TECHNICAL FIELD 0001 The present invention relates to a fluororesin composition, which is excellent in moldability and in which a melt processable tetrafluoroethylene/hexafluoropropylene copolymer and polytetrafluoroethylene are compounded, a process for preparing the same and a cable coated with the same.

BACKGROUND ART 0002 A copolymer of tetrafluoroethylene (hereinafter referred to as TFE) and hexafluoropropylene (hereinafter referred to as HFP) (hereinafter referred to as FEP) has heat resistance, chemical resistance, electric insulating properties, non-adhesiveness and low frictional properties equal to those of polytetrafluoroethylene (hereinafter referred to as PTFE) and therefore is often applied not only in the chemical industry, electric and electronic industries and machine industry, but also in a wide range of fields, from space development and aircraft industry to household products. Furthermore, FEP has melt flowability and can be melt processed by compression molding, extrusion molding, injection molding and fluid immersion coating. 0003 However, in comparison to general thermoplastic resin, FEP has an extremely high melt flow temperature and high melt viscosity and therefore, a molding temperature of 330 to 420 C., in some cases 440 C., is required. Molding at such high temperatures causes thermal decomposition of the polymer. Furthermore, when extrusion pressure is raised in order to increase the molding speed, surface roughness of the extruded article and abnormal flow (melt fracture) are caused. 0004 In order to solve the above problems and improve moldability without losing properties, JP-A-52-98761 discloses a fluororesin composition, in which PTFE is compounded in FEP. As a result, phenomena such as surface roughness of the molded article and melt fracture are said to have difficulty occurring, but the effects are still insufficient. 0005 Also, in recent years, FEP is used for cable coating material and the speed for molding may reach at least 1200 ft/minute and in some cases, 3000 ft/minute. This speed is within the melt fracture range of FEP. Consequently, the coated cable is large in wire diameter unevenness and electric properties such as insulation become uneven. Furthermore, the phenomenon of cone break occurs, that is the conular part formed in the die when coating comes off, and coating at high speed is difficult. 0006 Furthermore, in order to improve electric properties, an electric wire can be coated with resin in a foamed state. However, to obtain stable electric properties, the resin must be in a foamed state of even bubbles with a small bubble diameter.

DISCLOSURE OF INVENTION 0007 The present invention solves the above problems and provides a fluororesin composition, which is excellent in moldability and crack resistance and particularly, does not cause cone break when coating an electric wire, a process for preparing the composition and a cable coated with the composition. 0008 That is, the present invention relates to a fluororesin composition comprising a tetrafluoroethylene/hexafluoropropylene copolymer and polytetrafluoroethylene compounded thereto; the composition having a melt flow rate of at least 15 at 372 C. 0009 The content of the polytetrafluoroethylene is preferably 0.03 to 2 parts by weight based on 100 parts of the copolymer. 0010 The present invention also relates to a process for preparing a fluororesin composition which comprises kneading a tetrafluoroethylene/hexafluoropropylene copolymer and polytetrafluoroethylene with a multi-screw kneader. 0011 The multi-screw kneader is preferably a twin-screw extruder. 0012 The multi-screw kneader preferably has at least one kneading block. 0013 Kneading is preferably conducted while adding water. 0014 Kneading is preferably conducted while adding a gas containing oxygen. 0015 The copolymer and polytetrafluoroethylene are preferably pre-mixed. 0016 The present invention also relates to a cable comprising a core wire coated with the fluororesin composition. 0017 The core wire of the cable preferably comprises metal. 0018 The metal is preferably copper. 0019 The present invention also relates to a cable comprising a core wire coated with the fluororesin composition, which is foamed by inert gas. 0020 The inert gas is preferably carbon dioxide or nitrogen. 0021 The core wire of the cable preferably comprises metal. 0022 The metal is preferably copper.

BEST MODE FOR CARRYING OUT THE INVENTION 0023 The copolymer used in the present invention comprises TFE and HFP and the composition ratio thereof is preferably 75 to 90% by weight of TFE and 10 to 25% by weight of HFP based on the copolymer weight. More preferably, TFE is 80 to 90% by weight and HFP is 10 to 20% by weight. When TFE is less than 75% by weight, moldability and heat resistance tend to become poor as the melting point becomes low. When TFE is more than 90% by weight, the melting point becomes high and moldability tends to become poor. When HFP is less than 10% by weight, crack resistance tends to become poor. When HFP is more than 25% by weight, moldability becomes poor as the melting point becomes low and heat resistance and productivity tend to become poor. Also, the polymerization speed tends to become slow. The method for copolymerization is not particularly limited and examples are suspension polymerization and emulsion polymerization. The copolymer may also contain a small amount of a third component, a modifying agent or a filler. 0024 As the third component added to the copolymer, perfluoroalkyl vinylether is preferable. By adding perfluoroalkyl vinylether as a copolymer component, moldability and crack resistance tend to improve further. Examples of the perfluoroalkyl vinylether are vinylether represented by the formula:

CF2CFO (CF2)mF

0025 (wherein m is an integer of 1 to 6)(perfluoromethyl vinylether (hereinafter referred to as PMVE) when m is 1) and vinylether represented by the formula:

CF2CF(OCF2CF(CF3))nOC3F7

0026 (wherein n is an integer of 1 to 4). When n is 1 to 2, heat resistance is poor as the melting point becomes low and when n is 4, production costs tend to increase. Therefore, perfluoropropyl vinylether in which n3 (hereinafter referred to as C3VE) is preferable. Also, the copolymer composition ratio is preferably 67 to 89.5% by weight of TFE, 10 to 20% by weight of HFP and 0.5 to 13% by weight of perfluoroalkyl vinylether based on the polymer of TFE/HEP/perfluoroalkyl vinylether (hereinafter referred to as ternary copolymer). More preferably, TFE is 83 to 89.3% by weight, HFP is 10 to 15% by weight and perfluoroalkyl vinylether is 0.7 to 2% by weight. When TFE is less than 67% by weight, heat resistance tends to become extremely poor and when TFE is more than 89.5% by weight, moldability is poor as the melting point becomes high and crack resistance tends to become poor. When HFP is less than 10% by weight, crack resistance tends to become poor and when HFP is more than 20% by weight, moldability becomes poor as the melting point becomes low and heat resistance and productivity tend to become poor. When perfluoroalkyl vinylether is less than 0.5% by weight, the effect of copolymerizing perfluoroalkyl vinylether tends not to appear. When perfluoroalkyl vinylether is more than 13% by weight, the viscosity becomes low and moldability tends to become poor. In this case, the melt flow rate at 372 C. is at least 15. The ternary copolymer may also contain a small amount of a fourth component, a modifying agent or a filler. The method for copolymerization is not particularly limited and examples are suspension polymerization and emulsion polymerization. 0027 The content of PTFE compounded with the copolymer is preferably 0.03 to 2 parts by weight based on 100 parts by weight of the copolymer. More preferably, the lower limit is 0.05 part by weight and the upper limit is 0.5 part by weight. When PTFE is less than 0.03 part by weight, the effect of adding PTFE tends not to appear. When the amount is more than 2 parts by weight, the melt viscosity increases significantly and the molded article tends to become brittle. PTFE preferably has a molecular weight of at least 1,000,000, more preferably at least 3,000,000. When the molecular weight is less than 1,000,000, the molded article tends to be poor in crack resistance. PTFE is a homopolymer of TFE or a copolymer of TFE and hexafluoropropylene, tetrafluoroethylene or tetrafluoro ethylene chloride. In the case that PTFE is compounded as powder, the particle size is preferably at most 1,000 m, more preferably at most 800 m. When the particle size of PTFE is more than 1,000 m, dispersability with the copolymer tends to be inhomogeneous. The form of PTFE is not limited and can be powder, a dispersion or a suspension. 0028 The fluororesin composition of the present invention is prepared by mixing the above copolymer and PTFE and has a melt flow rate (hereinafter referred to as MFR) measured according to ASTM D-2116 of at least 15 at 372 C. The upper limit is preferably 45 and more preferably, the lower limit is 17.5 and the upper limit is 42.5. When the MFR at 372 C. is less than 15, the flowability is low and problems occur when using as, for example, coating material for a cable. That is, as mentioned above, the speed for coating a cable is extremely fast and therefore, when the MFR at 372 C. is less than 15, the conular part (cone part) formed in the die when coating comes off and the cable cannot be coated. When the MFR is more than 45, maintaining the cone part when coating is also difficult and coating of an electric wire tends to become difficult. 0029 The copolymer and PTFE used in the present invention are kneaded by a multi-screw kneader. It is important that the PTFE is sufficiently dispersed. When dispersion is insufficient, PTFE with high molecular weight aggregates when molding. For example, when a mixture of the copolymer and PTFE containing PTFE aggregate is used as coating material for a cable, the surface of the cable becomes uneven due to the PTFE aggregate, adversely affecting electric properties. However, as mentioned above, because the amount of PTFE is an extremely small amount of preferably 0.03 to 2 parts by weight, homogeneously dispersing is difficult. Therefore, a twin-screw extruder, which is particularly excellent in kneading function, is preferably used. More preferably, a multi-screw kneader having at least one kneading block is used. The number of kneading blocks can be determined according to the functions of the kneader. The kneading block can further improve the degree of dispersion of PTFE. Preferably, from the viewpoint of advancing kneading, as many kneading blocks as possible are installed within the range that the copolymer and PTFE are not damaged. 0030 Kneading by the multi-screw kneader is preferably conducted while adding water or air. Usually, water and air introduced into the extruder are removed by forming a vent hole in a cylinder and connecting a vacuum pump to the vent hole. However, by adding water or oxygen to the resin, the unstable terminal groups present in the fluororesin composition of the present invention can be stabilized. The unstable terminal groups are thought to cause air bubbles, voids and coloring in the molded article of the fluororesin composition. 0031 Water stabilizes carboxylic acid terminal groups and converts acid fluoride into carboxylic acid. The amount of water added must be an amount excessive of the theoretical amount required for the reaction. The amount is largely influenced by the pressure when adding and the state within the extruder and is determined while checking with an actual machine. The reaction for stabilizing carboxylic acid terminal groups is significantly advanced by adding a reaction accelerating agent such as an alkali metal compound and so water is preferably added as an aqueous solution in which an accelerating agent is dissolved. The concentration of the aqueous solution can be determined accordingly based on the necessary amount of the accelerating agent. As long as water is present in the kneader within the area in which stabilization treatment is conducted (hereinafter referred to as stabilization treatment area), the fluorine-containing polymer may be moistened to contain water before being added into the kneader or water may be supplied after adding the dried polymer into the kneader. Herein, the stabilization treatment area can be located, for example, at the screw part immediately after the melting zone formed by the kneading block of the twin-screw extruder. Also, modifications are possible, such as forming a long melting zone and the stabilization treatment area further downstream. Stabilization can theoretically be conducted if the amount of water supplied has the same number of molecules as the number of unstable terminal groups which develop in the kneader. However, in reality, an excessive amount of water, particularly water with at least 10 times the number of molecules of the number of unstable terminal groups, is preferably supplied. The upper limit is not particularly defined. 0032 Oxygen converts vinyl terminal groups into acid fluoride terminal groups. Furthermore, the function of oxidizing the few carbon atoms produced in depolymerization of the vinyl terminal groups to produce carbon dioxide can be obtained. 0033 The amount of oxygen (O2) present differs depending on the temperature at the reaction, the residence time in the stabilization treatment area, the type of extruder and the type and amount of unstable terminal groups. The amount is at least an amount equimolar to the amount of unstable terminal groups (CFCF2), which need to be stabilized. When considering diffusion loss and the amount discharged without contributing to the reaction, the amount is preferably an excess amount, for example at least 10 times the molar amount, particularly 50 to 500 times the molar amount. 0034 As the gas containing oxygen, oxygen can be diluted to a suitable concentration (for example 10 to 30% by volume) with inert gas such as nitrogen gas and argon gas and then supplied but preferably air is used as it is, from an economical viewpoint. 0035 As long as oxygen is present in the stabilization treatment area, oxygen may be contained in the fluorine-containing polymer before being added into the kneader or oxygen may be supplied after the fluorine-containing polymer is added into the kneader. Naturally, both methods may be used together. 0036 Also, kneading while simultaneously supplying water and oxygen (air) is preferable. 0037 The treatment time, that is the residence time, in the stabilization treatment area differs depending on the structure of the kneader, the supply method of water and air and the treatment temperature in the stabilization treatment area. Usually, less than 10 minutes is sufficient and 0.2 to 5 minutes is preferable. When the residence time becomes long, large shearing force is applied and the polymer tends to become damaged. 0038 The temperature of the stabilization treatment area is usually 200 to 450 C., preferably 300 to 400 C. 0039 In the present invention, gaseous substances produced in the stabilization treatment reaction, such as hydrogen fluoride, carbon dioxide and small amounts of monomers produced by decomposition, are drawn out from within the stabilized fluorine-containing polymer and discharged from the kneader. Therefore, a degassing area, in which the absolute pressure is maintained at 0.1 MPa or lower, is preferably located in the kneader successively to the stabilization treatment area. The absolute pressure in the degassing area differs depending on the melted state of the polymer and operation conditions such as the rotational speed of the extruder screw. The pressure is preferably reduced to a degree at which the polymer does not enter into the discharge nozzle. 0040 The fluorine-containing polymer obtained by stabilization treatment and discharged from the kneader of the present invention usually has the shape of a pellet. When the pellet is used in melt molding, air bubbles and voids do not develop and coloring does not occur in the obtained molded article. 0041 When necessary, the kneaded object (pellet) retrieved from the kneader can be subjected to the above fluorination treatment. 0042 Before kneading in a multi-screw extruder, the copolymer and PTFE are preferably pre-mixed, thereby further improving the degree of dispersion of PTFE. The powder mixer used for pre-mixing is not particularly limited and examples are a mixer, a mixing roll, a kneader, a ball mill, a banbury mixer and a blender. The pre-mixing method can be a dry method or a wet method. Furthermore, the copolymer and PTFE can be added to the reaction system before or during the polymerization reaction of the copolymer to be pre-mixed. 0043 The cable of the present invention is coated with the fluororesin composition of the present invention, in which the copolymer and PTFE are compounded. Because the fluororesin composition has high flowability of MFR of at least 15 at 372 C., even when molded at high speed, cone break does not occur and the wire diameter becomes even. As a result, a cable which is excellent in electric properties such as insulation can be obtained. 0044 An example of the cable is a LAN cable used for constructing a local area network (LAN) of personal computers. A LAN cable is used inside an office and therefore is required to have high flame retardancy. The fluororesin composition of the present invention can fulfill this requirement. The thickness of the resin composition coating of the cable can be determined according to the use. 0045 The core wire of the cable is preferably metal. Particularly, copper is preferable. 0046 Coating the cable with the fluororesin composition in a foamed state can be achieved by adding inert gas into the extruder when molding the electric wire. Inert gas dissolves relatively well in the FEP part, which has amorphous parts, and becomes bubbles when discharged from the die of the electric wire molding machine. The growth of the bubbles seems to stop due to the crystalline parts of the added PTFE and relatively small bubbles can be produced. The inert gas is not particularly limited as long as it is a gas which does not react with resin and from the viewpoints that availability and low cost, carbon dioxide or nitrogen is preferable. 0047 Hereinafter, specific Examples are described for explanation of the present invention, but the present invention is not limited thereto. 0048 Measurement Method 0049 (Lamp) 0050 Detection was conducted of parts in which the resin coating thickness was (preset diameter20 mil) by a lamp detector (made by Zumback, KW32 TRIO). 0051 (Spark) 0052 Detection was conducted of parts which were not coated with resin by a spark tester charged to 1.83 kV (made by CLINTON INSTRUMENT COMPANY, Model HF-20-H). 0053 (Cone break) 0054 Cone break was considered to occur when both the lamp detector and spark tester were simultaneously set off and continuing the test was temporarily not possible as the cone part was visually found to have broken. 0055 (Measurement of Melt Flow Rate (MFR)) 0056 Melt flow rate was measured according to ASTM D-2116 by the method of 372 C. and 5 kg load.

EXAMPLE 1 0057 100 parts by weight of FEP powder obtained by emulsion polymerizing TFE/HFP/C3VE in an amount of 85.8/13.2/1.0 (weight ratio) with ammonium persulfate (APS) as a polymerization initiator and 0.15 part by weight of PTFE fine powder (average particle size 450 m, number average molecular weight 5,000,000) were pre-mixed for 30 minutes by a powder mixer equipped with a stirrer and kneading block. 0058 The above powder (containing air) to which special pre-drying treatment was not conducted except that potassium carbonate was added so as to become 20 ppm (value converted to amount of potassium, equal to 4.3% of the total number of unstable terminal groups) was supplied at a speed of 50 kg/hour into a twin-screw extruder made by Japan Steel Works, Ltd. (screw shaft diameter: 47 mm, total length: 2468 mm, number of barrels: 15 (first barrel: raw material supplying area, second to fifth barrels: melting area, sixth to twelfth barrels: kneading and reacting area, thirteenth to fifteenth barrels: degassing area)). At an area further downstream from the powder supply port, deionized water and air (oxygen concentration approximately 20%) were supplied into the stabilization treatment area (kneading block area) at a flow rate of 1.5 kg/hour and 40 NL/minute respectively. The preset temperature of the stabilization treatment area was 380 to 420 C. and the absolute pressure was 2.5 MPa and the total time required for the all treatment including the time for melting by heating was 5 minutes (the residence time in the stabilization treatment area was presumed to be approximately 2 minutes). In this way, the fluororesin composition of the present invention in the form of pellets was obtained. The MFR of the fluororesin composition was 32.3 at 372 C. 0059 The obtained pellets were coated on a copper wire with a diameter of 20.1 mil by a 2-inch screw extruder and the cable of the present invention with a diameter of 35.5 mil was obtained. The coating speed was 1600 to 2800 ft/minute. In the extruder for coating an electric wire, the temperature was controlled in 5 zones in the main body and in 4 zones in the die. From the raw material supply side, each temperature was controlled to 0060 Main body: 327 C., 371 C., 388 C., 399 C., 416 C. 0061 Die: 427 C., 427 C., 427 C., 427 C. 0062 The coated cable was cooled by passing through an air-cooling zone and a water-cooling zone. 0063 The results of the above measurement methods are shown in Table 1.

COMPARATIVE EXAMPLE 1 0064 The fluororesin composition (MFR at 372 C.: 32.3) was obtained by the same method as in Example 1, except that PTFE fine powder was not used, and was coated on a copper wire. 0065 The results of the above measurement methods are shown in Table 1.

COMPARATIVE EXAMPLE 2 0066 The fluororesin composition (MFR at 372 C.: 10) was obtained by the same method as in Example 1, except that 100 parts by weight of FEP powder obtained by emulsion polymerizing TFE/HFP in an amount of 86.5/13.5 (weight ratio) with ammonium persulfate (APS) as a polymerization initiator and 0.15 part by weight of PTFE fine powder (average particle size 450 m, number average molecular weight 5,000,000) were pre-mixed for 30 minutes by a powder mixer equipped with a stirrer. Coating of a copper wire was attempted, but could not be conducted as cone break occurred even at a coating speed of 1600 ft/minute. 1TABLE 1Ex. 1Com. Ex. 1Lamp1600 ft/minute00(quantity/104 feet)2000 ft/minute1.68.32400 ft/minute6.18.22800 ft/minute1.311.9Cone Break1600 ft/minute00(times/104 feet)2000 ft/minute002400 ft/minute08.22800 ft/minute06Spark1600 ft/minute4.55.1(quantity/104 feet)2000 ft/minute06.32400 ft/minute1.520.62800 ft/minute1.314.9

Industrial Applicability 0067 According to the present invention, a fluroresin composition can be obtained, which is melt processable and excellent in moldability and crack resistance and particularly, does not cause cone break when coating an electric wire. Also, a cable evenly coated therewith can be obtained.