Exemplary thickening agents are added to control the viscosity of the binder compositions that are ultimately cured to make the adhesive binder component of the fiber product. The thickening agents may be polymeric materials and may be partially or fully water soluble. They are selected to enhance the binder compositions rheological properties (e.g., increase the composition's viscosity and surface tension) without substantially interfering with the composition's curability into an adhesive binder for the substrate fibers. Exemplary thickening agents may include polysaccharides, such as xanthan gum, guar gum, modified starches and the like; neutralized polyacrylic acid, such as sodium polyacrylate, modified celluloses, such as hydroxyethyl cellulose (HEC), carboxymethyl cellulose (CMC), as well as their soluble salts, polyacrylamides, and polyvinyl alcohols. The exemplary thickening agents may have a weight average molecular weight typically from 100,000 to 2,000,000 g/mol (e.g., 200,000 to 1,000,000 g/mol). The thickening agent (or agents) are typically added to the binder composition prior to its deposition on the fiber substrate, or alternatively may be added separately and approximately simultaneously with the other components of the binder composition to the fiber substrate.

The concentration of thickening agent in the binder composition may depend in part on the concentration of the other binder components in the composition. The carbohydrate binder compositions may be aqueous mixtures or solutions, and their viscosities depend in part on the how much the polymer precursors have been diluted by the water. For example, some concentrated binder compositions (e.g., solids concentrations of 45 to 70 wt. % or more) may have viscosities in the hundreds of centipoise at room temperature. The concentrated resins are typically diluted with water to, for example, a solids concentration of 10 to 30 wt. % solids (e.g., 10 to 20 wt. solids), reducing the binder composition's viscosity to less than 3 cPs at room temperature. Other binder compositions may have functional viscosities at high concentrations (e.g., 20 cPs at 50 wt. % solids concentration) but should be diluted to address processing challenges such as LOI, weight, and uniformity problems for the applied binder composition.

Thickening agents may be added to increase the viscosity of the aqueous binder composition to a range of 7 to 50 cPs at room temperature (i.e., 20° C.), as measured by a Brookfield viscometer operating at a speed of 60 revolutions per minute. Typically, binder composition viscosities in this range can be achieved at thickening agent concentrations between 0.03 to 0.3 wt. % of the total composition. The concentration range of thickening agent can depend on the type of agent used. For example, adding hydroxyethyl cellulose to a concentration range of 0.05 to 0.3 wt. % may be sufficient to increase the composition's viscosity into a 7 to 50 cPs range. The same viscosity range may be met by adding 0.03 wt. % to 0.2 wt. % xanthan gum to the aqueous binder composition.

In addition to the thickening agents, the binder compositions may also contain a surfactant that provides more precise control over the surface tension of the composition. The surfactant may be added in amounts to achieve a surface tension for the binder composition of 35 to 50 mN/m (e.g., 38 to 48 mN/m, 40 to 47 mN/m, etc.). These surfactants may include cationic, anionic, and/or non-ionic surfactants.

The binder formulations of the binder compositions may include one or more types of carbohydrates and nitrogen-containing compounds. The nitrogen-containing compounds may act as crosslinking agents for the carbohydrates in the cured binder. The carbohydrates used in the binder formulations may include reducing sugars that contain at least one aldehyde group, or are capable of forming an aldehyde group through isomerization. Exemplary reducing sugars may include glucose (dextrose), fructose, glyceraldehyde, galactose, allose, xylose, ribose, maltose, cellobiose, and lactose, among others.

The nitrogen-containing compounds may include a variety of compounds that can distinguish the class of binder formulation. One class of binder formulations uses an amino-amide as the nitrogen containing compound, which itself is a reaction product of an amine with a saturated or unsaturated reactant. Another class of binder formulations has as the nitrogen-containing compound a reaction product of a urea compound and aldehyde-containing compound. Each of these classes of nitrogen-containing compounds are described more detail below.

1. Carbohydrate/Amino-Amide Binder Formulations

The nitrogen-containing compounds may include amines capable of undergoing conjugate addition with a saturated or unsaturated reactant to form an amino-amide. The amino-amide then reacts during curing with the carbohydrate to form a polyimide. The amino-amide addition products may be formed by mixing the amine and saturated or unsaturated reactant in an aqueous medium at room temperature. The resulting addition products are either water-soluble, water-dispersible, or are present as an emulsion. In some binder formulations, the formation of the amino-amide from the reaction of the amine precursor with the saturated or unsaturated reactant may occur before the introduction of the carbohydrate, while other formulations mix all three precursors (i.e., the amine, saturated or unsaturated reactant, and carbohydrate) before the amino-amide is formed.

Each amine may have two or more primary and/or secondary amine groups to react and crosslink two or more carbohydrate molecules. The amines may include aliphatic, cycloaliphatic and aromatic amines. They may be linear or branched, and have additional functionalities and linkages such as alcohols, thiols, esters, amides, acids, and ethers, among others. Exemplary amines may include 1,2-diethylamine, 1,3-propanediamine, 1,4-butanediamine, 1,5-pentanediamine, 1,6-hexanediamine, diaminoxylene, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, as well as combinations of two or more of these amines. Natural and synthetic amino acids such as lysine, anginine, hestidine, etc., may also be used.

The curable amino-amide is formed through the selection of an unsaturated or saturated reactant that is an anhydride, carboxylic acid, ester, and salts and mixtures of such reactants. These unsaturated reactants may include maleic acid, fumaric acid, maleic anhydride, mono- and di-esters of maleic acid and fumaric acid, and salts and mixtures of these. Ammonium salts of the unsaturated acids of their monoesters conveniently can be utilized. Saturated reactants may include, without limitation, succinic anhydride, succinic acid, mono and diesters of succinic acid, glutaric acid and anhydride, phthalic acid and anhydride, tetrahydro phthalic acid and anhydride, mono and diesters of acid anhydrides and salts of the acids, and their mono esters.

In some formulations, the amino-amide product may be oligomerized before reacting with the carbohydrate. This oligomerization may be facilitated by heating the amino-amide solution until the amino-amide is dimerized, trimerized, tetramerized, etc., into the amino-amide oligomer. The heating conditions may include raising the temperature of the amino-amide solution to, for example, 120° C. to 150° C. for a time of up to 5 hours. In some instances, the oligomerized amino-amide product forms a stronger, more rigid cured binder product than then amino-amide monomer.

Then during the binder curing step, the majority of the carbohydrate reacts with the amino-amide intermediate, which contains an amic acid functional group, (i.e., an amide linkage in the vicinity of a carboxylic acid). An amic acid functional group is typically more reactive than a simple carboxylic acid. The amount of carbohydrate added is generally such that the molar ratio of carboxylic acid in the amino-amide to carbonyl or ketone in the carbohydrate is from 1:5 to 50:1, for example a ratio of 1:20 to 20:1, or a ratio of 1:10 to 10:1. Additional details about carbohydrate/amino-amide binder formulation are described in co-assigned U.S. patent application Ser. No. 12/539,263 to Shooshtari et al, filed Aug. 11, 2009, and titled “Curable Fiberglass Binder,” the entire contents of which are herein incorporated by reference for all purposes.

2. Carbohydrate/Urea Derivative Binder Formulations

The nitrogen-containing compounds may include urea derivative reaction products of urea (i.e., H₂N—CO—NH₂), and/or substituted ureas, with diformaldehyde compounds such as glyoxal. One specific class of these urea derivatives include imidazolidine compounds such as 4,5-dihydroxyimidazolidin-2-one, which has the chemical structure:

[Image Omitted]

4,5-dihydroxyimidazolidin-2-one

More specifically, the urea compound may be a substituted or unsubstituted urea having the formula:

[Image Omitted]

where R₁, R₂, R₃, and R₄are independently chosen from a hydrogen moiety (H), an alkyl group, an aromatic group, an alcohol group, an aldehyde group, a ketone group, a carboxylic acid group, and an alkoxy group. Exemplary alkyl groups include straight-chained, branched, or cyclic hydrocarbons of varying size (e.g., C₁-C₁₂, C₁-C₈, C₁-C₄, etc.). Exemplary aromatic (i.e., aryl) groups include substituted or unsubstituted phenyl moieties, among other aromatic constituents. Exemplary alcohol groups include —ROH, where R may be a substituted or unsubstituted, saturated or unsaturated, branched or unbranched, cyclic or acyclic, organic moiety. For example, R may be —(CH₂)_n, —, where n may be 1 to 12. Exemplary alcohols may also include polyols having two or more hydroxyl groups (—OH) in alcohol group. Exemplary aldehyde groups include —RC(═O)H, where R may be a monovalent functional group (e.g., a single bond), or a substituted or unsubstituted, saturated or unsaturated, branched or unbranched, cyclic or acyclic, organic moiety, such as —(CH₂), —, where n may be 1 to 12. Exemplary ketone groups may include —RC(═O)R′ where R and R′ can be variety of carbon containing constituents. Exemplary carboxylic acid groups may include —R—COOH, where R may be a monovalent functional group, such as a single bond, or a variety of carbon-containing constituents. Exemplary alkoxy groups include —OR_x, where R_xis an alkyl group.

The aldehyde-containing compound may contain one or more aldehyde functional groups. Exemplary aldehyde-containing compounds include acetaldehyde, propanaldehyde, butyraldehyde, acrolein, furfural, glyoxal, gluteraldehyde, and polyfurfural among others. Exemplary aldehyde-containing compounds may also include substituted glyoxal compounds having the formula:

[Image Omitted]

where R₅and R₆may be independently hydrogen (H), an alkyl group, an aromatic group, an alcohol group, an aldehyde group, a ketone group, a carboxylic acid group, and an alkoxy group, among other groups.

The reaction products of the urea compound and the aldehyde-containing compound may include an imidazolidine compound having the formula:

[Image Omitted]

where R₇, R₈, R₉, and R₁₀are independently, —H, —OH, —NH₂, an alkyl group, an aromatic group, an alcohol group, an aldehyde group, a ketone group, a carboxylic acid group, and an alkoxy group. In one specific example of the reaction between urea and glyoxal, the reaction product may be 4,5-dihydroxyimidazolidin-2-one.

The carbohydrate/urea derivative binder formulations may also include one or more catalysts to increase the rate of the crosslinking reactions between the carbohydrates and crosslinking agents when the composition is exposed to curing conditions. Exemplary catalysts may include alkaline catalysts and acidic catalysts. The acidic catalysts may include Lewis acids (including latent acids and metallic salts), as well as protic acids, among other types of acid catalysts. Lewis acid catalysts may include a salt of a deprotonized anion such as a sulfate, sulfite, nitrate, nitrite, phosphate, halide, or oxyhalide anion in combination with one or more metallic cations such as aluminum, zinc, iron, copper, magnesium, tin, zirconium, and titanium. Exemplary Lewis acid catalysts include aluminum sulfate, ferric sulfate, aluminum chloride, ferric chloride, aluminum phosphate, ferric phosphate, and sodium hypophosphite (SHP), among others. Exemplary latent acids include acid salts such as ammonium sulfate, ammonium hydrogen sulfate, mono and dibasic ammonium phosphate, ammonium chloride, and ammonium nitrate, among other latent acid catalysts. Exemplary metallic salts may include organo-titanates and organo-zirconates (such as those commercially manufactured under the tradename Tyzor® by DuPont), organo-tin, and organo-aluminum salts, among other types of metallic salts. Exemplary protic acids include sulfuric acid, phosphoric acid, hydrochloric acid, nitric acid, sulfonic acid compounds (i.e., R—S(═O)₂—OH) such as p-toluenesulfonic acid and methanesulfonic acid, and carboxylic acids, among other protic acids. Catalyst compositions may also include combinations of two or more catalysts, for example the combination of ammonium sulfate and diammonium phosphate.

The pH of the present binder compositions may vary depending upon the types and relative concentrations of the components used. Typically the pH of the present binder compositions are slightly acidic to alkaline with a pH range of about 6 to 8 (e.g., 6.5 to 7.5). The binder compositions have a pH that creates relatively little or no acid-based corrosion of metal fabrication equipment.

The reaction product of the urea derivative nitrogen-containing compound acts as a crosslinking agent for the carbohydrate. During a curing stage, the urea derivative can bond to two or more carbohydrates (either polymerized or unpolymerized) to form a crosslinked, polymeric cured binder.

The molar ratio of the (1) crosslinking reaction product of the urea compound and the aldehyde-containing compound to (2) the carbohydrate generally ranges from 1:2 to 1:50. Exemplary ratios of crosslinking agent to carbohydrate include a range from 1:4 to 1:10. Additional details about carbohydrate/urea derivative binder formulations are described in co-assigned U.S. patent application Ser. No. 13/490,638 to Shooshtari et al, filed Jun. 7, 2012, and titled “Formaldehyde-Free Binder Compositions with Urea-Formaldehyde Reaction Products,” the entire contents of which are herein incorporated by reference for all purposes.

3. Carbohydrate/Nitrogen-Containing Salt Binder Formulations

i. Salts of Inorganic Acids with Amines

In additional carbohydrate binder formulations, the nitrogen-containing compounds may include a nitrogen-containing salt. For example, the nitrogen-containing compound may include the salt product of the combination of an inorganic acid and an amine (e.g., an amine-acid salt). Exemplary inorganic acids may include a phosphorous-containing acid such as phosphoric acid, pyrophosphoric acid, phosphorous acid, and phosphine, among others. Exemplary inorganic acids may also include oxygenated inorganic acids such as sulfuric acid, sulfurous acid, nitric acid, boric acid, hypochloric acid, chlorate acid, among others. They may also include non-oxygenated inorganic acids such as hydrochloric acid and hydrogen sulfide, among others.