RELATED APPLICATIONS

The present application is a divisional application of U.S. patent application Ser. No. 11/855,036, entitled SPIN-ON PROTECTIVE COATINGS FOR WET-ETCH PROCESSING OF MICROELECTRONIC SUBSTRATES, filed Sep. 13, 2007, incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention is concerned with new protective coatings (primer layer, first protective coating, and optional second protective coating) and methods of using those coatings in the manufacture of microelectronic devices such as those used in microelectromechanical systems (MEMS).

2. Description of the Prior Art

Etchants used for deep etching may vary depending upon the etch selectivity requirements for the devices to be fabricated. Typical alkaline or basic etchants include those selected from the group consisting of KOH, TMAH, and NaOH. These etchants are typically provided in 10-45% solutions, and more typically about 30%. Basic etchants may contain amines such as ethylene diamine, ethanolamine, and/or water-miscible lower alcohols such as isopropanol to modulate the etching behavior of the solution. Bulk silicon etching is typically performed at temperatures in the range of 40Â° to 120Â° C. and most typically at 60Â° to 90Â° C. The etching times range from 1 to 24 hours and most typically are in the range of 5 to 15 hours.

Acidic etchants include aqueous solutions of hydrofluoric acid (HF), including concentrated (49% to 50%) HF, aqueous dilutions of the same, and buffered oxide etchants comprising aqueous mixtures of HF and ammonium fluoride. HF etchants are used primarily for etching silicon dioxide. Mixed acid etchants typically comprise mixtures of 70% nitric acid (HNO₃). 49% HF, and a diluent acid (e.g., 85% phosphoric acid (H₃PO₄) or 100% acetic acid) and are used primarily for bulk silicon etching. Common component ratios by volume for the mixtures are, for example,

HNO₃/HF/H₃PO₄=7:1:7 or 3:1:4.

Etching times for bulk silicon in these acid mixtures are typically in the range of 5 to 30 minutes and in some cases as long as 120 minutes at room temperature.

It is common in silicon etching processes to utilize a thin (100- to 300-nm) silicon nitride or silicon dioxide coating on the silicon substrate as a mask for patterned etching or as a passivating layer to enclose active circuitry. Therefore, the protective coating system described here is commonly applied onto Si₃N₄or SiO₂, which means good adhesion to these substrates is critical for obtaining acceptable protection.

In the prior art, etch protective coatings or masks for MEMS fabrication processes have been selected primarily by using a trial-and-error method because there are no general-purpose protective coatings on the market. The etch selectivity of the etchants to various materials is often used as a guide for MEMS process engineers. With a much lower etch rate than silicon, films of silicon nitride have been used as a protective layer or hardmask during KOH or TMAH bulk silicon etching. Silicon dioxide has a higher etch rate than silicon nitride. Therefore, it is only used as a protective/mask layer for very short etches. Gold (Au), chromium (Cr), and boron (B) have also been reportedly used in some situations. Non-patterned hard-baked photoresists have been used as masks, but they are readily etched in alkaline solutions. Polymethyl methacrylate was also evaluated as an etch mask for KOH. However, because of saponification of the ester group, the masking time of this polymer was found to decrease sharply from 165 minutes at 60Â° C. to 15 minutes at 90Â° C. Black wax (ApiezonÂ® W, available from Scientific Instrument Services, Inc., New Jersey) was also used as a protective coating in a 30% by weight KOH etch process (70Â° C.). After wet etching, the wax was removed using trichloroethylene.

Organic polymers are ideal candidates for protective coatings. The IC and MEMS industries have been using polymeric coating materials as photoresists, anti-reflective coatings, and planarization layers for many years. These materials are conveniently applied as thin films by the spin-on method and then baked or UV-cured to achieve the final coating form. One important requirement for the polymer is that it be highly soluble at room temperature in an environmentally friendly solvent. Because of the lack of a proper solvent, semicrystalline polyolefins such as polypropylene and polyethylene, as well as semicrystalline fluoropolymers such as TeflonÂ®, which are known to have excellent corrosion resistance to strong acids and strong bases, cannot be formulated into spin-coated compositions for protective coating applications. At the same time, many common thermoplastic polymers such as polystyrene, poly(cyclic olefins), polymethyl methacrylate, polydimethylsiloxanes, polyimides, polysulfones, and various photoresist polymers (e.g., polyhydroxystyrene and novolac resins) fail to survive many common, harsh deep-etching processes because of their susceptibility and permeability to the etchants, poor adhesion to the substrate, tendency to form coating defects, or lack of solubility in solvents accepted in the microelectronics industry.

SUMMARY OF THE INVENTION

The present invention is broadly concerned with a composition useful as a protective layer. The composition comprises a first polymer and a compatible compound dissolved or dispersed in a solvent system. The preferred first polymer is a styrene-acrylonitrile copolymer. While the compatible compound is preferably selected from the group consisting of: monomers, oligomers, and polymers comprising epoxy groups; poly(styrene-co-allyl alcohol); and mixtures thereof. The composition is substantially free of photoacid generators and other agents capable of initiating polymerization or crosslinking, and thus non-photosensitive. The present invention is also concerned with microelectronic structures including these compositions in both the flowable and hardened (i.e., after final bake) form, as well as methods of using these structures to form microelectronic devices.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a photograph showing a silicon nitride wafer coated with the inventive protective coating and after KOH etching.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention overcomes these problems by providing spin-applied, polymer coating systems which protect device features from corrosion and other forms of attack during deep-etching processes which utilize concentrated aqueous acids and bases. Furthermore, these coating systems can be easily removed at the end of the processes.

First Protective Layer

The first protective layer is formed from a composition comprising a first polymer and a compatible compound dispersed or dissolved in a solvent system. The first polymer is preferably a copolymer comprising recurring styrene monomers and acrylonitrile monomers.

Preferred styrene monomers have the formula

[Image Omitted]

Preferred acrylonitrile monomers have the formula

[Image Omitted]

In each of the above formulas (I) and (II):

- each Râ€² is individually selected from the group consisting of hydrogen and C₁-C₈(and preferably C₁-C₄) alkyls; and
- each R²is individually selected from the group consisting of hydrogen, C₁-C₈(and preferably C₁-C₄) alkyls, and C₁-C₈(and preferably C₁-C₄) alkoxys.

The first polymer preferably comprises from about 50% to about 90% by weight of monomer (I), more preferably from about 60% to about 80% by weight of monomer (I), and even more preferably from about 70% to about 75% by weight of monomer (I). The first polymer preferably comprises from about 10% to about 50% by weight of monomer (II), more preferably from about 20% to about 40% by weight of monomer (II), and even more preferably from about 25% to about 30% by weight of monomer (II). Each of the above percentages by weight is based upon the total weight of the first polymer taken as 100% by weight.

It is preferred that the first polymer have a weight average molecular weight of from about 10,000 Daltons to about 80,000 Daltons, preferably from about 20,000 Daltons to about 60,000 Daltons, and even more preferably from about 30,000 Daltons to about 50,000 Daltons.

Monomers other than monomers (I) and (II) can also be present in the first polymer, if desired. When other monomers are present, the combined weight of monomers (I) and (II) in the polymer is preferably at least about 60% by weight, and more preferably from about 70% to about 90% by weight, based upon the total weight of the first polymer taken as 100% by weight. Examples of suitable other monomers include those having functional groups that can react with groups in the primer layer for achieving chemical bonding between the two layers. These monomers may have, by way of example, haloalkyl (e.g., benzyl chloride, 2-chloroethyl methacrylate), ester (methacrylates, acrylates, maleates, fumarates, isocyanates), or anhydride functional groups, which react readily with functional groups such as hydroxyl, amino, or oxiranyl groups that can be present in the primer layer.

The first polymer should be included in the first protective layer composition at a level of from about 80% to about 98% by weight, and preferably from about 85% to about 95% by weight, based upon the total weight of solids in the first protective layer composition taken as 100% by weight.

The compatible compound present in the composition along with the first polymer can be monomeric, oligomeric, or polymeric, so long as it is compatible with the first polymer to improve adhesion of the first protective layer and to avoid phase separation in the first protective layer composition. If the compound is oligomeric (i.e., 2 to 10 repeat units) or polymeric (i.e., more than 10 repeat units), it is preferred that it have a molecular weight of less than about 3,000 Daltons, and preferably less than about 2,000 Daltons. Preferred such compounds include those selected from the group consisting of monomers, oligomers, and polymers comprising epoxy groups, poly(styrene-co-allyl alcohol), and mixtures thereof.

The compatible compound should be included in the first protective layer composition at a level of from about 2% to about 20% by weight, and preferably from about 5% to about 15% by weight, based upon the total weight of solids in the first protective layer composition taken as 100% by weight.

In embodiments where epoxy groups are utilized, the compatible compound preferably comprises from about 15% to about 30% by weight epoxy groups, and more preferably from about 20% to about 25% by weight of epoxy groups. In one preferred embodiment, the compound is a polymer that comprises recurring monomers having one or more epoxy groups per monomer, and preferably, at least two epoxy groups per monomer.

Preferred polymers for use as the compatible compound in the first protective layer composition include those selected from the group consisting of epoxy phenol novolac resins (e.g., D.E.N. 431, Dow Chemical), epoxy bisphenol A/F resins (e.g., D.E.R. 353, Dow Chemical), epoxy cresol novolac resins (e.g., ECN 1299, Ciba Geigy), epoxy bisphenol A resins (e.g., EPON 825, Shell Chemical), epoxy bisphenol A novolac resins (EPON SU-8, Shell Chemical), and mixtures thereof.

When the compatible compound is a polymer including epoxy groups, monomers other than those containing epoxy groups can also be present, if desired, provided that the epoxy quantities discussed above are achieved. Examples of suitable other monomers include those discussed above with respect to the first polymer.

The solvent system utilized in the first protective layer composition should have a boiling point of from about 120Â° C. to about 200Â° C., and preferably from about 130Â° C. to about 180Â° C. The solvent system should be utilized at a level of from about 70% to about 95% by weight, and preferably from about 80% to about 90% by weight, based upon the total weight of the first protective layer composition taken as 100% by weight. Preferred solvent systems include a solvent selected from the group consisting of methyl isoamyl ketone, di(ethylene glycol) dimethyl ether, ethyl-3-ethoxypropionate, propylene glycol monomethyl ether acetate, ethyl lactate, cyclohexanone, and mixtures thereof.

While the first protective layer composition can be a cross-linkable composition, it is preferably a non-crosslinkable composition. The final first protective layer should also be non-alkaline soluble (i.e., it is substantiallyâ€”less than 0.5% by weightâ€”insoluble in an aqueous solution having a pH of greater than about 8, and preferably greater than about 10). Finally, the first protective layer is preferably non-photosensitive (i.e., a pattern cannot be defined in the layer when it is exposed to about 1 J/cm²). Thus, the composition used to form the layer will be substantially free of photoacid generators (PAGs). â€œSubstantially freeâ€ means that the compositions include less than about 0.1% by weight, preferably less than about 0.05%, and preferably about 0% by weight, based upon the total weight of the composition taken as 100% by weight. It's also substantially free of other agents capable of initiating polymerization or crosslinking, either thermally or via light exposure.

The Primer Layer

There is preferably also a primer layer utilized in the protective systems of the invention. This layer should be included between the substrate and the first protective layer. Preferred primer layers are formed from primer layer compositions including a silane dispersed or dissolved in a solvent system. Aromatic organo silanes and amino silanes are particularly preferred silanes for use in the primer layers of the invention. The most preferred silanes have the formula

[Image Omitted]

where:

[Image Omitted]

- each of i, j, and k is individually selected from the group consisting of 0 and 1, and if one of i and j is 1, then the other of i and j is 0;
  - each R³is individually selected from the group consisting of hydrogen, the halogens, C₁-C₈(preferably C₁-C₄) alkyls, C₁-C₈(preferably C₁-C₄) alkoxys, C₁-C₈(preferably C₁-C₄) haloalkyls, aminos, and C₁-C₈(preferably C₁-C₄) alkylaminos;
- each R⁴is individually selected from the group consisting of C₁-C₈(preferably C₁-C₄) aliphatic groups;
- each X is individually selected from the group consisting of halogens, hydroxyls, C₁-C₄alkoxys and C₁-C₄carboxyls;
- Y is selected from the group consisting of oxygen and sulfur;
- Z is selected from the group consisting of nitrogen and phosphorus; and
- each d is individually selected from the group consisting of 0 and 1.

Particularly preferred silanes include phenylsilanes such as phenyltrimethoxysilane, phenyltrichlorosilane, phenyltriethoxysilane, phenyltriacetoxysilane, and diphenylsilanes such as diphenyldimethoxysilane, diphenyldichlorosilane, and diphenylsilanediol. The most preferred silanes include 2-phenylethyltrialkoxysilane, p/m-chlorophenyltrimethoxysilane, p/m-bromophenyltrimethoxysilane, (p/m-chloromethyl)phenyltrimethoxysilane, 2-(p/m-methoxy)phenylethyltrimethoxysilane, 2-(p/-chloromethyl)phenylethyltrimethoxysilane, 3,4-dichlorophenyltrichlorosilane, 3-phenoxypropyltrichlorosilane, 3-(N-phenylamino)propyltrimethoxysilane, and 2-(diphenylphosphino)ethyltriethoxysilane.

An effective primer layer composition according to the invention is a mixture of diphenyldialkoxysilane (e.g., diphenyldimethoxysi lane) and phenyltrialkoxysilane, (e.g., phenyltrimethoxysilane) or, even more preferably, a mixture of diphenylsilanediol and phenyltrimethoxysilane in a solution of 1-methoxy-2-propanol or 1-propoxy-2-propanol with from about 5-10% by weight water. A particularly effective primer layer composition for first protective layers comprising a poly(styrene-co-acrylonitrile) polymer is an alcohol and water solution containing from about 0.1-1.0% (preferably from about 0.25-0.5%) by weight diphenylsilanediol and from about 0.1-1.0% (preferably from about 0.25-0.5%) by weight of phenyltrimethoxysilane. Upon heating, diphenylsilanediol and phenylsilanetriol (the hydrolysis product of phenyltrimethoxysilane) condense to form siloxane bonds and establish a three-dimensional silicone coating layer on the substrate.

Another preferred silane has the formula

[Image Omitted]

Silanes having this structure are not only compatible with styrene-containing copolymers, but they are also reactive with ester, benzyl chloride, and/or epoxy groups that may be present in the first protective layer, and they are excellent adhesion promoters. One particularly preferred silane within the scope of this formula is

[Image Omitted]

This silane is 3-[N-phenylamino]propyltrimethoxysilane, and it is commercially available from Lancaster Synthesis and Gelest Corporation. Yet another preferred silane is 3-aminopropyltriethoxysilane.

The silane should be included in the primer layer composition at a level of from about 0.01% to about 0.5% by weight, preferably from about 0.01% to about 0.25% by weight, and even more preferably from about 0.01% to about 0.1% by weight, based upon the total weight of the primer layer composition taken as 100% by weight.

The solvent system utilized in the primer layer composition should have a boiling point of from about 100-220Â° C., and preferably from about 140-180Â° C. The solvent system should be utilized at a level of from about 80-99.9% by weight, and preferably from about 85-99% by weight, based upon the total weight of the primer layer composition taken as 100% by weight. Preferred solvent systems include a solvent selected from the group consisting of methanol, ethanol, isopropanol, butanol, 1-methoxy-2-propanol, ethylene glycol monomethyl ether, and 1-propoxy-2-propanol, and mixtures thereof. In one preferred embodiment, water is included in the solvent system at a level of from about 0.5-15% by weight, and preferably from about 0.5-10% by weight, based upon the total weight of the primer layer composition taken as 100% by weight.

The primer layer composition can optionally include low levels (e.g., from about 0.01-0.10% by weight) of a catalyst. Suitable catalysts include any inorganic or organic acid (e.g., hydrochloric acid, sulfuric acid, phosphoric acid, acetic acid) or an inorganic or organic base (e.g., potassium hydroxide, TMAH, ammonia, amines).

In a preferred embodiment, the protective system of the invention further includes a second protective layer on top of the first protective layer to provide further protection against concentrated aqueous acids such as hydrofluoric acid, nitric acid, phosphoric acid, acetic acid, and mixtures of the foregoing. This embodiment is useful in situations where a acid etching is utilized. Preferred second protective layers are formed from second protective layer compositions comprising a linear, slightly branched, or cyclic halogenated polymer dissolved or dispersed in a solvent system. Furthermore, these halogenated polymers should comprise high levels of halogen atoms (at least about 50% by weight halogen atoms, and preferably at least about 60% by weight halogen atoms). The most preferred halogenated polymers are chlorinated polymers such as those comprising recurring monomers having the formula

[Image Omitted]

Specific examples of preferred halogenated polymers include those selected from the group consisting of poly(vinyl chloride), polyvinylidene chloride, poly(vinylidene dichloride)-co-poly(vinyl chloride), chlorinated ethylene, chlorinated propylene, and mixtures thereof. Halogenated chlorinated rubber is also very effective.

The halogenated polymer should be included in the second protective layer composition at a level of from about 8-30% by weight, and preferably from about 10-20% by weight, based upon the total weight of the second protective layer composition taken as 100% by weight. The solvent system utilized in the second protective layer composition should have a boiling point of from about 100-220Â° C., and preferably from about 140-180Â° C. The solvent system should be utilized at a level of from about 70-92% by weight, and preferably from about 80-90% by weight, based upon the total weight of the second protective layer composition taken as 100% by weight.

Examples

The following examples set forth preferred methods in accordance with the invention. It is to be understood, however, that these examples are provided by way of illustration and nothing therein should be taken as a limitation upon the overall scope of the invention.

Application Processes

Prior to applying the primer layer, it is preferable to prepare the substrate by exposing it to brief (from about 15-60 seconds) oxygen plasma etching to clean and/or chemically activate the substrate surface to improve bonding by the primer layer. Plasma bombardment with heavy ions such as argon can also be beneficial for improving bonding. Such processes are especially effective for improving the bonding of the protective coating system to silicon nitride.

Preferred substrates for use in this process include those selected from the group consisting of Si substrates, SiO₂substrates, Si₃N₄substrates, SiO₂on silicon substrates, Si₃N₄on silicon substrates, glass substrates, quartz substrates, ceramic substrates, semiconductor substrates, and metal substrates.

The organosilane solution that makes up the primer layer is spin-applied onto the substrate at about 500-5,000 rpm, and preferably from about 1,000-2,000 rpm, for about 30-90 seconds. It is then baked at greater than about 100Â° C. for about 60-90 seconds to condense the organosilane molecules into a continuous film that is bonded to surface hydroxyl groups present on many microelectronic substrates. A particularly preferred baking temperature is at least about 200Â° C., and more preferably from about 200Â° C. to about 225Â° C., for about 60 to about 90 seconds. It is preferred that the primer layer have an average thickness (as measured by an ellipsometer over 5 different points) of less than about 10 nm and more preferably from about 2-8 nm.

For the first protective layer, the polymer, compatible compound, and any other ingredients are dissolved in a suitable solvent at a concentration of from about 5-25% by weight and spin coated onto the substrate at about 500-5,000 rpm, and preferably from about 1,000-3,000 rpm, for about 30-90 seconds. It is soft-baked at a temperature of from about 80-130Â° C. for about 60-120 seconds to dry the coating and then is subjected to a final bake at a temperature of from about 130-225Â° C. for about 60-90 seconds to densify the first protective layer and bond it thinly to the primer layer. The preferred process for baking styrene-acrylonitrile coatings is to bake them at a temperature of about 130Â° C. for about 120 seconds and then at a temperature of about 200Â° C. for about 60 seconds. During final bake in the embodiments where the compatible compound includes epoxy groups, the epoxy groups will react with the amine groups of the primer layer to form a bond such as:

[Image Omitted]

The polymer solids level and spinning conditions are adjusted typically to achieve a coating thickness after final bake of from about 1-10 Î¼m, and preferably from about 2-8 Î¼m, depending upon the degree of coverage required over device topography on the substrate.

The second protective layer (if utilized) is applied from a solvent solution in a manner similar to that described above with respect to the first protective layer. The solvents used to apply the second protective layer should be selected to minimize detrimental interaction with the first protective layer. It is preferred that the second protective layer have an average thickness (as measured by an ellipsometer over 5 different points) of from about 2 Î¼m to about 10 Î¼m, and more preferably from about 3 Î¼m to about 5 Î¼m. It will be appreciated that at these low thickness, the second protective layer is acting as a chemical barrier rather than purely as a physical barrier.

The structure coated with the protective system of the invention can now be subjected to typical processing steps, including wet etching processes. Wet etching involves contacting the structure with an etchant. In some applications, the structure is subjected to two etching stepsâ€”one with a basic etchant, and one with an acidic etchant. In other applications, the structure would only be contacted with one of basic or acidic etchants. Contact typically involves full immersion or dipping of the structure into the etchant bath, but it an also be accomplished by spraying, puddling, or spin-applying.

Typical alkaline or basic etchants include those selected from the group consisting of KOH, TMAH, and NaOH. These etchants are typically provided in 10-45% solutions, and more typically about 30%. Structure contact with basic etchants can be carried out for time periods of from about 5 minutes to about 24 hours, and more typically from about 4 hours to about 6 hours and at temperatures of from about 60Â° C. to about 100Â° C., and more typically from about 80Â° C. to about 90Â° C.

Typical acidic etchants include those selected from the group consisting of HF (typically 49%), concentrated H₃PO₄, and HF/H₃PO₄/HNO₃. Contact with acidic etchants can be carried out for time periods of from about 1 minute to about 30 minutes, and more typically from about 3 minutes to about 7 minutes at ambient temperatures.

It is preferred that the protective layer(s) or coating(s) be removed after the wet etching processes have been completed. A particularly preferred technique is stripping the coating(s) with solvents commonly used in microelectronic processing such as acetone, propylene glycol methyl ether acetate, ethyl lactate, or a commercially available, fluoride-containing cleaner. In this technique, the coated substrate is sprayed with, or immersed in, the solvent until the coating layer has fully dissolved. The substrate is then rinsed with fresh solvent until clean. The protective coating system described here is easily removed by dissolving the thermoplastic layer (the first coating layer) in a solvent such as acetone. The second coating layer, if present, is either dissolved at the same time or is lifted as the first layer dissolves.

Practicing the present invention will result in a protective layer system which suffers little or no lifting during acidic or basic etching processes. That is, the layer systems will exhibit less than about 2 mm, preferably less than about 1 mm, and more preferably less about 0 mm of lifting when subjected to: (1) about 2 hours (and even 8 hours) etching in an approximately 30-35% by weight aqueous KOH solution having a temperature of about 83-87Â° C.; or (2) about 30 minutes in an approximately 49% by weight aqueous HF solution at 70-75Â° C. Lifting is determined by measuring from the outside edge of the substrate to the furthest point on the layer system where the layer system is still attached to the substrate.

Furthermore, the inventive protective layer system will experience very little or no etchant penetration during etching processes. The inventive protective systems will have less than about 0.1 pinholes per cm²of substrate, and preferably less than about 0.05 pinholes per cm²of substrate, when observed under a microscope at 10Ã— magnification after: (1) about 2 hours in an approximately 30-35% by weight aqueous KOH solution having a temperature of about 83-87Â° C.; or (2) about 30 minutes in an approximately 49% by weight aqueous HF solution at 70-75Â° C.

Example 1Preparation of Primers I-IV

Primer I was prepared by dissolving 0.5 g of diphenyldichlorosilane in 99.5 g of xylene followed by filtering with a 0.2/0.45-Î¼m polypropylene filter.

Primer II was prepared by dissolving 0.5 g of diphenyldimethoxysilane in 90 g of isopropanol and 10 g of water followed by filtering with a 0.2/0.45-Î¼m polypropylene filter.

Primer III was prepared by dissolving 0.5 g of diphenylsilanediol and 0.5 g of phenyltrimethoxysilane in 90 g of propylene glycol monomethyl ether (PGME) and 10 g of water. The primer was aged for at least 24 hours so that the silanes were partially hydrolyzed and condensed. The primer was then filtered using a 0.2/0.45-Î¼m polypropylene filter.

Primer IV was prepared by dissolving 1.0 g of diphenylsilanediol and 1.0 g of phenyltrimethoxysilane in 88 g of PGME and 10 g of water. The primer was similarly aged and then filtered using a 0.2/0.45-Î¼m polypropylene filter.

Example 2Preparation of Primer V (Comparative Primer)

In a manner similar to Example 1, Primer V was prepared by adding 1.0 g of 3-aminopropyltriethoxysilane (obtained from Gelest, Inc, Morrisville, Pa.) into 95 g of PGME and 5 g of water. The primer was aged for at least 24 hours so that the silane was partially hydrolyzed and condensed. The primer was then filtered using a 0.2/0.45-Î¼m polypropylene filter.

Example 3Preparation of Primer VI

A diethyl fumarate-modified, amino functional silane was prepared by mixing one mole of N-(3-trimethoxysilyl)-propylethylenediamine with one mole of diethyl fumarate, followed by stirring at room temperature for 48 hours. The mixing process was exothermic, indicating the immediate reaction of the two components.

Primer VI was prepared by dissolving 1 g of the above modified silane into 90 g of PGME and 10 g of water. The mixture was aged for 24 to 48 hours at room temperature and then filtered using a 0.2/0.45-Î¼m polypropylene filter.

Example 4Preparation of Primer VII

Primer VII is an adhesion promoter based on 3-(N-phenyl)aminopropyltrimethoxysilane, which is very effective for polystyrene-co-acrylonitrile polymers, especially for coatings containing reactive groups such epoxy, ester, or chloromethyl (benzyl chloride) groups. Primer VII was prepared by dissolving 0.5 g of the aromatic amino silane in 90 g of PGME and 10 g of water.

The mixture was aged in a manner similar to the previous examples and filtered using a 0.2/0.45-Î¼m polypropylene filter.

Example 5Preparation of Coating Compositions A and B from a Copolymer of Styrene and Acrylonitrile

Commercially available styrene-acrylonitrile resins were used directly for coating formulations. Composition A was formulated by dissolving 12 g of poly(styrene-co-acrylonitrile) (SAN30: M_w=185,000, 30 wt % acrylonitrile, available from Aldrich) in 44 g of methyl isoamyl ketone (MIAK) and 44 g of di(ethylene glycol) dimethyl ether. Composition B was formulated by dissolving 18 g of SAN30 in 41 g of MIAK and 41 g of di(ethylene glycol) dimethyl ether. Both coating compositions were filtered twice using a 0.2/0.45-Î¼m polypropylene filter. Alternatively, a mixed solvent of propylene glycol monomethyl ether acetate (PGMEA) and ethyl lactate in a weight ratio of 9:1 was also used as the solvent. The change of solvent did not noticeably change the coating quality or adhesion.

Example 6Preparation of a Terpolymer and Formulation of Coating Composition C from the Terpolymer

In this procedure, a terpolymer of styrene, acrylonitrile, and glycidyl methacrylate was prepared. Styrene and glycidyl methacrylate were purified by passing through an aluminum oxide column. Acrylonitrile was purified by washing sequentially with a 5% by weight H₂SO₄solution, a 5% by weight NaOH solution, and water to remove inhibitors and amine impurities that might cause crosslinking of the polymer. It was dried over anhydrous calcium chloride and then 4-â„« molecular sieves.

A 500-ml two-neck flask containing a 1-inch magnetic stirring bar was charged with 100 g of cyclohexanone (or PGMEA) and a mixture of purified monomers including 35 g of styrene, 10 g of acrylonitrile, and 5 g of glycidyl methacrylate. Next, 300 mg of 2,2â€²-azobisisobutylnitrile (AIBN) (or benzoyl peroxide) were added to the mixture as an initiator. The side neck of the flask was capped with a rubber septum, and the main neck of the flask was connected to a water-cooled condenser with the top end of the condenser linked to a bubbler containing mineral oil. After fixing the entire glass assembly to a metal stand, the system was purged with nitrogen to remove oxygen through the side neck of the flask through a needle. The flask was heated using a hotplate at 80Â° C. for about 8 hours to polymerize the monomer mixture. During the reaction, the reactor was slowly purged with nitrogen to prevent oxygen from entering. The polymer obtained was then precipitated in a mixture of isopropanol or ethanol containing 20% by weight water in a fast-stirring blender. The polymer was recovered by filtration and vacuum-dried to remove any solvent or monomer residues. The yield or conversion of the reaction was 80% to 85%. Gel permeation chromatography (GPC) indicated the weight average molecular weight of the polymer was about 200,000 g/mole (relative to polystyrene standard).

Composition C (12.5% solids) was prepared by dissolving 12.5 g of the recovered dry polymers in 94.5 g of PGMEA and 10.5 g of ethyl lactate. It was filtered twice using 0.2/0.45-Î¼m polypropylene filters.

Example 7Preparation of a Terpolymer and Formulation of a Coating Composition D from the Terpolymer

A terpolymer of styrene, acrylonitrile, and butyl acrylate was prepared in this example. The styrene and acrylonitrile were purified according to the same method described in Example 6. Butyl acrylate was purified by passing through a column of aluminum oxide.

A mixture of purified monomers including 30 g of styrene, 15 g of acrylonitrile, and 5 g of butyl acrylate was polymerized in PGMEA, and the polymer was recovered using the same method described in Example 3. The conversion or the yield of the polymerization for this system was around 80%. GPC molecular weight (M_w) for this polymer was around 99,600 g/mole (relative to polystyrene standard).

Composition D (15% solids) was prepared by dissolving 15 g of the recovered dry polymer in 76.5 g of PGMEA and 8.5 g of ethyl lactate. It was filtered twice using 0.2/0.45-Î¼m polypropylene filters.

Example 8Preparation of a Quaterpolymer and Formulation of a Coating Composition E from the Polymer

In this procedure, a quaterpolymer of styrene, acrylonitrile, butyl acrylate, and glycidyl methacrylate was prepared. To accomplish this, styrene, butyl acrylate, and glycidyl methacrylate were purified by passing through a column of aluminum oxide. Acrylonitrile was purified by washing with 5 wt % H₂SO₄, 5 wt % NaOH, and deionized water sequentially followed then dried over anhydrous calcium chloride and 4 â„« molecular sieves.

A mixture of purified monomers including 25 g of styrene, 15 g of acrylonitrile, 5 g of butyl acrylate, and 5 g of glycidyl methacrylate was polymerized and recovered according to the methods described in Example 6. The conversion or the yield of the polymerization for this system was around 80%. GPC molecular weight (Mw) for this polymer was around 124,600 g/mole (relative to polystyrene standard). Composition E (15 wt % solids) was prepared by dissolving 15 g of the recovered dry polymers in 76.5 g of PGMEA and 8.5 g of ethyl lactate. It was filtered twice using 0.2/0.45-Î¼m polypropylene filters.

Example 9Preparation of Coating Composition F

Composition F was prepared by combining in solution 13.5 g of a copolymer of styrene and acrylonitrile (M_w=165,000, 25% acrylonitrile) and 1.5 g of polymethyl methacrylate (PMMA, M_w=120,000). The coating composition was filtered using a 0.2/0.45-Î¼m polypropylene filter.

Example 10Preparation of Coating Composition G

Composition G was prepared by dissolving 12 g of chlorinated rubber (CLORTEXÂ® 20 from American Tartaric Corporation) in 88 g of PGMEA, followed by filtering with a 0.2/0.45-Î¼m polypropylene filter.

Example 11Preparation of Coating Composition H

Composition II was prepared by dissolving 10 g of chlorinated PVC (TempRite 674Ã—571 from Noven, Inc.) in 90 g of cyclohexanone, followed by filtering with a 0.2/0.45-Î¼m polypropylene filter.

Example 12Procedure for Applying Primers I-VII and Coating Compositions A-G

A silicon, silicon nitride, or silicon nitride wafer with aluminum deposited at the central area was mounted on a spin-coater and centered properly. Under conditions of a spin acceleration rate of 20,000 rpm², a spin speed of 2,500 rpm, and a duration of 90 seconds, the wafer was first washed with acetone for about 20 seconds to remove any possible contaminants, and then an aliquot of 5 to 10 ml of the primer was dispensed onto the wafer. After spinning for about another 40 to 60 seconds, a uniform primer layer was obtained on top of the wafer. Subsequently, the primed wafer was baked on a hotplate at 100-130Â° C. for 1 minute to promote chemical bonding between the substrate and the primer as well as partial vulcanization of the primer. After the primed wafer cooled to room temperature, a layer of the particular coating composition (e.g., Composition A) was spin-applied and then baked on a hotplate sequentially at 100Â° C. for 2 minutes, 130Â° C. for 1 minute, and 205Â° C. for 1 minute.

Example 13KOH Deep-Etch Tests for Various Coating/Primer Combinations

The test equipment included a glass etchant tanker containing about 4000 ml of a 30% to 35% by weight aqueous KOH solution in which a TEFLONÂ® wafer boat holding the test substrates in a horizontal orientation was fully immersed. The etchant solution was heated using an internal heating unit or outer heating unit such as a hotplate, and the temperature of the etchant was controlled to 85Â° C.Â±1.5Â° C. In general, 4-inch wafers of silicon, silicon nitride, or silicon nitride with aluminum deposited at the central circular area (approximately 2 inches in diameter) were used for the test. For silicon wafers, the test was only conducted for 2 to 4 hours because of the high etch rate of silicon in KOH. For silicon nitride wafers, the test was extended to at least 8 hours. During the etch test, the solution was bubbled vigorously with nitrogen to provide agitation. After the etching period, wafer samples were removed, rinsed, dried, and then inspected for pinholes and edge lift or detachment of the coating layer(s).

Because aluminum is very reactive toward KOH solution, any penetration of the coating (either by pinholes or poor KOH resistance of the coating) was indicated by disappearance of aluminum at the area. The distance from the edge of the wafer to the front line of coating detachment in the radial direction was used as a measure of the adhesion quality of the primer/coating combination. Results are shown in Table 1.

TABLE 1KOH deep-etch test results for various coating/primer combinations.CoatingProtective CoatingResults MM ofExp #SubstrateO₂Plasma EtchPrimerCompositionBake ProcessLiftingComments1NitrideNoneNoneA100Â° C./120 sec4-30 mmâ€‚Control130Â° C./120 sec205Â° C./60 sec2Nitride + Al padNoneNoneA100Â° C./120 sec4-25 mmâ€‚Control130Â° C./120 sec205Â° C./60 sec3SiliconNoneNoneA100Â° C./120 secCompletelyControl130Â° C./120 seclifted205Â° C./60 sec4NitrideYesIIIA100Â° C./120 sec2-3 mm130Â° C./120 sec205Â° C./60 sec5Nitride + Al padYesIIIA100Â° C./120 sec1-3 mm130Â° C./120 sec205Â° C./60 sec6SiliconNoneIIIA100Â° C./120 sec5-30 mmâ€‚Edge lift not130Â° C./120 secuniform205Â° C./60 sec7NitrideYesIIIB100Â° C./120 sec1-3 mm130Â° C./120 sec205Â° C./60 sec8Nitride + Al padYesIIIB100Â° C./120 sec1-3 mm130Â° C./120 sec205Â° C./60 sec9SiliconNoneIIIB100Â° C./120 sec3-25 mmâ€‚Edge lift not130Â° C./120 secuniform205Â° C./60 sec10NitrideYesIVB100Â° C./120 sec1-2 mm130Â° C./120 sec205Â° C./60 sec11Nitride + Al padYesIVB100Â° C./120 sec1-3 mm130Â° C./120 sec205Â° C./60 sec12SiliconNoneIVB100Â° C./120 sec10-40 mmâ€ƒEdge lift not130Â° C./120 secuniform205Â° C./60 sec13NitrideYesIVB100Â° C./120 sec1-3 mm130Â° C./120 sec205Â° C./60 sec14Nitride + Al padYesIVB100Â° C./120 sec2-3 mm130Â° C./120 sec205Â° C./60 sec15SiliconNoneIVB100Â° C./120 sec8-26 mmâ€‚Edge lift not130Â° C./120 secuniform205Â° C./60 sec16NitrideYesVA100Â° C./120 sec1-5 mmEdge lift not130Â° C./120 secuniform250Â° C./60 sec17NitrideYesVA100Â° C./120 sec3-7 mmEdge lift not130Â° C./120 secuniform250Â° C./60 sec18NitrideNoneVIIB100Â° C./60 sec0205Â° C./60 sec19Nitride + Al padNoneVIIB100Â° C./60 sec2-4 mm205Â° C./60 sec20SiliconNoneVIIB100Â° C./60 sec0205Â° C./60 sec21NitrideNoneVIC100Â° C./60 sec4-6 mm205Â° C./60 sec22NitrideNoneVIC100Â° C./60 sec3-4 mm205Â° C./60 sec23NitrideNoneVIIC100Â° C./60 sec0205Â° C./60 sec24Nitride + Al padNoneVIIC100Â° C./60 sec0205Â° C./60 sec25SiliconNoneVIIC100Â° C./60 sec0205Â° C./60 sec26NitrideNoneVIID100Â° C./60 sec1-2 mm205Â° C./60 sec27Nitride + Al padNoneVIID100Â° C./60 sec1-2 mm205Â° C./60 sec28SiliconNoneVIID100Â° C./60 sec0205Â° C./60 sec29NitrideNoneVIIE100Â° C./60 sec0205Â° C./60 sec30Nitride + Al padNoneVIIE100Â° C./60 sec^â€ƒ1 mm205Â° C./60 sec31SiliconNoneVIIE100Â° C./60 sec0205Â° C./60 sec32NitrideNoneVIIF100Â° C./60 sec1-3 mm205Â° C./60 sec33Nitride + Al padNoneVIIF100Â° C./60 sec1-2 mm205Â° C./60 sec34SiliconNoneVIIF100Â° C./60 sec1-2 mm205Â° C./60 sec

Example 14Resistance of Coating Combinations to Concentrated Hydrofluoric Acid

The test described in this example provided a means for rating the resistance of coating combinations to hydrofluoric acid and the time for the hydrofluoric acid to penetrate the 1.5-micron thick coating layers.

At room temperature, a drop (approximately 0.2 ml) of 49% HF was placed in the center of a silicon wafer coated centrally with aluminum and another drop (approximately 0.2 ml) was placed on the area outside of the aluminum deposit. The wafers were then carefully observed for penetration of hydrofluoric acid through the coating, as indicated by the formation of hydrogen bubbles resulting from the aluminum reacting with hydrofluoric acid. When a silicon nitride-coated wafer was used as the test substrate, penetration of the coating by hydrofluoric acid was observed as etching of the gold-colored silicon nitride layer, which then exposed the gray-colored silicon substrate. The results are shown in Table 2.

TABLE 2Resistance of coating or coating combination to concentrated hydrofluoric acid.ProtectiveBake ProcessProtectiveBake ProcessExp #SubstratePrimerCoating 1Coating 1Coating 2Coating 2Results1Silicon NitrideNoneA130Â° C./60 secNoneN/ACoating dissolved or destroyed205Â° C./5 min2Silicon NitrideNoneA130Â° C./60 secG130Â° C./60 secNo penetration observed after 30 minutes,205Â° C./5 min205Â° C./5 minsubstrate darkened3Silicon NitrideVG130Â° C./60 secNoneN/ANo penetration observed after 30 minutes,205Â° C./5 minsubstrate darkened4Silicon NitrideIG130Â° C./60 secNoneN/ANo penetration observed after 30 minutes,205Â° C./5 minsubstrate darkened5Silicon NitrideIIG130Â° C./60 secNoneN/ANo penetration observed after 30 minutes,205Â° C./5 minsubstrate darkened6Silicon Nitride +VIH100Â° C./120 secNoneN/ANo penetration observed after 30 minutes.Al Pad130Â° C./120 sec205Â° C./60 sec

Example 15A Simulated Test for Resistance of Coating Combination to Mixed Acid

This test was conducted in a mechanical batch etching system using a mixture of nitric acid (70% by weight), hydrofluoric acid (49% by weight), and phosphoric acid (85% by weight) (HNO₃:HF:H₃PO₄=3:1:4) as an etchant. The silicon wafers were contained in a wafer carrier boat, which was then placed in the tool for exposure to the etchant. The wafers were tumbled during the entire length of the etching process (approximately 30 minutes). Once removed, the wafers were rinsed and evaluated for coating performance. The test was conducted at room temperature, with a constant fresh supply of etching solution applied to the substrates. Results are shown in Table 3.

TABLE 3Resistance of primer/coating combination to mixed acid etchants.ProtectiveBake ProcessProtectiveBake ProcessExp #SubstratePrimerCoating 1Coating 1Coating 2Coating 2Results1SiliconVG130Â° C./60 secNoneN/AMaterials lifted off substrate205Â° C./5 min2SiliconVA130Â° C./60 secNoneN/ACompletely dissolved after 10205Â° C./5 minminutes exposure3SiliconNoneA130Â° C./60 secNoneN/ACompletely dissolved after 10205Â° C./5 minminutes exposure4SiliconVA130Â° C./60 secG130Â° C./60 secMaterial lifted off of substrate205Â° C./5 min205Â° C./5 min5SiliconNoneA130Â° C./60 secG130Â° C./60 secNo observable lifting or205Â° C./5 min205Â° C./5 minpenetration6Silicon DioxideVG130Â° C./60 secNoneN/AMaterial lifted off of substrate205Â° C./5 min7Silicon DioxideNoneA130Â° C./60 secG130Â° C./60 secMaterial lifted off of substrate205Â° C./5 min205Â° C./5 min8SiliconNoneA130Â° C./60 secG130Â° C./60 secMinimal amount of lifting from250Â° C./5 min250Â° C./5 minthe edge of the wafer observedafter 10 minutes9SiliconVG130Â° C./60 secNoneN/ARandom penetration of film250Â° C./5 mincausing a bubble effect.10SiliconIIG130Â° C./60 secNoneN/AFilm completely lifted after 30250Â° C./5 minminutes of exposure11SiliconIG130Â° C./60 secNoneN/A100% of film lifted after 5250Â° C./5 minminutes exposure12SiliconIIA130Â° C./60 secG130Â° C./60 secExcellent coating, no lifting250Â° C./5 min250Â° C./5 minobserved even after 30 minutesof exposure13SiliconIA130Â° C./60 secG130Â° C./60 secExcellent coating, no lifting250Â° C./5 min250Â° C./5 minobserved even after 30 minutesof exposure

Example 16Alkaline-Resistant Coatings Comprising N-phenylaminopropyltrimethoxysilaneA. Preparation of Polymer Blend Solution

A polymer solution was made by adding 0.5 g of N-phenylaminopropyl-trimethoxysilane (obtained from Gelest, Morrisville, Pa.) to 50 g of a 25% solution of poly(styrene-co-acrylonitrile) (sold under the name of LUSTRAN, obtained from Bayer USA, Pittsburgh, Pa.) dissolved in a 1:1 mixture of MIAK and diethylene glycol dimethyl ether (â€œdiglymeâ€ ).

B. Silicon Nitride Wafer Coating

A primer solution of 0.1% N-phenylaminopropyltrimethoxy silane (obtained from Gelest) in a 90:10 mixture of PGME:deionized water was spin coated onto a 4-inch silicon nitride wafer at 1,500 rpm for 1 minute. The wafer was baked at 205Â° C. for 1 minute. The polymer blend solution described in Part A of this example was then spin coated at 200 rpm for 10 seconds followed by 1,500 rpm for 1 minute. The wafer was baked at 100Â° C. for 2 minutes, then at 130Â° C. for 2 minutes, and then at 160Â° C. for 2 minutes.

C. Silicon Wafer Coating

A primer solution of 0.1% N-phenylaminopropyltrimethoxy silane in a 90:10 mixture of PGME:deionized water was spin coated onto a 4-inch silicon wafer at 1,500 rpm for 1 minute. The wafer was baked at 205Â° C. for 1 minute. The polymer blend solution described in Part A of this example was then spin coated at 200 rpm for 10 seconds followed by 1,500 rpm for 1 minute. The wafer was baked at 100Â° C. for 2 minutes, then at 130Â° C. for 2 minutes, and then at 160Â° C. for 2 minutes.

D. Etch Testing of Silicon Nitride Wafer

The silicon nitride wafer coated in Part B of this example was etched in 30% aqueous KOH solution at 80-85Â° C. for 8 hours. After etching in KOH, the wafer was cleaned with DI water for 5 minutes and dried in air.

E. Etch Testing of Silicon Wafer

The silicon wafer coated in Part C of this example was etched in 30% aqueous KOH solution at 80-85Â° C. for 4 hours. After etching in KOH, the wafer was cleaned with DI water for 5 minutes and dried in air.

Example 17Alkaline-Resistant Coatings Comprising Poly(Styrene-co-allyl Alcohol)A. Preparation of Polymer Blend Solution

A polymer blend solution was made by dissolving 144 g of poly(styrene-co-acrylonitrile) copolymer (obtained from Bayer USA, Pittsburgh, Pa.) and 36 g of poly(styrene-co-allyl alcohol) (obtained from Sigma-Aldrich, Milwaukee, Wis.) in a mixture of 574 g of PGME (obtained from General Chemical, Parsippany, N.J.) and 246.2 grams of ethyl acetoacetate (â€œEAA,â€ obtained from Harcros, Kansas City, Kans.).

B. Silicon Nitride Wafer Coating

A primer solution of 0.1% N-phenylaminopropyltrimethoxy silane in a 90:10 mixture of PGME:deionized water was spin coated onto a 4-inch silicon nitride wafer at 1,500 rpm for 1 minute. The wafer was baked at 205Â° C. for 1 minute. The polymer blend solution described in Part A of this example was then spin coated at 200 rpm for 10 seconds followed by 1,500 rpm for 1 minute. The wafer was baked at 100Â° C. for 2 minutes, then at 130Â° C. for 2 minutes, and then at 160Â° C. for 2 minutes.

C. Silicon Wafer Coating

A primer solution of 0.1% N-phenylaminopropyltrimethoxy silane in a 90:10 mixture of PGME:deionized water was spin coated onto a 4-inch silicon wafer at 1,500 rpm for 1 minute. The wafer was baked at 205Â° C. for 1 minute. The polymer blend solution described in Part A of this example was then spin coated at 200 rpm for 10 seconds followed by 1,500 rpm for 1 minute. The wafer was baked at 100Â° C. for 2 minutes, then at 130Â° C. for 2 minutes, and then at 160Â° C. for 2 minutes.

D. Etch Testing of Silicon Nitride Wafer

The silicon nitride wafer coated in Part B of this example was etched in 30% aqueous KOH solution at 80-85Â° C. for 8 hours. After etching in KOH, the wafer was cleaned with DI water for 5 minutes and dried in air. The film exhibited 2-3 mm of edge lifting.

E. Etch Testing of Silicon Wafer

The silicon wafer coated in Part C of this example was etched in 30% aqueous KOH solution at 80-85Â° C. for 4 hours. After etching in KOH, the wafer was cleaned with DI water for 5 minutes and dried in air. The film exhibited 1-10 mm of edge lifting.

Example 18Alkaline-Resistant Coatings Comprising Poly(styrene-co-allyl Alcohol) and N-phenylaminopropyltrimethoxysilaneA. Preparation of Polymer Solution

A polymer solution was made by adding 5 g of N-phenylaminopropyl-trimethoxysilane (Gelest, Morrisville, Pa.) to 495 g of the polymer solution prepared in Part A of Example 17.

B. Silicon Nitride Wafer Coating

A primer solution of 0.1% N-phenylaminopropyltrimethoxy silane in a 90:10 mixture of PGME:deionized water was spin coated onto a 4-inch silicon nitride wafer at 1,500 rpm for 1 minute. The wafer was baked at 130Â° C. for 1 minute. The polymer blend solution prepared in Part A of this example was spin coated at 200 rpm for 10 seconds and then at 1,500 rpm for 1 minute. The wafer was baked at 100Â° C. for 2 minutes, then at 130Â° C. for 2 minutes, and then at 160Â° C. for 2 minutes.

C. Silicon Wafer Coating

A primer solution of 0.1% N-phenylaminopropyltrimethoxy silane in a 90:10 mixture of PGME:deionized water was spin coated onto a 4-inch silicon wafer at 1,500 rpm for 1 minute. The wafer was baked at 130Â° C. for 1 minute. The polymer blend solution in Part A of this example was spin coated at 200 rpm for 10 seconds followed by 1,500 rpm for 1 minute. The wafer was baked at 100Â° C. for 2 minutes, then at 130Â° C. for 2 minutes, and then at 160Â° C. for 2 minutes.

D. Etch Testing of Silicon Nitride Wafer

The silicon nitride wafer coated in Part B of this example was etched in 30% aqueous KOH solution at 80-85Â° C. for 8 hours. After etching in KOH, the wafer was cleaned with DI water for 5 minutes and dried in air. The film exhibited 1 mm of edge lifting.

E. Etch Testing of Silicon Wafer

The silicon wafer coated in Part C of this example was etched in 30% aqueous KOH solution at 80-85Â° C. for 4 hours. After etching in KOH, the wafer was cleaned with DI water for 5 minutes and dried in air. The film exhibited 1-4 mm of edge lifting.

Example 19Alkaline-resistant Coatings Comprising Epoxy Cresol Novolac ResinA. Preparation of Polymer Blend Solution

A polymer blend solution was made by dissolving 20-25 g of a poly(styrene-co-acrylonitrile) copolymer and 1-5 g of an epoxy cresol novolac resin (ECN1299, obtained from Ciba Geigy, Tarrytown, N.Y.) in a mixture of 37.5 g of ethyl-3-ethoxypropionate (â€œEEP,â€ obtained from Sigma-Aldrich, Milwaukee, Wis.) and 37.5 g of MIAK. The poly(styrene-co-acrylonitrile) and epoxy cresol novolac resin amounts were chosen so that the ratio of poly(styrene-co-acrylonitrile) to ECN1299 was 90/10 (wt/wt).

B. Silicon Nitride Wafer Coating

A primer solution of 0.1% N-phenylaminopropyltrimethoxy silane in a 90:10 mixture of PGME:deionized water was spin coated onto a 4-inch silicon nitride wafer at 1,500 rpm for 1 minute. The wafer was baked at 130Â° C. for 1 minute. The polymer blend solution in Part A of this example was spin coated at 200 rpm for 10 seconds followed by 1,500 rpm for 1 minute. The wafer was baked at 100Â° C. for 2 minutes, then at 130Â° C. for 2 minutes, and then at 160Â° C. for 2 minutes.

C. Silicon Wafer Coating

A primer solution of 0.1% N-phenylaminopropyltrimethoxy silane in a 90:10 mixture of PGME:deionized water was spin coated onto a 4-inch silicon wafer at 1,500 rpm for 1 minute. The wafer was baked at 130Â° C. for 1 minute. The polymer blend solution prepared in Part A of this example was spin coated at 200 rpm for 10 seconds followed by 1,500 rpm for 1 minute. The wafer was baked at 100Â° C. for 2 minutes, then at 130Â° C. for 2 minutes, and then at 160Â° C. for 2 minutes.

D. Etch Testing of Silicon Nitride Wafer

The silicon nitride wafer coated in Part B of this example was etched in 30% aqueous KOH solution at 80-85Â° C. for 8 hours. After etching in KOH, the wafer was cleaned with DI water for 5 minutes and dried in air. The results showed that the wafer was not attacked by the KOH, and no edge lifting occurred. The film did not lose adhesion. The wafer after etching is shown in FIG. 1.

E. Etch Testing of Silicon Wafer

The silicon wafer coated in Part C of this example was etched in 30% aqueous KOH solution at 80-85Â° C. for 4 hours. After etching in KOH, the wafer was cleaned with DI water for 5 minutes and dried in air. Results showed that the wafer was not attacked by KOH, and no edge lifting occurred.

Example 20Primer Solution

A primer solution was made by mixing 0.05 g of 3-aminopropyltriethoxysilane with 98.95 g of propylene glycol monomethyl ether, and 1.0 g of de-ionized water. After stirred for 4 hours, the primer solution was filtered through 0.1 Î¼m filter and stored in a plastic bottle.

Example 21Alkaline-Resistant Coatings Comprising Epoxy Cresol Novolac Resin1. Preparation of Polymer Blend Solution

A polymer blend solution was made by dissolving 22.5 g of a poly(styrene-co-acrylonitrile) copolymer and 2.5 g of ECM 299 in a mixture of 37.5 g of EEP, and 37.5 g of MIAK.

2. Wafer Coating

The primer solution from Example 20 was spin-coated onto a silicon wafer at 1,500 rpm for 1 minute. The wafer was baked at 205Â° C. for 1 minute. The polymer blend solution prepared in Part 1 of this example was spin coated at 200 rpm for 10 seconds and then at 1,500 rpm for 1 minute. The wafer was baked at 100Â° C. for 2 minutes, then at 130Â° C. for 2 minutes, and then at 160Â° C. for 2 minutes.

3. Etch Testing

The wafer coated in Part 2 of this example was etched in 30% KOH aqueous solution at 80-85Â° C. for 4 hours. After the KOH etch, the wafer was cleaned with deionized water for 5 minutes and dried in air. The KOH did not attack or affect the wafers, and there was no edge lifting.

Example 22Alkaline-Resistant Coatings Comprising Epoxy Cresol Novolac Resin1. Preparation of Polymer Blend Solution

A polymer blend solution was made by dissolving 22.5 g of the poly(styrene-co-acrylonitrile) copolymer used in Example 21 and 2.5 g of ECN1299 in a mixture of 37.5 g of EEP and 37.5 g of MIAK.

2. Wafer Coating

The primer solution prepared in Example 20 above was spin-coated on to a SiN wafer at 1,500 rpm for 1 minute. The wafer was baked at 205Â° C. for a minute. The polymer blend solution in Part 1 of this example was spin coated at 200 rpm for 10 seconds and then at 1,500 rpm for 1 minute. The wafer was baked at 100Â° C. for 2 minutes, then at 130Â° C. for 2 minutes, and then at 160Â° C. for 2 minutes.

3. Etch Testing

The wafer coated in Part 2 of this example was etched in a 30% KOH aqueous solution at 80-85Â° C. for 8 hours. After the KOH etch, the wafer was cleaned with dionized water for 5 minutes and dried in air. The KOH did not attack or affect the wafers, and there was no edge lifting.