldehyde groups and the water-dispersible, multi-arm amine are used as components of aqueous solutions or dispersions. To prepare an aqueous solution or dispersion comprising an aldehyde-functionalized polysaccharide (referred to herein as the â€œfirst aqueous solution or dispersionâ€ ), at least one aldehyde-functionalized polysaccharide is added to water to give a concentration of about 5% to about 40%, more particularly from about 5% to about 30%, and more particularly from about 10% to about 30% by weight relative to the total weight of the solution or dispersion. Additionally, a mixture of at least two different aldehyde-functionalized polysaccharides having different weight-average molecular weights, different degrees of aldehyde substitution, or both different weight-average molecular weights and degrees of aldehyde substitution may be used. Where a mixture of aldehyde-functionalized polysaccharides is used, the total concentration of the aldehyde-functionalized polysaccharides is about 5% to about 40% by weight, more particularly from about 5% to about 30%, and more particularly from about 10% to about 30% by weight relative to the total weight of the solution or dispersion.

Similarly, to prepare an aqueous solution or dispersion comprising a water-dispersible, multi-arm amine (referred to herein as the â€œsecond aqueous solution or dispersionâ€ ), at least one water-dispersible, multi-arm amine is added to water to give a concentration of about 5% to about 70% by weight, more particularly from about 20% to about 50% by weight relative to the total weight of the solution or dispersion. The optimal concentration to be used depends on the intended application and on the concentration of the aldehyde-functionalized polysaccharide used in the first aqueous solution or dispersion. Additionally, a mixture of different water-dispersible, multi-arm amines having different number-average molecular weights, different numbers of arms, or both different number-average molecular weights and different numbers of arms may be used. Where a mixture of water-dispersible, multi-arm amines is used, the total concentration of the multi-arm amines is about 5% to about 70% by weight, more particularly from about 20% to about 50% by weight relative to the total weight of the solution or dispersion.

For use on living tissue, it is preferred that the first aqueous solution or dispersion and the second aqueous solution or dispersion be sterilized to prevent infection. Any suitable sterilization method known in the art that does not adversely affect the ability of the components to react to form an effective hydrogel may be used, including, but not limited to, electron beam irradiation, gamma irradiation, ethylene oxide sterilization, or filtration through a 0.2 Î¼m pore membrane.

The first aqueous solution or dispersion and the second aqueous solution or dispersion may further comprise various additives depending on the intended application. Preferably, the additive does not interfere with effective gelation to form a hydrogel. The amount of the additive used depends on the particular application and may be readily determined by one skilled in the art using routine experimentation. For example, the first aqueous solution or dispersion and/or the second aqueous solution or dispersion may comprise at least one additive selected from pH modifiers, antimicrobials, colorants, surfactants, pharmaceutical drugs and therapeutic agents.

The first aqueous solution or dispersion and/or the second aqueous solution or dispersion may optionally include at least one pH modifier to adjust the pH of the solution(s) or dispersion(s). Suitable pH modifiers are well known in the art. The pH modifier may be an acidic or basic compound. Examples of acidic pH modifiers include, but are not limited to, carboxylic acids, inorganic acids, and sulfonic acids. Examples of basic pH modifiers include, but are not limited to, hydroxides, alkoxides, nitrogen-containing compounds other than primary and secondary amines, and basic carbonates and phosphates.

The first aqueous solution or dispersion and/or the second aqueous solution or dispersion may optionally include at least one antimicrobial agent. Suitable antimicrobial preservatives are well known in the art. Examples of suitable antimicrobials include, but are not limited to, alkyl parabens, such as methylparaben, ethylparaben, propylparaben, and butylparaben; triclosan; chlorhexidine; cresol; chlorocresol; hydroquinone; sodium benzoate; and potassium benzoate.

The first aqueous solution or dispersion and/or the second aqueous solution or dispersion may optionally include at least one colorant to enhance the visibility of the solution(s) or dispersion(s). Suitable colorants include dyes, pigments, and natural coloring agents. Examples of suitable colorants include, but are not limited to, FD&C and D&C colorants, such as FD&C Violet No. 2, FD&C Blue No. 1, D&C Green No. 6, D&C Green No. 5, D&C Violet No. 2; and natural colorants such as beetroot red, canthaxanthin, chlorophyll, eosin, saffron, and carmine.

The first aqueous solution or dispersion and/or the second aqueous solution or dispersion may optionally include at least one surfactant. Surfactant, as used herein, refers to a compound that lowers the surface tension of water. The surfactant may be an ionic surfactant, such as sodium lauryl sulfate, or a neutral surfactant, such as polyoxyethylene ethers, polyoxyethylene esters, and polyoxyethylene sorbitan.

Additionally, the first aqueous solution or dispersion and/or the second aqueous solution or dispersion may optionally include at least one pharmaceutical drug or therapeutic agent. Suitable drugs and therapeutic agents are well known in the art (for example see the United States Pharmacopeia (USP), Physician's Desk Reference (Thomson Publishing), The Merck Manual of Diagnosis and Therapy 18th ed., Mark H. Beers and Robert Berkow (eds.), Merck Publishing Group, 2006; or, in the case of animals, The Merck Veterinary Manual, 9th ed., Kahn, C. A. (ed.), Merck Publishing Group, 2005). Nonlimiting examples include anti-inflammatory agents, for example, glucocorticoids such as prednisone, dexamethasone, budesonide; non-steroidal anti-inflammatory agents such as indomethacin, salicylic acid acetate, ibuprofen, sulindac, piroxicam, and naproxen; fibrinolytic agents such as a tissue plasminogen activator and streptokinase; anti-coagulants such as heparin, hirudin, ancrod, dicumarol, sincumar, iloprost, L-arginine, dipyramidole and other platelet function inhibitors; antibodies; nucleic acids; peptides; hormones; growth factors; cytokines; chemokines; clotting factors; endogenous clotting inhibitors; antibacterial agents; antiviral agents; antifungal agents; anti-cancer agents; cell adhesion inhibitors; healing promoters; vaccines; thrombogenic agents, such as thrombin, fibrinogen, homocysteine, and estramustine; radio-opaque compounds, such as barium sulfate and gold particles and radiolabels.

Additionally, the second aqueous solution or dispersion comprising the multi-arm amine may optionally comprise at least one other multi-functional amine having one or more primary amine groups to provide other beneficial properties, such as hydrophobicity or modified crosslink density. The multi-functional amine is capable of inducing gelation when mixed with an oxidized polysaccharide in an aqueous solution or dispersion. The multi-functional amine may be a second water-dispersible, multi-arm amine, such as those described above, or another type of multi-functional amine, including, but not limited to, linear and branched diamines, such as diaminoalkanes, polyaminoalkanes, and spermine; branched polyamines, such as polyethylenimine; cyclic diamines, such as N, Nâ€²-bis(3-aminopropyl)piperazine, 5-amino-1,3,3- trimethylcyclohexanemethylamine, 1,3-bis(aminomethyl)cyclohexane, 1,4-diaminocyclohexane, and p-xylylenediamine; aminoalkyltrialkoxysilanes, such as 3-aminopropyltrimethoxysilane and 3-aminopropyltriethoxysilane; aminoalkyldialkoxyalkylsilanes, such as 3-aminopropyldiethoxymethylsilane, dihydrazides, such as adipic dihydrazide; linear polymeric diamines, such as linear polyethylenimine, Î±,Ï‰-amino-terminated polyethers, Î±,Ï‰-bis(3-aminopropyl)polybutanediol, Î²,Ï‰-1-amino-terminated polyethers (linear JeffaminesÂ®); comb polyamines, such as chitosan, polyallylamine, and polylysine, and di- and polyhydrazides, such as bis(carboxyhydrazido)polyethers and poly(carboxyhydrazido) star polyethers. Many of these compounds are commercially available from companies such as Sigma-Aldrich and Huntsman LLC. Typically, if present, the multi-functional amine is used at a concentration of about 5% by weight to about 1000% by weight relative to the weight of the multi-arm amine in the aqueous solution or dispersion.

When the first aqueous solution or dispersion and the second aqueous solution or dispersion are mixed they react to form a crosslinked hydrogel composition comprising at least one aldehyde-functionalized polysaccharide containing pendant aldehyde groups; and at least one water-dispersible, multi-arm amine wherein at least three of the arms are terminated by at least one primary amine group, and wherein the at least one aldehyde-functionalized polysaccharide and the at least one water-dispersible, multi-arm amine are crosslinked through covalent bonds formed between the pendant aldehyde groups of the aldehyde-functionalized polysaccharide and the primary amine groups of the water-dispersible, multi-arm amine. The covalent bonds may be imine, aminal or hemiaminal bonds. The degradation time of the hydrogel may be tuned for the needs of the intended application by using different amounts of the aldehyde-functionalized polysaccharide in the first aqueous solution or dispersion and the water-dispersible, multi-arm amine in the second aqueous solution or dispersion in terms of weight percent and/or by altering the amount of funtionalization of either amine on the water-dispersible, multi-arm amine or aldehyde on the aldehyde-functionalized polysaccharide, as shown in the Examples herein below.

The first aqueous solution or dispersion and the second aqueous solution or dispersion may be used to apply a coating to an anatomical site on tissue of a living organism. The two aqueous solutions or dispersions may be applied to the site in any number of ways. Once both solutions or dispersions are combined on a site, they crosslink to form a hydrogel which provides a coating on the site.

In one embodiment, the two aqueous solutions or dispersions are applied to the site sequentially using any suitable means including, but not limited to, spraying, brushing with a cotton swab or brush, or extrusion using a pipette, or a syringe. The solutions or dispersions may be applied in any order. Then, the solutions or dispersions are mixed on the site using any suitable device, such as a cotton swab, a spatula, or the tip of the pipette or syringe.

In another embodiment, the two aqueous solutions or dispersions are mixed manually before application to the site. The resulting mixture is then applied to the site before it completely cures using a suitable applicator, as described above.

In another embodiment, the first aqueous solution or dispersion and the second aqueous solution or dispersion are applied to the site simultaneously where they mix to form a hydrogel. For example, the two aqueous solutions or dispersions may be contained in separate barrels of a double-barrel syringe. In this way the two aqueous solutions or dispersions are applied simultaneously to the site with the syringe. Suitable double-barrel syringe applicators are known in the art. For example, Redl describes several suitable applicators for use in the invention in U.S. Pat. No. 6,620,125, (particularly FIGS. 1, 5, and 6, which are described in Columns 4, line 10 through column 6, line 47). The two aqueous solutions or dispersions may also be applied to the site using a dual-lumen catheter, such as those available from Bistech, Inc. (Woburn, Mass.). Additionally, injection devices for introducing two liquid components endoscopically into the body simultaneously are known in the art and may be adapted for the delivery of the two aqueous solutions or dispersions disclosed herein (see for example, Linder et al., U.S. Pat. No. 5,322,510).

In another embodiment, the first aqueous solution or dispersion and the second aqueous solution or dispersion may be premixed and delivered to the site using a double barrel syringe containing a motionless mixer, such as that available from ConProtec, Inc. (Salem, N.H.) or Mixpac Systems AG (Rotkreuz, Switzerland). Alternatively, the mixing tip may be equipped with a spray head, such as that described by Cruise et al. in U.S. Pat. No. 6,458,147. Additionally, the mixture of the two aqueous solutions or dispersions from the double-barrel syringe may be applied to the site using a catheter or endoscope. Devices for mixing a two liquid component tissue adhesive and delivering the resulting mixture endoscopically are known in the art and may be adapted for the mixing and delivery of the two aqueous solutions or dispersions disclosed herein (see for example, Nielson, U.S. Pat. No. 6,723,067; and Redl et al., U.S. Pat. No. 4,631,055).

In another embodiment, the two aqueous solutions or dispersions may be applied to the site using a spray device, such as those described by Fukunaga et al. (U.S. Pat. No. 5,582,596), Delmotte et al. (U.S. Pat. No. 5,989,215) or Sawhney (U.S. Pat. No. 6,179,862).

In another embodiment, the two aqueous solutions or dispersions may be applied to the site using a minimally invasive surgical applicator, such as those described by Sawhney (U.S. Pat. No. 7,347,850).

In another embodiment, the hydrogel tissue adhesive of the invention is used to bond at least two anatomical sites together. In this embodiment, the first aqueous solution or dispersion is applied to at least one anatomical site, and the second aqueous solution or dispersion is applied to at least one of either the same site or one other site using the methods described above. The two or more sites are contacted and held together manually or using some other means, such as a surgical clamp, for a time sufficient for the mixture to cure. Alternatively, a mixture of the two aqueous solutions or dispersions is applied to at least one of the anatomical sites to be bonded using methods described above. The two or more sites are contacted and held together manually or using some other means, such as a surgical clamp, for a time sufficient for the mixture to cure.

In another embodiment, the aldehyde-functionalized polysaccharide, and the water-dispersible, multi-arm amine may be used in the form of finely divided powders. The powders may be prepared using any suitable method. For example, each of the aqueous solutions or dispersions described above may be dried using heat, vacuum, a combination of heat and vacuum, or by lyophilization, to form powders. Optionally, the powders may be comminuted into finer particles using methods known in the art including, but not limited to, grinding, milling, or crushing with a mortar and pestle. The finely divided powders may be sterilized using the methods described above. The finely divided powders may be applied to an anatomical site on tissue of a living organism in a variety of ways. For example, the powders may be individually applied to the site in any order by sprinkling or spraying. Additionally, the powders may be premixed and the resulting mixture applied to the site by sprinkling or spraying. The powders may be hydrated on the site by the addition of an aqueous solution such as water or a suitable buffer (e.g., phosphate-buffered saline) or by the physiological fluids present at the site. The finely divided powders may also be used to bond two anatomical sites together as described above for the aqueous solutions or dispersions. Alternatively, the powders may be hydrated with water or a suitable aqueous solution prior to use to form the first and second aqueous solutions or dispersions, describer) above.

In another embodiment, the hydrogel tissue adhesive disclosed herein may be used in the form of a dried hydrogel. In this embodiment, a dried hydrogel is prepared by combining in a solvent at least one aldehyde-functionalized polysaccharide with at least one water-dispersible, multi-arm amine to form a hydrogel, and treating the hydrogel to remove at least a portion of the solvent to form the dried hydrogel. Suitable solvents include, but are not limited to, water, ethanol, isopropanol, tetrahydrofuran, hexanes, polyethylene glycol, and mixtures thereof. If two different solvents are used, the two solvents are miscible with each other. In one embodiment the solvent is water. The aldehyde-functionalized polysaccharide and the water-dispersible, multi-arm amine may be combined in various ways. For example, the first aqueous solution or dispersion comprising the aldehyde-functionalized polysaccharide and the second aqueous solution or dispersion comprising the water-dispersible, multi-arm amine, may be prepared and mixed as described above to form the hydrogel. The solutions or dispersions used to prepare the hydrogel may further comprise various additives depending on the intended application. Any of the additives described above may be used. The hydrogel is then treated to remove at least a portion of the solvent contained therein to form the dried hydrogel. Preferably, substantially all of the solvent is removed from the hydrogel. The solvent may be removed from the hydrogel using methods known in the art, for example, using heat, vacuum, a combination of heat and vacuum, or flowing a stream of dry air or a dry inert gas such as nitrogen over the hydrogel. The dried hydrogel may be sterilized using the methods described above. The dried hydrogel may be applied to an anatomical site in a number of ways, as described below. The dried hydrogel may be hydrated on the site by the addition of a suitable aqueous solution such as water or a buffer (e.g., phosphate-buffered saline) or by the physiological fluids present at the site.

In one embodiment, the dried hydrogel may be used in the form of a film. The dried hydrogel film may be formed by casting a mixture of the solutions or dispersions, as described above, on a suitable substrate and treating the resulting hydrogel to form a dried hydrogel film. The dried hydrogel film may be applied directly to an anatomical site. Additionally, the dried hydrogel film may be used to bond two anatomical sites together.

In another embodiment, the dried hydrogel may be used in the form of finely divided particles. The dried hydrogel particles may be formed by comminuting the dried hydrogel using methods known in the art, including, but not limited to, grinding, milling, or crushing with a mortar and pestle. The dried hydrogel particles may be applied to an anatomical site in a variety of ways, such as sprinkling or spraying, and may also be used to bond two anatomical sites together.

Kits

In one embodiment, the invention provides a kit comprising at least one aldehyde-functionalized polysaccharide containing pendant aldehyde groups and at least one water-dispersible, multi-arm amine wherein at least three of the arms are terminated by at least one primary amine group.

In another embodiment, the kit comprises a first aqueous solution or dispersion comprising at least one aldehyde-functionalized polysaccharide containing pendant aldehyde groups and a second aqueous solution or dispersion comprising at least one water-dispersible, multi-arm amine wherein at least three of the arms are terminated by at least one primary amine group. Each of the aqueous solutions or dispersions may be contained in any suitable vessel, such as a vial or a syringe barrel.

In another embodiment, the kit comprises at least one aldehyde-functionalized polysaccharide containing pendant aldehyde groups and at least one water-dispersible, multi-arm amine wherein at least three of the arms are terminated by at least one primary amine group in the form of finely divided powders, as described above. The powders may be contained in separate containers or they may be premixed and contained in a single container. The kit may also comprise an aqueous solution for hydrating the powders.

In another embodiment, the kit comprises a dried hydrogel as described above. The dried hydrogel may be in the form of a film, finely divided particles, or other dried forms. The kit may further comprise an aqueous solution for hydrating the dried hydrogel. The dried hydrogel particles may be contained in any suitable container.

Medical Applications:

The hydrogel disclosed herein may be useful as a tissue adhesive or sealant for medical applications that require a more rapid degradation time, including but not limited to, prevention of undesired tissue-to tissue adhesions resulting from trauma or surgery. In these applications, the aldehyde-functionalized polysaccharide and the water-dispersible, multi-arm amine, or the dried hydrogel may be applied to the desired anatomical site using the methods described above.

EXAMPLES

The present invention is further defined in the following Examples. It should be understood that these Examples, while indicating preferred embodiments of the invention, are given by way of illustration only. From the above discussion and these Examples, one skilled in the art can ascertain the essential characteristics of this invention, and without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various uses and conditions.

Reagent PreparationPreparation of Dextran Having Pendant Aldehyde Groups (AFD-15-90):

Dextran containing pendant aldehyde groups and having a weight-average molecular weight of about 15 kDa and a degree of aldehyde substitution of about 90% was prepared using a two step procedure. In the first step, dextran having a weight-average molecular weight of about 9 to about 11 kDa was reacted with allyl glycidyl ether to form an olefin intermediate, which was then reacted with ozone to form the dextran containing pendant aldehyde groups.

In the first step, 30 g of dextran (average molecular weight of 9-11 kDa, Sigma), and 30 mL of water were added into a 3-neck flask. The solution was cooled to 10Â° C. and then 39 mL of a 20 wt % NaOH solution was added. The resulting solution was stirred for 25 min, giving a faint yellow solution, and then 84.58 g (4 equiv) of allyl glycidyl ether (Aldrich) was added. The resulting mixture was heated to 65Â° C. for 5.5 hours, and then allowed to cool to room temperature, after which the pH was adjusted to 7.0 with 1 N HCl. The mixture was diluted with an additional 200 mL of water and purified using a Millipore Pellicon II ultrafiltration system (Millipore Corp., Billerica, Mass.), by filtration through 1 kDa cutoff filters with continuous replacement of filtrate with pure water until 5Ã— the initial solution volume had been collected as filtrate. A small sample was taken and lyophilized for analytical purposes. The remainder of the filtrate was used directly in the subsequent ozonolysis step. The degree of substitution was determined to be 1.33 by proton NMR from the ratio of integration between the olefin peaks and the anomeric peaks at 4.8-5.0.

In the second step, 460 mL of the filtrate resulting from step 1 was added to a 3-neck, 2 L flask equipped with magnetic stir bar, and sparge tube inlet. The solution was cooled in an ice bath to 0-5Â° C. and then sparging with ozone was begun from an ozone generator (ClearWater Tech, LLC., San Luis Obispo, Calif.; Model CD10) at 100% power which generates 7% ozone. Foaming occurred, which was controlled by the addition of a few drops of 1-heptanol. Samples were taken at 6.25 and 7.75 hours and analyzed using 13-C NMR. Disappearance of resonances at 118 and 134 ppm indicated that the olefin had been consumed after 7.75 hours. Then, a solution of sodium sulfite (23.3 g in 138 mL water) was added dropwise with stirring. A slight exotherm was observed and the reaction mixture was allowed to stir overnight under nitrogen. The mixture was transferred to a 1 L glass jar and filtered through a Millipore Pellicon II ultrafiltration system with 1 kDa cutoff filters. Water was continuously added to replace the filtrate collected, and the retentate was recycled back to the glass jar. This process was continued until more than 5Ã— the initial reaction volume had been collected in the filtrate. The purified solution was then frozen and lyophilized to give 53.9 g of a fluffy white solid. The degree of aldehyde substitution of the resulting solid product was determined to be 89% using the method of Zhao and Heindel (Pharmaceutical Research 8:400, 1991). The weight-average molecular weight of the aldehyde-functionalized dextran was determined to be about 15 kDa using size exclusion chromatography (SEC). This aldehyde-functionalized dextran is referred to herein as AFD-15-90.

A second preparation of this aldehyde-functionalized dextran was made using the same procedure. The degree of aldehyde substitution of the resulting product was determined to be 92% using the method of Zhao and Heindel and the weight-average molecular weight was found to be 16 kDa using SEC. This aldehyde-functionalized dextran is referred to herein as AFD-16-92.

Preparation of Inulin Having Pendant Aldehyde Groups (AFI-12-49):

Inulin containing pendant aldehyde groups and having a weight-average molecular weight of about 12 kDa and a degree of aldehyde substitution of about 49% was prepared using the two step procedure described above.

In the first step, 20 g of inulin (average molecular weight of about 4 kDa, Sigma) was suspended in 200 mL of water, heated to 70Â° C. for 1 hour to dissolve, and then cooled to 65Â° C. To this solution was added 23 mL of sodium hydroxide solution (20 wt % in water), followed by the slow addition of allyl glycidyl ether (50.7 g) via a syringe pump at a rate of 3 mL/min. After the addition, the mixture was heated to 65Â° C. for 6 hours. After which time, the reaction mixture was cooled to room temp and neutralized to pH 7 with 50% HCl. The reaction mixture was purified by ultrafiltration over a 1000 MWCO membrane (collect 10Ã— volume of waste).

¹H NMR (D₂O): d 5.95 ppm (m, integral 1.0, OCH₂C(H)=CH₂), 5.31 (dd, integral 2.1,OCH2(CH)=CH₂), 4.37 (br. s, integral 0.40), 4.25 (br. s, integral 0.76), 4.0-3.55 (br. m, integral 12.9).

In the second step, the filtrate was cooled to approximately 5Â° C. using an ice/water bath. Ozone was sparged into the stirred solution for 6 hours. 1-Heptanol was added (a few drops) to control foaming. At the end of the reaction, sodium sulfite solution (16 g in 100 mL water) was added to the cooled solution (cooled in an ice/water bath). The solution was stirred at room temperature overnight. The product was purified by ultrafiltration (MWCO 1000, collect 12Ã— volume of waste). The filtrate was lyophilized to yield a white solid.

Size exclusion chromatography (SEC) analysis of the product gave the following: M_w=1.2Ã—10⁴, M_n=7.3Ã—10³, M_z=1.5Ã—10⁴, M_w/M_n=1.6.

The degree of aldehyde substitution was determined to be about 49% by titration of the hydroxylamine adduct of the inulin aldehyde using the method described by Zhao and Heindel (Pharmaceutical Research 8:400, 1991). This aldehyde-functionalized inulin is referred to herein as AFI-12-49.

Preparation of Dextran Having Pendant Aldehyde Groups (AFD-7-86):

Dextran containing pendant aldehyde groups and having a weight-average molecular weight of about 5 to 11 kDa and a degree of aldehyde substitution of 86% was prepared using a two step procedure. In the first step, dextran having a weight-average molecular weight of about 5 to about 11 kDa was reacted with glycidol to form alkylated dextran. In the second step the alkylated dextran was oxidized with sodium periodate to oxidize the terminal diol groups added in the first step to give dextran having pendant aldehyde groups.

In the first step, 20 g of dextran (average molecular weight of 5-11 kDa, Sigma), was suspended in 20 mL of water and heated to 55Â° C. To this solution was added 25 mL of sodium hydroxide solution (20 wt % in water), followed by the slow addition of glycidol (36 g, Aldrich) using a syringe pump at a flow rate of 1.0 mUmin at 55Â° C. Then, the mixture was heated to 55Â° C. for 6 hours, after which the reaction mixture was cooled to room temperature. The product was washed twice with 20 mL of ether to remove excess reagent. The resulting yellow homogeneous mixture was neutralized with 50% HCl over ice (final pH was 7.3). The sample was precipitated in approximately 5Ã— volume of cold isopropanol (Ëœ0Â° C.). The isopropanol layer was decanted off, the solid product washed with cold isopropanol, and the process of dissolution followed by precipitation was repeated two more times. The solid product was dried under vacuum for 48 hours.

In the second step, 15 g of the solid product from the first step was dissolved in 150 mL of water in a round bottom flask and then the resulting solution was cooled to 4Â° C. Sodium periodate solution (8.25 g in 85 mL of water) was added to the round bottom flask dropwise over 30 min. The reaction mixture was stirred at 4Â° C. for 2 hours, and then 10.4 g (9.3 mL) of ethylene glycol was added to the reaction mixture, which was then stirred for 10 min. The product was purified using a TFF System (Millipore Corp., Billerica, Mass.) with a 1000 molecular weight cut off membrane and freeze dried to yield 10 g of white powder. The degree of aldehyde substitution of the product was determined to be 86% by titration of the hydroxylamine adduct using the method described by Zhao and Heindel (Pharmaceutical Research 8:400, 1991).

Size exclusion chromatography (SEC) analysis of the product gave the following: M_w=7.4Ã—10³, M_n=4.8Ã—10³, M_z=1.1Ã—10⁴, M_w/M_n=1.5. This aldehyde-functionalized dextran is referred to herein as AFD-7-86.

Preparation of Dextran Having Pendant Aldehyde Groups (AFD-9-120):

Dextran containing pendant aldehyde groups and having a weight-average molecular weight of about 9 kDa and a degree of aldehyde substitution of 120% was prepared using a two step procedure. In the first step, dextran having a weight-average molecular weight of about 5 to about 11 kDa was reacted with glycidol to form alkylated dextran. In the second step the alkylated dextran was oxidized with sodium periodate to oxidize the terminal diol groups added in the first step to give dextran having pendant aldehyde groups.

In the first step, three batches of dextran were reacted with glycidol to form the alkylated dextran. In two of the batches, 20 g of dextran (average molecular weight of 5-11 kDa, Sigma), was reacted with glycidol (36 g, Aldrich) in the same manner as described above, for the first step of the preparation of AFD-7-86. In the third batch, the mole ratio of glycidol to dextran was varied. Dextran (10 g) was dissolved in a solution formed by combining 10 mL of water and 12.5 mL sodium hydroxide solution (20 wt %). Glycidol (44 g, Aldrich) was added to the dextran solution using a syring pump at a rate of 0.7 mL/mn. The mixture was heated to 55Â° C. and 20 mL of water was added. The reaction mixture was heated at 55Â° C. for 6 hours. The product was isolated as described above for AFD-7-86. The three batches were combined to make a master batch of materials for the second step.

In the second step, 25 g of the solid product from the master batch described above was dissolved in 250 mL of water in a round bottom flask and then the resulting solution was cooled to 4Â° C. Sodium periodate solution (20.8 g in 125 mL of water) was added to the round bottom flask dropwise over 1 hour. The reaction mixture was stirred at 4Â° C. for 2 hours, and then 66 g of ethylene glycol was added to the reaction mixture, which was then stirred for 30 min. After which time, the reaction mixture was filtered. The filtrate was purified using a TFF System (Millipore Corp., Billerica, Mass.) with a 1000 molecular weight cut off membrane and freeze dried to yield 17 g of white powder. The degree of aldehyde substitution of the product was determined to be 120% by titration of the hydroxylamine adduct using the method described by Zhao and Heindel (Pharmaceutical Research 8:400, 1991).

Size exclusion chromatography (SEC) analysis of the product gave the following: M_w=8.9Ã—10³, M_n=6.8Ã—10³, M_z=1.2Ã—10⁴, M_w/M_n=1.3. This aldehyde-functionalized dextran is referred to herein as AFD-9-120.

Preparation of Dextran Having Pendant Aldehyde Groups (AFD-13-64):

Dextran containing pendant aldehyde groups and having a weight-average molecular weight of about 13 kDa and a degree of aldehyde substitution of 64% was prepared using a two step procedure. In the first step, dextran having a weight-average molecular weight of about 5 to about 11 kDa was reacted with glycidol to form alkylated dextran. In the second step the alkylated dextran was oxidized with sodium periodate to oxidize the terminal diol groups added in the first step to give dextran having pendant aldehyde groups.

The first step was carried out as described above for AFD-9-120. In the second step, 25 g of the solid product from the master batch of the alkylated dextran described above for AFD-9-120 was dissolved in 250 mL of water in a round bottom flask and then the resulting solution was cooled to 4Â° C. Sodium periodate solution (10.4 g in 60 mL of water) was added to the round bottom flask dropwise over 1 hour. The reaction mixture was stirred at 4Â° C. for 2 hours, and then 6 g of ethylene glycol was added to the reaction mixture, which was then stirred for 30 min. Then the reaction mixture was filtered. The filtrate was purified using a TFF System (Millipore Corp., Billerica, Mass.) with a 1000 molecular weight cut off membrane and freeze dried to yield 17 g of white powder. The degree of aldehyde substitution of the product was determined to be 64% by titration of the hydroxylamine adduct using the method described by Zhao and Heindel (Pharmaceutical Research 8:400, 1991).

Size exclusion chromatography (SEC) analysis of the product gave the following: M_w=1.3Ã—10⁴, M_n=9.8Ã—10³, M_z=1.8Ã—10⁴, M_w/M_n=1.3. This aldehyde-functionalized dextran is referred to herein as AFD-13-64.

Preparation of Dextran Having Pendant Aldehyde Groups (AFD-13-46):

Dextran containing pendant aldehyde groups and having a weight-average molecular weight of about 13 kDa and a degree of aldehyde substitution of 46% was prepared using a two step procedure. In the first step, dextran having a weight-average molecular weight of about 9 to about 11 kDa was reacted with allyl glycidyl ether to form an olefin intermediate, which was then reacted with ozone to form the dextran containing pendant aldehyde groups.

In the first step, 30 g of dextran (average molecular weight of 9-11 kDa, Sigma), and 30 mL of water were added into a 3-neck flask. The solution was cooled to 10Â° C. and then 39 mL of a 20 wt % NaOH solution was added. The resulting solution was stirred for 25 min, giving a faint yellow solution, and then 42.27 g (2 equiv) of allyl glycidyl ether (Aldrich) was added. The resulting mixture was heated to 65Â° C. for 5.5 hours and then allowed to cool to room temperature, after which the pH was adjusted to 7.0 with 1 N HCl. The mixture was diluted with an additional 200 mL of water and purified with a Millipore Pellicon II ultrafiltration system (Millipore Corp., Billerica, Mass.) using 1 kDa cutoff filters with continuous replacement of filtrate with pure water until 5Ã— the initial solution volume had been collected as filtrate. A small sample of the filtrate was taken and lyophilized for analytical purposes. The remainder of the filtrate was used directly in the subsequent ozonolysis step. The degree of substitution was found to be 0.84 by NMR, integrating the olefinic peaks relative to the anomeric resonances.

In the second step, 475 mL of the filtrate resulting from step 1 was added to a 3-neck, 2 L flask equipped with magnetic stir bar, and sparge tube inlet. The solution was cooled in an ice bath to 0-5Â° C. and then sparging with ozone was begun from an ozone generator (ClearWater Tech, LLC., San Luis Obispo, Calif.; Model CD10) at 100% power which generates 7% ozone. Foaming occurred, which was controlled by the addition of a few drops of 1-heptanol. Samples were taken at 2 and 4 hours and analyzed using 13-C NMR. Disappearance of resonances at 118 and 134 ppm indicated that the olefin had been consumed after 4 hours. Then, a solution of sodium sulfite (19.6 g in 117 mL of water) was added dropwise with stirring. A slight exotherm was observed and the reaction mixture was allowed to stir overnight under nitrogen. The mixture was transferred to a 1 L glass jar and filtered through a Millipore Pellicon II ultrafiltration system with 1 kDa cutoff filters. Water was continuously added to replace the filtrate collected, and the retentate was recycled back to the glass jar. This procedure was continued until more than 5Ã— the initial reaction volume had been collected in the filtrate. The purified solution was then frozen and lyophilized to give 28.6 g of a fluffy white solid. The degree of aldehyde substitution of the resulting solid product was determined to be 46% using the method of Zhao and Heindel (Pharmaceutical Research, 1991, 8:400). The weight-average molecular weight of the aldehyde-functionalized dextran was determined to be about 13 kDa using size exclusion chromatography (SEC). This aldehyde-functionalized dextran is referred to herein as AFD-13-46.

Preparation of Dextran Having Pendant Aldehyde Groups (AFD-19-64):

Dextran containing pendant aldehyde groups and having a weight-average molecular weight of about 19 kDa and a degree of aldehyde substitution of 60% was prepared using the two step procedure described above.

In the first step, 30 g of dextran (average molecular weight of 9-11 kDa, Sigma), and 30 mL of water were added into a 3-neck flask. The solution was cooled to 10Â° C. and then 39 mL of a 20 wt % NaOH solution was added. The resulting solution was stirred for 25 min, giving a faint yellow solution, and then 63.41 g (3 equiv) of allyl glycidyl ether (Aldrich) was added. The resulting mixture was heated to 65Â° C. for 5.5 hours, and then allowed to cool to room temperature, after which the pH was adjusted to 7.0 with 1 N HCl. The mixture was diluted with an additional 200 mL of water and purified using the Millipore Pellicon II ultrafiltration system, by filtration through 1 kDa cutoff filters with continuous replacement of filtrate with pure water until 5Ã— the initial solution volume had been collected as filtrate. A small sample was taken and lyophilized for analytical purposes. The remainder of the filtrate was used directly in the subsequent ozonolysis step. The degree of substitution was determined to be 0.99 by NMR from the ratio of integration between the olefin peaks and the anomeric peaks at 4.8-5.0.

In the second step, 475 mL of the filtrate resulting from step 1 was added to a 3-neck, 2 L flask equipped with magnetic stir bar, and sparge tube inlet. The solution was cooled in an ice bath to 0-5Â° C. and then sparging with ozone was begun from an ozone generator (ClearWater Tech, LLC., San Luis Obispo, Calif.; Model CD10) at 100% power which generates 7% ozone. Foaming occurred, which was controlled by the addition of a few drops of 1-heptanol. Samples were taken at 4 and 5.75 hours and analyzed using 13-C NMR. Disappearance of resonances at 118 and 134 ppm indicated that the olefin had been consumed after 5.75 hours. Then, a solution of sodium sulfite (23.3 g in 139 mL water) was added dropwise with stirring. A slight exotherm was observed and the reaction mixture was allowed to stir overnight under nitrogen. The mixture was transferred to a 1 L glass jar and filtered through a Millipore Pellicon II ultrafiltration system with 1 kDa cutoff filters. Water was continuously added to replace the filtrate collected, and the retentate was recycled back to the glass jar. This process was continued until more than 5Ã— the initial reaction volume had been collected in the filtrate. The purified solution was then frozen and lyophilized to give 39.1 g of a fluffy white solid. The degree of aldehyde substitution of the resulting solid product was determined to be 60% using the method of Zhao and Heindel (Pharmaceutical Research, 1991, 8:400). The weight-average molecular weight of the aldehyde-functionalized dextran was determined to be about 19 kDa using size exclusion chromatography (SEC). This aldehyde-functionalized dextran is referred to herein as AFD-19-64.

Preparation of Dextran Having Pendant Dialdehyde Groups (DAFD-10-16):

Dialdehyde-functionalized dextran in which the pendant dialdehyde groups are linked to the dextran backbone by an ether bond was prepared using a three step procedure.

Step 1:

To a 300 mL, two-neck flask equipped with a magnetic stir bar and nitrogen inlet was added 74.3 mL of a 40 wt % sodium hydroxide solution and 0.94 g (2.91 mmol) of tetrabutylammonium bromide. The solution was cooled to 5-10Â° C. and treated with 5.0 g (59.44 mmol) of 3-cyclopentene- 1-ol followed by dropwise addition of epichlorohydrin 22.0 g (237.76 mmol) over a 20 min period. The reaction mixture was stirred at room temperature overnight. Then, the reaction mixture was poured onto approximately 50 mL of ice/water and stirred to give a solution, which was extracted three times with 50 mL portions of diethyl ether. The combined organic layers were washed with brine solution until neutral to litmus and dried over MgSO₄. The solvent was removed on a rotary evaporator to yield a brown liquid. The crude product was purified by distillation. The product was collected at 118Â° C. and 25 mm Hg (3.3 kPa).

¹H NMR in CDCl₃Î´ ppm (2.42,m, 2H; 2.5,m 1H; 2.6,m,2H, 2.78,m,1H; 3.15,m,1H;3.4,m,1H; 3.65-3.68,m,1H;4.26,m,1H; 5.68s,2H)

Step 2:

Into a 10 mL, 2-neck flask equipped with a magnetic stir bar and reflux condenser with nitrogen inlet was placed 0.58 mL of water followed by 0.5778 g (3.567 mmol) of dextran having a weight-average molecular weight of about 9 to about 11 kDa. The solution was stirred to form a suspension. To the flask was added 0.75 mL of 20 wt % NaOH solution. After stirring for 30 min, 1.0 g (7.134 mmol) of glycidyl 3-cyclopentenyl ether was added. The solution was heated in an oil bath at 65Â° C. for 5.5 hours. Then, the reaction mixture was cooled to room temperature and the pH was adjusted to 7.0 with 0.5 M HCl. The resulting solution was diluted to approximately 400 mL with water, then purified using the Millipore Pellicon II ultrafiltration system with a 1000 molecular weight cutoff cassette. A small aliquot was lyophilized for analysis.

¹H NMR was obtained in D₂O. Î´ ppm (2.2,d; 2.4,d; 3.31-3.7,m;4.1,s;4.77,s;4.9,s(b); 5.55, s)

The remainder of the solution was treated with ozone to make functionalized dextran. From NMR, the degree of substitution was determined by integration of the anomeric peaks at 5.0-5.2 ppm vs. the olefinic peaks. The degree of substitution was found to be 0.52.

Step 3:

A 1 L, 3-neck flask containing 400 mL of the aqueous solution of functionalized dextran (from the previous step) at approximately 8Â° C. was sparged with ozone for 5.5 hours. The ozone flow was stopped and a solution of 0.45 g of sodium sulfite in 3 mL of water was added to the flask at 8Â° C. The solution was stirred overnight and purified by ultrafiltration on the Millipore Pellicon II ultrafiltration system using 1000 MWCO cassette. The final solution was frozen and lyophilized to yield 0.68 g of a foam-like solid.

¹H NMR was obtained in D₂O. Î´ ppm (1.318,m; 1.523,m; 1.8,m; 2.1,m; 2.3-2.48,m; 3.3-3.9,m; 4.9,s; 5.1, s(b); 5.5,s)

The degree of aldehyde substitution was determined to be about 16% by titration of the hydroxylamine adduct of the dialdehyde-functionalized dextran using the method described by Zhao and Heindel (Pharmaceutical Research 8:400, 1991). This dialdehyde-functionalized dextran is referred to herein as DAFD-10-16.

Preparation of Dextran Having Pendant Dialdehyde Groups (DAFD-Ester Linked):

Dialdehyde-functionalized dextran in which the pendant dialdehyde groups are linked to the dextran backbone by an ester bond was prepared using a two step procedure.

Step 1:

Into a 50 mL, 3-neck flask equipped with magnetic stir bar and a reflux condenser was placed 22 mL of dimethylacetamide (DMAC) followed by 1.817 g (11.217 mmol) of dextran having a weight-average molecular weight of about 9 to about 11 kDa and 1.09 g (25.71 mmol) of lithium chloride. A suspension formed, which was heated to 90Â° C. for one hour until a clear solution resulted. The solution was cooled to room temperature and 0.91 mL (11.217 mmol) of pyridine was added followed by dropwise addition of 2.18 g (11.217 mmol) of 3-cyclopentene carbonyl chloride. 4-Dimethylaminopyridine (DMAP, Aldrich) (30 mg) was added and the mixture was heated mixture at 60Â° C. overnight i.e., approximately 20 hours). After cooling, the resulting brown solution was added dropwise to 200 mL of cooled water with stirring to give a yellow solution. The pH was adjusted from 2.15 to 6.0 using 0.25 N NaOH solution. The crude product was purified on a Millipore Pellicon II ultrafiltration system using a 1000 molecular weight cutoff cassette. A small aliquot was frozen and lyophilized to obtain an analytical sample.

¹H NMR. Î´ ppm (2.59-2.66,m); (2.85,s); (3.0,s); (3.24(b),s); (3.46-3.51,m); (3.52-3.71,m); (3.84,d); (3.93,d); (4.91, s); (4.97,s); (5.12,t); (5.68,s)

Step 2:

A 1 L, 3-neck flask equipped with a magnetic stir bar and containing 350 mL of the solution resulting from the previous step at approximately 8Â° C. was sparged with an ozone stream for 5 hours. After discontinuing the ozone sparge, a solution of 1.41 g of sodium sulfite in 8.4 mL water was added. The resulting mixture was stirred at room temperature overnight, then purified on a Millipore Pellicon II ultrafiltration system using a 1000 molecular weight cutoff cassette filter. The solution was frozen and lyophilized to yield 1.92 g of a white solid.

¹H NMR was submitted in D₂O. Î´ ppm (3.49-3.79,m); (3.89-3.97,m); (4.97 d, (broad)); 5.16(s, (b))

This dialdehyde-functionalized dextran is referred to herein as DAFD-Ester Linked.

Preparation of Oxidized Dextran (D10-50)

Dextran aldehyde is made by oxidizing dextran in aqueous solution with sodium metaperiodate. An oxidized dextran having an average molecular weight of about 10,000 Da and an oxidation conversion of about 50% (i.e., about half of the glucose rings in the dextran polymer are oxidized to dialdehydes) is prepared from dextran having a weight-average molecular weight of 8,500 to 11,500 Daltons (Sigma) by the method described by Cohen et al. (copending and commonly owned International Patent Application Publication No. WO 2008/133847). A typical procedure is described here.

A 20-L reactor equipped with a mechanical stirrer, addition funnel, internal temperature probe, and nitrogen purge is charged with 1000 g of the dextran and 9.00 L of de-ionized water. The mixture is stirred at ambient temperature to dissolve the dextran and then cooled to 10 to 15Â° C. To the cooled dextran solution is added over a period of an hour, while keeping the reaction temperature below 25Â° C., a solution of 1000 g of sodium periodate dissolved in 9.00 L of de-ionized water. Once all the sodium periodate solution has been added, the mixture is stirred at 20 to 25Â° C. for 4 more hours. The reaction mixture is then cooled to 0Â° C. and filtered to clarify. Calcium chloride (500 g) is added to the filtrate, and the mixture is stirred at ambient temperature for 30 min and then filtered. Potassium iodide (400 g) is added to the filtrate, and the mixture is stirred at ambient temperature for 30 min. A 3-L portion of the resulting red solution is added to 9.0 L of acetone over a period of 10 to 15 min with vigorous stirring by a mechanical stirrer during the addition. After a few more minutes of stirring, the agglomerated product is separated from the supernatant liquid. The remaining red solution obtained by addition of potassium iodide to the second filtrate is treated in the same manner as above. The combined agglomerated product is broken up into pieces, combined with 2 L of methanol in a large stainless steel blender, and blended until the solid becomes granular. The granular solid is recovered by filtration and dried under vacuum with a nitrogen purge. The granular solid is then hammer milled to a fine powder. A 20-L reactor is charged with 10.8 L of de-ionized water and 7.2 L of methanol, and the mixture is cooled to 0Â° C. The granular solid formed by the previous step is added to the reactor and the slurry is stirred vigorously for one hour. Stirring is discontinued, and the solid is allowed to settle to the bottom of the reactor. The supernatant liquid is decanted by vacuum, 15 L of methanol is added to the reactor, and the slurry is stirred for 30 to 45 min while cooling to 0Â° C. The slurry is filtered in portions, and the recovered solids are washed with methanol, combined, and dried under vacuum with a nitrogen purge to give about 600 g of the oxidized dextran, which is referred to herein as D10-50.

The degree of oxidation of the product is determined by proton NMR to be about 50% (equivalent weight per aldehyde group=146). In the NMR method, the integrals for two ranges of peaks are determined, specifically, â€”O₂CHx- at about 6.2 parts per million (ppm) to about 4.15 ppm (minus the HOD peak) and â€”OCHx- at about 4.15 ppm to about 2.8 ppm (minus any methanol peak if present). The calculation of oxidation level is based on the calculated ratio (R) for these areas, specifically, R=(OCH)/(O₂CH).

Preparation of Eight-Arm PEG 10K Octaamine (P8-10-1):

Eight-arm PEG 10K octaamine (M_n=10 kDa) is synthesized using the two-step procedure described by Chenault in co-pending and commonly owned U.S. Patent Application Publication No. 2007/0249870. In the first step, the 8-arm PEG 10K chloride is made by reaction of thionyl chloride with the 8-arm PEG 10K octaalcohol. In the second step, the 8-arm PEG 10K chloride is reacted with aqueous ammonia to yield the 8-arm PEG 10K octaamine. A typical procedure is described here.

The 8-arm PEG 10K octaalcohol (M_n=10000; NOF SunBright HGEO-10000), (100 g in a 500-mL round-bottom flask) is dried either by heating with stirring at 85Â° C. under vacuum (0.06 mm of mercury (8.0 Pa)) for 4 hours or by azeotropic distillation with 50 g of toluene under reduced pressure (2 kPa) with a pot temperature of 60Â° C. The 8-arm PEG 10K octaalcohol is allowed to cool to room temperature and thionyl chloride (35 mL, 0.48 mol) is added to the flask, which is equipped with a reflux condenser, and the mixture is heated at 85Â° C. with stirring under a blanket of nitrogen for 24 hours. Excess thionyl chloride is removed by rotary evaporation (bath temp 40Â° C.). Two successive 50-mL portions of toluene are added and evaporated under reduced pressure (2 kPa, bath temperature 60Â° C.) to complete the removal of thionyl chloride. Proton NMR results from one synthesis are:

¹H NMR (500 MHz, DMSO-d6) Î´ 3.71-3.69 (m, 16H), 3.67-3.65 (m, 16H), 3.50 (s, Ëœ800H).

The 8-arm PEG 10K octachloride (100 g) is dissolved in 640 mL of concentrated aqueous ammonia (28 wt %) and heated in a pressure vessel at 60Â° C. for 48 hours. The solution is sparged for 1-2 hours with dry nitrogen to drive off 50 to 70 g of ammonia. The solution is then passed through a column (500 mL bed volume) of strongly basic anion exchange resin (PuroliteÂ® A-860, The Purolite Co., Bala-Cynwyd, Pa.) in the hydroxide form. The eluant is collected and three 250-mL portions of de-ionized water are passed through the column and also collected. The aqueous solutions are combined, concentrated under reduced pressure (2 kPa, bath temperature 60Â° C.) to about 200 g, frozen in portions and lyophilized to give the 8-arm PEG 10K octaamine, referred to herein as P8-10-1, as a colorless waxy solid.

Preparation of 8-Arm PEG 10K Hexadecaamine (P8-10-2):

An 8-arm PEG 10K hexadecaamine, referred to herein as â€œP8-10-2â€ , having two primary amine groups at the end of the arms, was prepared using a two step procedure, as described by Arthur in WO 2008/066787, in which 8-arm PEG 10K was reacted with methanesulfonyl chloride in dichloromethane in the presence of triethylamine to produce 8-arm PEG 10K mesylate, which was subsequently reacted with tris(2-aminoethyl)amine to give the 8-arm PEG 10K hexadecaamine. A typical synthesis is described here.

To a solution of 10 g of 8-arm PEG 10K (M_n=10,000; NOF, Tokyo, Japan) in 50 mL of dichloromethane stirred under nitrogen and cooled to 0Â° C. is added 2.2 mL of triethylamine, followed by 1.2 mL of methanesulfonyl chloride. The mixture is allowed to warm to room temperature and is stirred overnight. The reaction mixture is transferred to a separatory funnel and washed gently three times with 15 mL portions of 1 M potassium dihydrogen phosphate, followed by 15 mL of 1 M potassium carbonate, and then 15 mL of water. The dichloromethane layer is dried over magnesium sulfate, filtered, and concentrated by rotary evaporation to afford 11.17 g of 8-arm PEG 10K mesylate.

A mixture of 10 g of 8-arm PEG 10K mesylate and 45 mL of tris(2-aminoethyl)amine dissolved in 45 mL of water is stirred at room temperature for 24 hours. The reaction mixture is diluted with 45 mL of 5% (w/w) aqueous sodium bicarbonate and extracted with a total of 500 mL of dichloromethane divided in 3 portions. The dichloromethane solution is dried over sodium sulfate, and concentrated by rotary evaporation to 20 to 25 g. Ether (100 mL) is added to the concentrated dichloromethane solution with vigorous stirring, and the mixture is cooled to 0Â° C., causing a waxy solid to separate from solution. The solvent is decanted from the waxy solid, and the waxy solid is dried under vacuum to give the 8-arm PEG 10K hexadecaamine (P8-10-2).

EXAMPLES 1-15In-Vitro Burst Testing of a Sealed Scalpel Incision in Swine Uterine Horn

The purpose of these Examples was to demonstrate the burst strength of a seal made with various hydrogels of an incision made in swine uterine horn.

A syringe pump system was used to measure the burst strength of a seal of an incision made in a section of swine uterine horn. The syringe pump (Model No. 22, Harvard Apparatus, Holliston, Mass.) was modified to be equipped with two 30 mL syringes, which were connected together through a â€œYâ€ junction. Water was pumped through a single piece of TygonÂ® R-36 tubing (0.6 cm diameter) and through a pressure gauge (Model PDG 5000L, Omega Engineering, Stamford, Conn.). An approximately 12.5 cm section of clean swine uterine horn, obtained from a local abattoir, was fitted on one end with a metal plug with a feed line fitting for water feed from the syringe pump and on the other end with a metal plug with a threaded hole which could be sealed with a machine screw. The plugs were held in place with nylon ties around the outside of the intestine. An incision was made through the uterine horn wall into the interior by puncturing with a Bard Parkerâ„¢ surgical blade handle 5 (obtained from BD Surgical Products, Franklin Lakes, N.J.), fitted with a #15 surgical blade. The incision on the outside of the uterine horn was wider than the scalpel blade (typically 4-5 mm) while the hole through the inside wall was about 3 mm (about equal to the blade). This size incision mimics the distance between the interrupted sutures if an intestine were to be cut and later sutured. The uterine horn was filled with water containing a purple dye via the syringe pump until water began to leak from the open hole in the end plug and also from the scalpel puncture in the uterine horn wall. The pump was then turned off and the end plug was sealed with the machine screw. The scalpel incision site was blotted dry using a paper towel.

The aldehyde-functionalized polysaccharide and multi-arm PEG amine solutions, as shown in Table 1, were prepared in water with shaking overnight at 37Â° C. and 175 rpm. The two solutions were applied to the incision using a double barrel syringe (Mixpac Systems AG (Rotkreuz, Switzerland) fitted with a 16 or a 12 step static mixer (Mixpac Systems AG). After the application, the adhesive was allowed to cure at room temperature for no longer than 2 min. Burst pressure testing, also referred to herein as leak pressure testing, was done by pressurizing the sealed intestine with water from the syringe pump at a flow rate of 11 mL/min until the bioadhesive seal began to leak, at which point the pressure was recorded. Adhesive failure was attributed when the water leaked under the seal between the hydrogel and the tissue surface. Cohesive failure was attributed when the water penetrated and leaked through the hydrogel itself. The results of the burst testing are summarized in Table 1.

TABLE 1Burst Pressure Testing ResultsAldehyde-FunctionalizedMulti-ArmAve BurstPolysaccharidePEGPressure,ExampleSolutionAmine Solutionpsi1AFD-15-90P8-10-1/P8-10-21.240 wt %(1:2 w/w)(8.3 kPa)20 wt %2AFD-15-90P8-10-1/P8-10-22.440 wt %(1:2 w/w)(16 kPa)30 wt %3AFD-15-90P8-10-1/P8-10-22.825 wt %(1:2 w/w)(19 kPa)20 wt %4AFD-15-90P8-10-1/P8-10-21.325 wt %(1:2 w/w)(9.0 kPa)10 wt %5AFD-7-86P8-10-14.230 wt %50 wt %(29 kPa)6AFD-7-86P8-10-21.130 wt %20 wt %(7.6 kPa)7AFD-7-86P8-10-1/P8-10-22.730 wt %(9:1 w/w)(19 kPa)30 wt %8AFD-9-120P8-10-13.025 wt %30 wt %(21 kPa)9AFD-9-120P8-10-1/P8-10-22.525 wt %(1:2 w/w)(18 kPa)25 wt %10AFD-13-64P8-10-12.525 wt %30 wt %(18 kPa)11AFD-13-64P8-10-1/P8-10-24.225 wt %(1:2 w/w)(30 kPa)25 wt %12AFI-12-49P8-10-1/P8-10-22.640 wt %(9:1 w/w)(18 kPa)30 wt %13AFI-12-49P8-10-1/P8-10-22.825 wt %(9:1 w/w)(19 kPa)30 wt %14AFI-12-49P8-10-1/P8-10-24.740 wt %(1:1 w/w)(32 kPa)30 wt %15AFI-12-49P8-10-1/P8-10-24.240 wt %(1:2 w/w)(29 kPa)30 wt %

The results shown in Table 1 demonstrate that hydrogels formed by reacting an aldehyde-functionalized polysaccharide containing pendant single aldehyde groups with a mixture of an eight-arm branched end polyethylene glycol amine having two primary amino groups at the end of the polymer arms (i.e. P8-10-2) and an eight-arm polyethylene glycol amine (P8-10-1) having one primary amine group at the end of the polymer arms, adhered well to and sealed biological tissue.

EXAMPLES 16-26 In Vitro Biocompatibility Testingâ€”Cytotoxicity

The purpose of these Examples was to demonstrate the safety of hydrogels resulting from the reaction of an aldehyde-functionalized polysaccharide with a multi-arm PEG amine in an in vitro test.

The testing was done using NIH3T3 human fibroblast cell cultures according to ISO10993-5:1999. The NIH3T3 human fibroblast cells were obtained from the American Type Culture Collection (ATCC; Manassas, Va.) and were grown in Dulbecco's modified essential medium (DMEM), supplemented with 10% fetal calf serum.

NIH3T3 human fibroblast cell cultures were challenged with hydrogels made by combining equal volumes of an aqueous solution of an aldehyde-funtionalized polysaccharide and an aqueous solution of multi-arm PEG amine, as shown in Table 2. The aqueous solutions were prepared and mixed to form hydrogels as described in Examples 1-15. Each hydrogel was placed in the bottom of a well in a polystyrene culture plate such that about % of the well bottoms were covered. The wells were then sterilized under UV light and seeded with 50,000-100,000 NIH3T3 cells.

The cells grew normally confluent and coated the well bottom, growing up to the edges of the hydrogels; however, they did not overgrow the hydrogels. These results, summarized in Table 2, demonstrate a lack of cytotoxicity of the hydrogels, as well as the lack of adhesion of cell cultures to the hydrogels.

TABLE 2Cytotoxicity ResultsAldehyde-FunctionalizedMulti-ArmPolysaccharidePEGExampleSolutionamine solutionCytotoxicity16AFI-12-49P8-10-1/P8-10-2nontoxic25 wt %(9:1 w/w)30 wt %17AFI-12-49P8-10-1/P8-10-2nontoxic40 wt %(1:1 w/w)30 wt %18AFI-12-49P8-10-1/P8-10-2nontoxic40 wt %(1:2 w/w)25 wt %19AFD-9-120P8-10-1nontoxic25 wt %30 wt %20AFD-9-120P8-10-1/P8-10-2nontoxic25 wt %(1:2 w/w)25 wt %21AFD-13-64P8-10-1nontoxic25 wt %30 wt %22AFD-13-64P8-10-1/P8-10-2nontoxic25 wt %(1:2 w/w)25 wt %23AFD-15-90P8-10-1/P8-10-2nontoxic25 wt %(1:2 w/w)20 wt %25AFD-15-90P8-10-1/P8-10-2nontoxic40 wt %(1:2 w/w)20 wt %26AFD-15-90P8-10-1/P8-10-2nontoxic40 wt %(1:2 w/w)30 wt %

EXAMPLES 27-37 In Vitro Degradation of Hydrogels

The purpose of these Examples was to demonstrate that hydrogels formed by the reaction of an aldehyde-functionalized polysaccharide with a multi-arm PEG amine are hydrolyzed readily in an in vitro test.

The hydrogel samples were prepared by mixing equal volumes of an aqueous solution of an aldehyde-functionalized polysaccharide and an aqueous solution of a multi-arm PEG amine, as shown in Table 3. The aqueous solutions were prepared and mixed to form hydrogels as described in Examples 1-15. After the hydrogels cured, the samples were weighed and placed inside jars containing PBS (phosphate buffered saline) at pH 7.4. The jars were placed inside a temperature-controlled shaker set at 80 rpm and 37Â° C. The samples were removed from the jars at various times, blotted to remove excess solution, and weighed. Then, the samples were returned to the jars.

The results are summarized in Table 3. The percent swell reported in the table is the weight of the hydrogel measured during the course of the study divided by the initial weight of the hydrogel, multiplied by 100.

TABLE 3In Vitro Degradation of HydrogelsAldehyde-FunctionalizedMulti-ArmPolysaccharidePEGTimeExampleSolutionAmine Solution(hours)% Swell27AFD-15-90P8-10-1/P8-10-2010040 wt %(1:2 w/w)633230 wt %24285542599624319221821620726420338419145618452817628AFD-15-90P8-10-1/P8-10-2010040 wt %(1:2 w/w)615020 wt %241025487967419264216592645838446456515284929AFD-15-90P8-10-1/P8-10-2010025 wt %(1:2 w/w)621420 wt %24176541529612919212521612526411238410945610752810730AFD-7-86P8-10-167940 wt %50 wt %24031AFI-12-49P8-10-1/P8-10-26040 wt %(9:1 w/w)75030 wt %32AFD-13-64P8-10-132020 wt %30 wt %6033AFD-13-64P8-10-1/P8-10-235830 wt %(9:1 w/w)6030 wt %34AFD-13-64P8-10-1/P8-10-2636630 wt %(1:1 w/w)4822330 wt %3125935AFI-12-49P8-10-1/P8-10-26040 wt %(9:1 w/w)30 wt %36AFI-12-49P8-10-1/P8-10-26040 wt %(1:1 w/w)75030 wt %37AFI-12-49P8-10-1/P8-10-2611640 wt %(1:2 w/w)752025 wt %

The results in Table 3 demonstrate that hydrogels formed by the reaction of an aldehyde-functionalized polysaccharide with a multi-arm PEG amine are hydrolyzed readily in an in vitro test. By using different amounts of the components in terms of wt % and/or by altering the amount of funtionalization of either amine on the PEG amines or aldehyde on the aldehyde-functionalized polysaccharide, the time for degradation can be tuned from a few hours to many days. The hydrolysis results suggest that the hydrogels disclosed herein should degrade readily in vivo.

EXAMPLES 38 and 39 In Vitro Degradation of Hydrogels Formed Using Dialdehyde-Functionalized Dextrans

The purpose of these Examples was to examine the in vitro degradation of hydrogels formed by the reaction of dialdehyde-functionalized dextrans with a multi-arm PEG amine.

An aqueous solution containing dialdehyde-functionalized dextran DAFD-10-16 (Example 38) or DAFD-10-Ester Linked (Example 39) at a concentration of 20 wt % was mixed with an aqueous solution containing multi-arm PEG amine P8-10-1 (25 wt %) to form a hydrogel, as described in Examples 1-15. The degradation of the hydrogels was determined using the method described in Examples 27-37. The results are summarized in Table 4.

TABLE 4In Vitro Degradation of HydrogelsAldehyde-FunctionalizedMulti-ArmPolysaccharidePEGTimeExampleSolutionAmine Solution(hours)% Swell38DAFD-10-16P8-10-1010020 wt %25 wt %12492258424562448243222442624739DAFD-EsterP8-10-10100Linked25 wt %123620 wt %245.343.6

These results demonstrate that dialdehyde functionalized dextrans form hydrogels gels with the multi-arm PEG amine P-8-10-1 and that hydrogels with a wide range of degradation rates in an aqueous environment can be obtained. Specifically, long lived hydrogels can be formed using aldehyde-functionalized dextran having pendant dialdehyde groups where the linkage to the dextran backbone is chemically stable as in the ether linked dialdehyde-functionalized dextran (Example 38). Much faster degrading hydrogels can also be prepared by using aldehyde-functionalized dextran having pendant dialdehyde groups where the linkage of the the pendant dialdehyde groups is potentially hydrolytically unstable, such as an ester linkage (Example 39).

EXAMPLES 40-44 Stability of Aldehyde-Functionalized Dextrans in Aqueous Solutionâ€”Viscosity Measurements

The purpose of these Examples was to demonstrate the higher stability of aldehyde-functionalized dextrans in aqueous solution compared to oxidized dextran D10-50 using viscosity measurements.

Aqueous solutions of oxidized dextran (25 wt %) and various aldehyde-functionalized dextrans (25 wt %), as shown in Table 5, were heated at 45Â° C. for 12 days. The viscosity of the aqueous solutions was measured at 30Â° C. at various time points. The results are summarized in Table 5.

TABLE 5Viscosity of Aqueous Solutions of Oxidizeddextran and Aldehyde-Functionalized DextranViscosityViscosityViscosityViscosityDecrease(cP)(cP)(cP)after 12ExampleDextranDay 0Day 6Day 12days40AFD-13-17.3717.3517.94â€‚0%6441AFD-13-12.613.011.011%4642AFD-19-15.717.615.1â€‚4%6443AFD-15-14.314.312.711%9044,D10-50201815.622%Comparative

The results in Table 5 show that the aqueous solutions containing the aldehyde-functionalized dextrans having pendant aldehyde groups had a decrease in viscosity after 12 days ranging from 0% to 11%, whereas the viscosity of the aqueous solution containing the oxidized dextran decreased by 22% over the same time period. These results suggest that the aldehyde-functionalized dextrans having pendant aldehyde groups are more stable in aqueous solution than the oxidized dextran.

EXAMPLES 45-48 Stability of Aldehyde-Functionalized Dextrans in Aqueous Solutionâ€”Rheometry Measurements

The purpose of these Examples was to demonstrate the stability of aldehyde-functionalized dextrans in aqueous solution. Oscillating disk rheometry of the hydrogels resulting from the reaction of the aldehyde-functionalized dextrans with multi-arm polyether amines was used as a measure of the stability of the aldehyde-functionalized dextran solutions.

Double barrel syringes containing an aqueous solution of various aldehyde-functionalized polysaccharides in one barrel and an aqueous solution of a multi-arm PEG amine in the other barrel, as shown in Table 6, were prepared in duplicate. Two other double barrel syringes were filed with an aqueous solution of oxidized dextran D10-50 in one barrel and an aqueous solution of P8-10-1 (20 wt %) in the other barrel. The aqueous solutions contained in the double barrel syringes were expressed through a static mixing tip onto the sample platform of a Model APA2000 rheometer (Alpha Technologies, Akron, Ohio), and the storage modulus (Gâ€²) of the mixture was measured and taken as the value on Day zero. The value of Gâ€² at 60 seconds was taken as a measure of speed of gelation.

One group of the syringes was stored at 25Â° C. for various periods of time and the second group of syringes was heated at 40Â° C. for various periods of time (as shown in Table 6) to provide thermally aged aqueous solutions of the aldehyde-functionalized polysaccharides. The storage modulus of the mixed solutions was measured as described above at various times. The results are shown in Table 6, expressed as the percent of the Day zero Gâ€².

TABLE 6Rheometry Results of Hydrogel FormationPercentPercentAlehyde-of Day 0of Day 0FunctionalizedMulti-ArmGâ€²Gâ€²PolysaccharidePEG(60 sec)(60 sec)ExampleSolutionAmine Solution25Â° C.40Â° C.45AFD-15-90P8-10-194%56%(19 wt %)(20 wt %)(Day 20)(Day 20)46AFD-16-92P8-10-196%58%(20 wt %)(20 wt %)(Day 26)(Day 26)47AFI-12-49P8-10-2/P8-10-94%81%(25 wt %)1 (2:1) 20 wt %(Day 26(Day 26)48,D10-50P8-10-175%Did not gelComparative(25 wt %)(20 wt %)(Day 30)(Day 30)

The results in Table 6 suggest that the aldehyde-functionalized polysaccharides are more stable in aqueous solution than oxidized dextran.

EXAMPLE 49 Thermal Stability of AFD-13-64 in Aqueous Solution Using Rheometry Measurements

The purpose of this Example was to demonstrate the thermal stability of aldehyde-functionalized dextran AFD-13-64 in aqueous solution using oscillating disk rheometry.

Two double barrel syringes, each containing an aqueous solution of AFD-13-64 (20 wt%) in one barrel and an aqueous solution of P8-10-1 (20 wt %) in the other barrel were prepared. One syringe was heated at 40Â° C. for 19 days; the other syringe was stored at 4Â° C. for the same period of time. Then, the storage modulus of the mixtures resulting from each syringe was measured using a Model APA2000 rheometer (Alpha Technologies, Akron, Ohio). The storage modulus obtained for the mixture resulting from the syringe that was stored at 40Â° C. for 19 days was essentially identical to that obtained from the mixture resulting from the syringe that was stored at 4Â° C. for the same period of time, suggesting that the aldehyde-functionalized dextran AFD-13-64 has good thermal stability.

EXAMPLE 50, ComparativeAldehyde-Functionalized Carboxymethyldextran Containing Pendant Aldehyde Groups Attached by an Amide Linkage

The purpose of this Example was to demonstrate that an aldehyde-functionalized polysaccharide containing pendant aldehyde groups that are attached to the polysaccharide by an amide linkage is not as stable in aqueous solution as an aldehyde-functionalized polysaccharide containing pendant aldehyde groups that are attached to the polysaccharide by an ether linkage.

Preparation of 11 kDa carboxymethyldextran with decree of carboxymethylation of 1.1 (CMDX-11-1.1):

Dextran having an average molecular weight of 8.5-11 kDa (Sigma) was dissolved in 123.75 mL of 6 N NaOH at 0Â° C. To this cold solution was added 30.75 g of chloroacetic acid (Aldrich). This reaction mixture was heated to 60Â° C. for 20 min, then cooled, and neutralized to pH 7.0 with concentrated HCl. The product was precipitated by adding the neutralized solution dropwise to 1.0 L of methanol. The solids were collected by filtration and re-precipitated from methanol. The entire procedure was then repeated three times to raise the degree of substituion to the desired level. After the final repeat, the product was further purified by ultrafiltration. The solution was diafiltered using a Millipore Pellicon II TFF system. A total of 6 volumes of permeate was collected while continuously adding water to maintain a constant retentate volume. The retentate was then collected and lyophilized to give 14.25 g of a fluffy white solid. The degree of carboxymethylation was determined by the method of Ho et al. (Anal. Chem. 52:916, 1980) to be 1.1. This carboxymethyldextran product is referred to herein as CMDX-11-1.1. ¹H NMR Î´ 8 4.9-5.2 mult. (1H), 3.4-4.4 mult (9.5H).

Preparation of Aldehyde-Functionalized Carboxymethyldextran Containing Pendant Aldehyde Groups Attached by an Amide Linkage:

To a 3 liter, 3 necked flask was added 13.7 g of CMDX-60-1.7 and 916.6 mL of a 1:1 solution of teramethylethylene diamine buffer and dimethylformamide (DMF). A clear solution having a of pH 4.94 was formed. The pH was adjusted to 4.7 by addition of 1.0 M HCl. To the solution was added 47.74 g of 1-ethyle-3(3-dimethylaminopropyl)carbodiimide (Sigma) followed by 28.87 g of n-hydroxysuccinimide (Aldrich). The pH of the solution was readjusted to 4.7 and stirred for 2 hours. Then, 4-aminobutyraldehdye diethyl acetal (53.88 g) was added in portions over 3.5 hours so that the pH did not rise above 4.7. Toward the end of the reaction, the pH was allowed to rise to 6.25 and then the reaction mixture was stirred overnight. The reaction mixture was transferred to a glass jar, diluted with water and filtered on a Millipore Pellicon II ultrafiltration system with 1 kDa cutoff filters. A total of 5 volumes were collected as permeate while continuously recycling and adding fresh water to replace the permeate. The filtered solution was lyophilized to give a white solid product. The above procedure was then repeated starting with the white solid product to increase the loading of pendant acetal groups. The final yield was 20.3 g.

The acetal groups were removed by dissolving the solid in 400 mL of water and treating with 1.0 M HCl at pH 2.5 overnight. After neutralizing with NaOH, the solution was filtered on the Millipore Pellicon II ultrafiltration system as previously described and lyophilized to give 16.45 g of white solid. The molecular weight was determined by size exclusion chromatography to be 49 kDa. The degree of aldehyde substitution per ring was determined by NMR of the hydrolized sample to be 0.37. In the NMR method, the integrals for two ranges of peaks are determined, specifically, â€”O₂CHx- at about 6.2 parts per million (ppm) to about 4.15 ppm (minus the HOD peak) and â€”OCHx- at about 4.15 ppm to about 2.8 ppm (minus any methanol peak if present). The calculation of oxidation level is based on the calculated ratio (R) for these areas, specifically, R=(OCH)/(O₂CH).

Instability of the Aldehyde-Functionalized Carboxymethyldextran in Aqueous Solution:

An aqueous solution of aldehyde-functionalized carboxymethyldextran containing pendant aldehyde groups attached by an amide linkage was made by dissolving 5.1 g of the solid product obtained as described above in 15.3 g of autoclaved water. The mixture was shaken at 190 rpm in an incubator at 37Â° C. for 1 hour. The resulting solution was filtered through a 5.0 Î¼m membrane and two 5 mL samples of the solution were placed in 55Â° C. incubator. After 19 hours both samples had formed amber gels which exhibited no flow.