BACKGROUND OF THE INVENTION 0001 The present invention relates to a semiconductor laser device having a protective coating with a high-reliability formed on an end surface, and to a method for manufacturing the same. 0002 As shown in FIG. 5, most semiconductor laser devices are composed of, for example, protective coatings 43a and 43b, each having an identical reflectance, formed on light emitting end surfaces 41a and 41b of a GaAs laser chip 4. Reference numeral 42 denotes an active layer of the laser chip 4. In the case where the protective coatings 43a and 43b are composed of Al2O3 in FIG. 5, if a refractive index of the Al2O3 film is set to be 1.60 while a refractive index of the laser chip 4 is set to be 3.50, a reflectance of the protective coatings 43a and 43b corresponding to a coating thickness d varies as shown in FIG. 6 (provided that a laser emission wavelength 7800 ). 0003 FIG. 6 indicates that regardless of the coating thickness d of the protective coatings 43a and 43b, the reflectance thereof is smaller than that of the case without the protective coatings 43a and 43b (i.e. the reflectance of the light emitting end surfaces 41a and 41b). The reflectance becomes smallest when an optical coating thickness (refractive index ncoating thickness d) is an odd multiple of /4, while the reflectance becomes approximately equal to that in the case without the protective coatings 43a and 43b when the optical coating thickness is an integral multiple of /2. This is because the refractive index (1.60) of the protective coatings 43a and 43b is smaller than the refractive index (3.50) of the GaAs laser chip 4. 0004 Contrary to this, in the case where the refractive index of the protective coatings 43a and 43b is larger than the refractive index of the GaAs laser chip 4 (for example, if such material as Si is used as the protective coatings 43a and 43b, the reflectance thereof is larger than that in the case without the protective coatings 43a and 43b, regardless of the coating thickness), the reflectance becomes largest when the optical coating thickness is an odd multiple of /4, while the reflectance becomes approximately equal to that in the case without the protective coatings 43a and 43b when the optical coating thickness is an integral multiple of /2. 0005 In the case of high output semiconductor laser devices with optical output as high as 20 mW or more, as shown in FIG. 7, for increasing optical output Pf from the side of a main emitting end surface (front end surface), the reflectance of the protective coating 43a on the side of the main emitting end surface 41a is generally set lower than that in the case without the protective coating 43a, while the reflectance of the protective coating 43b on the side of a rear emitting end surface 41b is set higher than that in the case without the protective coating 43b. 0006 For example, the reflectance of the protective coating (Al2O3) 43a on the main emitting end surface 41a is set to be approx. 15% or less. This reflectance is obtained with the coating thickness of approx. 700 to 1600 . 0007 The protective coating 43b on the rear emitting end surface 41b, if composed with use of a film having a refractive index larger than that of the laser chip 4, is not capable of providing a sufficiently high reflectance as a single layer. Accordingly, an Al2O3 film with a thickness of /4 as a first layer 431 and a third layer 433, and an amorphous Si with a thickness of /4 as a second layer 432 and a fourth layer 434, are laminated. Then finally, an Al2O3 film with a thickness of /2 as a fifth layer 435 is laminated. This makes it possible to form a protective coating 43b having a reflectance as high as approx. 85% or more. It is noted that reference numeral 43 denotes an active layer. 0008 Description will now be given of a method for forming protective coatings 43a and 43b having the above-described reflectance on light emitting end surfaces 41a and 41b of a semiconductor laser chip 4. 0009 First, after one side of an n-GaAs substrate is polished, a p-electrode (comprising an ohmic electrode and a bonding electrode) is formed by evaporation or sputtering. A photomask is made thereon and, then, the p-electrode is patterned by etching. 0010 Subsequently, after the other side of the n-GaAs substrate is polished, an n-electrode (comprising an ohmic electrode and a bonding electrode) is formed by evaporation or sputtering according to the above procedures. After that, the electrodes and the substrate are alloyed at appox. 400 to 500 C. 0011 Next, as shown in FIG. 8, a cleavage line 49 is formed by scribing extensively disposed between an electrode 44 of an arbitrary element in a semiconductor laser wafer 5 and an electrode 44 of an adjoining element in direction orthogonal to an emitting section (channel) 42. Then, as shown in FIG. 9, the semiconductor laser wafer 5 is cleaved and divided into a plurality of laser bars (bar-shaped laser chips) 51. 0012 Next, as shown in FIG. 10, a plurality of the laser bars 51 obtained by dividing are loaded in a laser bar fixing device 6 such that the electrodes 44 face towards the same side. All the laser bars 51 should be loaded so that all the emitting end surfaces 41a are positioned on the same side and, therefore, all the emitting end surfaces 41b are positioned on the same side. Next, on the emitting end surfaces 41a and 41b of laser bars 51 loaded in the laser bar fixing device 6, a protective coating having a specified reflectance is formed generally by using a vacuum evaporator 7 schematically shown in FIG. 11. The vacuum evaporator 7 is provided with a vapor source 72, a holder 73 for holding a plurality of the laser bar fixing devices 6, and a crystal oscillator 74 for monitoring the thickness of evaporated films, all in a chamber 71. 0013 Following description discusses procedures of forming the protective coating. First, in the case for evaporating a protective coating onto the emitting end surface 41a, the holder 73 is disposed such that the emitting end surface 41a of a laser bar 51 faces the vapor source 72 side as shown in FIG. 11. Then, the chamber 71 is evacuated through a duct 75. After a specified degree of vacuum is obtained, an evaporation material 76 put in the vapor source 72 is heated and evaporated by electron beams and the like so that a protective coating is evaporated onto the emitting end surface 41a of the laser. After evaporation is completed, the holder 73 is then rotated 180 for evaporating a protective coating onto the emitting end surface 41b according to the above procedures. 0014 Here, a forming speed (evaporation rate) for forming a protective coating on the both light emitting end surfaces 41a and 41b is controlled so as to be approximately constant till completion of evaporation. The evaporation rate is in this case controlled with a heating temperature. In the case of electron beam evaporation, therefore, the evaporation rate may be controlled with the intensity of electron beams. It is well known that in the case of resistance heating, the evaporation rate is controlled with an amount of electric current passed through a resistor. The evaporation rate is generally set in a range between several /sec to 30 /sec in the case of the evaporation material of Al2O3 Evaporation is conducted while coating thickness is monitored with use of the crystal oscillator 74. Evaporation is terminated when a prescribed coating thickness is obtained. 0015 Although not shown in FIG. 7, in the case of a high output type semiconductor laser device, a low reflecting protective coating 43a (having a reflectance of approx. 15% or less) is formed on the side of the main emitting end surface 41a, and then a multilayered high reflecting protective coating 43b is formed on the side of the rear emitting end surface 41b. The multilayered high reflecting protective coating 43b is composed of a laminated structure made up of: a first layer 431 and a third layer 433, each consisting of an Al2O3 film with a thickness equal to /4; a second layer 432 and a fourth layer 434, each consisting of an Si film with a thickness equal to /4; and a fifth layer 435 consisting of an Al2O3 film with a thickness equal to /2. For evaporation of this film, Al2O3 and Si are mounted on the vapor source 72 as evaporation materials 76. Then the first layer 431, the third layer 433, and the fifth layer 435, each consisting of an Al2O3 film are evaporated through irradiation of the evaporation material Al2O3 with electron beams, and the second layer 432 and the fourth layer 434, each consisting of an Si film, are evaporated through irradiation of the evaporation material Si with electron beams. 0016 However, the above-stated prior semiconductor laser devices have a following problem. In forming protective coatings 43a and 43b of laser chip 4 by evaporation, an oxide (Al2O3), that is a material of the protective coatings 43a and 43b, is decomposed to generate oxygen immediately after start of evaporation process, which increases partial pressure of oxygen molecules. The oxygen, colliding or bonding with end surfaces 41a and 41b of the laser chip 4, is highly likely to cause damage to the end surfaces 41a and 41b. Further, in the case where active layer 42 of the laser chip 4 and vicinity layers thereof contain aluminum, the damage is considered to be larger. If thus-fabricated semiconductor laser device is operated with high output, necessary reliability may not be provided. 0017 For high output type semiconductor laser devices, as shown in FIG. 12, there has been proposed a method for forming a protective coating 43a on the side of a main emitting end surface 41a of a laser chip 4 utilizing high thermal conductivity of Si, in which an Si film 436 having high thermal conductivity is formed first and then a low reflecting protective coating 437 is formed (JP-A 1-289289). In the drawing, reference numeral 43b denotes a multilayered high reflecting protective coating on the side of a rear emitting end surface 41b composed of a first layer 431, a second layer 432, a third layer 433, a fourth layer 434, and a fifth layer 435, and reference numeral 42 denotes an active layer. 0018 In this example, heat generated in the vicinity of the main emitting end surface 41a by light emission of the semiconductor laser device is efficiently discharged by the Si film 436, which controls deterioration of the semiconductor laser device caused by long term supply of current. The Si film 436 has a film thickness of around /4 (approx. 532 in an embodiment). 0019 Further, according to the high output type semiconductor laser device disclosed in the JP-A 1-289289, in forming protective coating 43a on the main emitting end surface 41a, the Si film 436 having high thermal conductivity is formed first for increasing heat dissipation to improve reliability. In this case, the Si film 436 is firstly formed, which is free from generation of oxygen due to decomposition of the material in the process of evaporation, thereby enabling creation of a coating in the vicinity of the emitting end surface 41a of the laser chip 4 immediately after start of evaporation process under conditions of low partial pressure of oxygen. Therefore, an effect of controlling the above-stated damage in the vicinity of the emitting end surface 41a may be achieved. 0020 In this case, however, the Si film 436 has a thickness as high as approx. 532 (almost equal to /4), which may cause leakage current in the Si film 436 (light emitting end surface), and may affect oscillation characteristics of the semiconductor laser device. 0021 JP-A 2000-361037 discloses a semiconductor laser device capable of controlling generation of leakage current in the vicinity of the light emitting end surface by setting the thickness of the Si film to 40 or less. 0022 According to the above constitution, before an oxide is formed as a protective coating, an Si film is formed, which is free from generation of oxygen due to decomposition. Consequently, creation of the coating is conducted immediately after start of Si film forming under conditions of low partial pressure of oxygen, which prevents oxygen with high energy from colliding or boding with the light emitting end surface. Further, if oxygen is decomposed in the process of oxide forming and so the oxygen partial pressure increases, collision or bonding of the oxygen with the light emitting end surface is prevented. Thus, the damages given to the light emitting end surface in the process of protective coating formation are controlled. 0023 Here, if the semiconductor laser chip has an active layer including Al, the damages given to the light emitting end surface is effectively controlled. 0024 In addition, the Si film has a film thickness as small as 40 or less. This reduces generation of leakage current in the Si film or on the light emitting end surface, thereby preventing negative influence on the oscillation characteristics. 0025 Thus, in the case where a protective coating having a specified reflectance is formed on a light emitting end surface of a semiconductor laser chip by evaporation, it becomes possible to reduce damages given to the end surface of a laser chip in creation of a protective coating, and to control generation of leakage current in the vicinity of the end surface of the laser chip. Therefore, it becomes possible to improve reliability of a laser device. 0026 However, in the case where the Si film 436 is formed on the main emitting end surface 41a, as shown in FIG. 13, it is possible that Au in the electrode metal film 45 and Si in the protective coating 437 on the end surface react and Au diffuses into the end surface of the main emitting end surface 41a. 0027 If a region where Au and Si react (Au/Si reaction region 438) exists over an emission point 42a (an active layer part) as shown in FIG. 13, it may cause leakage current through the diffused Au (in the end surface), and may affect oscillation characteristics of the semiconductor laser device.

BRIEF DESCRIPTION OF THE INVENTION 0028 According to the present invention, in forming a semiconductor laser device, an electrode comprising Au is patterned so that the electrode does not exist in the vicinity of a light emitting end surface. Thereby, even when an Si film is formed on the light emitting end surface, the Si film is prevented from contacting with the light emitting end surface. 0029 In addition, after patterning the electrode, an insulating film (a silicon nitride film) is formed on the electrode for preventing the Si in the protective coating on the end surface from contacting with Au in the electrode, even when the Si film contacts with a surface of the electrode. 0030 More specifically, the present invention provides a semiconductor laser device, comprising: 0031 an electrode metal film formed on a crystal surface of a semiconductor substrate; and 0032 an Si film formed on a light emitting end surface; 0033 wherein an interval of a specified distance is provided between the electrode metal film and the light emitting end surface. 0034 The semiconductor laser device according to the present invention is useful, in particular, when the electrode metal film comprises Au. 0035 Further, in the semiconductor laser device according to the present invention, an insulating film is further formed on the above electrode metal film. Particularly, in the semiconductor laser device according to the present invention, the insulating film comprises SiNx, Al2O3, SiO2 or TiO2. 0036 In the semiconductor laser device according to the present invention, the interval provided between the electrode metal film and the light emitting end surface is 1 m or more, preferably 3 m or more, more preferably 6 m or more, and most preferably 11 m or more. 0037 The present invention also provides a method for manufacturing a semiconductor laser device, comprising: 0038 a step of forming a p- (or an n-) electrode by forming an ohmic electrode metal film on one crystal surface of a semiconductor laser wafer, forming a bonding electrode metal film thereon, and patterning the electrode metal films; 0039 a step of forming an n- (or a p-) electrode by forming an ohmic electrode metal film on the other crystal surface of the semiconductor laser wafer, forming a bonding electrode metal film thereon, and patterning the electrode metal films; 0040 a step of dividing the semiconductor laser wafer into individual laser bars, each bar comprising a plurality of semiconductor laser chips by scribing cleavage lines on the semiconductor laser wafer; 0041 a step of forming an Si film on a light emitting end surface which appears in the step of dividing the semiconductor laser wafer; and 0042 a step of forming a protective coating on the Si film. 0043 In particular, the present invention also provides a method for manufacturing a semiconductor laser device, comprising: 0044 a step of forming a first type of electrode by forming an ohmic electrode metal film on one crystal surface of a semiconductor laser wafer, forming a bonding electrode metal film thereon, and patterning the electrode metal films; 0045 a step of forming a second type of electrode by forming an ohmic electrode metal film on the other crystal surface of the semiconductor laser wafer, forming a bonding electrode metal film thereon, and patterning the electrode metal films; 0046 a step of dividing the semiconductor laser wafer into individual laser bars, each bar comprising a plurality of semiconductor laser chips by scribing cleavage lines on the semiconductor laser wafer; 0047 a step of forming an Si film on a light emitting end surface which appears in the step of dividing the semiconductor laser wafer; and 0048 a step of forming a protective coating on the Si film, 0049 wherein the first type of electrode and the second type of electrode are different and are either a p-electrode or an n-electrode. 0050 The method for manufacturing the semiconductor laser device according to the present invention is useful, in particular, when the electrode metal film comprises Au. 0051 Further, in the method for manufacturing the semiconductor laser device of the present invention, the electrode metal films are patterned so that an interval between adjoining two p-electrodes and/or an interval between adjoining two n-electrodes are 2 m or more, preferably 6 m or more, more preferably 12 m or more, and most preferably 22 m or more. 0052 That is, according to the method for manufacturing the semiconductor laser device of the present invention, since adjoining two electrodes are disposed on a semiconductor laser wafer at an interval of the above described distance, it becomes possible to eliminate generation of leakage current in the vicinity of the laser end surface and, thus, to manufacture a semiconductor laser device having an improved reliability as a laser device, even when errors occur in the step of patterning an electrode on a semiconductor laser wafer, in the step of scribing the semiconductor laser wafer, or in the step of dividing the semiconductor laser wafer into individual laser bars. 0053 Further, in the method for manufacturing the semiconductor laser device according to the present invention, an insulating film is formed on the electrode metal film prior to forming the Si film. In this case, the insulating film comprises SiNx, Al2O3, SiO2 or TiO2, and preferably the insulating film comprises SiNx. 0054 In addition, the method for manufacturing the semiconductor laser device according to the present invention further comprises a step of alloying the semiconductor laser wafer and the ohmic electrode after the step of forming a p- (or an n-) electrode and the step of forming an n- (or a p-) electrode. 0055 For example, after a p- (or an n-) electrode is patterned, a p-ohmic electrode is alloyed with the semiconductor laser wafer by heating the wafer at 400 to 500 C. and, after an n- (or a p-) electrode is patterned, an n-ohmic electrode is alloyed with the semiconductor laser wafer by heating the wafer at 400 to 500 C.

BRIEF DESCRIPTION OF THE DRAWINGS 0056 The present invention will become more fully understood from the detailed description given hereinbelow and the accompanying drawings which are given by way of illustration only, and thus are not limitative of the present invention, and wherein: 0057 FIGS. 1A and 1B are enlarged cross-sectional views of main light emitting end surfaces of the semiconductor laser device according to a first embodiment (A) and a second embodiment (B) of the present invention; 0058 FIG. 2 is a schematic illustration explaining the exposing accuracy in the manufacturing method according to the present invention; 0059 FIG. 3 is a schematic view showing a wafer of a semiconductor laser device; 0060 FIG. 4 is a schematic illustration explaining the scribing accuracy in the manufacturing method according to the present invention; 0061 FIG. 5 is a schematic view showing a protective coating of the prior semiconductor laser device; 0062 FIG. 6 is a view showing a change in a reflectance relative to a film thickness of the protective coating of the semiconductor laser device of FIG. 5; 0063 FIG. 7 is a schematic view showing a protective coating of the prior high output semiconductor laser device; 0064 FIG. 8 is a schematic view showing a method for forming protective coatings in a semiconductor laser device; 0065 FIG. 9 is a schematic view showing a method for forming protective coatings, continuing from FIG. 8; 0066 FIG. 10 is a schematic view showing a method for forming protective coatings, continuing from FIG. 9; 0067 FIG. 11 is a schematic view showing a vacuum evaporator; 0068 FIG. 12 is a schematic view showing a protective coating of another prior high output semiconductor laser device; and 0069 FIG. 13 is an enlarged cross-sectional view of main light emitting end surfaces of the prior semiconductor laser device.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 0070 The embodiments of the present invention will be described hereinafter in detail with reference to the accompanied drawings. First, the principles of the embodiments will be briefly described. 0071 According to the present invention, in the case where an Si film is formed on a light emitting end surface of a semiconductor laser chip having an electrode comprising Au and, a protective coating having a specified reflectance is formed thereon, the electrode is formed at an interval of a specified distance from the laser emitting end surface in order to prevent the electrode comprising Au and the above Si film from contacting each other. Thereby, Au diffusion into the above Si film may be prevented, and generation of leakage current in the vicinity of the light emitting end surface may be controlled. 0072 That is, the present invention enables to improve reliability of a laser device.

First Embodiment 0073 1. Constitution of the Present Semiconductor Laser Device 0074 An enlarged cross-sectional view of a main emitting end surface of a semiconductor laser device according to a first embodiment of the present invention is depicted in FIG. 1A. In the semiconductor laser device according to the first embodiment of the present invention, a p- (or an n-) electrode 14 comprising an ohmic electrode and a bonding electrode is formed on one crystal surface of a laser wafer and, an n- (or a p-) electrode 15 comprising an ohmic electrode and a bonding electrode is formed on the other crystal surface of the laser wafer. 0075 Particularly, in a semiconductor laser device according to the first embodiment of the present invention, a first type of electrode comprising an ohmic electrode and a bonding electrode is formed on one crystal surface of a laser wafer and, a second type of electrode comprising an ohmic electrode and a bonding electrode is formed on the other crystal surface of the laser wafer, wherein the first type of electrode and the second type of the electrode are different and are either an n-electrode and a p-electrode. 0076 For the sake of simplicity for describing the present invention in the Specification and the Drawings, the ohmic electrode and the bonding electrode are not described separately. However, in practice, an ohmic electrode is formed first on a substrate and a bonding electrode is formed thereon by vacuum evaporating. An ohmic electrode is for ohmic contacting a substrate and a bonding electrode, and a bonding electrode is for enabling buffering and adhesion upon wire-bonding or die bonding. 0077 When a term electrode is simply used herein, it means a combination of ohmic and bonding electrodes. 0078 A protective coating 13a is formed on a main emitting end surface 11a by forming an Si film 136 and forming an Al2O3 protective coating 137 thereon. In FIG. 1A, an emitting end surface 11b on the opposed side to the main emitting end surface 11a is omitted, an edge of an electrode is disposed at a specified distance from the emitting end surface 11b as in the side of the main emitting end surface 11a, and a protective coating 13b is formed like the protective coating 13a. In addition, in the case of a high output type semiconductor laser device, the same protective coating 13b as that shown in FIG. 12 is formed. 0079 In order to prevent the Si film 136 from contacting with electrodes 14 and 15 when the film is formed, ends of the electrodes 14 and 15 are disposed at a specified distance from the emitting end surface of the laser device. If the distance from the ends of the electrodes to emitting end surfaces is 1 m or more, the Si film does not contact with the electrodes when the film is formed by evaporation. Therefore, even when electrodes comprise Au, it is not possible that Si in the Si film reacts with Au to deteriorate reliability of a semiconductor laser device. In addition, the distance from the ends of the electrodes to emitting end surfaces depends on a width of the semiconductor laser device (a cavity length), and is set so as not to cause problems in wire-bonding or die-bonding. For example, when a semiconductor laser device having a cavity with a length of 800 m is die-bonded, no problem arises if the distance from the ends of the electrodes to emitting end surfaces is 200 m or less. 0080 2. A Method of Producing the Semiconductor Laser Device 0081 First, after an n-GaAs substrate is polished, an ohmic electrode and a bonding electrode are formed in this order on one side of crystal surfaces of the substrate by using the conventional technique such as vacuum evaporating, sputtering and the like, and the electrodes are patterned into a p- (or an n-) electrode 14. In this case, an interval between adjoining two electrodes 14 is set to be (2l) m. 0082 After that, the substrate is heated in a furnace heated to 400 to 500 C. under the nitrogen atmosphere to alloy the substrate and the ohmic electrode. Thus, formation of the electrode 14 is completed. 0083 Next, on the other side of the substrate, an ohmic electrode and a bonding electrode are formed to form an electrode 15. Then, the bonding electrode is coated with a photoresist 17. After that, as shown in FIG. 2, the position of the wafer on which the photoresist 17 has been applied is adjusted based on the pattern of the electrode 14 which has been made by using a double-side aligner, and the positioned wafer is exposed to the light. A pattern for forming an electrode 15 is made on the photoresist on the bonding electrode by developing. In this case, an interval between adjoining two electrodes 15 is set to be (2m) m. 0084 Here, since an error in aligning electrode patterns made on the both sides of the wafer is around 10 m, in order to secure a distance of 1 m or more from ends of electrodes 14 and 15 to the emitting end surface after cleaving the wafer along a center line between adjoining two electrodes 14 (or 15) in a subsequent step, either an interval between adjoining two electrodes 14 (2l) or an interval between adjoining two electrodes 15 (2m) is set to be 22 m or more. In this case, the other interval between the other electrodes is set to be 2 m or more. Alternatively, both an interval between adjoining two electrodes 14 (2l) and an interval between adjoining two electrodes 15 (2m) may be set to be 22m or more. 0085 Then, areas of the electrode comprising an Au layer, which are uncovered with the photoresist, is etched by using an iodine etchant, and the photoresist is removed. 0086 Finally, the substrate is heated in a furnace heated to 400 to 500 C. under the nitrogen atmosphere to alloy the substrate and the ohmic electrode. Thus, formation of the electrode 15 is completed. 0087 It is effective that electrodes are patterned prior to alloying the substrate and the electrodes because it is impossible to thoroughly etch the alloyed electrodes with an iodine etchant. 0088 Next, as shown in FIG. 3, a cleavage line 19 is formed by scribing extensively disposed between an electrode 14 of a specified element in a semiconductor laser wafer and an electrode 14 of an adjoining element in a direction orthogonal to an emitting section (channel) 12. In this case, since an error in scribing is around 5 m, in order to secure distances of 1 m or more from ends of electrodes 14 and 15 to the cleaved end surface (l and m), it is necessary to set intervals between adjoining two electrodes (2l) and (2m) to be 12 m or more. 0089 Next, as shown in FIG. 4, the wafer 3 is divided into laser bars 31 by cleaving. In this case, since an error in cleaving is around 2 m, in order to secure a distances of 1 m or more from ends of electrodes 14 and 15 to the cleaved end surface (l and m), it is necessary to set intervals between adjoining two electrodes (2l) and (2m) to be 6 m or more. 0090 Then, in the same procedures as shown in FIG. 10, a plurality of the laser bars 31 obtained by dividing are loaded in a laser bar fixing device 6 such that the electrodes 14 face towards the same side. Further, all the laser bars 31 should be loaded so that all the emitting end surfaces 11a are positioned on the same side and, therefore, all the emitting end surfaces 11b are positioned on the same side. Next, on the emitting end surfaces 11a and 11b of laser bars 31 loaded in the laser bar fixing device 6, a protective coating having a specified reflectance is formed generally by using a vacuum evaporator 7 schematically shown in FIG. 11. The vacuum evaporator 7 is provided with a vapor source 72, a holder 73 for holding a plurality of the laser bar fixing devices 6, and a crystal oscillator 74 for monitoring the thickness of evaporated films, all in a chamber 71. 0091 The following description discusses procedures of forming the protective coating. First, in the case for evaporating a protective coating onto the emitting end surface 11a, the holder 73 is disposed such that the emitting end surface 11a of a laser bar 31 faces the vapor source 72 side as shown in FIG. 11. Then, the chamber 71 is evacuated through a duct 75. After a specified degree of vacuum is obtained, an evaporation material 76 put in the vapor source 72 is heated and evaporated by electron beams and the like so that a protective coating is evaporated onto the emitting end surface 11a of the laser. 0092 Specifically, an Si film 136 with a film thickness of approx. 20 is firstly formed on the light emitting end surface 11a at a film creation speed of 1 /sec or less. Then, an Al2O3 protective coating 137 with a specified film thickness is formed at a film creation speed of 80 /sec or less. The thickness of the Al2O3 protective coating 137 is set so as to obtain a reflectance as low as 15% or less. More particularly, when calculated letting a refractive index of an Al2O3 film be 1.60, a refractive index of a laser chip be 3.50, and an emission wavelength () be 7800 , a coating thickness corresponding to a reflectance of approx. 15% or less is about 700 to 1600 (see FIG. 6). 0093 As described above, a protective coating 13a is formed. After formation of the protective coating 13a is completed, the holder 73 is then rotated 180 for evaporating a protective coating onto the emitting end surface 11b based on the same procedures. 0094 Although not shown in FIG. 1, in the case of a high output type semiconductor laser device, a low reflecting protective coating 13a (having a reflectance of approx. 15% or less) is formed on the side of the main emitting end surface 11a, and then a multilayered high reflecting protective coating 13b is formed on the side of the rear emitting end surface 11b. 0095 The multilayered high reflecting protective coating 13b is composed of a laminated structure made up of: a first layer 131 and a third layer 133, each consisting of an Al2O3 film with a thickness equal to /4; a second layer 132 and a fourth layer 134, each consisting of an Si film with a thickness equal to /4; and a fifth layer 135 consisting of an Al2O3 film with a thickness equal to /2. For evaporation of this film, Al2O3 and Si are mounted on the vapor source 72 as evaporation materials 76. Then the first layer 131, the third layer 133, and the fifth layer 135, each consisting of an Al2O3 film, are evaporated through irradiation of the evaporation material Al2O3 with electron beams, and the second layer 132 and the fourth layer 134, each consisting of an Si film, are evaporated through irradiation of the evaporation material Si with electron beams. 0096 Here, a forming speed (evaporation rate) for forming a protective coating on the both light emitting end surfaces 11a and 11b is controlled so as to be approximately constant till completion of evaporation. The evaporation rate is in this case controlled with a heating temperature. In the case of electron beam evaporation, therefore, the evaporation rate may be controlled with the intensity of electron beams. It is well known that in the case of resistance heating, the evaporation rate is controlled with an amount of electric current passed through a resistor. The evaporation rate is generally set in a range between several /sec to 30 /sec in the case of the evaporation material of Al2O3. Evaporation is conducted while coating thickness is monitored with use of the crystal oscillator 74. Evaporation is terminated when a prescribed coating thickness is obtained.

Second Embodiment 0097 1. Constitution of the Present Semiconductor Laser Device 0098 An enlarged cross-sectional view of a main emitting end surface of a semiconductor laser device according to a second embodiment of the present invention is depicted in FIG. 1B. As in the semiconductor laser device according to the first embodiment of the present invention, a p- (or an n-) electrode 14 comprising an ohmic electrode and a bonding electrode is formed on one crystal surface of a laser wafer and, an n- (or a p-) electrode 15 comprising an ohmic electrode and a bonding electrode is formed on the other crystal surface of the laser wafer. 0099 Particularly, in a semiconductor laser device according to the second embodiment of the present invention, a first type of electrode comprising an ohmic electrode and a bonding electrode is formed on one crystal surface of a laser wafer and, a second type of electrode comprising an ohmic electrode and a bonding electrode is formed on the other crystal surface of the laser wafer, wherein the first type of electrode and the second type of the electrode are different, and are either an n-electrode and a p-electrode. 0100 Ends of these electrodes are disposed at a specified distance from an emitting end surface as in the semiconductor laser device according to the first embodiment of the present invention. 0101 In the semiconductor laser device according to the second embodiment of the present invention, an insulating film 16 comprising silicon nitride and the like is further formed on the electrode 15. 0102 As in the semiconductor laser device according to the first embodiment of the present invention, a protective coating 13a is formed on a main emitting end surface 11a by forming an Si film 136 and forming an Al2O3 protective coating 137 thereon. In FIG. 1A, an emitting end surface 11b on the opposed side to the main emitting end surface 11a is omitted, an end of an electrode is disposed at a specified distance from the emitting end surface 11b as in the side of the main emitting end surface 11a, and a protective coating 13b is formed like the protective coating 13a. In addition, in the case of a high output type semiconductor laser device, the same protective coating 13b as that shown in FIG. 12 is formed. 0103 As described above, since the insulating film 16 is formed on the electrode 15, the Si film 136 never contact directly with the electrode 15 even when the Si film contacts with the electrode 15, in some cases, in forming the film. Therefore, even when the electrode 15 comprises Au, since Au diffusion into an end surface by reaction of Au and Si is prevented, generation of leakage current in the vicinity of the light emitting end surface can be controlled, leading to improved reliability of a laser device. 0104 2. A Method of Producing the Semiconductor Laser Device 0105 In the semiconductor laser device according to the second embodiment of the present invention, electrodes 14 and 15 are formed by patterning and alloying based on the same procedure as those for manufacturing the semiconductor laser device according to the first embodiment of the present invention. Then, an SiNx insulating film 16 having a thickness of 0.3 to 0.4 m is formed on the electrode 15 by plasma chemical vapor deposition. The insulating film 16 may comprise not only SiNx, but also Al2O3, SiO2 or TiO2. 0106 After that, according to the same procedures as those for producing the semiconductor laser device of the first embodiment, cleavage lines are formed to divide into laser bars 31. 0107 Further, after a protective coating is formed on an end surface based on the same procedures as those for the first embodiment, the end surface is protected with a resist film according to the conventional technique for protecting an end surface with a resist film, and the insulating film SiNx on the electrode is etched with BHF. 0108 The invention being thus described according to the above embodiments, it will be obvious that the same may be varied in many ways. For example, in the case where an Si film is applied as a fist layer of an end surface on the other side opposing to a main emitting end surface, it is also effective that ends of the electrodes are disposed at a specified distance from the end surface. 0109 Such variations are not to be regarded as a departure from the spirit and scope of the invention, and all such modifications as would be obvious to one skilled in the art are intended to be included within the scope of the following claims.