FIELD OF THE INVENTION 0001 The present invention relates to a process and apparatus for solvent casting capable of conveying a web without slipping off from pin tenters.

BACKGROUND OF THE INVENTION 0002 Generally, solvent casting produces a part of films, such as cellulose acetate, polycarbonate and cellophane. In the solvent casting process, dope which is a polymer solution is cast from a casting die onto a casting support of belt type or drum type, stripped off after being dehumidified to some extent on the casting support, dried while being carried by a tenter machine with being held at both side edges, and further dried while being conveyed over rollers. (JP 62-46625A, JP 62-46626A, etc.). 0003 The tenter machine includes a pin tenter and a clip tenter, and the pin tenter has a function of inserting the side edges of the web into the pins of itself by thrusting the edge of the web downward by an inserting device, such as an engaging brush. However, in conveyance of the web by a conventional pin tenter machine, the web once inserted in the pin tenters often slips off from the pin tenter thereby losing the state of being conveyed. When the speed of the conveyance increases, this phenomenon particularly becomes conspicuous and disturbs an improvement in the productivity of film forming.

SUMARRY OF THE INVENTION 0004 An object of the invention is to solve the foregoing problems and, to provide a process and apparatus for solvent casting that is able to favorably convey a film web without slipping off from a pin tenter machine even in the case of increasing the speed of conveyance of the web. 0005 By investing eagerly the phenomenon that the web slips off from the pin tenter, it was found that, when the temperature of an engaging brush is high upon inserting the web into pins of the pin tenter, the gelatinized web returns to the state of sol and adheres to the engaging brush which causing the slipping off. Increasing the speed of conveyance of the web elevates a gelation temperature due to the increase of residual volatile components in the web, thereby induces that the web easily adheres to the pin tenter. 0006 Based on the foregoing finding, the present invention provides to restrain the web from increasing of the temperature by cooling an inserting device, such as an engaging brush. 0007 A process for solvent casting of the invention comprises casting a polymer solution onto a casting support, cooling the polymer solution to gelatinize on the casting support to form web, stripping off the web from the casting support, thrusting side edges of the web into pins of a pin tenter by an inserting device, and drying the web while conveying the web with carrying the side edges of the web by the pin tenter, wherein the inserting device is cooled so that the surface temperature of the web in contact with the inserting device does not exceed a gelation temperature of the polymer solution. 0008 According to the process for solvent casting of the invention, the web is prevented from adhering to the inserting device by restraining the web from the temperature rise over the gelation temperature because of its contact with the inserting device being cooled. 0009 An apparatus for solvent casting of the invention comprises, a casting means for casting a dope of a polymer solution onto a casting support to form web, a stripping means for stripping off the web from the support, an inserting device for thrusting side edges of the web into pins of a pin tenter, and a drying means for drying the web stripped off while conveying the web with carrying the side edges of the web by the pin tenter, wherein said inserting device is provided with a cooling means. 0010 According to the solvent casting apparatus of the invention, the web is prevented from adhering to the inserting device by restraining the web from the temperature rise over the gelation temperature because of its contact with the inserting device being cooled.

BRIEF DESCRIPTION OF THE DRAWINGS 0011 FIG. 1 is a schematic side elevation of a tenter drying section of a solvent casting apparatus which embodies the invention. 0012 FIG. 2 is a schematic illustration looking at the tenter drying section of the solvent casting apparatus from a conveying direction of the web which embodies the invention. 0013 FIG. 3 is a schematic plan view of the tenter drying section of the solvent casting apparatus which embodies the invention.

DETAILED DESCRIPTION OF THE INVENTION 0014 In a process for solvent casting of the invention, the surface temperature of the web is prevented by cooling of the inserting device from elevating over the gelation temperature of the web while being in contact with the inserting device, i.e. from touching of the inserting device to the web to departing therefrom. The cooling means for cooling the inserting device is not particularly limited. The cooling may be conducted either by introducing cooling air into a covered inserting device using a cooling air supply or by directly cooling the inserting device. 0015 The surface temperature of the web is rendered so as not to exceed the gelation temperature of the web by cooling, and the surface temperature is preferred to be lower than the gelation temperature by 2 C. or more, particularly preferably lower than the gelation temperature by 3 C. or more. Regarding the temperature of the cooling air, although it may be appropriately set according to the inserting device, etc., it is preferable to be from 40 C. to 0 C., more preferably from 30 C. to 10 C. 0016 When the cooling air is employed as the cooling means, it is desirable to remove foreign matters around the web. That is, dust generates by inserting the web into the pins of a pin tenter, and often scattered around the web by blowing the cooling air. The scattered dust adheres to the web to render the web unsuitable as a product, and thereby, an yield of the product becomes worse. Accordingly, by providing a suction removal means for removing foreign matters such as the dust generated by inserting the web into the pins of a pin tenter, the surface of the web can be kept clean by the removal of the foreign matters, and as a result, a reduction of the yield can be prevented. 0017 Therefore, when sucking foreign matters around the web, cooling air supply and suction simultaneously occur at the place of inserting web into a pin tenter by the inserting device. It is preferable that a static pressure at this place is from 100 to 100 Pa, desirably from 70 to 70 Pa and more desirably from 50 to 50 Pa as compared with atmospheric pressure outside the cover. When the static pressure is less than 100 Pa, cooling efficiency degrades caused by sucking high temperature drying wind in the tenter machine. As a result, the surface temperature of the web is unable to be lowered enough. When the static pressure exceeds 100 Pa, the yield of product degrades by scattering foreign matters such as dust. 0018 The inserting device has any structure capable of inserting web into pins of a pin tenter. An example of the inserting device is a rotor on the periphery of which brush is planted. 0019 The polymer solutions applicable to the process for solvent casting of the invention are solutions of cellulose ester, polycarbonate, aramid group polymers, norbornen group polymers, etc. Preferable cellulose esters are lower fatty acid esters of cellulose. The lower fatty acid means a fatty acid having 6 carbon atoms or less. A preferable number of carbon atoms is 2 (cellulose acetate), 3 (cellulose propionate) or 4 (cellulose butylate). Among these, cellulose acetate is particularly preferable. A mixture of fatty acid esters may be used, such as cellulose acetate propionate or cellulose acetate butylate. 0020 The film produced by the process for solvent casting of the invention can be applied to protection film for polarizing plate, optically functional films (optical compensation sheet, antireflection film, brightness improvement membrane), etc. 0021 Preferred embodiments of the process for solvent casting according to the invention will hereinafter be described with reference to the attached drawings. 0022 FIG. 1 is a schematic side elevational view of a tenter drying section of the solvent casting apparatus carrying out the process for solvent casting of the invention. FIG. 2 is a schematic illustration looking at the tenter drying section of the solvent casting forming apparatus, and FIG. 3 is a schematic plan view of the tenter drying section. 0023 In FIG. 1, reference numeral 10 indicates a pin tenter which is freely travelable in the right direction in the drawing, and web 20 is conveyed with carrying on the upper part of the pin tenters 10. Reference numeral 30 indicates an engaging brush provided revolvably as the inserting device, and by a depressing the web 20 by the lower end of the engaging brush 30, the web 20 is inserted into pins of the pin tenter 10. 0024 The engaging brush 30 is placed in a box type brush cover 40 of which the bottom is opened, so as to shield it from drying wind. On the upper parts of the brush cover 40 at almost the center in the conveying direction, cooling air introduction inlet 41 is provided and from which, the cooling air is introduced into the brush cover 40. 0025 A cooling air introduction means (not shown) are coupled with the cooling air introduction inlet 41 through an air duct (not shown). The brush cover 40 and the cooling air introduction means compose the cooling means for cooling the engaging brush 30. Furthermore, two exhaust outlets 42 are provided in the conveying direction on the outer wall of the brush cover 40, and on the inside of the exhaust outlets 42, a guide plate 43 which extends to the neighborhood of the upper surface of web 20 are provided. 0026 On the outside of the exhaust outlets 42, a suction means (not shown) is coupled with them through an air duct (not shown). 0027 In accordance with the foregoing construction of the tenter drying section, the pin tenters convey the web 20 in such a way that the web 20 traveling from the casting section is depressed with the engaging brushes 30 which are revolving to be inserted into pins of the pin tenters 10 thereby being carried by pin tenters 10. Then, the web 20 is dried while being conveyed in the state of being carried by the pin tenters 10. 0028 Meanwhile, the cooling air is introduced into the brush covers 40 through cooling air introduction inlets 41 from a cooling air supply means. Introduced cooling air is sent from the upper part to the lower part inside the brush covers 40, and, in this stage, it cools the engaging brushes 30. Accordingly, although the web 20 contacts with the engaging brushes 30 on being depressed by them, the web 20 is not heated by them and the surface temperature of the web does not rise higher than it's gelation temperature. 0029 Furthermore, the air on the web 20 is sucked by the suction means through exhaust outlets 42. By the suction, dust generating during inserting the web 20 into the pins of pin tenters 10, etc., are exhausted outside brush covers 40. Therefore, a good quality of the web can be maintained because the dust does not adhere onto the web 20. 0030 In the brush covers 40, cooling air is introduced and simultaneously exhausted by the suction, and a static pressure in the area where the web 20 is inserted into the pins by the engaging brushes 30 is settled from 100 Pa to 100 Pa as compared with an atmospheric pressure outside the brush covers 40. That is, an effective cooling is assured within the foregoing range by adjusting the amounts of cooling air and exhaust air by suction.

EXAMPLES 0031 A cellulose triacetate film was produced with a solvent casting apparatus having a tenter drying section shown in FIG. 1. Recipe of the dope employed is shown as follows: 1Triacetate:200 mass partsPlasticizer:24 mass partsDichloromethane:650 mass partsMethanol:112 mass partsButanol:12 mass partsUltraviolet absorber:2 mass parts

0032 As the plasticizer, triphenylphosphate and biphenyldiphenylphosphate were employed, and as the UV absorber, 2 (2-hydroxy-3, 5-di-tert-amylphenyl)-5-benzotriazole (1.3 mass %), 2 (2-hydroxy-3, 5-di-tert-butylphenyl)-5-chloro benzotriazole (0.7 mass %) were employed. 0033 Using the foregoing dope, experimentation was carried out with changing the surface temperature of the web and the static pressure inside the brush covers. Results are shown Table 1. 2TABLE 1StaticCoolingBrush CoverCoolingSuctionPressureWebWebAdhesionScatterAirPeripheralAirExhaustInsideSurfaceGelationBetweenofTemp.Temp.AmountAmountBrush CoverTempTemp.Web andForeign( C.)( C.)(m3/min)(m3/min)(Pa)( C.)( C.)BrushMattersEx.11760591006.76.7SlightlyNone for6 monthsEx.2176058704.76.7WeaklyNone for6 monthsEx.3176057503.76.7NoneNone for6 monthsEx.41760535016.7NoneNone for6 monthsEx.51760527006.7NoneYielddegradedafter3 monthsEx.617605110016.7NoneYielddegradedafter1 monthEx.7176050.712036.7NoneYielddegradedafter1 weekComp.176051212086.7FailedEx.to engage1

0034 In Table 1, Ex., Comp. and Temp. are abbreviations of Example, Comparative and Temperature respectively. 0035 According to the present invention, web can be conveyed surely without slipping from pin tenters even when the pin tenters convey the web at a high speed. As a result, the productivity of film can be improved.