CROSS REFERENCE TO RELATED APPLICATION

This application is a continuation of U.S. patent application Ser. No. 09/973,778, filed Oct. 11, 2001, the contents of which are herein incorporated by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to the field of integrated optical devices, and in particular to a method of reducing stress-induced mechanical problems in optical components, especially optical components that are deep-etched, such as multiplexers and demultiplexers employing echelon gratings.

2. Description of the Related Art

The manufacture of integrated optical devices such as optical Multiplexers (Mux) and Demultiplexers (Dmux) requires the fabrication optical quality elements, such as waveguides and gratings highly transparent in the 1.30 and 1.55 Î¼m optical bands. These silica-based optical elements are basically composed of three films: buffer, core and cladding. For reasons of simplicity, the buffer and cladding are typically of the same composition and of same refractive index. In order to confine the 1.55 Î¼m (and/or 1.30 Î¼m) wavelength laser beam, the core must have a higher refractive index than the buffer (cladding). This required refractive index difference is called the â€˜delta-nâ€™ and is one of the most important characteristics of these silica-based optical elements. It is very difficult to fabricate such transparent silica-based optical elements in the 1.55 Î¼m wavelength (and/or 1.30 wavelength) optical region while maintaining the suitable â€˜delta-nâ€™ and while preventing stress-induced mechanical and problems.

Our co-pending U.S. patent application Ser. No. 09/867,772 entitled â€œMethod of Depositing Optical Quality Filmsâ€ , describes an improved Plasma Enhanced Chemical Vapour Deposition technique of these silica-based elements which allows the achievement of the required â€˜delta-nâ€™ while eliminating the undesirable residual Si:Nâ€”H oscillators (observed as a FTIR peak centered at 3380 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.515 Î¼m), SiNâ€”H oscillators (centered at 3420 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.479 Î¼m) and SiOâ€”H oscillators (centered at 3510 cm^âˆ’1and whose 2^ndharmonics could cause an optical absorption between 1.408 and 1.441 Î¼m) after a high temperature thermal treatment in a nitrogen ambient at 800Â° C.

Another co-pending patent application, Ser. No.______ , filed on Sep. 21, 2001, entitled â€œMethod of Depositing an Optical Quality Silica Film by PECVDâ€ , shows that to such a high temperature thermal treatment are associated some residual stress-induced mechanical problems of deep-etched optical elements (mechanical movement of the side-walls), some residual stress-induced mechanical problems at the buffer/core interface or at the core/cladding interface (micro-structural defects, micro-voiding and separation) and some residual stress-induced optical problems (polarisation dependant power loss) which can be eliminated by an improved process allowing the simultaneous optimization of the optical and of the mechanical properties of buffer (cladding) and core in a seven-dimensional space, namely a first independent variable, the SiH₄flow; a second independent variable, the N₂O flow; a third independent variable, the N₂flow; a fourth independent variable, the PH₃flow; a fifth independent variable, the total deposition pressure; a sixth independent variable, the optimised post-deposition thermal treatment; and the observed silica-based optical elements characteristics.

Recently published literature reveals various PECVD (Plasma Enhanced Chemical Vapor Deposition) approaches to obtain these high performance optically transparent silica-based optical elements: Valette S., New integrated optical multiplexer-demultiplexer realized on silicon substrate, ECIO '87, 145, 1987; Grand G., Low-loss PECVD silica channel waveguides for optical communications, Electron. Lett., 26 (25), 2135, 1990; Bruno F., Plasma-enhanced chemical vapor deposition of low-loss SiON optical waveguides at 1.5-Î¼m wavelength, Applied Optics, 30 (31), 4560, 1991; Kapser K., Rapid deposition of high-quality silicon-oxinitride waveguides, IEEE Trans. Photonics Tech. Lett., 5 (12), 1991; Lai Q., Simple technologies for fabrication of low-loss silica waveguides, Elec. Lett., 28 (11), 1000, 1992; Lai Q., Formation of optical slab waveguides using thermal oxidation of SiOx, Elec. Lett., 29 (8), 714, 1993; Liu K., Hybrid optoelectronic digitally tunable receiver, SPIE, Vol 2402, 104, 1995; Tu Y., Single-mode SiON/SiO2/Si optical waveguides prepared by plasma-enhanced Chemical vapor deposition, Fiber and integrated optics, 14, 133, 1995; Hoffmann M., Low temperature, nitrogen doped waveguides on silicon with small core dimensions fabricated by PECVD/RIE, ECIO'95, 299, 1995; Bazylenko M., Pure and fluorine-doped silica films deposited in a hollow cathode reactor for integrated optic applications, J. Vac. Sci. Technol. A 14 (2), 336, 1996; Poenar D., Optical properties of thin film silicon-compatible materials, Appl. Opt. 36 (21), 5112, 1997; Hoffmann M., Low-loss fiber-matched low-temperature PECVD waveguides with small-core dimensions for optical communication systems, IEEE Photonics Tech. Lett., 9 (9), 1238, 1997; Pereyra I., High quality low temperature DPECVD silicon dioxide, J. Non-Crystalline Solids, 212, 225, 1997; Kenyon T., A luminescence study of silicon-rich silica and rare-earth doped silicon-rich silica, Fourth Int. Symp. Quantum Confinement Electrochemical Society, 97-11, 304, 1997; Alayo M., Thick SiOxNy and SiO2 films obtained by PECVD technique at low temperatures, Thin Solid Films, 332, 40, 1998; Bulla D., Deposition of thick TEOS PECVD silicon oxide layers for integrated optical waveguide applications, Thin Solid Films, 334, 60, 1998; Valette S., State of the art of integrated optics technology at LETI for achieving passive optical components, J. of Modern Optics, 35 (6), 993, 1988; Ojha S., Simple method of fabricating polarization-insensitive and very low crosstalk AWG grating devices, Electron. Lett., 34 (1), 78, 1998; Johnson C., Thermal annealing of waveguides formed by ion implantation of silica-on-Si, Nuclear Instruments and Methods in Physics Research, B141, 670, 1998; Ridder R., Silicon oxynitride planar waveguiding structures for application in optical communication, IEEE J. of Sel. Top. In Quantum Electron., 4 (6), 930, 1998; Germann R., Silicon-oxynitride layers for optical waveguide applications, 195^thmeeting of the Electrochemical Society, 99-1, May 1999, Abstract 137, 1999; Worhoff K., Plasma enhanced cyhemical vapor deposition silicon oxynitride optimized for application in integrated optics, Sensors and Actuators, 74, 9, 1999; Offrein B., Wavelength tunable optical add-after-drop filter with flat passband for WDM networks, IEEE Photonics Tech. Lett., 11 (2), 239, 1999.

A comparison of these various PECVD techniques is summarised in FIG. 1 which describes the approaches and methods used to modify the â€˜delta-nâ€™ between buffer (cladding) and core with a post-deposition thermal treatment.

The various techniques can be grouped in main categories: PECVD using unknown chemicals, unknown chemical reactions and unknown boron (B) and/or phosphorus (P) chemicals and unknown chemical reactions to adjust the â€˜delta-nâ€™ (When specified, the post-deposition thermal treatments range from 400 to 1000Â° C.); PECVD using TEOS and unknown means of adjusting the â€˜delta-nâ€™ (The post-deposition thermal treatments are not specified); PECVD using oxidation of SiH₄with O₂coupled with silicon ion implantation or adjustment of silicon oxide stoichiometry as means of adjusting the â€˜delta-nâ€™ (The post-deposition thermal treatments range from 400 to 1000Â° C.) PECVD using oxidation of SiH₄with O₂coupled with the incorporation of CF₄(SiH₄/O₂/CF₄flow ratio) an means of adjusting the â€˜delta-nâ€™ (Wen specified, the post-deposition thermal treatments range from 100 to 1000Â° C.) PECVD using oxidation of SiH₄with N₂O coupled with variations of N₂O concentration (SiH₄/N₂O flow ratio) as means of adjusting the silicon oxide stoechiometry and the â€˜delta-nâ€™ (The post-deposition thermal treatments range from 400 to 1100Â° C.); PECVD using oxidation of SiH₄with N₂O coupled with variations of N₂O concentration and with the incorporation of Ar (SiH₄/N₂O/Ar flow ratio) as means of adjusting the silicon oxide stoechiometry and the â€˜delta-nâ€™ (The post-deposition thermal treatments is 1000Â° C.); PECVD using oxidation of SiH₄with N₂O coupled with the incorporation of NH₃(SiH₄/N₂O/NH₃flow ratio) as to form silicon oxynitrides with various â€˜delta-nâ€™ (When specified, the post-deposition thermal treatments range from 700 to 1100Â° C.); PECVD using oxidation of SiH₄with N₂O coupled with the incorporation of NH₃and Ar (SiH₄/N₂O/NH₃/Ar flow ratio) as to form silicon oxynitrides with various â€˜delta-nâ€™ (The post-deposition thermal treatments are not specified); PECVD using oxidation of SiH₄with N₂O coupled with the incorporation of NH₃and N₂chemicals variation (SiH₄/N₂O/NH₃/N₂flow ratio) as to form silicon oxynitrides with various â€˜delta-nâ€™ (The post-deposition thermal treatments range from 850 to 1150Â° C.); and PECVD using oxidation of SiH₄with N₂O and O₂coupled with the incorporation of CF₄, N₂and He (SiH₄/(N₂O/N₂)/O₂/CF₄flow ratio) as to form complex mixtures of carbon and fluorine containing silicon oxide as means of adjusting the â€˜delta-nâ€™ (The post-deposition thermal treatments is 425Â° C.).

Our co-pending patent application Ser. No. 09/833,711 entitled â€œOptical Quality Silica Filmsâ€ describes an improved Plasma Enhanced Chemical Vapour Deposition technique of low optical absorption buffer (cladding) which shows that the independent control of the SiH₄, N₂O and N₂gases as well as of the total deposition pressure via an automatic control of the pumping speed of the vacuum pump in a five-dimensional space: a first independent variable, the SiH₄flow; a second independent variable, the N₂O flow; a third independent variable, the N₂flow; a fourth independent variable; the total deposition pressure (controlled by an automatic adjustment of the pumping speed); and the observed film characteristics is key to eliminating the undesirable residual Si:Nâ€”H oscillators (observed as a FTIR peak centered at 3380 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.515 Î¼m), SiNâ€”H oscillators (centered at 3420 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.479 Î¼m) and SiOâ€”H oscillators (centered at 3510 ^âˆ’1and whose 2^ndharmonics could cause an optical absorption between 1.408 and 1.441 Î¼m) after thermal treatments at a low post-deposition temperature of 800Â° C. to provide improved silica films with reduced optical absorption in the 1.55 Î¼m wavelength (and/or 1.30 wavelength) optical region.

Our co-pending patent application Ser. No. 09/867,662 entitled â€œMethod of Depositing Optical Filmsâ€ describes a new improved Plasma Enhanced Chemical Vapour Deposition technique of low optical absorption core which shows that the independent control of the SiH₄, N₂O, N₂and PH₃gases as well as of the total deposition pressure via an automatic control of the pumping speed of the vacuum pump in a six-dimensional space: a first independent variable, the SiH₄flow; a second independent variable, the N₂O flow; a third independent variable, the N₂flow; a fourth independent variable, the PH₃flow; a fifth independent variable; the total deposition pressure (controlled by an automatic adjustment of the pumping speed); and the observed waveguides characteristics, is key to achieving the required â€˜delta-nâ€™ while still eliminating the undesirable residual Si:Nâ€”H oscillators (observed as a FTIR peak centered at 3380 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.515 Î¼m), SiNâ€”H oscillators (centered at 3420 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.479 Î¼m) and SiOâ€”H oscillators (centered at 3510 cm^âˆ’1and whose 2^ndharmonics could cause an optical absorption between 1.408 and 1.441 Î¼m) after thermal treatments at a low post-deposition temperature of 800Â° C. as to provide improved silica waveguides with reduced optical absorption in the 1.55 Î¼m wavelength (and/or 1.30 wavelength) optical region.

Our co-pending application Ser. No.______ filed on September 21, entitled â€œMethod of Depositing an Optical Quality Silica Film by PECVDâ€ describes a technique which shows that the simultaneous optimization of the optical and of the mechanical properties of buffer (cladding) and core in a seven-dimensional space: a first independent variable, the SiH₄flow; a second independent variable, the N₂O flow; a third independent variable, the N₂flow; a fourth independent variable, the PH₃flow; a fifth independent variable, the total deposition pressure; a sixth independent variable, the optimised post-deposition thermal treatment; and the observed silica-based optical elements characteristics is key to achieving the required â€˜delta-nâ€™ while eliminating the undesirable residual Si:Nâ€”H oscillators (observed as a FTIR peak centered at 3380 ^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.515 Î¼m), SiNâ€”H oscillators (centered at 3420 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.479 Î¼m) and SiOâ€”H oscillators (centered at 3510 ^âˆ’1and whose 2^ndharmonics could cause an optical absorption between 1.408 and 1.441 Î¼m) after an optimised thermal treatment in a nitrogen which can provide improved silica-based optical elements with reduced optical absorption in the 1.55 Î¼m wavelength (and/or 1.30 wavelength) optical region without the residual stress-induced mechanical problems of deep-etched optical elements (mechanical movement of side-walls), without the residual stress-induced mechanical problems at the buffer/core or core/cladding interfaces (micro-structural defects, micro-voiding and separation) and without the residual stress-induced optical problems (polarisation dependant power loss).

Our co-pending pending patent application, Ser. No. 09/799,491 entitled Method Of Making A Functional Device With Deposited Layers Subject To High Temperature Annealâ€ describes a new improved technique involving the deposition of thick PECVD silica films on the back face of the silicon wafer in order to prevent the wafer warp problem following high temperature anneals and to achieve a stable manufacturing of high performance high temperature annealed PECVD optical silica films with lower polarisation dependence.

An object of the present invention is to an optimised process which allow the elimination of these residual stress-induced mechanical problems of deep-etched optical elements (mechanical movement of the side-walls), of these residual stress-induced mechanical problems at the buffer/core interface or at the core/cladding interface (micro-structural defects, micro-voiding and separation) and of these residual stress-induced optical problems (polarisation dependant power loss).

SUMMARY OF THE INVENTION

The invention allows an improvement in PECVD optical quality silica-based optical elements to be obtained using a commercially available PECVD system, such as the â€œConcept Oneâ€ system manufactured by Novellus Systems in California, U.S.A, and a standard diffusion tube.

According to the present invention there is provided a method of making optical quality films, comprising the steps of depositing a first silica film on a wafer by PECVD (Plasma Enhanced Chemical Vapor Deposition); subjecting the wafer to a first heat treatment to reduce optical absorption, wafer warp, and compressive stress;

depositing a second silica film on the wafer by PECVD; and subsequently subjecting the wafer to a second heat treatment to reduce optical absorption, wafer warp and tensile stress.

The invention is typically applied to the fabrication of photonic devices, in which case the first layer can be a buffer layer and the second layer a core layer. The buffer layer is preferably applied symmetrically on the front and back faces of the wafer.

The method is preferably applied in conjunction with the methods described in our co-pending U.S. patent applications referred to herein, and which are all herein incorporated by reference.

In another aspect the invention provides a method of making a photonic device by PECDV (Plasma Enhanced Chemical Vapor Deposition) comprising depositing a thick first silica buffer layer on the back side of a wafer; depositing a thick silica buffer layer on the front side of said wafer; subjecting the wafer to a first heat treatment to reduce optical absorption, wafer warp, and compressive stress; depositing a silica core layer; subsequently to the previous step subecting the wafer to a second heat treatment to reduce optical absorption, wafer warp and tensile stress; and depositing a silica cladding layer on said silica core layer.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will now be described in more detail, by way of example, only with reference to the accompanying drawings, in which:

FIG. 1 shows various PECVD chemical reactions approaches and the reported method used to control the refractive index and to reduce the optical absorption of silica films;

FIG. 2 shows the FTIR fundamental infrared absorption peaks and their corresponding higher harmonics peaks associated with the residual compounds resulting from high temperature thermal treatments of PECVD silica-based optical components in a nitrogen ambient;

FIG. 3a shows the basic FTIR spectra of various buffers (claddings) obtained with a typical PECVD process after a 180 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 3b shows the basic FTIR spectra of various buffers (claddings) obtained with the PECVD deposition technique described in our co-pending patent application Ser. No. 09/833,711 and after a thermal treatment in a nitrogen ambient at 800Â° C.;

FIG. 3c shows the basic FTIR spectra of various Cores obtained at 2.60 Torr with the PECVD deposition technique described in our other pending patent application Ser. No. 09/867,662 and after a thermal treatment in a nitrogen ambient at 800Â° C.;

FIG. 3d shows the basic FTIR spectra of various cores obtained with the new PECVD deposition technique and after a 30 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 4a shows the in-depth FTIR spectra from 810 to 1000 cm^âˆ’1of various buffers (claddings) obtained with a typical PECVD process after a 180 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 4b shows the in-depth FTIR spectra from 810 to 1000 cm^âˆ’1of various Buffers (Clads) obtained with the PECVD deposition technique described in our pending patent application Ser. No. 09/833,711 after a thermal treatment in a nitrogen ambient at 800Â° C.;

FIG. 4c shows the in-depth FTIR spectra from 810 to 1000 cm^âˆ’1of various Cores obtained at 2.60 Torr with the PECVD deposition technique described in our other pending patent application Ser. No. 09/867,662;

FIG. 4d shows the in-depth FTIR spectra from 810 to 1000 cm^âˆ’1of various cores obtained with the new PECVD deposition technique after a 30 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 5c shows the in-depth FTIR spectra from 1260 to 1500 cm^âˆ’1of various Cores obtained at 2.60 Torr with the PECVD deposition technique described in our other pending patent application Ser. No. 09/867,662;

FIG. 5d shows the in-depth FTIR spectra from 1260 to 1500 cm^âˆ’1of various Cores obtained with the new PECVD deposition technique after a 30 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 6a shows the in-depth FTIR spectra from 1500 to 1600 cm^âˆ’1of various Buffers (Clads) obtained with a typical PECVD process after a 180 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 6b shows the in-depth FTIR spectra from 1500 to 1600 cm^âˆ’1of various Buffers (Clads) obtained with the PECVD deposition technique described in our pending patent application Ser. No. 09/833,711 after a thermal treatment in a nitrogen ambient at 800Â° C.;

FIG. 6c shows the in-depth FTIR spectra from 1500 to 1600 cm^âˆ’1of various Cores obtained at 2.60 Torr with the PECVD deposition technique described in our other pending patent application Ser. No. 09/867,662 after a thermal treatment in a nitrogen ambient at 800Â° C.;

FIG. 6d shows the in-depth FTIR spectra from 1500 to 1600 cm^âˆ’1of various Cores obtained with the new PECVD deposition technique after a 30 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 7a shows the in-depth FTIR spectra from 1700 to 2200 cm^âˆ’1of various Buffers (Clads) obtained with a typical PECVD process after a 180 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 7b shows the in-depth FTIR spectra from 1700 to 2200 cm^âˆ’1of various Buffers (Clads) obtained with the PECVD deposition technique described in our pending patent application Ser. No. 09/833,711 after a thermal treatment in a nitrogen ambient at 800Â° C.;

FIG. 7c shows the in-depth FTIR spectra from 1700 to 2200 cm^âˆ’1of various Cores obtained at 2.60 Torr with the PECVD deposition technique described in our other pending patent application Ser. No. 09/867,662 after a thermal treatment in a nitrogen ambient at 800Â° C.;

FIG. 7d shows the in-depth FTIR spectra from 1700 to 2200 cm^âˆ’1of various Cores obtained with the new PECVD deposition technique after a 30 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 8a shows the in-depth FTIR spectra from 2200 to 2400 cm^âˆ’1of various Buffers (Clads) obtained with a typical PECVD process after a 180 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 8b shows the in-depth FTIR spectra from 2200 to 2400 cm^âˆ’1of various Buffers (Clads) obtained with the PECVD deposition technique described in our pending patent application Ser. No. 09/833,711 after a thermal treatment in a nitrogen ambient at 800Â° C.;

FIG. 8c shows the in-depth FTIR spectra from 2200 to 2400 cm^âˆ’1of various Cores obtained at 2.60 Torr with the PECVD deposition technique described in our other pending patent application titled 09/867,662 after a thermal treatment in a nitrogen ambient at 800Â° C.;

FIG. 8d shows the in-depth FTIR spectra from 2200 to 2400 cm^âˆ’1of various Cores obtained with the new PECVD deposition technique after a 30 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 9a shows the in-depth FTIR spectra from 3200 to 3900 cm^âˆ’1of various Buffers (Clads) obtained with a typical PECVD process after a 180 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 9b shows the in-depth FTIR spectra from 3200 to 3900 cm^âˆ’1of various Buffers (Clads) obtained with the PECVD deposition technique described in our pending patent application Ser. No. 09/833,711 after a thermal treatment in a nitrogen ambient at 800Â° C.;

FIG. 9c shows the in-depth FTIR spectra from 3200 to 3900 cm^âˆ’1of various Cores obtained at 2.60 Torr with the PECVD deposition technique described in our other pending patent application Ser. No. 09/867,662 after a thermal treatment in a nitrogen ambient at 800Â° C.;

FIG. 9d shows the in-depth FTIR spectra from 3200 to 3900 cm^âˆ’1of various Cores obtained with the new PECVD deposition technique after a 30 minutes thermal treatment in a nitrogen ambient at various temperatures;

FIG. 10 shows the stress hysteresis of buffer (cladding) core in a nitrogen ambient using a 180 minutes stabilisation at 800Â° C.;

FIG. 11 shows SEM pictures of a grating and of a waveguide with quasi-vertical side-walls deep-etched through buffer and core;

FIG. 12 shows gradually sloped side-wall formation from the elastic strain of deep-etched buffer/core optical elements resulting from the (compressive stress Buffer)/(tensile stress Core) combination;

FIG. 13 shows side-wall angle measurements of neighboring a 5.0 Î¼m wide deep-etched waveguide and 1150 Î¼m wide deep-etched grating and the relative position between an isolated 5.0 Î¼m wide deep-etched waveguide and its neighboring 1150 Î¼m wide deep-etched grating at two different magnifications;

FIG. 14 shows how the interfacial stress relief of the shear stress building at the buffer/core or core/cladding interfaces results in a noticeable modification of the micro-structure of these interfaces;

FIG. 15 shows the interfacial stress relief of the shear stress building at the buffer/core or core/cladding interfaces results in an important modification of the micro-structure and in the formation of micro-voids in Core and near these interfaces;

FIG. 16 shows the stress relief contraction of the tensile stress core during SEM preparation;

FIG. 17 shows the required buffer/core/cladding optical elements structure;

FIG. 18a shows the deposition of a 0.5 Î¼m thick Buffer on the front face of the wafer;

FIG. 18b shows the deposition of a 10.0 Î¼m thick buffer on the back face of the wafer;

FIG. 18c shows the deposition of a 0.5 Î¼m thick PECVD silicon nitride on the back face of the wafer;

FIG. 18d shows a wet-etch of the 0.5 Î¼m thick Buffer on the front face of the wafer and of 0.1 Î¼m of the 0.5 Î¼m thick PECVD silicon nitride on the back face of the wafer;

FIG. 18e shows the deposition of a 0.3 Î¼m thick PECVD silicon nitride on the front face of the wafer;

FIG. 18f shows the deposition of a 10.0 Î¼m thick buffer on the front face of the wafer;

FIG. 18g shows a first optimised thermal treatment of in accordance with one embodiment of the invention;

FIG. 18h shows the deposition of a 5.0 Î¼m thick core on the front face of the wafer;

FIG. 18i shows a second optimised thermal treatment in accordance with the invention;

FIG. 18j shows the deep-etching of a core with a 2.0 Î¼m penetration into a buffer;

FIG. 18k shows the deposition of a 10.0 Î¼m thick cladding on the front face of the wafer;

FIG. 18l shows the pattern and wet-etch of the 10.0 Î¼m thick cladding on the front face of the wafer;

FIG. 19 show the temperature profile of the first optimized thermal treatment;

FIG. 20 shows the temperature profile of the second optimized thermal treatment;

FIG. 21 shows the shape of the wafer before any processing;

FIG. 22 shows the shape of the wafer after deposition of a 5.0 Î¼m thick Core on the front face of the wafer (i.e. FIG. 18h); and

FIG. 23 shows the shape of the wafer after the second optimised thermal treatment of this patent application (i.e. FIG. 18i).

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

FIG. 2 lists some FTIR fundamental infrared absorption peaks and their corresponding higher harmonics peaks associated with the various residual compounds resulting the Plasma Enhanced Chemical Vapour Deposition (PECVD) of buffer (cladding) from a silane (SiH₄) and nitrous oxide (N₂O) gas mixture at a relatively low temperature of 400Â° C. using the following reaction:
SiH₄(g)+2N₂O(g)â†’SiO₂+2N₂(g)+2H₂(g)

and following high temperature thermal treatments in a nitrogen ambient. It is very clear from this FIG. 2 that the FTIR fundamental infrared absorption peaks and their corresponding higher harmonics peaks associated of the residual compounds resulting from high temperature thermal treatments of PECVD silica films in a nitrogen ambient will contribute to the optical absorption in the 1.30 to 1.55 Î¼m optical bands:

The second vibration harmonics of the HOâ€”H oscillators in trapped water vapour in the micro-pores of the silica films (3550 to 3750 cm^âˆ’1) increases the optical absorption near 1.333 to 1.408 Î¼m. The second vibration harmonics of the SiOâ€”H oscillators in the silica films (3470 to 3550 cm^âˆ’1) increases the optical absorption near 1.408 to 1.441 Î¼m. The second vibration harmonics of the Si:Nâ€”H oscillators in the silica films (3300 to 3460 cm^âˆ’1) increases the optical absorption near 1.445 to 1.515 Î¼m. The second vibration harmonics of the SiNâ€”H oscillators in the silica films (3380 to 3460 cm^âˆ’1) increases the optical absorption near 1.445 to 1.479 Î¼m. The third vibration harmonics of the Siâ€”H oscillators in the silica films (2210 to 2310 cm^âˆ’1) increases the optical absorption near 1.443 to 1.505 Î¼m. The fourth vibration harmonics of the Siâ• O oscillators in the silica films (1800 to 1950 cm^âˆ’1) increases the optical absorption near 1.282 to 1.389 Î¼m. The fifth vibration harmonics of the Nâ• N oscillators in the silica films (1530 to 1580 cm^âˆ’1) increases the optical absorption near 1.266 to 1.307 Î¼m.

The negative effects of these the oscillators on the optical properties of silica-based optical components are reported in the literature: Grand G., Low-loss PECVD silica channel waveguides for optical communications, Electron. Lett., 26 (25), 2135, 1990; Bruno F., Plasma-enhanced chemical vapor deposition of low-loss SiON optical waveguides at 1.5-Î¼m wavelength, Applied Optics, 30 (31), 4560, 1991; Imoto K., High refractive index difference and low loss optical waveguide fabricated by low temperature processes, Electronic Letters, 29 (12), 1993; Hoffmann M., Low temperature, nitrogen doped waveguides on silicon with small core dimensions fabricated by PECVD/RIE, ECIO'95, 299, 1995; Bazylenko M., Pure and fluorine-doped silica films deposited in a hollow cathode reactor for integrated optic applications, J. Vac. Sci. Technol. A 14 (2), 336, 1996; Pereyra I., High quality low temperature DPECVD silicon dioxide, J. Non-Crystalline Solids, 212, 225, 1997; Kenyon T., A luminescence study of silicon-rich silica and rare-earth doped silicon-rich silica, Electrochem. Soc. Proc. Vol. 97-11, 304, 1997; Alayo M., Thick SiOxNy and SiO2 films obtained by PECVD technique at low temperatures, Thin Solid Films, 332, 40, 1998; Germann R., Silicon-oxynitride layers for optical waveguide applications, 195^thmeeting of the Electrochemical Society, 99-1, May 1999, Abstract 137, 1999; Worhoff K., Plasma enhanced chemical vapor deposition silicon oxynitride optimized for application in integrated optics, Sensors and Actuators, 74, 9, 1999.

This literature describes the tentative elimination of optical absorption (i.e. of the six residual oscillators) using the discussed thermal decomposition reactions during thermal treatments under a nitrogen ambient at a maximum temperature lower than 1350Â° C., the fusion point of the silicon wafer.

Optical Absorption of Typical PECVD Buffer (Cladding) Following a 180 Minutes Thermal Treatment in a Nitrogen Ambient at Various High Temperatures

FIG. 3a, FIG. 4a, FIG. 6a, FIG. 7a, FIG. 8a and FIG. 9a show the FTIR spectra of typically deposited PECVD silica films before and after a 180 minutes long high temperature thermal treatment in a nitrogen ambient at a temperature of either 600, 700, 800, 900, 1000 or 1100Â° C. It is clear that the higher the thermal decomposition temperature of the high temperature thermal treatment in a nitrogen ambient, the better the basic FTIR spectra of the treated silica films:

FIG. 3a shows the expected gradually more intense and smaller FWHM Siâ€”Oâ€”Si â€œrocking modeâ€ absorption peak (centred at 460 cm^âˆ’1) and Siâ€”Oâ€”Si â€œin-phase-stretching modeâ€ absorption peak (centred at 1080 cm^âˆ’1) as the temperature of the 180 minutes long thermal treatment in a nitrogen ambient is increased from 600Â° C. to 1100Â° C.;

FIG. 4a shows that the elimination of the Siâ€”OH oscillators (centered at 885 cm^âˆ’1) is easy and already complete after the 180 minutes long thermal treatment in a nitrogen ambient at 600Â° C. FIG. 4a also shows that the elimination of the Siâ€”ON oscillators (centred at 950 cm^âˆ’1) is much more difficult and that the higher the temperature of the 180 minutes long thermal treatment in a nitrogen ambient, the more nitrogen incorporation as Siâ€”ON oscillators (i.e. as SiONH and/or SiON₂compounds);

FIG. 6a shows that the elimination of the Nâ• N oscillators (centered at 1555 cm^âˆ’1) is also very difficult and does require the temperature of the high temperature thermal treatment in a nitrogen ambient to reach 1000Â° C.;

FIG. 7a shows that there is very little influence of the temperature of the high temperature thermal treatment in a nitrogen ambient on the Siâ• O oscillators (centered at 1875 cm^âˆ’1) and on the unknown oscillator (centered at 2010 cm^âˆ’1).

FIG. 8a shows that the elimination of the Siâ€”H oscillators (centered at 2260 cm^âˆ’1and which 3^rdharmonics could cause an optical absorption between 1.443 and 1.508 Î¼m) is easy and already complete after the 180 minutes long thermal treatment in a nitrogen ambient at 600Â° C.

FIG. 9a shows that the elimination of the Si:Nâ€”H oscillators (centered at 3380 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.515 Î¼m) is also very difficult and does require the temperature of the high temperature thermal treatment in a nitrogen ambient to reach 1100Â° C. The complete elimination of the Si:Nâ€”H oscillators is highly difficult because the nitrogen atoms of these oscillators are bonded to the silicon atoms of the SiO2 network via two covalent bonds. FIG. 9a also shows that the elimination of the SiNâ€”H oscillators (centered at 3420 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.479 Î¼m) is almost as difficult and does require the temperature of the high temperature thermal treatment in a nitrogen ambient to reach 1000Â° C. FIG. 9a also shows that the elimination of the SiOâ€”H oscillators (centered at 3510 cm^âˆ’1and whose 2^ndharmonics could cause an optical absorption between 1.408 and 1.441 Î¼m) is slightly easier and does require the temperature of the high temperature thermal treatment in a nitrogen ambient to reach 900Â° C. Finally, FIG. 9a also shows that the elimination of the HOâ€”H oscillators (centered at 3650 cm^âˆ’1and whose 2^ndharmonics could cause an optical absorption between 1.333 and 1.408 Î¼m) is very easy since already complete after the high temperature thermal treatment in a nitrogen ambient of only 600Â° C.

It is clear from the various FTIR spectra that it is necessary to use extremely high temperature thermal treatments in a nitrogen ambient in order to eliminate the residual optical absorption of typically deposited PECVD silica films. In particular, it is demonstrated that the elimination of the residual nitrogen and hydrogen of typically deposited PECVD silica films is very difficult since: the residual Si:Nâ€”H oscillators (whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.515 Î¼m) does require a temperature of 1100Â° C. because the nitrogen atoms of these oscillators are bonded to the silicon atoms of the SiO2 network via two covalent bonds; the elimination of the SiNâ€”H oscillators (whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.479 Î¼m) does require a temperature of 1000Â° C.; the elimination of the SiOâ€”H oscillators (whose 2^ndharmonics could cause an optical absorption between 1.408 and 1.441 Î¼m) does require a temperature of 900Â° C.

It is then very difficult to achieve high optical quality silica-based optical components from typically deposited PECVD silica films using thermal treatments in nitrogen ambient at temperatures lower than 1100Â° C.

Optical Absorption of PECVD Buffer (Cladding) Deposited by the Technique Described in Co-Pending Patent Application Ser. No. 09/833,711 Following a 180 Minutes Thermal Treatment in a Nitrogen Ambient at a Reduced Temperature of 800Â° C.

This patent application describes a new improved Plasma Enhanced Chemical Vapour Deposition technique of buffer (cladding) which shows that the independent control of the SiH₄, N₂O and N₂gases as well as of the total deposition pressure via an automatic control of the pumping speed of the vacuum pump in a five-dimensional space, namely: the first independent variable, the SiH₄gas flow, being fixed at 0.20 std litre/min; the second independent variable, the N₂O gas flow, being fixed at 6.00 std litre/min; the third independent variable, the N₂gas flow, being fixed at 3.15 std litre/min; the fourth independent variable, the total deposition pressure, being 2.00 Torr, 2.10 Torr, 2.20 Torr, 2.30 Torr, 240 Torr, 2.50 Torr, or 2.60 Torr.

The fifth dimension is the observed FTIR characteristics of various buffers (claddings), as reported in: FIG. 3b, FIG. 4b, FIG. 6b, FIG. 7b, FIG. 8b and FIG. 9b.

These dimensions permit the elimination of these residual nitrogen and hydrogen atoms as to achieve high optical quality silica-based optical components from typically deposited PECVD silica films a 180 minutes thermal treatment in a nitrogen ambient at a reduced temperature of 800Â° C.

FIG. 3b, FIG. 4b, FIG. 6b, FIG. 7b, FIG. 8b and FIG. 9b show the FTIR spectra of PECVD silica films deposited using a commercially available PECVD system, the â€œConcept Oneâ€ system manufactured by Novellus Systems in California, U.S.A, using the fixed flow rates of silane (SiH₄), of nitrous oxide (N₂O) and of nitrogen (N₂O), as described in our co-pending patent application Ser. No. 09/833,711. These spectra are obtained before and after a 180 minutes thermal treatment in a nitrogen ambient at a reduced temperature of 800Â° C. in a standard diffusion tube. It is clear that this technique allows the achievement of high optical quality silica films after a 180 minutes thermal treatment in a nitrogen ambient at a reduced temperature of 800Â° C. and that the independent control of the downstream pressure of this improved PECVD deposition technique has a major effect on the FTIR spectra of the treated silica films.

FIG. 3b shows a more intense and smaller FWHM Siâ€”Oâ€”Si â€œrocking modeâ€ absorption peak (centred at 460 cm^âˆ’1) and Siâ€”Oâ€”Si â€œin-phase-stretching modeâ€ absorption peak (centred at 1080 cm^âˆ’1) as the total deposition pressure is increased from 2.00 Torr to 2.40 Torr followed by a slight degradation as the pressure is increased further more up to 2.60 Torr.

FIG. 4b shows the gradual elimination of the Siâ€”OH oscillators (centered at 885 cm^âˆ’1) as the total deposition pressure is increased from 2.00 Torr up to the optimum pressure of 2.40 Torr followed by a slight degradation as the pressure is increased further more up to 2.60 Torr. FIG. 4b also shows the gradual elimination of the Siâ€”ON oscillators (centred at 950 cm^âˆ’1) as the total deposition pressure is increased from 2.00 Torr to 2.40 Torr followed by a slight degradation as the pressure is increased further more up to 2.60 Torr. The optimum separation and deep valley observed at 2.40 Torr is an indication that the silica films resulting from this optimum deposition pressure are composed of high quality SiO₂material. This contrasts with the upper-mentioned results of typical PECVD silica films which still incorporate a lot of Siâ€”ON oscillators even after much higher temperature thermal treatments in a nitrogen ambient.

FIG. 6b shows the gradual and total elimination of the Nâ• N oscillators (centered at 1555 cm^âˆ’1) as the total deposition pressure is increased from 2.00 Torr to 2.60 Torr. This also contrasts with the upper-mentioned results of typical PECVD silica films which require a 180 minutes thermal treatment in a nitrogen ambient at a temperature of 1000Â° C. in order to achieve similar results.

FIG. 7b shows the gradual elimination of the Siâ• O oscillators (centered at 1875 cm^âˆ’1) and on the unknown oscillator (centered at 2010 cm^âˆ’1) as the total deposition pressure is increased from 2.00 Torr to 2.40 Torr followed by a slight degradation as the pressure is increased further more up to 2.60 Torr. These effects are not that important since only the fourth harmonics of the Siâ• O oscillators could absorb in the 1.30 to 1.55 Î¼m optical bands.

FIG. 8b shows that the Siâ€”H oscillators (centered at 2260 cm^âˆ’1and which 3^rdharmonics could cause an optical absorption between 1.443 and 1.508 Î¼m) are completely eliminated for all deposition pressures.

FIG. 9b shows the spectacular gradual elimination of the Si:Nâ€”H oscillators (centered at 3380 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.515 Î¼m) as the total deposition pressure is increased from 2.00 Torr to 2.60 Torr. This contrasts with the upper-mentioned results of typical PECVD silica films which require a thermal treatment in a nitrogen ambient at a temperature of 1100Â° C. in order to achieve similar results. FIG. 9b also shows a spectacular gradual elimination of the SiNâ€”H oscillators (centered at 3420 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.479 Î¼m) as the total deposition pressure is increased from 2.00 Torr to 2.60 Torr. This also contrasts with the upper-mentioned results of typical PECVD silica films which require a thermal treatment in a nitrogen ambient at a temperature of 1000Â° C. in order to achieve similar results. FIG. 9b also shows that the SiOâ€”H oscillators (centered at 3510 cm^âˆ’1and whose 2^ndharmonics could cause an optical absorption between 1.408 and 1.441 Î¼m) are completely eliminated for all deposition pressures. This also contrasts with the upper-mentioned results of typical PECVD silica films which require a thermal treatment in a nitrogen ambient at a temperature of 900Â° C. in order to achieve similar results. Finally, FIG. 9b also shows that the elimination of the HOâ€”H oscillators (centered at 3650 cm^âˆ’1and whose 2^ndharmonics could cause an optical absorption between 1.333 and 1.408 Î¼m) are completely eliminated for all deposition pressures.

It is clear from the various FTIR spectra that the technique described in this co-pending patent application avoids the need for extremely high temperature thermal treatments in a nitrogen ambient in order to eliminate the residual optical absorption of typically deposited PECVD silica films. In particular, it is demonstrated that the elimination of the residual nitrogen and hydrogen of typically deposited PECVD silica films is completely achieved after a 180 minutes thermal treatment in a nitrogen ambient at a reduced temperature of 800Â° C.:

The residual Si:Nâ€”H oscillators (whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.515 Î¼m) are completely eliminated as the total deposition pressure is increased from 2.00 Torr to 2.60 Torr;

The residual SiNâ€”H oscillators (whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.479 Î¼m) are also completely eliminated as the total deposition pressure is increased from 2.00 Torr to 2.60 Torr;

The residual SiOâ€”H oscillators (whose 2^ndharmonics could cause an optical absorption between 1.408 and 1.441 pm) are also completely eliminated as the total deposition pressure is increased from 2.00 Torr to 2.60 Torr.

It is then very easy to achieve high optical quality buffer (cladding) after a 180 minutes thermal treatment in a nitrogen ambient at a reduced temperature of 800Â° C. if we use the technique described in our patent pending application â€˜Plasma Enhanced Chemical Vapour Deposition of low optical absorption silica films for Mux/Dmux optical devicesâ€™.

Optical Absorption of PECVD Core Deposited by Our Co-Pending Patent Application 09/867,662 After a 180 Minutes Thermal Treatment in a Nitrogen Ambient at a Reduced Temperature of 800Â° C.

This co-pending patent application shows the spectacular effect of a fifth independent variable, the phosphine, PH₃, gas flow, on the optimization of the optical properties of the various core in a six-dimensional space: the first independent variable, the SiH₄gas flow, being fixed at 0.20 std litre/min; the second independent variable, the N₂O gas flow, being fixed at 6.00 std litre/min; the third independent variable, the N₂gas flow, being fixed at 3.15 std litre/min. The fourth independent variable, the PH₃gas flow, is varied and can be 0.00 std litre/min, 0.12 std litre/min, 0.25 std litre/min, 0.35 std litre/min, 0.50 std litre/min, or 0.65 std litre/min. The fifth independent variable, the total deposition pressure, is fixed at 2.60 Torr;

The sixth dimension is the observed FTIR characteristics of various buffer (cladding) and core waveguides, as reported in: FIG. 3c, FIG. 4c, FIG. 5c, FIG. 6c, FIG. 7c, FIG. 8c, & FIG. 9c.

FIG. 3c, FIG. 4c, FIG. 5c, FIG. 6c, FIG. 7c, FIG. 8c and FIG. 9c show the FTIR spectra of PECVD silica films deposited using a commercially available PECVD system, the â€œConcept Oneâ€ system manufactured by Novellus Systems in California, U.S.A, using the fixed optimum total deposition pressure and the fixed flow rates of silane (SiH₄), of nitrous oxide (N₂O) and of nitrogen (N₂O), as described in our patent pending application â€˜Silica waveguides for Mux/Dmux optical devicesâ€™. These spectra are obtained after a 180 minutes high temperature thermal treatment in a nitrogen ambient at a fixed temperature of only 800Â° C. in a standard diffusion tube. It is clear that this technique allows the achievement of high optical quality silica waveguides after a 180 minutes thermal treatment in a nitrogen ambient at a reduced temperature of 800Â° C.

FIG. 3c shows that the intense and small FWHM Siâ€”Oâ€”Si â€œrocking modeâ€ absorption peak (centred at 460 cm^âˆ’1) and Siâ€”Oâ€”Si â€œin-phase-stretching modeâ€ absorption peak (centred at 1080 cm^âˆ’1) of the fixed deposition pressure of 2.60 Torr of FIG. 3b is maintained in FIG. 3c as the PH₃flow rate is gradually increased from 0.00 std litre/min to 0.65 std litre/min. This means that at a fixed deposition pressure of 2.60 Torr, the control of the PH₃gas flow independently of the SiH₄gas flow, of the N₂O gas flow and of the N₂gas flow has no effect on the basic FTIR spectra of the treated silica films;

FIG. 4c shows that an even more gradual elimination of the Siâ€”OH oscillators (centered at 885 cm^âˆ’1) is observed at the total deposition pressure of 2.60 Torr as the PH₃flow rate is increased from 0.00 std litre/min to 0.65 std litre/min. FIG. 4c also shows that a gradual elimination of the Siâ€”ON oscillators (centred at 950 cm^âˆ’1) is also observed at the total deposition pressure of 2.60 Torr as the PH₃flow rate is increased from 0.00 std litre/min up to the optimum 0.25 std litre/min followed by a very slight degradation as the PH₃flow rate is increased further more up to 0.65 std litre/min. This spectacular improved elimination of the residual Siâ€”ON oscillators after a 180 minutes thermal treatment of only 800Â° C. contrasts with the upper-mentioned results of typical PECVD silica films of FIG. 4a which still incorporate a lot of Siâ€”ON oscillators even after a thermal treatment in a nitrogen ambient at a much higher temperature of 1100Â° C. This also contrasts with the upper-mentioned results of PECVD buffer (cladding) deposited at a non-optimized pressure of less than 2.40 Torr by our pending patent application â€˜Plasma Enhanced Chemical Vapour Deposition of low optical absorption silica films for Mux/Dmux optical devicesâ€™ of FIG. 4b which still incorporate a lot of Siâ€”ON oscillators even after a 180 minutes thermal treatment in a nitrogen ambient at a much higher temperature of 800Â° C. The optimum separation and deep valley between the Siâ€”Oâ€”Si â€œin-phase-stretching modeâ€ absorption peak (1080 cm^âˆ’1) and the Siâ€”Oâ€”Si â€œbending modeâ€ absorption peak (810 cm^âˆ’1) of the fixed deposition pressure of 2.60 Torr of FIG. 4b is maintained and in fact slightly improved as the PH₃flow rate is gradually increased from 0.00 std litre/min to 0.35 std litre/min.

FIG. 5c shows that a gradual appearance of the Pâ• O oscillators (centered at 1330 cm^âˆ’1and which does not have a higher harmonics which could cause optical absorption in the 1.30 to 1.55 Î¼m optical bands) is observed at the total deposition pressure of 2.60 Torr as the PH₃flow rate is increased from 0.00 std litre/min to 0.65 std litre/min. This FTIR absorption peak is used to calibrate the phosphorus incorporation in core.

FIG. 6c shows that of the Nâ• N oscillators (centered at 1555 cm^âˆ’1) are completely eliminated at the total deposition pressure of 2.60 Torr for all PH₃flow rate values from 0.00 std litre/min to 0.65 std litre/min. This contrasts with the upper-mentioned results of typical PECVD silica films of FIG. 6a which require a 180 minutes thermal treatment in a nitrogen ambient at a temperature of 1000Â° C. in order to achieve similar results. This also contrasts with the upper-mentioned results of PECVD buffer (cladding) deposited at a non-optimized pressure of less than 2.40 Torr by our pending patent application â€˜Plasma Enhanced Chemical Vapour Deposition of low optical absorption silica films for Mux/Dmux optical devicesâ€™ of FIG. 6b which still incorporate a lot of Nâ• N oscillators even after a 180 minutes thermal treatment in a nitrogen ambient at a much higher temperature of 800Â° C.

FIG. 7c shows that the Siâ• O oscillators (centered at 1875 cm^âˆ’1) and the unknown oscillator (centered at 2010 cm^âˆ’1) at the total deposition pressure of 2.60 Torr are not influenced by the PH₃flow rate from 0.00 std litre/min to 0.65 std litre/min. These effects are not that important since only the fourth harmonics of the Siâ• O oscillators could absorb in the 1.30 to 1.55 Î¼m optical bands;

FIG. 8c shows that the Siâ€”H oscillators (centered at 2260 cm^âˆ’1and which third harmonics could cause an optical absorption between 1.443 and 1.508 Î¼m) at the total deposition pressure of 2.60 Torr are still completely eliminated by any of all PH₃flow rates from 0.00 std litre/min to 0.65 std litre/min.

FIG. 9c shows that the spectacular complete elimination of the Si:Nâ€”H oscillators (centered at 3380 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.515 Î¼m) at the total deposition pressure of 2.60 Torr is maintained for all PH₃flow rates from 0.00 std litre/min to 0.65 std litre/min. This contrasts with the upper-mentioned results of typical PECVD silica films which require a thermal treatment in a nitrogen ambient at a temperature of 1100Â° C. in order to achieve similar results. This also contrasts with the upper-mentioned results of PECVD buffer (cladding) deposited at a non-optimized pressure of less than 2.40 Torr by our pending patent application â€˜Plasma Enhanced Chemical Vapour Deposition of low optical absorption silica films for Mux/Dmux optical devicesâ€™ of FIG. 9b which still incorporate a lot of Si:Nâ€”H oscillators even after a 180 minutes thermal treatment in a nitrogen ambient at a much higher temperature of 800Â° C. FIG. 9c also shows that the a spectacular complete elimination of the SiNâ€”H oscillators (centered at 3420 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.479 Î¼m) at the total deposition pressure of 2.60 Torr is also maintained for all PH₃flow rates from 0.00 std litre/min to 0.65 std litre/min. This contrasts with the upper-mentioned results of typical PECVD silica films which require a thermal treatment in a nitrogen ambient at a temperature of 1000Â° C. in order to achieve similar results. This also contrasts with the upper-mentioned results of PECVD buffer (cladding) deposited at a non-optimized pressure of less than 2.40 Torr by our pending patent application â€˜Plasma Enhanced Chemical Vapour Deposition of low optical absorption silica films for Mux/Dmux optical devicesâ€™ of FIG. 9b which still incorporate a lot of SiNâ€”H oscillators even after a 180 minutes thermal treatment in a nitrogen ambient at a much higher temperature of 800Â° C. FIG. 9c also shows that the complete elimination of the SiOâ€”H oscillators (centered at 3510 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.408 and 1.441 Î¼m) at the total deposition pressure of 2.60 Torr is maintained for all PH₃flow rates from 0.00 std litre/min to 0.65 std litre/min. This contrasts with the upper-mentioned results of typical PECVD silica films which require a thermal treatment in a nitrogen ambient at a temperature of 900Â° C. in order to achieve similar results. Finally, FIG. 9c also shows that the complete elimination of the HOâ€”H oscillators (centered at 3650 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.333 and 1.408 Î¼m) at the total deposition pressure of 2.60 Torr is maintained for all PH₃flow rates from 0.00 std litre/min to 0.65 std litre/min.

It is clear from the various FTIR spectra that our pending patent application titled â€˜Silica waveguides for Mux/Dmux optical devicesâ€™ allows the use of various PH₃flow rates from 0.00 std litre/min to 0.65 std litre/min. as to achieve core with the required â€˜delta-nâ€™ after a 180 minutes thermal treatment in a nitrogen ambient at a reduced temperature of 800Â° C. while maintaining excellent optical quality.

Optical Absorption of PECVD Buffer (Cladding) and Core Deposited by Our CO-Pending Patent Application Entitled Method of Depositing an Optical Quality Silica Film by PECVD After a 30 Minutes Thermal Treatment in a Nitrogen Ambient at a Reduced Temperatures of 600 to 900Â° C.

This patent application shows the spectacular flexibility of the post-deposition thermal treatment the optimization of the optical and of the mechanical properties of buffer (cladding) and core in a seven-dimensional space: a first independent variable, the SiH₄flow, being fixed at 0.20 std litre/min; a second independent variable, the N₂O flow, being fixed at 6.00 std litre/min; a third independent variable, the N₂flow, being fixed at 3.15 std litre/min; a fourth independent variable, the PH₃flow, being fixed at 0.50 std litre/min; a fifth independent variable, the total deposition pressure, being fixed at 2.60 Torr.

The sixth independent variable, the post-deposition thermal treatment is varied and consists of a 30 minutes duration thermal treatment in a nitrogen ambient at 600Â° C., 700Â° C., 750Â° C., 800Â° C., 850Â° C., or 900Â° C.;

A seventh dimension is the observed FTIR characteristics of various buffer (cladding) and core silica-based optical elements, as reported in: FIG. 3d, FIG. 4d, FIG. 5d, FIG. 6d, FIG. 7d, FIG. 8d, & FIG. 9d.

FIG. 3d, FIG. 4d, FIG. 5d, FIG. 6d, FIG. 7d, FIG. 8d and FIG. 9d show the FTIR spectra of PECVD silica films deposited using a commercially available PECVD system, the â€œConcept Oneâ€ system manufactured by Novellus Systems in California, U.S.A, using the fixed optimum total deposition pressure and the fixed flow rates of silane (SiH₄), of nitrous oxide (N₂O), of nitrogen (N₂), and of phosphine (PH₃) as described in our patent pending application â€˜Silica waveguides for Mux/Dmux optical devicesâ€™. These spectra are obtained after 30 minutes thermal treatments in a nitrogen ambient at various temperatures in a standard diffusion tube. It is clear that this new patent application describes a way to independently optimize the thermal treatment and the optical properties of buffer, core and cladding as to allow the thermal treatment optimization of the mechanical properties of the silica-based optical elements without any interaction with the optical properties stable of these optical elements:

FIG. 3d shows that the intense and small FWHM Siâ€”Oâ€”Si â€œrocking modeâ€ absorption peak (centred at 460 cm^âˆ’1) and Siâ€”Oâ€”Si â€œin-phase-stretching modeâ€ absorption peak (centred at 1080 cm^âˆ’1) of the fixed deposition pressure of 2.60 Torr of FIG. 3b and of the fixed PH₃flow rate of 0.50 std litre/min of the FIG. 3c is maintained as the temperature of the 30 minutes thermal treatments in a nitrogen ambient is gradually decreased from 900Â° C. to 600Â° C. This means that independently of the SiH₄gas flow of the N₂O gas flow of the N₂gas flow and of the PH₃gas flow and as long as the deposition pressure is fixed to 2.60 Torr, the basic FTIR spectra of silica-based optical components are not affected by the temperature variation (between 600Â° C. and 900Â° C.) of the 30 minutes thermal treatment in a nitrogen ambient;

FIG. 4d shows that the elimination of the Siâ€”OH oscillators (centered at 885 cm^âˆ’1) of the fixed deposition pressure of 2.60 Torr of FIG. 4b and of the fixed PH₃flow rate of 0.50 std litre/min of the FIG. 4c is maintained. FIG. 4d also shows that the elimination of the Siâ€”ON oscillators (centred at 950 cm^âˆ’1) of the fixed deposition pressure of 2.60 Torr of FIG. 4b and of the fixed PH₃flow rate of 0.50 std litre/min of the FIG. 4c is also maintained. This very spectacular improved elimination of the residual Siâ€”ON oscillators after a 30 minutes thermal treatment of only 600Â° C. contrasts with the upper-mentioned results of typical PECVD silica films of FIG. 4a which still incorporate a lot of Siâ€”ON oscillators even after a 180 minutes thermal treatment in a nitrogen ambient at a much higher temperature of 1100Â° C. This also contrasts with the upper-mentioned results of PECVD buffer (cladding) deposited at a non-optimized pressure of less than 2.40 Torr by our pending patent application â€˜Plasma Enhanced Chemical Vapour Deposition of low optical absorption silica films for Mux/Dmux optical devicesâ€™ of FIG. 4b which still incorporate a lot of Siâ€”ON oscillators even after a 180 minutes thermal treatment in a nitrogen ambient at a much higher temperature of 800Â° C. The optimum separation and deep valley between the Siâ€”Oâ€”Si â€œin-phase-stretching modeâ€ absorption peak (1080 cm^âˆ’1) and the Siâ€”Oâ€”Si â€œbending modeâ€ absorption peak (810 cm^âˆ’1) of the fixed deposition pressure of 2.60 Torr of FIG. 4b and of the fixed PH₃flow rate of 0.50 std litre/min of the FIG. 4c is also maintained. This means that this new technique allows the elimination of the Siâ€”OH oscillators and of the Siâ€”ON oscillators independently of the thermal treatment of buffer, core and cladding as to allow the thermal treatment optimization of the mechanical properties of the silica-based optical elements without any interaction with the Siâ€”OH oscillators and of the Siâ€”ON oscillators of these optical elements.

FIG. 5d shows the gradual appearance of the Pâ• O oscillators (centered at 1330 cm^âˆ’1and which does not have a higher harmonics which could cause optical absorption in the 1.30 to 1.55 Î¼m optical bands) as the temperature of the 30 minutes thermal treatment in a nitrogen ambient is increased from 600Â° C. to 900Â° C.

FIG. 6d shows that the elimination of the Nâ• N oscillators (centered at 1555 cm^âˆ’1) of the fixed deposition pressure of 2.60 Torr of FIG. 6b and of the fixed PH₃flow rate of 0.50 std litre/min of the FIG. 6c is maintained. This also contrasts with the upper-mentioned results of typical PECVD silica films of FIG. 6a which require a 180 minutes thermal treatment in a nitrogen ambient at a temperature of 1000Â° C. in order to achieve similar results. This also contrasts with the upper-mentioned results of PECVD buffer (cladding) deposited at a non-optimized pressure of less than 2.40 Torr by our pending patent application â€˜Plasma Enhanced Chemical Vapour Deposition of low optical absorption silica films for Mux/Dmux optical devicesâ€™ of FIG. 6b which still incorporate a lot of Nâ• N oscillators even after a 180 minutes thermal treatment in a nitrogen ambient at a much higher temperature of 800Â° C. This means that this new technique allows the elimination of the Nâ• N oscillators independently of the thermal treatment of buffer, core and cladding as to allow the thermal treatment optimization of the mechanical properties of the silica-based optical elements without any interaction with the Nâ• N oscillators of these optical elements.

FIG. 7d shows that the Siâ• O oscillators (centered at 1875 cm^âˆ’1) and the unknown oscillator (centered at 2010 cm^âˆ’1) of the fixed deposition pressure of 2.60 Torr of FIG. 7b and of the fixed PH₃flow rate of 0.50 std litre/min of the FIG. 7c are unchanged. These effects are not that important since only the fourth harmonics of the Siâ• O oscillators could absorb in the 1.30 to 1.55 Î¼m optical bands;

FIG. 8d shows that the elimination of the Siâ€”H oscillators (centered at 2260 cm^âˆ’1and which third harmonics could cause an optical absorption between 1.443 and 1.508 Î¼m) of the fixed deposition pressure of 2.60 Torr of FIG. 8b and of the fixed PH₃flow rate of 0.50 std litre/min of the FIG. 8c is maintained. This means that this new technique allows the elimination of the Siâ€”H oscillators independently of the thermal treatment of buffer, core and cladding as to allow the thermal treatment optimization of the mechanical properties of the silica-based optical elements without any interaction with the Siâ€”H oscillators of these optical elements.

FIG. 9d shows that the spectacular complete elimination of the Si:Nâ€”H oscillators (centered at 3380 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.515 Î¼m) of the fixed deposition pressure of 2.60 Torr of FIG. 9b and of the fixed PH₃flow rate of 0.50 std litre/min of the FIG. 9c is maintained. This contrasts with the upper-mentioned results of typical PECVD silica films of FIG. 9a which require a 180 minutes thermal treatment in a nitrogen ambient at a temperature of 1100Â° C. in order to achieve similar results. This also contrasts with the upper-mentioned results of PECVD buffer (cladding) deposited at a non-optimized pressure of less than 2.40 Torr by our pending patent application â€˜Plasma Enhanced Chemical Vapour Deposition of low optical absorption silica films for Mux/Dmux optical devicesâ€™ of FIG. 9b which still incorporate a lot of Si:Nâ€”H oscillators even after a 180 minutes thermal treatment in a nitrogen ambient at a much higher temperature of 800Â° C. FIG. 9d shows that the a spectacular complete elimination of the SiNâ€”H oscillators (centered at 3420 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.479 Î¼m) of the fixed deposition pressure of 2.60 Torr of FIG. 9b and of the fixed PH₃flow rate of 0.50 std litre/min of the FIG. 9c is also maintained. This contrasts with the upper-mentioned results of typical PECVD silica films of FIG. 9a which require a thermal treatment in a nitrogen ambient at a temperature of 1000Â° C. in order to achieve similar results. This also contrasts with the upper-mentioned results of PECVD buffer (cladding) deposited at a non-optimized pressure of less than 2.40 Torr by our pending patent application â€˜Plasma Enhanced Chemical Vapour Deposition of low optical absorption silica films for Mux/Dmux optical devicesâ€™ of FIG. 9b which still incorporate a lot of Si:Nâ€”H oscillators even after a 180 minutes thermal treatment in a nitrogen ambient at a much higher temperature of 800Â° C. FIG. 9d also shows that the complete elimination of the SiOâ€”H oscillators (centered at 3510 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.408 and 1.441 Î¼m) of the fixed deposition pressure of 2.60 Torr of FIG. 9b and of the fixed PH₃flow rate of 0.50 std litre/min of the FIG. 9c is maintained. This contrasts with the upper-mentioned results of typical PECVD silica films which require a thermal treatment in a nitrogen ambient at a temperature of 900Â° C. in order to achieve similar results. Finally, FIG. 9d also shows that the complete elimination of the HOâ€”H oscillators (centered at 3650 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.333 and 1.408 Î¼m) of the fixed deposition pressure of 2.60 Torr of FIG. 9b and of the fixed PH₃flow rate of 0.50 std litre/min of the FIG. 9c is maintained. This means that this new technique allows the elimination of the Si:Nâ€”H oscillators, of the SiNâ€”H oscillators, of the SiOâ€”H oscillators and of the HOâ€”H oscillators independently of the thermal treatment of buffer, core and cladding as to allow the thermal treatment optimization of the mechanical properties of the silica-based optical elements without any interaction with the Si:Nâ€”H oscillators, with the SiNâ€”H oscillators, with the SiOâ€”H oscillators or with the HOâ€”H oscillators of these optical elements.

It is clear from these various FTIR spectra that this technique allows the optimisation of the post-deposition thermal treatments of buffer (cladding) and core as to eliminate the various thermally-induced and stress-related residual mechanical problems.

Residual Stress-Induced Mechanical Problems at the Buffer/Core Interface or at the Core/Cladding Interface

The Stress Hysteresis of Buffer (Cladding) and Core

FIG. 10 shows the stress hysteresis in a nitrogen ambient of buffer (cladding) and core during the heating of the silicon wafer from room temperature to 800Â° C., during its stabilization for 180 minutes at 800Â° C. and during its natural cooling from 800Â° C. to room temperature.

FIG. 10 shows that the mechanical stress of buffer (cladding) is compressive at about âˆ’250 MPa prior to the stress hysteresis cycle; is compressive throughout the complete stress hysteresis cycle; decreases (almost linearly) as the temperature linearly increases (an expected situation since the (almost constant) coefficient of linear expansion of silica-based buffer (cladding) is smaller than the one of the underlying silicon; shows three plastic deformation regions during the stress hysteresis cycle (Region B1, from 450Â° C. to 575Â° C., where it decreases much faster than what is expected from a linear decrease associated with its elastic deformation; Region B2, from 575Â° C. to 650Â° C., where it is almost constant; Region B3, during the 180 minutes stabilization at 800Â° C., where it decreases as the temperature remains unchanged); and is compressive at about âˆ’150 MPa after the stress hysteresis cycle.

FIG. 10 shows that the mechanical stress of core is tensile at about 175 MPa prior to the stress hysteresis cycle; is tensile throughout the complete stress hysteresis cycle; increases (almost linearly) as the temperature linearly decreases (an expected situation since the (almost constant) coefficient of linear expansion of silica-based core is smaller than the one of the underlying silicon); shows two plastic deformation regions during the stress hysteresis cycle (Region C1, from 450Â° C. to 675Â° C., where it reverses its trends and in fact decreases as the temperature is increasing; Region C2, from 675Â° C. to 800Â° C., where it is almost constant); and is tensile at about 40 MPa after the stress hysteresis cycle.

FIG. 10 shows that the optical elements of the device are to be prepared from a (compressive stress buffer)/(tensile stress core) combination bi-layer after a 180 minutes thermal treatment in a nitrogen ambient at a reduced temperature of 800Â° C. To this particular combination are associated some residual stress-induced mechanical problems of deep-etched optical elements (mechanical movement of side-walls), some residual stress-induced mechanical problems at the buffer/core or core/cladding interfaces (micro-structural defects, micro-voiding and separation) and some residual stress-induced optical problems (polarisation dependant power loss).

Stress-Induced Mechanical Movement of the Side-Walls of Deep-Etched Optical Elements

Optical elements, such as gratings or waveguides, require deep-etched (compressive stress buffer)/(tensile stress core) with vertical side-walls and with a seamless buffer/core interface.

FIG. 11 shows SEM pictures of a grating and a waveguide with deep-etched vertical side-walls and with a seamless buffer/core interface deep-etched through buffer and core.

FIG. 12 shows a stress-relief mechanism involving the elastic strain of such a deep-etched (compressive stress buffer)/(tensile stress core) optical element. From this sequence of three graphical representations, it is clear that such a (compressive stress buffer)/(tensile stress core) deep-etched optical element will systematically result in a positively sloped elastic strain of the optical element's side-wall.

This stress-relieve mechanism shows that the lateral strain of the compressive stress buffer forces the deep-etched side-wall of buffer to move outward; and the lateral strain of the tensile stress core forces the deep-etched side-wall of core to move inward.

This combination of strains will systematically result in deep-etched (compressive stress buffer)/(tensile stress core) optical elements with a positive slope side-wall, i.e. a side-wall with an angle smaller than 90Â°.

To estimate the amplitude of this effect, lets consider the hypothetical of zero bonding at the buffer/(Silicon wafer) interface, of zero bonding at the buffer/core interface, and of zero bonding at the buffer/core interface. The outward elastic strain of the side-wall of the compressive stress buffer, Îµ_B, and the inward elastic strain of the side-wall of the tensile stress core, Îµ_C, would simply be:
Îµ_B=Ïƒ_B/Î•_B; Îµ_C=Ïƒ_C/Î•_C

where Ïƒ_Band E_Bare respectively the mechanical stress and the modulus of elasticity of buffer and where Ïƒ_Cand E_Care respectively the mechanical stress and the modulus of elasticity of core.

The modulus of elasticity of silica thin films measured by micro-indentation and measured by electrostatic membrane deflection are respectively reported as 70 GPa and 69 GPa in the following two references: Thin Solid Films, Vol. 283, p. 15, (1996); IEEE Transactions on Electron Devices, Vol. ED25, No.10, p.1249, (1978)

To the âˆ’150 MPa compressive stress of buffer and 40 MPa tensile stress of core reported in FIG. 10 at room temperature would then be associated a strain of about âˆ’0.21% (âˆ’0.15 GPa/70 GPa) for buffer and of about 0.057% (0.040 GPa/70 GPa) for core. The negative sign indicates that the strain is outward.

This means that the buffer portion of a 5.0 Î¼m wide deep-etched waveguide not bonded to the underlying silicon wafer and not bonded to the core portion of the same deep-etched waveguide would laterally expand by about 0.011 Î¼m (0.21% of 5 Î¼m) and that the buffer portion of a 1150 Î¼m wide deep-etched grating not bonded to the underlying silicon wafer and not bonded to the core portion of the same deep-etched grating would laterally expand by about 2.46 Î¼m (0.21% of 1150 Î¼m). Similarily the core portion of the 5.0 Î¼m wide deep-etched waveguide not bonded to the underlying buffer portion of the same deep-etched waveguide would laterally expand by about 0.0029 Î¼m (0.057% of 5 Î¼m) and that the core portion of a 1150 Î¼m wide deep-etched grating not bonded to the underlying buffer portion of the same deep-etched grating would laterally expand by about 0.66 Î¼m (0.057% of 1150 Î¼m).

In reality, since buffer is bonded to the underlying silicon wafer and to the upper core at the buffer/core interface, the effect of the outward strain of buffer and of the inward strain of core would be observed as a noticeably different sloped side-wall for a narrow waveguide and for a wide grating.

If we assume a 2.0 Î¼m deep-etched buffer and a 5.0 Î¼m deep-etch core then the single-sided strain of the upper core surface of the 5.0 Î¼m wide deep-etched waveguide and of the 1150 Î¼m wide deep-etched grating could be as high as 0.0070 Î¼m (50% of (0.011+0.0029 Î¼m)) and 1.56 Î¼m (50% of (2.46+0.66 Î¼m)) respectively with respect to the bottom of the resulting 7.0 Î¼m deep-etch optical element. The expected 89.9Â° (90Â°-arctan(0.0070 Î¼m/7.0 Î¼m)) side-wall slope of the deep-etched waveguide would not be noticeable on a SEM picture but the expected 77.4Â° (90Â°-arctan(1.56 Î¼m/7.0 Î¼m)) side-wall slope of the deep-etched grating would certainly be easy to see on a SEM picture.

FIG. 13 shows four SEM pictures. The first two SEM pictures show the relative position between an isolated 5.0 Î¼m wide deep-etched waveguide and its neighboring 1150 Î¼m wide deep-etched grating at two different magnifications. The third SEM picture confirms that side-wall of the 5.0 Î¼m wide deep-etched waveguide facing the neighboring grating has a slope of about 90Â°. The fourth SEM picture confirms that side-wall of the 1150 Î¼m wide deep-etched grating facing the neighboring deep-etched waveguide has a much smaller slope of about 84Â°, slightly larger than the expected 77.4Â° slope. The difference between the measured and expected values will be discussed below.

The mechanical stress of buffer and core must be minimized as to maintain the ideal verticality of the side-wall of the waveguides, of the grating and of the other integrated optical elements of the optical device and allow minimum power loss from undesirable reflection and refraction of the infrared optical beams at the side-wall of these optical elements.

Stress-Induced Micro-Structural Defects at the Buffer/Core Interface or at the Core/Cladding Interface

FIG. 14 shows a graphical representation of the variable intensity shear stress building at the (compressive stress buffer)/(tensile stress core) interface and at the (tensile stress core)/(compressive stress cladding) interface during the stress hysteresis cycle of FIG. 10 and during the various thermal treatments in a nitrogen ambient.

If the bonding of the buffer/core interface or of the core/cladding interface is strong enough, the exposure of the various optical elements to the various thermal treatments in a nitrogen ambient can result in a modification of the micro-structure near these interfaces.

FIG. 14 also shows some SEM pictures demonstrating the induced modification of the microstructure of core near these buffer/core and core/cladding interfaces.

Stress-Induced Micro-Voiding at the Buffer/Core Interface or at the Core/Cladding Interface

FIG. 15 shows a graphical representation of the variable intensity shear stress building at the (compressive stress buffer)/(tensile stress core) interface and at the (tensile stress core)/(compressive stress cladding) interface during the stress hysteresis cycle of FIG. 10 and during the various thermal treatments in a nitrogen ambient. In this case, the intensity of the shear stress is such that it results in the formation of micro-voids in core and near the interfaces as an interfacial stress relief mechanism. These micro-voids are delineated during wafer preparation for SEM using a very light acid dip etch before loading in the electronic microscope.

If the bonding of the buffer/core interface or of the core/cladding interface is strong enough, the exposure of the various optical elements to the various thermal treatments in a nitrogen ambient can result in such a modification of the micro-structure near these interfaces that micro-voids are forming in core and near these interfaces.

FIG. 15 also shows some SEM pictures demonstrating that the induced modification of the microstructure of core near these buffer/core and core/cladding interfaces is cause the formation of micro-voids. It is clear on these SEM pictures that the micro-voids are generated and aligned horizontally in a plane about 0.5 Î¼m away from the buffer/core interface. This is not that surprising since the transition from the (compressive stress buffer) to the (tensile stress core) is not absolutely abrupt at the interface and since micro-voids cannot form in a material under compressive stress.

Stress-Induced Separation at the Buffer/Core Interface or at the Core/Cladding Interface

FIG. 16 shows some SEM pictures which demonstrate the stress relief of the variable intensity shear stress building at the (compressive stress buffer)/(tensile stress core) interface and at the (tensile stress core)/(compressive stress cladding) interface during the stress hysteresis cycle of FIG. 10, during the various thermal treatments in a nitrogen ambient or simply during wafer cleavage for SEM pictures.

In this case, the bonding of the buffer/core interface (or core/cladding interface) is not strong enough anymore and core partially slip on buffer at the buffer/core interface (or cladding partially delaminate from core at the core/cladding interface).

In one particular case, the interface separation is only observed between core and buffer, indicating that core contraction is the root cause of the delamination.

The second SEM picture of FIG. 16 shows the contraction of the 1150 Î¼m wide grating. It is clear from this picture that a portion of core has slipped aside over buffer and over a distance of about 0.40 Î¼m at the periphery of the grating. This is in line with the upper calculated contraction of 0.66 Î¼m. The slip is again initiated from a point located at the tip of the seam of the cladding and slightly away from the buffer/core interface from which a crack did propagate horizontally in core and about 0.5 Î¼m away from the buffer/core interface. Since a crack cannot propagate in a material under compressive stress, this crack propagation did require core to be in tensile stress. Since the transition from the compressive stress buffer to the tensile stress core is not absolutely abrupt at the interface, it is normal to see the crack initiation slightly away from the buffer/core interface. The tensile stress-relief mechanism of core has partially releases its energy by propagating a 0.40 Î¼m long crack in core and by allowing its side-wall to slip by 0.40 Î¼m. This lateral of core explains the difference between the observed 84Â° of FIG. 13 and the expected 77Â° from the upper calculation of the expected side-wall slope.

Optimised Stress-Releasing Process of Buffer (Cladding) and Core

It is clearly demonstrated that the mechanical stresses of core, buffer and cladding play a key role in the side-wall slope of deep-etched optical elements.

It is also clearly demonstrated from these various FTIR spectra, from the stress hysteresis of buffer, core and cladding and from the various presented SEM pictures that the optimization of the thermal treatments (i.e. the use of the Regions B1, B2, B3, C1 and C2 of the stress hysteresis of FIG. 10) is key to achieving the required â€˜delta-nâ€™; and reducing the optical absorption in the 1.55 Î¼m wavelength (and/or 1.30 wavelength) associated with the following undesirable residual oscillators: Si:Nâ€”H oscillators (observed as a FTIR peak centered at 3380 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.515 Î¼m); SiNâ€”H oscillators (centered at 3420 cm^âˆ’1whose 2^ndharmonics could cause an optical absorption between 1.445 and 1.479 Î¼m); SiOâ€”H oscillators (centered at 3510 cm^âˆ’1and whose 2^ndharmonics could cause an optical absorption between 1.408 and 1.441 Î¼m); and eliminating the residual stress of deep-etched optical elements in core. This results in mechanical movement of core side-walls; micro-structural defects, micro-voiding and separation at the buffer/core or core/cladding interfaces; residual stress-induced optical problems

Description of the Required Buffer/Core/Cladding Optical Elements Structure

An example of the required buffer/core/cladding optical elements structure is shown in FIG. 17. It consists in a 10 Î¼m thick buffer 12 followed by a deep-etched 5 Î¼m thick core 20 and followed by a 10 Î¼m thick cladding 22.

In reality, to perform this optical elements structure, the following steps should be carried out as shown in FIGS. 18a to 18l:

FIG. 18a shows that in order to eliminate the marks left by the wafer holder of the PECVD equipment on the front face of the wafer during the deposition of a 10.0 Î¼m buffer on the back face of the wafer, a 0.5 Î¼m thick sacrificial buffer 30 is deposited on, and later removed from, the front face of the wafer.

As discussed in one of our co-pending patent application Ser. No. 09/799 FIG. 18b shows that in order to prevent the wafer warp pr various thermal treatments a 10.0 Î¼m thick buffer 14 is deposited on the back face of the silicon wafer to compensate for the 10.0 Î¼m to be deposited on the front face of the wafer;

FIG. 18c shows that in order to protect the buffer on the back face of the wafer during the wet-etch of the 0.5 Î¼m thick sacrificial buffer on the front face of the wafer, a 0.5 Î¼m thick layer of PECVD nitride 32 is deposited on the back face of the wafer. About 0.1 Î¼m of the 0.5 Î¼m thick layer of PECVD nitride will be removed on the back face of the wafer during the subsequent wet-etch of the 0.5 Î¼m thick sacrificial buffer on the front face of the wafer;

FIG. 18d shows that in order to remove the sacrificial 0.5 Î¼m thick buffer on the front face of the wafer and the undesirable marks left by the wafer holder of the PECVD equipment an non-patterned wet-etch is performed simultaneously on both faces of the wafer. This wet-etch removes all of the 0.5 Î¼m think buffer on the front face of the wafer and about 0.1 Î¼m of the 0.5 Î¼m thick PECVD silicon nitride deposited on the back face of the wafer;

FIG. 18e shows that in order to compensate for the remaining 0.4 Î¼m of PECVD silicon nitride on the back face of the wafer and to prevent the wafer warp problem associated with the various thermal treatments a 0.3 Î¼m thick PECVD silicon nitride layer 18 on the front face of the wafer (the difference of 0.1 Î¼m is to take into account another removal of about 0.1 Î¼m of PECVD silicon nitride in a later wet-etch step of the process).

FIG. 18f shows that in order to produce the first layer of the optical elements, a 10.0 Î¼m thick buffer layer 12 is deposited on the front face of the wafer.

FIG. 18g shows that in order to achieve the required optical and mechanical properties of buffer, the first optimized thermal treatment should preferably be carried out on the above-formed structure consisting of 10.0 Î¼m thick buffer 12 on the front face of the wafer 10, its equivalent 10.0 Î¼m thick buffer 14 on the back face of the wafer, a remaining 0.4 Î¼m thick PECVD silicon nitride layer 16 on the back face of the wafer, and a compensating 0.3 Î¼m thick PECVD silicon nitride layer 18 on the front face of the wafer;

FIG. 18h shows that in order to produce the first layer of the optical elements, a 5.0 Î¼m thick core 20 is desposited on the front face of the wafer.

FIG. 18i shows that in order to achieve the required optical and mechanical properties of core, the second optimized thermal treatment should be performed on the 5.0 Î¼m thick core 20 on the front face of the wafer, the underlying 10.0 Î¼m thick buffer 12 on the front face of the wafer, its equivalent 10.0 Î¼m thick buffer 14 von the back face of the wafer, the remaining 0.4 Î¼m thick PECVD silicon nitride layer 16 on the back face of the wafer, the compensating 0.3 Î¼m thick PECVD silicon nitride layer 18 on the front face of the wafer;

FIG. 18j shows that in order to define the optical elements, the 5.0 Î¼m thick core on the front face of the wafer patterned and deep-etched with a small penetration of about 2.0 Î¼m into the 10.0 Î¼m thick buffer.

FIG. 18k shows that in order to produce the third layer of the optical elements, a 10.0 Î¼m thick cladding layer 22 is deposited on the front face of the wafer.

FIG. 18l shows that in order to define the optical elements, it is necessary to pattern and wet-etch the 10.0 Î¼m thick cladding 22 on the front face of the wafer while protecting the 10.0 Î¼m thick buffer on the back face of the wafer with the remaining 0.4 Î¼m of PECVD silicon nitride on the back face of the wafer which will be consumed by about 0.1 Î¼m as to finish with a residual 0.3 Î¼m of PECVD silicon nitride on the back face of the wafer.

The two optimized thermal treatments of FIG. 18g, and FIG. 18i allow the optimized optical and mechanical properties of the optical elements.

Description of the First Optimised Thermal Treatment:

The first optimized thermal treatment is required to achieve the required optical and mechanical properties of buffer.

FIG. 18g shows that the first optimized thermal treatment of this is performed on a structure comprising a 10.0 Î¼m thick buffer on the front face of the wafer, an equivalent 10.0 Î¼m thick buffer on the back face of the wafer, a remaining 0.4 Î¼m thick PECVD silicon nitride on the back face of the wafer, and a compensating 0.3 Î¼m thick PECVD silicon nitride on the front face of the wafer.

The goal of this first optimized thermal treatment is to reduce the optical absorption, the wafer warp and the compressive stress of buffer.

Reduction of Optical Absorption of Buffer Following a Thermal Treatment:

It is clear from FIG. 9a that it is important to reach a temperature of at least 1100Â° C. to eliminate the optical absorption of typical PECVD buffer.

It is clear from FIG. 9b that our patent application titled â€˜Plasma Enhanced Chemical Vapour deposition of low optical silica films for Mux/Dmux optical devicesâ€™ allows the minimum temperature to be reduced to about 800Â° C. in order to eliminate the optical absorption of these special buffer deposited by this patent pending technique.

So, a thermal treatment temperature of at least 800Â° C. will ensure the elimination of the optical absorption of these special buffer deposited by this patent pending technique.

Reduction of Wafer Warp Due to a Thermal Treatment of Buffer:

FIG. 18g uses the principles of our patent application titled â€˜A Technique to Allow the Manufacturing of Silica Waveguides in MUX/DMUX Optical Devicesâ€™ and a structure consisting of a 10.0 Î¼m thick buffer on the front face of the wafer, its equivalent 10.0 Î¼m thick buffer on the back face of the wafer, a remaining 0.4 Î¼m thick PECVD silicon nitride on the back face of the wafer, and a compensating 0.3 Î¼m thick PECVD silicon nitride on the front face of the wafer.

This structure prevents the wafer warp problem associated with the thermal treatment to be performed on the 10.0 Î¼m thick buffer on the back face of the silicon wafer. The symmetry of films on the front face as well as on the back face of the silicon wafer allows the use of a wide variety of thermal treatments without the associated wafer warp problem.

Reduction of the Compressive Mechanical Stress of Buffer Following the First Optimised Thermal Treatment:

It is clear from FIG. 10 that the mechanical stress of buffer is compressive at about âˆ’250 MPa prior to the stress hysteresis cycle and following its Plasma Enhanced Chemical Vapor Deposition at a substrate temperature of 400Â° C. and following its cooling at room temperature; follows an elastic deformation and decreases linearly as the temperature is increased linearly from room temperature to about 450Â° C., an expected situation since the coefficient of linear expansion of silica-based buffer is smaller than the one of the underlying silicon; follows three plastic deformations during the stress hysteresis cycle up to 800Â° C. (Region B1, from 450Â° C. to 575Â° C., where the compressive mechanical stress decreases much faster than what is expected from a linear decrease associated with its elastic deformation; Region B2, from 575Â° C. to 650Â° C., where the compressive mechanical stress is almost constant; and Region B3, during the 180 minutes stabilization at 800Â° C., where the compressive mechanical stress gradually decreases as the temperature remains unchanged at 800Â° C.); follows another elastic deformation and increases linearly as the temperature is decreased linearly from 800Â° C. to room temperature, an expected situation since the coefficient of linear expansion of silica-based buffer is smaller than the one of the underlying silicon; and is still compressive at about âˆ’150 MPa after the stress hysteresis cycle up to 800Â° C.

The compressive mechanical stress of buffer prior to the thermal treatment is well in control at about âˆ’250 MPa. In order to reduce its compressive mechanical stress and to prevent the upper-discussed mechanical problems reported in FIG. 12, FIG. 13, FIG. 14, FIG. 15 and FIG. 16 following the deep-etch of FIG. 18j, it is necessary to make sure that all wafers are exposed to the exact same optimized thermal treatment, particularly in the regions B1, B2 and B3 of FIG. 10; make sure that the maximum temperature of the thermal treatment exceeds 800Â° C. as to reduce even more the room temperature compressive stress following the elastic deformation as the temperature is decreased linearly from the maximum temperature to room temperature (Cooling to RT of FIG. 10); and make sure that the duration of the thermal treatment at the maximum temperature is long enough as to allow the compressive stress to relax (Region B3 of FIG. 10).

The temperature profile of the first optimized thermal treatment is shown on FIG. 19. This optimized thermal treatment is characterized by a constant flow of 10 liters/minute of nitrogen throughout the process; a 13 minutes duration wafer push into a diffusion tube stabilized at a temperature of 400Â° C. (This stabilization temperature of 400Â° C. is important since each one of the 125 wafers of a load sees a slightly different temperature profile up to this stabilization temperature during the 13 minutes duration wafer push step of FIG. 19. Since this stabilization temperature of 400Â° C. is lower than the minimum temperature of 450Â° C. causing the first plastic deformation associated with region B1 of FIG. 10, the slight variation of temperature profile from wafer-to-wafer will have no effect on the post-thermal-treatment mechanical stress); a 10 minutes stabilization time prior ramp-up of the temperature of the diffusion tube; a controlled ramp-up at a rate of 5Â° C./minute up to the maximum thermal treatment temperature of 900Â° C. in order to cross the Region B1 and Region B2 of FIG. 10 in a controlled and repeatable fashion for all of the wafers in the load; a 180 minutes duration thermal treatment at the maximum thermal treatment temperature of 900Â° C. in order to allow a repeatable stress relaxation in the Region B3 of FIG. 10 for all of the wafers in the load; a controlled ramp-down at a rate of 2.5Â° C./minute down to 400Â° C. in order to control the cooling rate and the (nitrogen) ambient as to reproduce the elastic behavior of FIG. 10 for all of the wafers in the load; and a 13 minutes duration wafer pull from the diffusion tube stabilized at a temperature of 400Â° C.

Description of the Second Optimised Thermal Treatment:

The second optimized thermal treatment is required as to achieve the required optical and mechanical properties of core.

FIG. 18i shows that the second optimized thermal treatment of this patent application is performed on a structure comprising a 10.0 Î¼m thick buffer on the front face of the wafer, its equivalent 10.0 Î¼m thick buffer on the back face of the wafer, a remaining 0.4 Î¼m thick PECVD silicon nitride on the back face of the wafer, a compensating 0.3 Î¼m thick PECVD silicon nitride on the front face of the wafer, and a 5.0 Î¼m thick core on the front face of the wafer.

The goal of this second optimized thermal treatment is to reduce the optical absorption, the wafer warp and the tensile stress of core.

Reduction of Optical Absorption of Core Following a Thermal Treatment:

It is clear from FIG. 9c that our patent application titled â€˜Silica waveguides for Mux/Dmux optical devicesâ€™ allows the achievement of excellent optical quality core following a 180 minutes thermal treatment in a nitrogen ambient at a reduced temperature of 800Â° C.

It is clear from FIG. 9d that our patent application titled â€˜A technique to optimize the optical and mechanical properties of silica-based optical elements in integrated optical devicesâ€™ allows the optimization of the temperature of the thermal treatment as to simultaneously minimize the optical absorption and the mechanical stress of core.

Reduction of the Tensile Mechanical Stress of Core Following the Second Optimised Thermal Treatment:

It is can be seen from FIG. 10 that the mechanical stress of core is tensile at about 175 MPa prior to the stress hysteresis cycle and following its Plasma Enhanced Chemical Vapor Deposition at a substrate temperature of 400Â° C. and following its cooling at room temperature; follows an elastic deformation and decreases linearly as the temperature is increased linearly from room temperature to about 450Â° C., an expected situation since the coefficient of linear expansion of silica-based core is smaller than the one of the underlying silicon; follows two plastic deformations during the stress hysteresis cycle up to 800Â° C. (Region C1, from 450Â° C. to 675Â° C., where the tensile mechanical stress decreases as the temperature is increased; Region C2, from 675Â° C. to 800Â° C., where the tensile mechanical stress is almost constant); follows another elastic deformation and increases linearly as the temperature is decreased linearly from 800Â° C. to room temperature, an expected situation since the coefficient of linear expansion of silica-based core is smaller than the one of the underlying silicon; and is still tensile at about 40 MPa after the stress hysteresis cycle up to 800Â° C.

The tensile mechanical stress of core prior to the thermal treatment is well in control at about 175 MPa. In order to reduce its tensile mechanical stress and to prevent the upper-discussed mechanical problems reported in FIG. 12, FIG. 13, FIG. 14, FIG. 15 and FIG. 16 following the deep-etch of FIG. 18j, it is necessary to make sure that all wafers are exposed to the exact same optimized thermal treatment, particularly in the regions C1 and C2 of FIG. 10; make sure that the maximum temperature of the thermal treatment exceeds 800Â° C. as to reduce even more the room temperature tensile stress following the elastic deformation as the temperature is decreased linearly from the maximum temperature to room temperature (Cooling to RT of FIG. 10); and make sure that the duration of the thermal treatment at the maximum temperature is long enough as to allow the tensile stress to relax (Region C2 of FIG. 10).

The temperature profile of the second optimized thermal treatment is shown on FIG. 20. This optimized thermal treatment is characterized by a constant flow of 10 liters/minute of nitrogen throughout the process; a 13 minutes duration wafer push into a diffusion tube stabilized at a temperature of 400Â° C. (This stabilization temperature of 400Â° C. is important since each one of the 125 wafers of a load sees a slightly different temperature profile up to this stabilization temperature during the 13 minutes duration wafer push step of FIG. 20. Since this stabilization temperature of 400Â° C. is lower than the minimum temperature of 450Â° C. causing the first plastic deformation associated with region C1 of FIG. 10;, the slight variation of temperature profile from wafer-to-wafer will have no effect on the post-thermal-treatment mechanical stress); a 10 minutes stabilization time prior ramp-up of the temperature of the diffusion tube; a controlled ramp-up at a rate of 5Â° C./minute up to the maximum thermal treatment temperature of 900Â° C. in order to cross the Region C1 and Region C2 of FIG. 10 in a controlled and repeatable fashion for all of the wafers in the load; a 180 minutes duration thermal treatment at the maximum thermal treatment temperature of 900Â° C. in order to allow a repeatable stress relaxation in the Region C2 of FIG. 10 for all of the wafers in the load; a controlled ramp-down at a rate of 2.5Â° C./minute down to 400Â° C. in order to control the cooling rate and the (nitrogen) ambient as to reproduce the elastic behavior of FIG. 10 for all of the wafers in the load; and a 13 minutes duration wafer pull from the diffusion tube stabilized at a temperature of 400Â° C.

Demonstration of the Stress-Releasing Process of the Buffer/Core Structure

FIG. 21 shows the shape of the silicon wafer before any processing. The relatively flat shape is typical of a SEMI standard silicon wafer.

FIG. 22 shows the shape of the same silicon wafer just after the deposition of the 5.0 Î¼m thick core on the front face of the wafer, i.e. at the process step corresponding to FIG. 18h. It is clear that the tensile mechanical stress of core is causing the silicon wafer to warp upward in a U shape.

FIG. 23 shows the shape of the same silicon wafer just after the second optimized thermal, i.e. at the process step corresponding to FIG. 18i. It is clear that the shape of the silicon wafer returns to its initial shape and that the overall structure is completely stress-released after this second optimized thermal treatment.

The deep-etch of the structure associated to FIG. 18j can now be performed without the associated mechanical problems reported in FIG. 12, FIG. 13, FIG. 14, FIG. 15 and FIG. 16.

It will be seen that these optimised thermal treatments allow the elimination of these residual stress-induced mechanical problems of deep-etched optical elements (mechanical movement of the side-walls), of these residual stress-induced mechanical problems at the buffer/core interface or at the core/cladding interface (micro-structural defects, micro-voiding and separation) and of these residual stress-induced optical problems (polarisation dependant power loss) without the wafer warp problem following the optimised process.

Wafers in accordance with the invention are preferably made using the technique described in our co-pending co-our pending patent application Ser. No. 09/799, 491 describes a technique involving the deposition of thick PECVD silica films on the back face of the silicon wafer in order to prevent the wafer warp problem associated with the required high temperature thermal treatments required to achieve low optical absorption silica film.

As discussed the invention involves the use of the two optimized heat treatments of FIG. 19 and FIG. 20.

It is clear from the FTIR spectra of: FIG. 3d, FIG. 4d, FIG. 5d, FIG. 6d, FIG. 7d, FIG. 8d, & FIG. 9d, from the stress hysteresis of buffer, core and cladding of FIG. 10 and from the wafer curvature results of FIG. 21, FIG. 22 and FIG. 23 that this new technique is key to achieve the required â€˜delta-nâ€™ while eliminating the undesirable residual Si:Nâ€”H oscillators, SiNâ€”H oscillators and SiOâ€”H oscillators after the two optimised thermal treatments of FIG. 19 and FIG. 20 which can provide improved silica-based optical elements with reduced optical absorption in the 1.55 Î¼m wavelength (and/or 1.30 wavelength) optical region and without the residual stress-induced mechanical problems reported in FIG. 12, FIG. 13, FIG. 14, FIG. 15 and FIG. 16 of deep-etched optical elements.

It will be appreciated by one skilled in the art that many variations of the present invention are possible.

Variations Concerning the PECVD Deposition:

The PECVD equipment could be different from the Novellus Concept One. The basic requirement is to provide independent control of the four basic control parameters: SiH₄gas flow rate, N₂O gas flow rate, N₂gas flow rate and total deposition pressure. The PECVD silica films could be deposited at a temperature different than 400Â° C. It could be deposited at any temperature between 100 and 650Â° C.

The SiH₄silicon raw material gas could be replaced by an alternate silicon containing gas, such as: silicon tetra-chloride, SiCl₄, silicon tetra-fluoride, SiF₄, disilane, Si₂H₆, dichloro-silane, SiH₂Cl₂, chloro-fluoro-silane SiCl₂F₂, difluoro-silane, SiH₂F₂or any other silicon containing gases involving the use of hydrogen, H, chlorine, Cl, fluorine, F, bromine, Br, and iodine, I;

The N₂O oxidation gas could be replaced by an alternate oxygen containing gas, such as: oxygen, O₂, nitric oxide, NO₂, water, H₂O, hydrogen peroxide, H₂O₂, carbon monoxide, CO or carbon dioxide, CO₂;

The N₂carrier gas could be replaced by an alternate carrier gas, such as: helium, He, neon, Ne, argon, Ar or krypton, Kr;

The PH₃doping gas could be replaced by an alternate gas, such as: diborane, B₂H₆, Arsine (AsH₃), Titanium hydride, TiH₄or germane, GeH₄, Silicon Tetrafluoride, SiF₄of carbon tetrafluoride, CF₄;

Variations Concerning Buffer (Cladding):

The buffer (cladding) local optimum (SiH₄gas flow of 0.20 std litre/min, N₂O gas flow of 6.00 std litre/min, N₂gas flow of 3.15 std litre/min and a total deposition pressure of 2.60 Torr) is this four-independent-variables space could have a different set of coordinates (SiH₄, N₂O, N₂, deposition pressure) using the same Novellus Concept One equipment;

The buffer (cladding) local optimum could have a different set of coordinates (SiH₄, N₂O, N₂, deposition pressure) in different PECVD equipment.

The 0.5 Î¼m thick sacrificial buffer on the front face of the wafer could be as thin as 0.01 Î¼m and as thick as 10 Î¼m.

The 10.0 Î¼m thick buffer on the back face of the silicon wafer could be as thin as 1.0 Î¼m and as thick as 100.0 Î¼m if buffer on the front face of the silicon wafer is as thin as 1.0 Î¼m and as thick as 100.0 Î¼m. In all cases, the goal is to deposit about the same thickness on both faces as to compensate their mechanical properties.

The 10.0 Î¼m thick buffer deposited on the front face of the wafer in order to produce the optical elements could be as thin as 1.0 Î¼m and as thick as 100.0 Î¼m.

The 10.0 Î¼m thick cladding deposited on the front face of the wafer in order to produce the optical elements could be as thin as 1.0 Î¼m and as thick as 100.0 Î¼m.

The wet-etch removing all of the 0.5 Î¼m think buffer on the front face of the wafer could remove as little as 0.01 Î¼m and as much as 10 Î¼m of PECVD silicon nitride deposited on the back face of the wafer.

Variations Concerning the Core

The core local optimum (SiH₄gas flow of 0.20 std litre/min, N₂O gas flow of 6.00 std litre/min, N₂gas flow of 3.15 std litre/min, PH₃gas flow of 0.57 std litre/min, and a total deposition pressure of 2.60 Torr) is this five-independent-variables space could have a different set of coordinates (SiH₄, N₂O, N₂, PH₃, deposition pressure) using the same Novellus Concept One equipment.

The core local optimum could have a different set of coordinates (SiH₄, N₂O, N₂, PH₃, deposition pressure) in another PECVD equipment.

The 5.0 Î¼m thick core deposited on the front face of the wafer in order to produce the first layer of the optical elements could be as thin as 0.5 Î¼m and as thick as 50.0 Î¼m.

The pattern and deep-etch of the core on the front face of the wafer in order to define the optical elements could have a penetration as small as 0.2 Î¼m and as large as 20.0 Î¼m into the underlying buffer.

Variations Concerning PECVD Nitride:

The 0.5 Î¼m thick layer of PECVD nitride deposited on the back face of the wafer could be as thin as 0.01 Î¼m and as thick as 10 Î¼m.

The 0.3 Î¼m thick layer of PECVD nitride deposited on the front face of the wafer could be as thin as 0.01 Î¼m and as thick as 10 Î¼m.

Variations Concerning the Mechanical Stress of Buffer:

The âˆ’250 MPa compressive mechanical stress of as deposited buffer could be tensile up to +250 MPa or compressive up to âˆ’750 MPa.

The stress hysteresis cycle of buffer up to 800Â° C. could be different than the one reported in FIG. 10.

The âˆ’150 MPa compressive mechanical stress of thermally treated buffer could be tensile up to +150 MPa or compressive up to âˆ’450 MPa.

Variations Concerning the First Optimized Thermal Treatment:

The 10 liters/minute of nitrogen constant flow could be as 1 liter/minute and as high as 100 liters/minute.

The 13 minutes duration wafer push into a diffusion tube could be as short as 1.3 minutes and as long as 130 minutes.

The 400Â° C. stabilization temperature of the tube could be as low as 300Â° C. and as high as 700Â° C.

The 10 minutes stabilization time prior ramp-up of the temperature of the diffusion tube could be eliminated or increased up to 100 minutes.

The 5Â° C./minute controlled ramp-up could be decreased down 1Â° C./minute or increased up to 25Â° C./minute.

The 900Â° C. maximum thermal treatment temperature could be as low 800Â° C. and as high as 1300Â° C.

The 180 minutes duration thermal treatment at the maximum thermal treatment temperature could be reduced to 30 minutes or increased to 24 hours.

The 2.5Â° C./minute controlled ramp-down could be decreased down 1Â° C./minute or increased up to 25Â° C./minute.

The 13 minutes duration wafer pull from the diffusion tube could be as short as 1.3 minutes and as long as 130 minutes.

The nitrogen ambient could be replaced by other ambient gases such as: oxygen, O₂, hydrogen, H₂, water vapour, H₂O, argon, Ar, fluorine, F₂, carbon tetrafluoride, CF₄, nitrogen trifluoride, NF₃, hydrogen peroxide, H₂O₂

Variations Concerning the Second Optimized Thermal Treatment

The 10 liters/minute of nitrogen constant flow could be as 1 liter/minute and as high as 100 liters/minute.

The 13 minutes duration wafer push into a diffusion tube could be as short as 1.3 minutes and as long as 130 minutes.

The 400Â° C. stabilization temperature of the tube could be as low as 300Â° C. and as high as 700Â° C.

The 10 minutes stabilization time prior ramp-up of the temperature of the diffusion tube could be eliminated or increased up to 100 minutes.

The 5Â° C./minute controlled ramp-up could be decreased down 1Â° C./minute or increased up to 25Â° C./minute.

The 900Â° C. maximum thermal treatment temperature could be as low 600Â° C. and as high as 1300Â° C.

The 180 minutes duration thermal treatment at the maximum thermal treatment temperature could be reduced to 30 minutes or increased to 24 hours.

The 2.5Â° C./minute controlled ramp-down could be decreased down 1Â° C./minute or increased up to 25Â° C./minute.

The 13 minutes duration wafer pull from the diffusion tube could be as short as 1.3 minutes and as long as 130 minutes.

The nitrogen ambient could be replaced by other ambient gases such as: oxygen, O₂, hydrogen, H₂, water vapour, H₂O, argon, Ar, fluorine, F₂, carbon tetrafluoride, CF₄, nitrogen trifluoride, NF₃, hydrogen peroxide, H₂O₂

Variations Concerning the Mechanical Stress of Core:

The +175 MPa tensile mechanical stress of as deposited core could be compressive up to âˆ’325 MPa or tensile up to +675 MPa.

The stress hysteresis cycle of core up to 800Â° C. could be different from the one reported in FIG. 10.

The +40 MPa tensile mechanical stress of thermally treated core could be compressive up to âˆ’60 MPa or tensile up to +140 MPa.

The invention has many applications and can be use to manufacture Mux or Dmux devices, or other devices such as Add-After-Drop Filters (AADF) devices; arrayed Wave Guide (AWG) and Arrayed Wave Guide Grating (AWGG) devices; Athermal Arrayed Wave Guide (AAWGG) devices; charged Coupled Devices (CCD) devices; Distributed Feedback Laser Diode (DFB-LD) devices; Erbium Doped Fiber Amplifier (EDFA) devices; Fiber-To-The-Home (FTTH) application devices; Four Wave Mixing (FWM) devices; Fresnel Mirror (FM) devices; Laser Diode (LD) devices; Light Emitting Diodes (LED) devices; Mach-Zenhder (MZ), Mach-Zenhder Interferometer (MZI), Mach-Zenhder Interferometer Multiplexer (MZIM) devices; Micro-Opto-Electro-Mechanical Systems (MOEMS) devices; Monitor Photo Diode (MPD) devices; Multi-Wavelength Optical Sources (MWOS) devices; Optical Add/Drop Multiplexers (OADM) devices; Optical Amplifier (AF) devices; Optical Cross-Connect (OCC, OXC) devices; Optical Cross Point (OCP) devices; Optical Filter (OF) devices; Optical Interferometer (OI) devices; Optical Network Unit (ONU) devices; Optical Saw Wave (OSW) devices; Optical Splitter (OS) devices; Optical Switch (OSW) and Optical Switch Module (OSM) devices; Photonic ATM (PATM) switching devices; Planar Lightwave Circuits (PLC) devices; Positive Emitter Coupled Logic (PECL) devices; Quarter Wave (QW) devices; Receiver Photo Diode (RPD) devices; Semiconductor Optical Amplifier (SOA) devices; Spot-Size converter integrated Laser Diode (SS-LD) devices; Sub-Carrier Multiplexing Optical Network Unit (SCM-ONU) devices; Temperature Insensitive Arrayed Wave Guide (TI-AWG) devices; Thermo-Optic (TO) devices and Thermo-Optic Switch (TOS) devices; Time Compression Multiplexing - Time Division Multiple Access (TCM-TDMA) devices; Time Division Multiplexing (TDM) devices; Tunable Receiver (TR) devices; Uniform-Loss Cyclic-Frequency Arrayed Wave Guide (ULCF-AWG) devices; Vertical Cavity Surface Emitting Laser (VCSEL) devices; Wavelength Dispersive Multiplexing (WDM), Wavelength Dispersive Multiplexing Transceivers (WDMT) devices; Micro-Electro-Mechanical Systems (MEMS) device: Information Technologies MEMS devices; Medical/Biochemical MEMS devices; Biochips devices; Lab-On-A-Chip (LOAC) devices; Micro-Total Analysis System (Î¼-TAS) devices; Automotive MEMS devices; Industrial/Automation MEMS devices; Environmental Monitoring MEMS devices; and Telecommunications MEMS devices.

It will be appreciated that the above list is not exhaustive and other variations will be apparent to one skilled in the art. It is intended to cover all such variations within the scope of the appended claims.