CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of Chinese patent application No.: 2004100109212, filed Jun. 15, 2004

FIELD OF THE INVENTION

The present invention relates to a method for preparation of poly(o-phenylenediamine) nano-belt.

BACKGROUND OF THE INVENTION

In recent years, conductive polymers apply in many fields extensively. Polyaniline became one of the most studied conductive polymers due to its good chemical stability and good conductivity. At the same time, polymers based on aniline derivatives attracted wide attentions from the chemical community. Poly(o-phenylenediamine) possesses high aromaticity and high thermal stability. Such kind of conductive polymer was used as the catalyst for electrochemical reduction of dioxygen as well as sensor for many chemical species. Poly(o-phenylenediamine) can be obtained by electrochemical polymerization of monomer o-phenylenediamine or by the chemical oxidative polymerization of monomer o-phenylenediamine.

Since the discovery of carbon nanotube, scientists focused their attention on molecular conductive wire. Conductive polymers possess long conjugation length and good conductivity. They have wide potential applications in the field of molecular conductive wire. Therefore preparation of conductive polymers having ID structure has not only important theoretical significance but also huge applied value. Zhang et al fabricated conductive polymer nanowire with soft lithography (2000 Nano Lett. 2:1373). Jang et al. prepared polypyrrole nanotube by using inverse micro-emulsion polymerization in non-polar solvent (2003 Chem. Commun. 720). Wan's research group prepared polyaniline and polypyrrole nanotube by using P-naphthalene sulfonic acid as dopant and surfactant (Wan et al., Chinese Patent No. 98109916.5; Wei et al., 2002 Langmuir, 18:917; Zhang et al., 2002 Macromolecules, 35:5937). Alternatively, many research groups used hard template technology such as using porous Al₂O₃etc. as the template to form 1D structure of conductive polymer in the empty space of the template. However, the method has the following drawbacks: it is necessary to perform quite complicated post-synthesis process to remove the templates. At the same time, the 1D structures already obtained might easily be destroyed or be turned into aggregate in the course of their release from the hard template. For example, see following literatures: Martin et al., 1991 Adv. Mater., 3:457; Cai et al., 1989 J. Am. Chem. Soc., 111:4138; Martin et al., 1990 J. Am. Chem. Soc., 112:8976; Cai et al., 1991 Chem. Mater., 3:960; Wu et al., 1994 Chem. Mater. 6:1109; Wu et al., 1994 Science, 264:1757; Martin et al., 1993 Synth. Met., 55-57:1165; Parthasarathy et al., 1994 Nature, 369:298; Van Dyke et al., 1990 Langmuir, 6:1118; Penner et al., 1986 J. Electrochem. Soc., 133:2206; Cepak et al., 1999 Chem. Mater., 11:1363.

SUMMARY OF THE INVENTION

The present invention provides a method for preparation of poly(o-phenylenediamine) nano-belt comprising mixing aqueous solutions of o-phenylenediamine and of oxidant in a mole ratio of 1:0.1-1 under stirring; standing for 0.5-2 hrs at room temperature; and obtaining poly(o-phenylenediamine) nano-belt.

According to the present invention, o-phenylenediamine is used as the raw material. Preferably, the oxidant is selected from the group consisted of silver nitrate and ferric chloride.

In the absence of template and surfactant, o-phenylenediamine and corresponding oxidant are directly mixed while stirring in the mole ratio of 1:0.1-1 and then is allowed to stand for 0.5-2 hrs and finally a large amount of poly(o-phenylenediamine) nano-belt is obtained. The nano-belt has a length of several hundred micrometers, width of several hundred nanometers and thickness of tens nanometers. The oxidant of silver nitrate can give wider and more uniform poly(o-phenylenediamine) nano-belt than ferric chloride. The method is simple, quick and suitable for large-scale manufacture. The poly(o-phenylenediamine) nano-belt thus prepared possesses excellent semiconductor properties and is one of the most promising conductive polymer materials.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows the SEM images of the poly(o-phenylenediamine) nano-belt prepared by mixing aqueous solutions of o-phenylenediamine and of silver nitrate.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT EXAMPLES Example 1

4 mL of aqueous solution of o-phenylenediamine in a concentration of 0.072 M was mixed with aqueous solution of silver nitrate in a concentration of 0.12 M in the mole ratio of 1:1 in a small beaker. The mixture was allowed to stand for 1.5 hr at room temperature and large amount of poly(o-phenylenediamine) nano-belt was formed.

Example 2

4 mL of aqueous solution of o-phenylenediamine in a concentration of 0.072 M was mixed with aqueous solution of silver nitrate in a concentration of 0.12 M in the mole ratio of 1:0.5 in a small beaker. The mixture was allowed to stand for 0.5 hr at room temperature and large amount of poly(o-phenylenediamine) nano-belt was formed.